CN105439609A - 一种长效抗菌砂基透水砖及其制作方法 - Google Patents

一种长效抗菌砂基透水砖及其制作方法 Download PDF

Info

Publication number
CN105439609A
CN105439609A CN201510761825.XA CN201510761825A CN105439609A CN 105439609 A CN105439609 A CN 105439609A CN 201510761825 A CN201510761825 A CN 201510761825A CN 105439609 A CN105439609 A CN 105439609A
Authority
CN
China
Prior art keywords
water
permeable brick
dry
sand
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510761825.XA
Other languages
English (en)
Inventor
李诺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Linuo New Materials Trade Co Ltd
Original Assignee
Hefei Linuo New Materials Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Linuo New Materials Trade Co Ltd filed Critical Hefei Linuo New Materials Trade Co Ltd
Priority to CN201510761825.XA priority Critical patent/CN105439609A/zh
Publication of CN105439609A publication Critical patent/CN105439609A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种长效抗菌砂基透水砖，本发明将柳叶、榆树皮炭化处理后经室温研磨，孔隙表面吸附羧甲基壳聚糖，提高产品的吸附性和长效杀菌性，以改性后的糖滤泥为成孔剂，将沙漠沙水洗烘干再配伍碳化硅陶瓷渣、沸石等粗骨料在不影响砖体透水性的情况下明显提高了产品的强度和抗折性能，利用本发明制得的砂基透水砖不仅工艺简单，生产成本低，而且具有孔隙率高、透水透气性佳、保水性效果优的优点，还可降温、降噪、调节气候，消除城市热岛效应，提高空气质量、保持地表水循环等多项功能。

Description

一种长效抗菌砂基透水砖及其制作方法
技术领域
本发明涉及建筑材料技术领域，尤其涉及一种长效抗菌砂基透水砖及其制作方法。
背景技术
近些年来砂基透水砖成为关注热点，这种砂基透水砖，是以沙漠里的沙子为原料，透水性能好，防滑，还不像一般透水砖那样容易被灰尘堵塞，但是成本太高，推广砂基透水砖是实现沙漠沙资源化的有效途径，一方面在矿石资源日益紧缺的情况下，可以将沙漠沙作为一种廉价的建筑用材，另一方面对于我国大面积的沙漠治理、沙漠变废为宝是有益的。然而目前关于砂基透水砖的研究较少，传统的砂基透水砖的生产工艺落后、成本高、功能单一、抗压强度和透水性能不能同时达到透水砖的行业标准。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种长效抗菌砂基透水砖及其制作方法。
本发明是通过以下技术方案实现的：
一种长效抗菌砂基透水砖，由下列重量份的原料制成：沙漠沙36-39、废玻璃粉7-9、碳化硅陶瓷渣17-19、沸石18-20、水泥6-8、糖滤泥17-19、可再分散性乳胶粉5-7、羧甲基壳聚糖3.2-3.5、废机油4-6、桐油酸酐3-5、磺酸钙0.8-1.1、铝酸钠0.4-0.5、柳叶6-8、榆树皮2-3、适量水。
所述的一种长效抗菌砂基透水砖的制作方法，包括以下步骤：
（1）将柳叶、榆树皮烘干放入炭化炉中于450-500℃的温度下，隔绝空气炭化20-30分钟，冷却至室温加入羧甲基壳聚糖、废机油研磨40-50分钟，烘干；
（2）将糖滤泥水洗后于50-60℃温度下烘干，送入高速混合机中加入桐油酸酐、磺酸钙、铝酸钠和适量的水，以1400-1500转/min的速度高速搅拌15-20分钟，干燥，超声研磨成粉烘干；
（3）将沙漠沙水洗烘干后加入碳化硅陶瓷渣、沸石于725-815℃高温煅烧处理后粉碎至120-140目，加入步骤（1）、（2）物料及其他剩余成分混匀，投入球磨机中球磨2-3小时，喷水造粒、陈化2天后压制成生砖坯；
（4）将生砖坯自然晾晒风干，在箱式电阻炉中于1060-1100℃烧结1-2小时，自然冷却至室温出料。
本发明的优点是：本发明将柳叶、榆树皮炭化处理后经室温研磨，孔隙表面吸附羧甲基壳聚糖，提高产品的吸附性和长效杀菌性，以改性后的糖滤泥为成孔剂，将沙漠沙水洗烘干再配伍碳化硅陶瓷渣、沸石等粗骨料在不影响砖体透水性的情况下明显提高了产品的强度和抗折性能，利用本发明制得的砂基透水砖不仅工艺简单，生产成本低，而且具有孔隙率高、透水透气性佳、保水性效果优的优点，还可降温、降噪、调节气候，消除城市热岛效应，提高空气质量、保持地表水循环等多项功能。
具体实施方式
一种长效抗菌砂基透水砖，由下列重量份的原料制成：沙漠沙36、废玻璃粉7、碳化硅陶瓷渣17、沸石18、水泥6、糖滤泥17、可再分散性乳胶粉5、羧甲基壳聚糖3.2、废机油4、桐油酸酐3、磺酸钙0.8、铝酸钠0.4、柳叶6、榆树皮2、适量水。
所述的一种长效抗菌砂基透水砖的制作方法，包括以下步骤：
（1）将柳叶、榆树皮烘干放入炭化炉中于450℃的温度下，隔绝空气炭化20分钟，冷却至室温加入羧甲基壳聚糖、废机油研磨40分钟，烘干；
（2）将糖滤泥水洗后于50℃温度下烘干，送入高速混合机中加入桐油酸酐、磺酸钙、铝酸钠和适量的水，以1400转/min的速度高速搅拌15分钟，干燥，超声研磨成粉烘干；
（3）将沙漠沙水洗烘干后加入碳化硅陶瓷渣、沸石于725℃高温煅烧处理后粉碎至120目，加入步骤（1）、（2）物料及其他剩余成分混匀，投入球磨机中球磨2小时，喷水造粒、陈化2天后压制成生砖坯；
（4）将生砖坯自然晾晒风干，在箱式电阻炉中于1060℃烧结1小时，自然冷却至室温出料。
使用本发明生产的砂基透水砖的技术参数指标如下：抗压强度48.6MPa，透水系数为0.086cm/s，透水砖的保水性为0.836g/cm2。

Claims (2)

1.一种长效抗菌砂基透水砖，其特征在于，由下列重量份的原料制成：沙漠沙36-39、废玻璃粉7-9、碳化硅陶瓷渣17-19、沸石18-20、水泥6-8、糖滤泥17-19、可再分散性乳胶粉5-7、羧甲基壳聚糖3.2-3.5、废机油4-6、桐油酸酐3-5、磺酸钙0.8-1.1、铝酸钠0.4-0.5、柳叶6-8、榆树皮2-3、适量水。
2.根据权利要求1所述的一种长效抗菌砂基透水砖的制作方法，其特征在于包括以下步骤：
（1）将柳叶、榆树皮烘干放入炭化炉中于450-500℃的温度下，隔绝空气炭化20-30分钟，冷却至室温加入羧甲基壳聚糖、废机油研磨40-50分钟，烘干；
（2）将糖滤泥水洗后于50-60℃温度下烘干，送入高速混合机中加入桐油酸酐、磺酸钙、铝酸钠和适量的水，以1400-1500转/min的速度高速搅拌15-20分钟，干燥，超声研磨成粉烘干；
（3）将沙漠沙水洗烘干后加入碳化硅陶瓷渣、沸石于725-815℃高温煅烧处理后粉碎至120-140目，加入步骤（1）、（2）物料及其他剩余成分混匀，投入球磨机中球磨2-3小时，喷水造粒、陈化2天后压制成生砖坯；
（4）将生砖坯自然晾晒风干，在箱式电阻炉中于1060-1100℃烧结1-2小时，自然冷却至室温出料。
CN201510761825.XA 2015-11-11 2015-11-11 一种长效抗菌砂基透水砖及其制作方法 Withdrawn CN105439609A (zh)