CN101376587B - 金砖书写板制备方法 - Google Patents
金砖书写板制备方法 Download PDFInfo
- Publication number
- CN101376587B CN101376587B CN2008101562706A CN200810156270A CN101376587B CN 101376587 B CN101376587 B CN 101376587B CN 2008101562706 A CN2008101562706 A CN 2008101562706A CN 200810156270 A CN200810156270 A CN 200810156270A CN 101376587 B CN101376587 B CN 101376587B
- Authority
- CN
- China
- Prior art keywords
- writing board
- base substrate
- gold brick
- major ingredient
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明的目的是提供一种金砖书写板的制作方法，以该方法制作的金砖书写板敲之有声、断之无孔、颗粒细腻、吸水透气，其包括以下步骤：采取阳澄湖湖底下8m-12m深处的澄泥，晾晒后粉碎，用筛子筛除大于1mm部分，得到主料；把下述成份按重量比配制成物料：主料80-100，无定形二氧化硅15-20，三氧化二铝20-30，水泥15-25；水20-30；将上述物料置于模具中制成坯体；将坯体在加热炉中加热，温度400-500℃，时间2-3小时；将烧制后坯体置于空气中自然冷却。
Description
技术领域
本发明涉及一种书写板的制备方法，具体地说，是一种金砖书写板制备方法。
背景技术
所谓″金砖″，实际上是规格为二尺二、二尺、一尺七等见方的不同大小的方砖的雅称。古籍《金砖墁地》有这样的解释：″专为皇宫烧制的细料方砖，颗粒细腻，质地密实，敲之有金石之声，称’金砖’；又因砖运北京’京仓’，供皇宫专用，称之’京砖’，后逐步演化称’金砖’。″
金砖御窑位于江苏省苏州市相城区陆慕镇御窑村，御窑村原名余窑村，千百年来当地村民烧制砖瓦的传统世代相袭。
陆墓(今作陆慕)，在苏州齐门外北八里，临元和塘两岸，东濒阳澄湖。由于陆慕镇的黄泥适宜制坯成砖，且做工考究、烧制有方、技艺独特，所产金砖细腻坚硬，″敲之有声，断之无孔″，所以明永乐皇帝赐封陆慕砖窑为″御窑″。现在北京故宫的太和殿、中和殿、保和殿、天安门城楼以及十三陵之一的定陵内所铺设的就是御窑金砖，这些大方砖上尚有明永乐、正德，清乾隆等年号和″苏州府督造″等印章字样。
御窑金砖是我国窑砖烧制业中的一朵奇葩，明清以来受到历代帝王的青睐，成为皇宫建筑的专用产品。到明代嘉靖时，金砖烧制进入全盛期。清朝末年以后，因战争连年，金砖的生产时断时续，随之消失。
金砖除用作地砖、墙砖以外，还可用作书写板(书写介质)。用作书写板时，一般是用毛笔蘸水在其上书写；夏天时书写的水迹挥发的时间约5-10分钟；冬天约10-20分钟。如果用墨汁书写，将永久保存墨迹。
发明内容
本发明的目的是提供一种金砖书写板的制作方法，以该方法制作的金砖书写板敲之有声、断之无孔、颗粒细腻、吸水透气。
该金砖书写板制备方法，包括以下步骤：
制主料：采取阳澄湖湖底下8-12m深处的澄泥，把澄泥晾晒后粉碎，用筛子筛除大于1mm部分，得到主料；
配物料：把下述成份按重量比配制成物料并拌匀：主料80-100，无定形二氧化硅15-20，三氧化二铝20-30，水泥15-25；水20-30；
制坯：将上述物料置于模具中，以2-5kg/cm2压力踩踏成坯体；
烧制：将坯体在加热炉中加热，温度400-500℃，时间2-3小时；
冷却：将烧制后坯体置于空气中自然冷却。
阳澄湖位于苏州市区的东北，跨苏州市区、工业园区、昆山市及常熟市，是江苏省重要的淡水湖泊之一。面积120平方公里。阳澄湖活水性较好，水体清澄，透明度高，平均值为133厘米，含钙、镁、硅、铝氧比值高。湖底底质好，硬地占65％以上，表层多数是沙质澄泥。阳澄湖水特别清澈温软，这种温软饱满的水滋养的泥土也特别粘糯柔润，以这种柔润细腻的泥土烧造出来的金砖质地也特别精良。
本发明中，不易采用湖底8m范围内的澄泥，因为湖底的8m的范围内，水草的根须太多，含水率高，动植物的排泄物过多。超过湖底12m的澄泥，含水量底，结块严重。湖底下8-12m深处的澄泥，粘性好，含水适中。
二氧化硅，是一种坚硬难溶的固体。天然的二氧化硅分为晶态和无定形两大类，晶态二氧化硅主要存在于石英矿中。无定形二氧化硅为白色固体或粉末。化学性质很稳定。不溶于水也不跟水反应，性质不活泼。添加适当的二氧化硅，可使得坯体的热稳定性较好，减少坯体的膨胀炸裂。
三氧化二铝也就是氧化铝。纯净氧化铝是白色无定形粉末，俗称矾土，熔点2050℃，密度3.9-4.0g/cm3，沸点2980℃，不溶于水，为两性氧化物，能溶于无机酸和碱性溶液中。添加适当的三氧化二铝，可使得坯体的骨架强度增加，使得坯体的烧结范围变宽。
水泥是作为粘接剂的。
本发明把澄泥晾晒后粉碎，用筛子筛除大于1mm部分，并采用无定形二氧化硅和二氧化硅，保证了产品颗粒细腻。
制坯时，适于以2-5kg/cm2压力踩踏制成。
烧制时一般温度400-500℃，时间2-3小时。温度过高，产品会变形；温度过低，不但烧不透，强度也不高，易碎。
本发明是一种金砖书写板的制作方法，该方法制作的金砖书写板敲之有声、断之无孔、颗粒细腻、吸水透气，使得传统工艺被″复活″。该金砖书写板黛青光滑，古朴坚实，面平如砥象一方黛玉，光滑似镜若一块乌金，敲击时还会发出金属般铿锵之声，具有较高的实用价值和收藏价值。
上述金砖书写板制备方法，采取阳澄湖湖底下10m深处的澄泥。
上述金砖书写板制备方法，物料中各成份的重量比：主料90，无定形二氧化硅18，三氧化二铝25，水泥20；水26。
上述金砖书写板制备方法，坯体大小为60cm*60cm*5cm，加热时温度为470℃，时间2.5小时。
上述金砖书写板制备方法，坯体大小为40cm*40cm*3cm，加热时温度为430℃，时间2.5小时。
具体实施方式
实施例1：
按下述步骤制备金砖书写板：
制主料：采取阳澄湖湖底下8-9m深处的澄泥，把澄泥晾晒后粉碎，用筛子筛除大于1mm部分，得到主料；
配物料：把下述成份按重量比配制成物料并拌匀：主料90，无定形二氧化硅18，三氧化二铝25，水泥20；水26；
制坯：将上述物料置于模具中，以人工踩踏成坯体，压力大约为2-4kg/cm2；坯体大小为60cm*60cm*5cm；
烧制：将坯体在加热炉中加热，温度为470℃，时间2.5小时；
冷却：将烧制后坯体置于空气中自然冷却得成品。
在该制成的金砖书写板上夏天时书写的水迹挥发的时间约8-10分钟；冬天约15-20分钟。
实施例2：
按下述步骤制备金砖书写板：
制主料：采取阳澄湖湖底下10-11m深处的澄泥，把澄泥晾晒后粉碎，用筛子筛除大于1mm部分，得到主料；
配物料：把下述成份按重量比配制成物料并拌匀：主料100，无定形二氧化硅20，三氧化二铝20，水泥15；水20；
制坯：将上述物料置于模具中，以人工踩踏成坯体，压力大约为3-5kg/cm2；坯体大小为40cm*40cm*3cm；
烧制：将坯体在加热炉中加热，加热时温度为430℃，时间2.5小时；
冷却：将烧制后坯体置于空气中自然冷却得成品。
在该制成的金砖书写板上夏天时书写的水迹挥发的时间约5-8分钟；冬天约10-15分钟。
Claims (5)
1.金砖书写板制备方法，其特征是：包括以下步骤：
制主料：采取阳澄湖湖底下8-12m深处的澄泥，把澄泥晾晒后粉碎，用筛子筛除大于1mm部分，得到主料；
配物料：把下述成份按重量份数配制成物料并拌匀：主料80-100，无定形二氧化硅15-20，三氧化二铝20-30，水泥15-25；水20-30；
制坯：将上述物料置于模具中，以压力2-5kg/cm2踩踏成坯体；
烧制：将坯体在加热炉中加热，温度400-500℃，时间2-3小时；
冷却：将烧制后坯体置于空气中自然冷却。
2.根据权利要求1所述制备方法，其特征是：采取阳澄湖湖底下10m深处的澄泥。
3.根据权利要求1或2所述制备方法，其特征是：物料中各成份的重量份数：主料90，无定形二氧化硅18，三氧化二铝25，水泥20；水26。
4.根据权利要求1或2所述制备方法，其特征是：坯体大小为60cm*60cm*5cm，加热时温度为470℃，时间2.5小时。
5.根据权利要求1或2所述制备方法，其特征是：坯体大小为40cm*40cm*3cm，加热时温度为430℃，时间2.5小时。