CN101358116A - 60固含量丙烯酸酯类油性压敏胶水及其制备方法 - Google Patents

60固含量丙烯酸酯类油性压敏胶水及其制备方法 Download PDF

Info

Publication number
CN101358116A
CN101358116A CNA2007100444074A CN200710044407A CN101358116A CN 101358116 A CN101358116 A CN 101358116A CN A2007100444074 A CNA2007100444074 A CN A2007100444074A CN 200710044407 A CN200710044407 A CN 200710044407A CN 101358116 A CN101358116 A CN 101358116A
Authority
CN
China
Prior art keywords
sensitive adhesive
solid content
solid
viscosity
pressure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100444074A
Other languages
English (en)
Inventor
曹英杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Zeafee Digital Inkjet Composite Material Co Ltd
Original Assignee
Shanghai Zeafee Digital Inkjet Composite Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Zeafee Digital Inkjet Composite Material Co Ltd filed Critical Shanghai Zeafee Digital Inkjet Composite Material Co Ltd
Priority to CNA2007100444074A priority Critical patent/CN101358116A/zh
Publication of CN101358116A publication Critical patent/CN101358116A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种60固含量丙烯酸酯类油性压敏胶，其固含量为≥60％，优选60－62％，黏度1000－3500CPS，优选1500－2500CPS，其原料配方包含丙烯酸异辛酯、丙烯酸丁酯、醋酸乙烯酯、丙烯酸、分子量调节剂、偶氮二异丁腈、乙酸乙酯、乙醇、固化剂、黏度调节剂。本发明还提供了制备60固含量丙烯酸酯类油性压敏胶的工艺步骤和条件。由于固含量得到提高，在涂布同样干胶膜的状态下，可以降低湿胶涂布量，从而降低成本，降低能耗；又由于其黏度在1000－3500CPS范围之内，故对于普通的逗号刮刀比较适用。

Description

60固含量丙烯酸酯类油性压敏胶水及其制备方法
技术领域
本发明属于压敏胶技术领域，具体涉及一种丙烯酸酯类油性压敏胶水及其制作方法。
背景技术
按使用分类，压敏胶水有水性、醇溶性和油溶性三类。其中，水性压敏胶存在耐水性差、内聚力低、粘接材料少、表面活性剂析出等一系列问题，因此在推广上遇到较大问题；而醇溶性丙烯酸酯类压敏胶固含量比较低，成本比较高，性能不及油溶性压敏胶，因此推广应用也有一定的局限性；目前丙烯酸酯类油性压敏胶的使用量是相对较大的品种。但是，油性压敏胶在生产时放热量大，固含量越高反应越难控制，而且高固含的胶水黏度高，不利于均匀涂布，因此现有丙烯酸酯类油性压敏胶的固含量一般控制在50％以下。油性压敏胶的特性，使得现有丙烯酸酯类油性压敏胶存在固含量低、其生产过程不利于节约能源和环保，且成本高的缺点。
发明内容
本发明的任务是针对现有丙烯酸酯类压敏胶的不足，提供一种能够利于涂布，节约能源，耐水的高固含量丙烯酸酯类压敏胶配方及其制备方法。
本发明技术方案：
一种丙烯酸酯类油性压敏胶，其特征在于压敏胶的固含量为≥60％，优选60-62％，黏度1000-3500CPS，优选1500-2500CPS，其原料配方及各成份的含量为：
丙烯酸异辛酯      20-50％
丙烯酸丁酯        10-40％
醋酸乙烯酯      10-30％
丙烯酸          1-5％
分子量调节剂    5-10‰
偶氮二异丁腈    5-10‰
乙酸乙酯        10-50％
乙醇            10-50％
固化剂          1-10‰
黏度调节剂      1-10‰。
本发明提供的制备丙烯酸酯类油性压敏胶的工艺步骤和条件是：
按原料配方将丙烯酸异辛酯、丙烯酸丁酯、醋酸乙烯酯、丙烯酸、分子量调节剂、偶氮二异丁腈、乙酸乙酯和乙醇均匀混合，然后加入反应釜，加入量为反应釜的1/5，开始加热，在70-85℃之间反应1-2小时后，滴加剩余的反应物在2-5小时内滴加完成，滴加完成后保温2-5小时后，降温至50℃以下，加入固化剂和黏度调节剂，随后即可出料。
产品指标为固含量为≥60％，黏度1000-3500CPS。
由于本发明产品固含量得到提高，在涂布同样干胶膜的状态下，可以降低湿胶涂布量，从而降低成本，降低能耗；又由于其黏度在1000-3500CPS范围之内，故对于普通的逗号刮刀比较适用。
具体实施方式
本实施例采用配方为：
丙烯酸异辛酯    25％
丙烯酸丁酯      17％
醋酸乙烯酯      15％
丙烯酸          4％
分子量调节剂    5‰
偶氮二异丁腈    5‰
乙酸乙酯        19％
乙醇            18％
固化剂          5‰
黏度调节剂      5‰
上述所选材料均为工业级试剂。
本实施例的制备工艺步骤和条件是：
按上述原料配方将丙烯酸异辛酯、丙烯酸丁酯、醋酸乙烯酯、丙烯酸、分子量调节剂、偶氮二异丁腈、乙酸乙酯和乙醇均匀混合，然后加入反应釜，加入量为反应釜的1/5，开始加热，在70-85℃之间反应1-2小时后，滴加剩余的反应物且在2-5小时内滴加完成，滴加完成后保温2-5小时后，降温至50℃以下，加入固化剂和黏度调节剂，随后即可出料。
产品指标为固含量为60-62，黏度1500-2500CPS。

Claims (3)

1.一种60固含量丙烯酸酯类油性压敏胶，其特征在于压敏胶的固含量为≥60％，黏度1000-3500CPS，其原料配方及各成份的含量为：
丙烯酸异辛酯    20-50％
丙烯酸丁酯      10-40％
醋酸乙烯酯      10-30％
丙烯酸          1-5％
分子量调节剂    5-10‰
偶氮二异丁腈    5-10‰
乙酸乙酯        10-50％
乙醇            10-50％
固化剂          1-10‰
黏度调节剂      1-10‰。
2.根据权利要求1所述的一种60固含量丙烯酸酯类油性压敏胶，其特征在于压敏胶的固含量优选60-62％，黏度优选1500-2500CPS。
3.一种制备60固含量丙烯酸酯类油性压敏胶的方法，其工艺步骤和条件是：
按原料配方将丙烯酸异辛酯、丙烯酸丁酯、醋酸乙烯酯、丙烯酸、分子量调节剂、偶氮二异丁腈、乙酸乙酯和乙醇均匀混合，然后加入反应釜，加入量为反应釜的1/5，开始加热，在70-85℃之间反应1-2小时后，滴加剩余的反应物在2-5小时内滴加完成，滴加完成后保温2-5小时后，降温至50℃以下，加入固化剂和黏度调节剂，随后即可出料。
CNA2007100444074A 2007-07-31 2007-07-31 60固含量丙烯酸酯类油性压敏胶水及其制备方法 Pending CN101358116A (zh)