CN101404396A - 双层热收缩套管 - Google Patents

双层热收缩套管 Download PDF

Info

Publication number
CN101404396A
CN101404396A CNA2008100365999A CN200810036599A CN101404396A CN 101404396 A CN101404396 A CN 101404396A CN A2008100365999 A CNA2008100365999 A CN A2008100365999A CN 200810036599 A CN200810036599 A CN 200810036599A CN 101404396 A CN101404396 A CN 101404396A
Authority
CN
China
Prior art keywords
layer
double
flame retardant
heat shrinkable
crystal type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008100365999A
Other languages
English (en)
Other versions
CN101404396B (zh
Inventor
王志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CYG Electronics Shanghai Co Ltd
Original Assignee
CYG Electronics Shanghai Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CYG Electronics Shanghai Co Ltd filed Critical CYG Electronics Shanghai Co Ltd
Priority to CN2008100365999A priority Critical patent/CN101404396B/zh
Publication of CN101404396A publication Critical patent/CN101404396A/zh
Application granted granted Critical
Publication of CN101404396B publication Critical patent/CN101404396B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种双层热收缩套管，包括连成一体的外层和内层，外层为结晶型改性聚烯烃材料层，内层为阻燃型热熔胶层。采用本发明的双层热收缩套管用作汽车电线的套管，能够有效防止铜腐蚀以及热氧老化，能够对汽车线束接点和端子进行有效密封绝缘，有效的防止潮湿环境下汽车电线端子及接头被腐蚀，能够对电线端子接头进行耐磨、耐油、阻燃保护。

Description

双层热收缩套管
技术领域
本发明涉及一种汽车电线用套管，特别涉及一种双层热收缩套管。
背景技术
热收缩材料，又称高分子形状记忆材料。这些材料辐射交联以后具有记忆效应。所谓“记忆效应”，简单说就是交联聚合物材料，高温时在外力作用下扩张，冷却后能保持住扩张时形态，继续加热后又能回复扩张前形态。热收缩材料广泛应用在电子、电力、工矿设施、船舶、航天航空、汽车等重要领域。随着中国经济的迅速发展，国内汽车制造业也迅猛地发展，汽车线束及管路用热缩套管得到了较大的发展。这种热缩套管的质量影响到整个汽车的性能和质量，热缩套管的性能和质量主要表现在其绝缘性、密封性、阻燃性、耐磨性和耐油保护性能等方面。现有技术的热缩套管由于在生产中所采用的材料组成存在一定的问题，其性能和质量好存在一定的缺陷，例如汽车电线端子及接头易老化，绝缘性不好产生短路导致一些燃烧事故的发生等，从而造成一定数量的人身及财产损失。
发明内容
本发明的目的，在于克服上述现有技术存在的问题，提供一种采用新型材料的双层热收缩套管。
本发明的目的是这样实现的：一种双层热收缩套管，包括连成一体的外层和内层，所述的外层为结晶型改性聚烯烃材料层，它由下列物质按所附重量份制备而成：
热塑性聚烯烃    100份，
阻燃剂          25-60份，
抗氧剂          1-5份，
润滑及加工助剂    1-6份，
黑色色母          4-8份，
交联助剂          1-3份；
所述的内层为阻燃型热熔胶层，它由下列物质按所附重量份制备而成：
聚酰胺热熔胶    100份，
阻燃助剂        8-15份，
抗氧剂          0.5-1.5份。
所述的用于制备结晶型改性聚烯烃材料层的阻燃剂由无机阻燃剂10-20份和有机阻燃剂15-40份组成，无机阻燃剂选自氢氧化铝或氢氧化镁，有机阻燃剂为十溴二苯乙烷。
所述的用于制备结晶型改性聚烯烃材料层的抗氧剂选自季戊四醇酯、硫代二丙酸二月桂酯、硫代二丙酸十八酯、N，N，-二(2-萘基)对苯二胺、2-硫醇基苯并咪唑和2，2，4-三甲基-1，2-二轻化喹啉聚合体中的一种。
所述的用于制备结晶型改性聚烯烃材料层的润滑及加工助剂选自PE蜡和硅树脂中的一种。
所述的用于制备结晶型改性聚烯烃材料层的交联助剂选自三烯丙基异氰尿酸酯、三羟甲基丙烷三丙烯酸脂和三羟甲基丙烷三甲基丙烯酸酯中的一种。
所述的用于制备阻燃型热熔胶层的阻燃助剂为十溴二苯乙烷和三氧化二锑的混合物。
所述的用于制备阻燃型热熔胶层的抗氧剂选自N，N′-双[3-(3，5-二叔丁基-4-羟基苯基)丙酰]肼、季戊四醇酯、硫代二丙酸二月桂酯和硫代二丙酸十八酯中的一种。
采用本发明的双层热收缩套管用作汽车电线的套管，能够有效防止铜腐蚀以及热氧老化，能够对汽车线束接点和端子进行有效密封绝缘，有效的防止潮湿环境下汽车电线端子及接头被腐蚀，能够对电线端子接头进行耐磨、耐油、阻燃保护。同时本发明中的配方设计符合国际环保标准，符合当前国际化倡导的绿色环保汽车的要求。
具体实施方式
实施例1
首先取热塑性聚烯烃100公斤、氢氧化铝15公斤、十溴二苯乙烷20公斤、季戊四醇酯3公斤、PE蜡3公斤、黑色色母4公斤、三烯丙基异氰尿酸酯2公斤混配造粒得到结晶型改性聚烯烃粒料。另取聚酰胺热熔胶100公斤、十溴二苯乙烷和三氧化二锑的混合物10公斤、N，N′-双[3-(3，5-二叔丁基-4-羟基苯基)丙酰]肼1公斤混配造粒得到阻燃型热熔胶粒料。然后将上述结晶型改性聚烯烃粒料置于外层、阻燃型热熔胶粒料置于内层，通过特殊设备熔融共挤成型，得到外层为结晶型改性聚烯烃材料层、内层为阻燃型热熔胶层的双层套管。最后将双层套管经高能伽玛射线辐照后扩张定型，即得到本发明的一种双层热收缩套管。
实施例2
首先取热塑性聚烯烃100公斤、氢氧化镁10公斤、十溴二苯乙烷30公斤、硫代二丙酸二月桂酯4公斤、硅树脂4公斤、黑色色母5公斤、三羟甲基丙烷三丙烯酸脂1公斤混配造粒得到结晶型改性聚烯烃粒料。另取聚酰胺热熔胶100公斤、十溴二苯乙烷和三氧化二锑的混合物12公斤、季戊四醇酯0.8公斤混配造粒得到阻燃型热熔胶粒料。然后将上述结晶型改性聚烯烃粒料置于外层、阻燃型热熔胶粒料置于内层，通过特殊设备熔融共挤成型，得到外层为结晶型改性聚烯烃材料层、内层为阻燃型热熔胶层的双层套管。最后将双层套管经高能伽玛射线辐照后扩张定型，即得到本发明的一种双层热收缩套管。
实施例3
首先取热塑性聚烯烃100公斤、氢氧化铝20公斤、十溴二苯乙烷15公斤、硫代二丙酸十八酯2公斤、PE蜡6公斤、黑色色母8公斤、三羟甲基丙烷三甲基丙烯酸酯3公斤混配造粒得到结晶型改性聚烯烃粒料。另取聚酰胺热熔胶100公斤、十溴二苯乙烷和三氧化二锑的混合物15公斤、硫代二丙酸二月桂酯1.5公斤混配造粒得到阻燃型热熔胶粒料。然后将上述结晶型改性聚烯烃粒料置于外层、阻燃型热熔胶粒料置于内层，通过特殊设备熔融共挤成型，得到外层为结晶型改性聚烯烃材料层、内层为阻燃型热熔胶层的双层套管。最后将双层套管经高能伽玛射线辐照后扩张定型，即得到本发明的一种双层热收缩套管。
实施例4
首先取热塑性聚烯烃100公斤、氢氧化镁18公斤、十溴二苯乙烷40公斤、N，N，-二(2-萘基)对苯二胺5公斤、硅树脂1公斤、黑色色母6公斤、三烯丙基异氰尿酸酯1.5公斤混配造粒得到结晶型改性聚烯烃粒料。另取聚酰胺热熔胶100公斤、十溴二苯乙烷和三氧化二锑的混合物8公斤、硫代二丙酸十八酯0.5公斤混配造粒得到阻燃型热熔胶粒料。然后将上述结晶型改性聚烯烃粒料置于外层、阻燃型热熔胶粒料置于内层，通过特殊设备熔融共挤成型，得到外层为结晶型改性聚烯烃材料层、内层为阻燃型热熔胶层的双层套管。最后将双层套管经高能伽玛射线辐照后扩张定型，即得到本发明的一种双层热收缩套管。

Claims (7)

1、一种双层热收缩套管，包括连成一体的外层和内层，其特征在于：所述的外层为结晶型改性聚烯烃材料层，它由下列物质按所附重量份制备而成：
热塑性聚烯烃        100份，
阻燃剂              25-60份，
抗氧剂              1-5份，
润滑及加工助剂      1-6份，
黑色色母            4-8份，
交联助剂            1-3份；
所述的内层为阻燃型热熔胶层，它由下列物质按所附重量份制备而成：
聚酰胺热熔胶        100份，
阻燃助剂            8-15份，
抗氧剂              0.5-1.5份。
2、如权利要求1所述的双层热收缩套管，其特征在于：所述的用于制备结晶型改性聚烯烃材料层的阻燃剂由无机阻燃剂10-20份和有机阻燃剂15-40份组成，无机阻燃剂选自氢氧化铝或氢氧化镁，有机阻燃剂为十溴二苯乙烷。
3、如权利要求1所述的双层热收缩套管，其特征在于：所述的用于制备结晶型改性聚烯烃材料层的抗氧剂选自季戊四醇酯、硫代二丙酸二月桂酯、硫代二丙酸十八酯、N，N，-二(2-萘基)对苯二胺、2-硫醇基苯并咪唑和2，2，4-三甲基-1，2-二轻化喹啉聚合体中的一种。
4、如权利要求1所述的双层热收缩套管，其特征在于：所述的用于制备结晶型改性聚烯烃材料层的润滑及加工助剂选自PE蜡和硅树脂中的一种。
5、如权利要求1所述的双层热收缩套管，其特征在于：所述的用于制备结晶型改性聚烯烃材料层的交联助剂选自三烯丙基异氰尿酸酯、三羟甲基丙烷三丙烯酸脂和三羟甲基丙烷三甲基丙烯酸酯中的一种。
6、如权利要求1所述的双层热收缩套管，其特征在于：所述的用于制备阻燃型热熔胶层的阻燃助剂为十溴二苯乙烷和三氧化二锑的混合物。
7、如权利要求1所述的双层热收缩套管，其特征在于：所述的用于制备阻燃型热熔胶层的抗氧剂选自N，N′-双[3-(3，5-二叔丁基-4-羟基苯基)丙酰]肼、季戊四醇酯、硫代二丙酸二月桂酯和硫代二丙酸十八酯中的一种。
CN2008100365999A 2008-04-24 2008-04-24 双层热收缩套管 Active CN101404396B (zh)