CN101368013A - 一种双重改性复合型内墙建筑涂料及其制备方法 - Google Patents

一种双重改性复合型内墙建筑涂料及其制备方法 Download PDF

Info

Publication number
CN101368013A
CN101368013A CNA2008101560433A CN200810156043A CN101368013A CN 101368013 A CN101368013 A CN 101368013A CN A2008101560433 A CNA2008101560433 A CN A2008101560433A CN 200810156043 A CN200810156043 A CN 200810156043A CN 101368013 A CN101368013 A CN 101368013A
Authority
CN
China
Prior art keywords
percent
modified
water
wall construction
polyvinyl alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008101560433A
Other languages
English (en)
Other versions
CN101368013B (zh
Inventor
郭文录
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chen Gang
Huacheng International Industrial Construction Co.,Ltd.
Original Assignee
Jiangsu University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu University of Science and Technology filed Critical Jiangsu University of Science and Technology
Priority to CN2008101560433A priority Critical patent/CN101368013B/zh
Publication of CN101368013A publication Critical patent/CN101368013A/zh
Application granted granted Critical
Publication of CN101368013B publication Critical patent/CN101368013B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于建筑涂料领域。所公开的一种双重改性复合型内墙建筑涂料按其质量百分比由以下组分组成：改性膨润土浆料为20～50％，改性聚乙烯醇胶水为15－25％，熟石灰浆料为15～25％，钛白粉为5～10％，滑石粉为5～10％，消泡剂(磷酸三丁酯)为0.01～0.02％，TFC－1分散剂为0.1～0.4％，丙二醇成膜助剂为0.3～0.7％，水为5％～12％。该涂料具有涂刷均匀，无滚刷痕迹，表面光滑，流平性好，手感好，成膜效果好，不含防腐剂，无毒无害；不沉淀，不脱粉，所有性能可满足内墙建筑涂料的技术要求，是目前乳胶漆内墙建筑涂料的最佳替代品。

Description

一种双重改性复合型内墙建筑涂料及其制备方法
技术领域
本发明涉及的是一种复合型内墙建筑涂料，更具体地说，是涉及一种双重改性复合型内墙建筑涂料及其制备方法。属于建筑涂料领域。
背景技术
单纯用膨润土改性的建筑涂料和单纯用聚乙烯醇改性的建筑涂料，以及膨润土和聚乙烯醇改性的建筑涂料在国内外建筑领域早已出现和使用，但这几种涂料涂刷不均匀，有滚刷痕迹，表面粗糙，手感不好，耐久性差，易起皮，达不到和丙烯酸乳胶漆一样的效果。而用丙烯酸乳液制造的内墙建筑涂料，也有致命的弱点，例如，有机物和有害挥发物含量高，对环境有污染，表面粗糙不光滑，影响手感。另外，还由于需要添加防腐剂，导致影响人们身体健康。因此，研发一种既具有涂刷均匀，无滚刷痕迹，表面光滑，手感好等优点，又能满足无毒无害，成本低的要求的内墙建筑涂料实为人们所期盼。
发明内容
为了克服现有技术存在的缺陷，满足人们对内墙建筑涂料的要求，本发明的目的是采用改性膨润土和改性聚乙烯醇的技术方法，从而解决上述现有技术存在的问题，提供一种双重改性复合型内墙建筑涂料及其制备方法。
为了达到上述目的，本发明的一种双重改性复合型内墙建筑涂料的组分及其质量百分比为：改性膨润土浆料为20～50％，改性聚乙烯醇胶水为15-25％，熟石灰浆料为15～25％，钛白粉为5～10％，滑石粉为5～10％，消泡剂(磷酸三丁脂)为0.01～0.02％，TFC-1分散剂为0.1～0.4％，丙二醇成膜助剂为0.3～0.7％，水5％～12％。
其中，所述的改性膨润土浆料由水，膨润土，碳酸钠和轻质碳酸钙组成。其制备方法是：设定组分的总份数为10份，先加7份的水，在水的温度达到70-80℃的条件下加入1.9份膨润土，当膨润土完全化解后，再加入0.1份碳酸钠进行改性20-30min，然后加入轻质碳酸钙1份，降温至20-30度，最后过滤，得到改性膨润土浆料。
所述的改性聚乙烯醇胶水，由水，聚乙烯醇(PVA)，TX-10表面活性剂，已二异氰酸脂和泡花碱组成，其制备方法是：
加9.23份水，升温至88-92℃时加入0.6份PVA至完全溶解，搅拌下加入0.01份表面活性剂TX-10，冷却至20-30℃，加入0.16份己二异氰酸脂和泡花碱交联，搅拌30min，得到改性聚乙烯醇胶水。总份数为10。
所述的熟石灰浆料是由生石灰用水化解，静止50小时后去除掉清液，得熟石灰浆料。
本发明的一种双重改性复合内墙建筑涂料的制备方法其步骤是：
(1)将改性膨润土浆料与改性聚乙烯醇胶水混合并高速搅拌均匀；
(2)将熟石灰浆料加入并搅拌均匀；
(3)依次加入钛白粉、滑石粉、消泡剂、分散剂、成膜助剂和水，低速搅拌均匀；
(4)将涂料进入砂磨机研磨两遍，过滤，调粘度，包装装桶。
本发明的一种双重改性复合型内墙建筑涂料及其制备方法，所制备出的改性膨润土和改性聚乙烯醇复合型内墙建筑涂料，具有以下优点：涂刷均匀，无滚刷痕迹，表面光滑，流平性好，手感好，成膜效果好，不含防腐剂，无毒无害；不沉淀，不腐，不脱粉，效果好，成本低，所有性能可满足内墙建筑涂料的技术要求，是乳胶漆内墙建筑涂料的最佳替代品。该涂料投资少、成本低、性能优良、有着很好的发展前景。
具体实施方式
下面结合实施例对本发明的一种双重改性复合型内墙建筑涂料及其制备方法作进一步的详述。
实例1
原料配方：改性膨润土浆料50kg，改性聚乙烯醇胶水15kg，熟石灰浆料15kg，钛白粉5kg，滑石粉5kg，消泡剂为0.01kg，分散剂为0.1kg，成膜助剂0.39kg，水9.5kg。各组分质量之和为100％。
制备方法：
将改性膨润土浆料与改性聚乙烯醇胶水混合，高速搅拌15分钟，然后加入熟石灰浆料搅拌15分钟、均匀，依次加入钛白粉、滑石粉、消泡剂、分散剂、成膜助剂和水，低速搅拌30分钟、均匀，然后将涂料进入砂磨机研磨两遍，用300目筛过滤，包装装桶。
实例2
原料配方：改性膨润土浆料20kg，改性聚乙烯醇胶水25kg，熟石灰浆料25kg，钛白粉10kg，滑石粉10kg，消泡剂为0.02kg，分散剂为0.3kg，成膜助剂0.68kg，水9kg。
制备方法与实施例1相同。
实例3
原料配方：改性膨润土浆料40kg，改性聚乙烯醇胶水18kg，熟石灰浆料20kg，钛白粉8kg，滑石粉6kg，消泡剂为0.01kg，分散剂为0.29kg，成膜助剂0.7kg，水7kg。
制备方法与实施例1相同。
实例4
原料配方：改性膨润土浆料35kg，改性聚乙烯醇胶水20kg，熟石灰浆料18kg，钛白粉6kg，滑石粉8kg，消泡剂为0.02kg，分散剂为0.4kg，成膜助剂0.58kg，水12kg。
制备方法与实施例1相同。

Claims (5)

1.一种双重改性复合型内墙建筑涂料，其特征在于，该涂料按质量百分比由以下组分组成：改性膨润土浆料为20～50％，改性聚乙烯醇胶水为15-25％，熟石灰浆料为15～25％，钛白粉为5～10％，滑石粉为5～10％，消泡剂(磷酸三丁脂)为0.01～0.02％，TFC-1分散剂为0.1～0.4％，丙二醇成膜助剂为0.3～0.7％，水为5％～12％。
2.根据权利要求1所述的一种双重改性复合型内墙建筑涂料，其特征在于，所述的改性膨润土浆料所含成份的质量份数是:水为7份，膨润土为1.9份，碳酸钠为0.1份，轻质碳酸钙为1份，各成份质量之和为10份。
3.根据权利要求1所述的一种双重改性复合型内墙建筑涂料，其特征在于，所述的改性聚乙烯醇胶水所含成份的质量份数是:水为9.23份，聚乙烯醇为0.6份，TX-10表面活性剂为0.01份，已二异氰酸脂和泡花碱为0.16份，各成份质量之和为10份。
4.根据权利要求1所述的一种双重改性复合型内墙建筑涂料，其特征在于，所述的熟石灰浆料是由生石灰用水化解，静止50小时后去除掉清液，得熟石灰浆料。
5.一种制备权利要求1所述的一种双重改性复合型内墙建筑涂料的方法，其特征在于，该方法按以下步骤进行：
第一步，制备出改性膨润土浆料、改性聚乙烯醇胶水；按照7份的水，在水的温度达到70-80℃的条件下加入1.9份膨润土，当膨润土完全化解后，再加入0.1份碳酸钠进行改性20-30min，然后加入轻质碳酸钙1份，降温至20-30度，最后过滤，制备得到改性膨润土浆料；按照9.23份水，升温至88-92℃加入0.6份PVA至完全溶解，搅拌下加入0.01份TX-10表面活性剂，冷却至20-30℃时加入0.16份己二异氰酸脂和泡花碱交联，搅拌30min，制备得到改性聚乙烯醇胶水；
第二步，按双重改性复合型内墙建筑涂料组分配比；
第三步，制备双重改性复合型内墙建筑涂料；先将第一步制备出的改性膨润土浆料和改性聚乙烯醇胶水混合，高速搅拌15分钟；然后加入熟石灰浆料搅拌15分钟、均匀；再依次加入钛白粉、滑石粉、消泡剂、分散剂、成膜助剂和水，低速搅拌30分钟、均匀；最后将涂料进入砂磨机研磨两遍，用300目筛过滤，包装装桶。
CN2008101560433A 2008-09-19 2008-09-19 一种双重改性复合型内墙建筑涂料及其制备方法 Expired - Fee Related CN101368013B (zh)