CN110951340A - 一种环保涂料 - Google Patents
一种环保涂料 Download PDFInfo
- Publication number
- CN110951340A CN110951340A CN201911091345.1A CN201911091345A CN110951340A CN 110951340 A CN110951340 A CN 110951340A CN 201911091345 A CN201911091345 A CN 201911091345A CN 110951340 A CN110951340 A CN 110951340A
- Authority
- CN
- China
- Prior art keywords
- per mill
- agent
- mill
- per
- thickener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及化工涂料技术领域，具体涉及一种环保涂料，按质量百分比的组成配比如下：去离子水150‑350‰、硅片剂0.1‑1.5‰、分散剂2‑8‰、润湿剂0.5‑4.5‰、钛白粉100‑250‰、云母粉25‑150％、高钙粉100‑300‰、消泡剂0.5‑4.5‰、净味粉2‑6‰、硅丙乳液30‑120‰、硅酸钾150‑350‰、稳定剂2‑8‰、杀菌剂0.5‑3.5‰、增稠剂A0.5‑3.5‰、增稠剂B0.5‑3.5‰、纤维素2‑8‰、增稠剂C2‑10‰；它具有能够减少涂料中VOC及有害物质，其性能指标超过合成树脂乳液内墙标准，达到合成树脂乳液外墙标准，且具有防火、防霉功能，提高涂料的性能。
Description
【技术领域】
本发明涉及化工涂料技术领域，具体涉及一种环保涂料。
【背景技术】
涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。涂料属于有机化工高分子材料，所形成的涂膜属于高分子化合物类型。按照现代通行的化工产品的分类，涂料属于精细化工产品。
涂料一般由四种基本成分：成膜物质(树脂、乳液)、颜料(包括体质颜料)、溶剂和添加剂(助剂)。(1)成膜物质是涂膜的主要成分，包括油脂、油脂加工产品、纤维素衍生物、天然树脂、合成树脂和合成乳液。(2)颜料一般分两种，一种为着色颜料，常见的钛白粉，铬黄等，还有种为体质颜料，也就是常说的填料，如碳酸钙，滑石粉。(3)助剂如消泡剂，流平剂等，还有一些特殊的功能助剂，如底材润湿剂等，这些助剂一般不能成膜并且添加量少，但对基料形成涂膜的过程与耐久性起着相当重要的作用。(4)溶剂包括烃类，溶剂、醇类、醚类、酮类和酯类物质；溶剂和水的主要作用在于使成膜基料分散而形成黏稠液体。此外根据涂料中使用的主要成膜物质可将涂料分为油性涂料、纤维涂料、合成涂料和无机涂料；按涂料或漆膜性状可分溶液、乳胶、溶胶、粉末、有光、消光和多彩美术涂料等。
但是现有的涂料技术GB/T9756-2009、GB/T9755-2014标准要求过低，特别是有害物质限量，GB18582-2008中有害物质远高于国际水平。
【发明内容】
本发明的目的在于针对现有技术的缺陷和不足，提供一种环保涂料。
本发明所述的一种环保涂料，其按质量百分比的组成配比如下：去离子水150-350‰、硅片剂0.1-1.5‰、分散剂2-8‰、润湿剂0.5-4.5‰、钛白粉100-250‰、云母粉25-150％、高钙粉100-300‰、消泡剂0.5-4.5‰、净味粉2-6‰、硅丙乳液30-120‰、硅酸钾150-350‰、稳定剂2-8‰、杀菌剂0.5-3.5‰、增稠剂A0.5-3.5‰、增稠剂B0.5-3.5‰、纤维素2-8‰、增稠剂C2-10‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水240‰、硅片剂0.7‰、分散剂5‰、润湿剂2‰、钛白粉150‰、云母粉75％、高钙粉200‰、消泡剂2‰、净味粉4‰、硅丙乳液70‰、硅酸钾250‰、稳定剂5‰、杀菌剂1.5‰、增稠剂A2‰、增稠剂B2‰、纤维素)5‰、增稠剂C6‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水220‰、硅片剂0.5‰、分散剂5‰、润湿剂2.2‰、钛白粉180‰、云母粉85％、高钙粉210‰、消泡剂3‰、净味粉3‰、硅丙乳液60‰、硅酸钾220‰、稳定剂4‰、杀菌剂1.5‰、增稠剂A1.5‰、增稠剂B1.5‰、纤维素5‰、膨润土增稠剂6‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水260‰、硅片剂0.9‰、分散剂5.2‰、润湿剂2.4‰、钛白粉170‰、云母粉75％、高钙粉210‰、消泡剂3‰、净味粉3‰、硅丙乳液60‰、硅酸钾200‰、稳定剂3‰、杀菌剂3‰、增稠剂A2‰、增稠剂B2‰、纤维素4‰、增稠剂C5.5‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水200‰、硅片剂0.5‰、分散剂4.8‰、润湿剂2.6‰、钛白粉200‰、云母粉84％、高钙粉220‰、消泡剂2，5‰、净味粉2.5‰、硅丙乳液50‰、硅酸钾220‰、稳定剂3.5‰、杀菌剂3.5‰、增稠剂A3.5‰、增稠剂B3.5‰、纤维素3.5‰、增稠剂C4.5‰。
进一步地，所述增稠剂A为型号为936型的增稠剂。
进一步地，增稠剂B为型号是618型的增稠剂。
进一步地，增稠剂C为膨润土增稠剂。
进一步地，所述纤维素为型号为250HBR的羟乙基纤维素。
本发明有益效果为：本发明所述的一种环保涂料，它具有能够减少涂料中VOC及有害物质，其性能指标超过合成树脂乳液内墙标准，达到合成树脂乳液外墙标准，且还具有防火、防霉功能，极大地提高涂料的性能。
【具体实施方式】
下面以及实施例来详细说明本发明，其中的示意性实施例以及说明仅用来解释本发明，但并不作为对本发明的限定。
本具体实施方式所述的一种环保涂料，其按质量百分比的组成配比如下：去离子水150-350‰、硅片剂0.1-1.5‰、分散剂2-8‰、润湿剂0.5-4.5‰、钛白粉100-250‰、云母粉25-150％、高钙粉100-300‰、消泡剂0.5-4.5‰、净味粉2-6‰、硅丙乳液30-120‰、硅酸钾150-350‰、稳定剂2-8‰、杀菌剂0.5-3.5‰、增稠剂A0.5-3.5‰、增稠剂B0.5-3.5‰、纤维素2-8‰、增稠剂C2-10‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水240‰、硅片剂0.7‰、分散剂5‰、润湿剂2‰、钛白粉150‰、云母粉75％、高钙粉200‰、消泡剂2‰、净味粉4‰、硅丙乳液70‰、硅酸钾250‰、稳定剂5‰、杀菌剂1.5‰、增稠剂A2‰、增稠剂B2‰、纤维素)5‰、增稠剂C6‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水220‰、硅片剂0.5‰、分散剂5‰、润湿剂2.2‰、钛白粉180‰、云母粉85％、高钙粉210‰、消泡剂3‰、净味粉3‰、硅丙乳液60‰、硅酸钾220‰、稳定剂4‰、杀菌剂1.5‰、增稠剂A1.5‰、增稠剂B1.5‰、纤维素5‰、膨润土增稠剂6‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水260‰、硅片剂0.9‰、分散剂5.2‰、润湿剂2.4‰、钛白粉170‰、云母粉75％、高钙粉210‰、消泡剂3‰、净味粉3‰、硅丙乳液60‰、硅酸钾200‰、稳定剂3‰、杀菌剂3‰、增稠剂A2‰、增稠剂B2‰、纤维素4‰、增稠剂C5.5‰。
进一步地，环保涂料按质量百分比的组成配比如下：去离子水200‰、硅片剂0.5‰、分散剂4.8‰、润湿剂2.6‰、钛白粉200‰、云母粉84％、高钙粉220‰、消泡剂2，5‰、净味粉2.5‰、硅丙乳液50‰、硅酸钾220‰、稳定剂3.5‰、杀菌剂3.5‰、增稠剂A3.5‰、增稠剂B3.5‰、纤维素3.5‰、增稠剂C4.5‰。
进一步地，所述增稠剂A为型号为936型的增稠剂。
进一步地，增稠剂B为型号是618型的增稠剂。
进一步地，增稠剂C为膨润土增稠剂。
进一步地，所述纤维素为型号为250HBR的羟乙基纤维素。
具体实施例一，无机涂料配料单如下:
其制备工艺，采用如下步骤：
步骤一：把上述配料单中的水加入分散罐中；
步骤二：再将上述配料单中的分散剂、消泡剂加入水中，开动分散机(600转/min)进搅拌；
步骤三：再加入上述配料单的硅片剂、润湿剂、钛白粉、云母粉、高钙粉、净味粉、硅酸钾、稳定剂、杀菌剂的组成物料，通过分散机来高速分散10分钟，得搅拌浆料；
步骤四：上步骤三中的搅拌浆料再转入研磨机中研磨，将研磨好的浆料降温后加入罐内；
步骤五：将泡好的纤维素(用90Kg水提前溶解)加入罐内分散30分钟；
步骤六：将步骤五中做好的浆料转入搅拌机，调节转速为400转左右，加入乳液、消泡剂、调节剂，乳液、消泡剂、调节剂加入前先测PH值再加入，PU值8-9，然后再搅拌20分钟后将转速调至250-300转，慢慢消泡，待罐内无气泡后加入增稠剂检测粘度，如果达不到120KU，可再补加碱溶涨增稠剂；
步骤七：以上工序完成后等产品温度降至常温加入防腐剂搅拌10分钟即可。
本发明配方有10Kg余水，可清洗乳液、助剂工具等，然后加入罐中。本配方在冬天可降低纤维素及增稠剂的用量，粘度可降至110KU,过滤、包装、入库。
本发明的优点如下：本产品的性能指标超过国标GB18582-2008标准，具有以下特点：
①VOC及有害物质达到国际最低标准型的环保涂料。
②产品超过合成树脂乳液内墙标准GB/T9756-2009.
③达到合成树脂乳液外墙标准GB/T9755-2014。
④同时具有防火功能，GB/T14402-2007、GB/T20284-2006(燃烧性能A.(A2))。
⑤达到防霉标准，GB/T1741-2007。产品用途广泛，如儿童房间、学校、地下室、机场、建筑外墙等。
本发明属于化工涂料类水溶性产品常温成膜，非危险品运输，保质期长，施工方便，滚涂、刷涂、喷涂均可。对施工现场要求不高，在水泥底、中性腻子底等均可施工。
本发明有益效果为：本发明所述的一种环保涂料，它具有能够减少涂料中VOC及有害物质，其性能指标超过合成树脂乳液内墙标准，达到合成树脂乳液外墙标准，且还具有防火、防霉功能，极大地提高涂料的性能。
以上所述仅是本发明的较佳实施方式，故凡依本发明专利申请范围所述特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。
Claims (9)
1.一种环保涂料，其特征在于：按质量百分比的组成配比如下：去离子水150-350‰、硅片剂0.1-1.5‰、分散剂2-8‰、润湿剂0.5-4.5‰、钛白粉100-250‰、云母粉25-150％、高钙粉100-300‰、消泡剂0.5-4.5‰、净味粉2-6‰、硅丙乳液30-120‰、硅酸钾150-350‰、稳定剂2-8‰、杀菌剂0.5-3.5‰、增稠剂A0.5-3.5‰、增稠剂B0.5-3.5‰、纤维素2-8‰、增稠剂C2-10‰。
2.根据权利要求1所述的一种环保涂料，其特征在于：按质量百分比的组成配比如下：去离子水240‰、硅片剂0.7‰、分散剂5‰、润湿剂2‰、钛白粉150‰、云母粉75％、高钙粉200‰、消泡剂2‰、净味粉4‰、硅丙乳液70‰、硅酸钾250‰、稳定剂5‰、杀菌剂1.5‰、增稠剂A2‰、增稠剂B2‰、纤维素)5‰、增稠剂C6‰。
3.根据权利要求1所述的一种环保涂料，其特征在于：按质量百分比的组成配比如下：去离子水220‰、硅片剂0.5‰、分散剂5‰、润湿剂2.2‰、钛白粉180‰、云母粉85％、高钙粉210‰、消泡剂3‰、净味粉3‰、硅丙乳液60‰、硅酸钾220‰、稳定剂4‰、杀菌剂1.5‰、增稠剂A1.5‰、增稠剂B1.5‰、纤维素5‰、膨润土增稠剂6‰。
4.根据权利要求1所述的一种环保涂料，其特征在于：按质量百分比的组成配比如下：去离子水260‰、硅片剂0.9‰、分散剂5.2‰、润湿剂2.4‰、钛白粉170‰、云母粉75％、高钙粉210‰、消泡剂3‰、净味粉3‰、硅丙乳液60‰、硅酸钾200‰、稳定剂3‰、杀菌剂3‰、增稠剂A2‰、增稠剂B2‰、纤维素4‰、增稠剂C5.5‰。
5.根据权利要求1所述的一种环保涂料，其特征在于：按质量百分比的组成配比如下：去离子水200‰、硅片剂0.5‰、分散剂4.8‰、润湿剂2.6‰、钛白粉200‰、云母粉84％、高钙粉220‰、消泡剂2，5‰、净味粉2.5‰、硅丙乳液50‰、硅酸钾220‰、稳定剂3.5‰、杀菌剂3.5‰、增稠剂A3.5‰、增稠剂B3.5‰、纤维素3.5‰、增稠剂C4.5‰。
6.根据权利要求1所述的一种环保涂料，其特征在于：所述增稠剂A为型号为936型的增稠剂。
7.根据权利要求1所述的一种环保涂料，其特征在于：增稠剂B为型号是618型的增稠剂。
8.根据权利要求1所述的一种环保涂料，其特征在于：增稠剂C为膨润土增稠剂。
9.根据权利要求1所述的一种环保涂料，其特征在于：所述纤维素为型号为250HBR的羟乙基纤维素。