CN103588456A - 一种蒸压粉煤灰尾矿砖 - Google Patents

一种蒸压粉煤灰尾矿砖 Download PDF

Info

Publication number
CN103588456A
CN103588456A CN201310555563.2A CN201310555563A CN103588456A CN 103588456 A CN103588456 A CN 103588456A CN 201310555563 A CN201310555563 A CN 201310555563A CN 103588456 A CN103588456 A CN 103588456A
Authority
CN
China
Prior art keywords
tailing
brick
raw material
powder
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310555563.2A
Other languages
English (en)
Other versions
CN103588456B (zh
Inventor
王长富
毛东超
王玉童
刘伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Original Assignee
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd filed Critical ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority to CN201310555563.2A priority Critical patent/CN103588456B/zh
Publication of CN103588456A publication Critical patent/CN103588456A/zh
Application granted granted Critical
Publication of CN103588456B publication Critical patent/CN103588456B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种蒸压粉煤灰尾矿砖，其是由下述重量份的原料制得：粉煤灰50-60，尾矿20-25，电解石13-16，石膏25-30，沸石6-8，复合改性矿物粉体2-4。复合改性矿物粉体能显著增加本发明的强度以及使用寿命，不易开裂，本发明同时具有尾矿利用率高的特点，可有效推动尾矿在蒸压砖领域的利用。

Description

一种蒸压粉煤灰尾矿砖
技术领域
本发明涉及蒸压砖领域，确切地说是一种蒸压粉煤灰尾矿砖。
背景技术
利用粉煤灰、煤渣、煤矸石、尾矿渣、化工渣或者天然砂、海涂泥等（以上原料的一种或数种）作为主要原料，不经高温煅烧而制造的一种新型墙体材料称之为免烧砖，又称蒸压砖。
发明内容
本发明的目的在于提供一种蒸压粉煤灰尾矿砖。
上述目的通过以下方案实现：
    一种蒸压粉煤灰尾矿砖，其特征在于：其是由下述重量份的原料制得：粉煤灰50-60，尾矿20-25，电解石13-16，石膏25-30，沸石6-8，复合改性矿物粉体2-4；
所述的复合改性矿物粉体由下述重量份的原料制得：
高岭石3-7、闪石8-15、海泡石5-7、氯化钠1-2、硅烷偶联剂KH550 1-2、当归油1-2、氢氧化铝4-6，乙酸钙0.1-0.2；
所述的复合改性矿物粉体制备方法：
（1）是将高岭石、闪石、海泡石粉碎至颗粒大小为2-16目，将粉碎后的矿物加入清水里，搅拌均匀，浸泡10-15小时后，离心处理15-25min，所述离心机的转速为1500-1800r/min，离心之后，经过过滤、干燥步骤得到复合矿物粉体的初成品；
（2）将步骤（1）所得复合矿物粉体的初成品在500-550℃下煅烧2-4小时，然后，取出，与其余原料一并加入适量水中研磨，加10-15%盐酸溶液调PH为4-5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，即得。
所述的一种蒸压粉煤灰尾矿砖 ，其特征在于：制备方法为：
（1）、将各原料混匀后，加适量水混合均匀，得混合料；
（2）、浇筑入模成型，后静置时间为2-3h；
（3）、进行蒸压养护，养护温度为180℃-190℃，养护时间为7-8h，压力为1.2-1.3MPa，即得。　　
所述的一种蒸压粉煤灰尾矿砖 ，其特征在于：所述的水和各原料总量的质量比为0.2-0.3∶1。
本发明的有益效果为：复合改性矿物粉体能显著增加本发明的强度以及使用寿命，不易开裂，本发明同时具有尾矿利用率高的特点，可有效推动尾矿在蒸压砖领域的利用。
具体实施方式
    一种蒸压粉煤灰尾矿砖，其是由下述重量kg的原料制得：粉煤灰55，尾矿20，电解石13，石膏25，沸石6，复合改性矿物粉体2；
所述的复合改性矿物粉体由下述重量份的原料制得：
高岭石5、闪石8、海泡石5、氯化钠1、硅烷偶联剂KH550  2、当归油1、氢氧化铝4，乙酸钙0.2；
    所述的复合改性矿物粉体制备方法：
（1）是将高岭石、闪石、海泡石粉碎至颗粒大小为4目，将粉碎后的矿物加入清水里，搅拌均匀，浸泡10小时后，离心处理15min，所述离心机的转速为1500r/min，离心之后，经过过滤、干燥步骤得到复合矿物粉体的初成品；
（2）将步骤（1）所得复合矿物粉体的初成品在550℃下煅烧4小时，然后，取出，与其余原料一并加入适量水中研磨，加10%盐酸溶液调PH为5，研磨浆料至500目后，再加氢氧化钠调为中性，喷雾干燥，即得。
所述的一种蒸压粉煤灰尾矿砖 ，制备方法为：
（1）、将各原料混匀后，加适量水混合均匀，所述的水和各原料总量的质量比为0.3∶1，得混合料；
（2）、浇筑入模成型，后静置时间为3h；
（3）、进行蒸压养护，养护温度为190℃，养护时间为8h，压力为1.2MPa，即得。　　
经检测本实施例生产的蒸压砖其各项性能均能满足JC239-2001《粉煤灰砖》MU10等级要求，其抗压强度为13.7MPa，抗折强度为4.1MPa，干燥收缩、碳化系数、抗冻性实验合格。

Claims (3)

1.一种蒸压粉煤灰尾矿砖，其特征在于：其是由下述重量份的原料制得：粉煤灰50-60，尾矿20-25，电解石13-16，石膏25-30，沸石6-8，复合改性矿物粉体2-4；
所述的复合改性矿物粉体由下述重量份的原料制得：
高岭石3-7、闪石8-15、海泡石5-7、氯化钠1-2、硅烷偶联剂KH550 1-2、当归油1-2、氢氧化铝4-6，乙酸钙0.1-0.2；
所述的复合改性矿物粉体制备方法：
是将高岭石、闪石、海泡石粉碎至颗粒大小为2-16目，将粉碎后的矿物加入清水里，搅拌均匀，浸泡10-15小时后，离心处理15-25min，所述离心机的转速为1500-1800r/min，离心之后，经过过滤、干燥步骤得到复合矿物粉体的初成品；
（2）将步骤（1）所得复合矿物粉体的初成品在500-550℃下煅烧2-4小时，然后，取出，与其余原料一并加入适量水中研磨，加10-15%盐酸溶液调PH为4-5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，即得。
2.根据权利要求1所述的一种蒸压粉煤灰尾矿砖 ，其特征在于：制备方法为：
（1）、将各原料混匀后，加适量水混合均匀，得混合料；
（2）、浇筑入模成型，后静置时间为2-3h；
（3）、进行蒸压养护，养护温度为180℃-190℃，养护时间为7-8h，压力为1.2-1.3MPa，即得。
3.根据权利要求2所述的一种蒸压粉煤灰尾矿砖 ，其特征在于：所述的水和各原料总量的质量比为0.2-0.3∶1。
CN201310555563.2A 2013-11-11 2013-11-11 一种蒸压粉煤灰尾矿砖 Active CN103588456B (zh)