CN105418153A - 一种新型环保绿化砂基透水砖及其制作方法 - Google Patents
一种新型环保绿化砂基透水砖及其制作方法 Download PDFInfo
- Publication number
- CN105418153A CN105418153A CN201510763442.6A CN201510763442A CN105418153A CN 105418153 A CN105418153 A CN 105418153A CN 201510763442 A CN201510763442 A CN 201510763442A CN 105418153 A CN105418153 A CN 105418153A
- Authority
- CN
- China
- Prior art keywords
- water
- dry
- permeable brick
- sand
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种新型环保绿化砂基透水砖,本发明将油菜秸秆炭化处理后经室温研磨,孔隙表面吸附玄武岩纤维、纳米氮化铝粉,提高产品的吸附性和强度,以改性后的糖滤泥为成孔剂,将沙漠沙水洗烘干再配伍废烧粘土砖颗粒料、花岗岩、珍珠岩等粗骨料在不影响砖体透水性的情况下明显提高了产品的强度和抗折性能,以松香树脂替代水泥作为粘结料并配合其他有效助剂相互作用,利用本发明制得的砂基透水砖韧性大、透水效果好、强度高,产品不但可以长草绿化,而且具有40-45MPa抗压强度,使产品能大量用于江河、水库大堤防洪、护坡绿化及机场辅道绿化,增加停机面积、减少飞机起降时冲出跑道造成灾难,防止各类生物在绿化带钻洞。
Description
技术领域
本发明涉及建筑材料技术领域,尤其涉及一种新型环保绿化砂基透水砖及其制作方法。
背景技术
近些年来砂基透水砖成为关注热点,这种砂基透水砖,是以沙漠里的沙子为原料,透水性能好,防滑,还不像一般透水砖那样容易被灰尘堵塞,但是成本太高,推广砂基透水砖是实现沙漠沙资源化的有效途径,一方面在矿石资源日益紧缺的情况下,可以将沙漠沙作为一种廉价的建筑用材,另一方面对于我国大面积的沙漠治理、沙漠变废为宝是有益的。然而目前关于砂基透水砖的研究较少,传统的砂基透水砖的生产工艺落后、成本高、功能单一、抗压强度和透水性能不能同时达到透水砖的行业标准。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种新型环保绿化砂基透水砖及其制作方法。
本发明是通过以下技术方案实现的:
一种新型环保绿化砂基透水砖,由下列重量份的原料制成:沙漠沙37-38、废烧粘土砖颗粒料17-19、花岗岩12-14、珍珠岩11-12、糖滤泥15-17、松香树脂7-9、水玻璃5-6、玄武岩纤维4-6、纳米氮化铝粉0.7-0.9、丁酸二辛酯3-4、油菜秸秆6-8、适量水。
所述的一种新型环保绿化砂基透水砖的制作方法,包括以下步骤:
(1)将油菜秸秆烘干放入炭化炉中于450-500℃的温度下,隔绝空气炭化20-30分钟,冷却至室温加入玄武岩纤维、纳米氮化铝粉、丁酸二辛酯研磨40-50分钟,烘干;
(2)将硅钙渣、糖滤泥水洗后于50-60℃温度下烘干,送入高速混合机中加入松香树脂、水玻璃和适量的水,以1400-1500转/min的速度高速搅拌15-20分钟,干燥,超声研磨成粉烘干;
(3)将沙漠沙水洗烘干后加入废烧粘土砖颗粒料于750-820℃高温煅烧处理后粉碎至120-140目,加入步骤(1)、(2)物料及其他剩余成分混匀,投入球磨机中球磨2-3小时,喷水造粒、陈化2天后压制成生砖坯;
(4)将生砖坯自然晾晒风干,在箱式电阻炉中于1060-1100℃烧结1-2小时,自然冷却至室温出料。
本发明的优点是:本发明将油菜秸秆炭化处理后经室温研磨,孔隙表面吸附玄武岩纤维、纳米氮化铝粉,提高产品的吸附性和强度,以改性后的糖滤泥为成孔剂,将沙漠沙水洗烘干再配伍废烧粘土砖颗粒料、花岗岩、珍珠岩等粗骨料在不影响砖体透水性的情况下明显提高了产品的强度和抗折性能,以松香树脂替代水泥作为粘结料并配合其他有效助剂相互作用,利用本发明制得的砂基透水砖韧性大、透水效果好、强度高,产品不但可以长草绿化,而且具有40-45MPa抗压强度,使产品能大量用于江河、水库大堤防洪、护坡绿化及机场辅道绿化,增加停机面积、减少飞机起降时冲出跑道造成灾难,防止各类生物在绿化带钻洞。
具体实施方式
一种新型环保绿化砂基透水砖,由下列重量份的原料制成:沙漠沙37、废烧粘土砖颗粒料17、花岗岩12、珍珠岩11、糖滤泥15、松香树脂7、水玻璃5、玄武岩纤维4、纳米氮化铝粉0.7、丁酸二辛酯3、油菜秸秆6、适量水。
所述的一种新型环保绿化砂基透水砖的制作方法,包括以下步骤:
(1)将油菜秸秆烘干放入炭化炉中于450℃的温度下,隔绝空气炭化20分钟,冷却至室温加入玄武岩纤维、纳米氮化铝粉、丁酸二辛酯研磨40分钟,烘干;
(2)将硅钙渣、糖滤泥水洗后于50℃温度下烘干,送入高速混合机中加入松香树脂、水玻璃和适量的水,以1400转/min的速度高速搅拌15分钟,干燥,超声研磨成粉烘干;
(3)将沙漠沙水洗烘干后加入废烧粘土砖颗粒料于750℃高温煅烧处理后粉碎至120目,加入步骤(1)、(2)物料及其他剩余成分混匀,投入球磨机中球磨2小时,喷水造粒、陈化2天后压制成生砖坯;
(4)将生砖坯自然晾晒风干,在箱式电阻炉中于1060℃烧结1小时,自然冷却至室温出料。
使用本发明生产的砂基透水砖的技术参数指标如下:抗压强度43.5MPa,透水系数为0.068cm/s,透水砖的保水性0.796g/cm2。
Claims (2)
1.一种新型环保绿化砂基透水砖,其特征在于,由下列重量份的原料制成:沙漠沙37-38、废烧粘土砖颗粒料17-19、花岗岩12-14、珍珠岩11-12、糖滤泥15-17、松香树脂7-9、水玻璃5-6、玄武岩纤维4-6、纳米氮化铝粉0.7-0.9、丁酸二辛酯3-4、油菜秸秆6-8、适量水。
2.根据权利要求1所述的一种新型环保绿化砂基透水砖的制作方法,其特征在于包括以下步骤:
(1)将油菜秸秆烘干放入炭化炉中于450-500℃的温度下,隔绝空气炭化20-30分钟,冷却至室温加入玄武岩纤维、纳米氮化铝粉、丁酸二辛酯研磨40-50分钟,烘干;
(2)将硅钙渣、糖滤泥水洗后于50-60℃温度下烘干,送入高速混合机中加入松香树脂、水玻璃和适量的水,以1400-1500转/min的速度高速搅拌15-20分钟,干燥,超声研磨成粉烘干;
(3)将沙漠沙水洗烘干后加入废烧粘土砖颗粒料于750-820℃高温煅烧处理后粉碎至120-140目,加入步骤(1)、(2)物料及其他剩余成分混匀,投入球磨机中球磨2-3小时,喷水造粒、陈化2天后压制成生砖坯;
(4)将生砖坯自然晾晒风干,在箱式电阻炉中于1060-1100℃烧结1-2小时,自然冷却至室温出料。