CN101328686B - Non-coating sport and leisure fabric having high hydraulic pressure resistance - Google Patents
Non-coating sport and leisure fabric having high hydraulic pressure resistance Download PDFInfo
- Publication number
- CN101328686B CN101328686B CN200710023857A CN200710023857A CN101328686B CN 101328686 B CN101328686 B CN 101328686B CN 200710023857 A CN200710023857 A CN 200710023857A CN 200710023857 A CN200710023857 A CN 200710023857A CN 101328686 B CN101328686 B CN 101328686B
- Authority
- CN
- China
- Prior art keywords
- fabric
- coating
- crux
- inch
- scope
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a non-coating sports leisure fabric with higher water-pressure resistance. The fabric is characterized in that: at least one yarn type of warp yarn or weft yarn is high-shrinkage yarn or superfine fiber; the fabric is woven at a higher density, and silicon-containing soft resin is added to fill in interfiber clearance during functional finishing after weaving; and finally, only calendering is carried out without adopting coating processing. A method for making the fabric comprises the steps of weaving, raw fabric scouring, relaxation, dyeing and functional finishing. The non-coating sports leisure fabric has smooth and thick feeling, simple and easy manufacturing method, higher density and higher water-pressure resistance.
Description
Technical field:
The present invention relates to the method for a kind of textiles and preparation thereof.
Background technology:
Modern life people pursue comfortable, environmental protection in dress.The dress material that has higher water-fast pressure energy now on the market is handled through coating or pad pasting processing basically.And the higher water pressure resistance lining that has of our exploitation just is meant and need do coating processing or pad pasting processing during fabrication; But plain weave or plain weave alternative construction through selecting higher density for use; Institutional framework is arranged closely; Add flood agent and siliceous soft resina when machining functions is put in order through special processing and in the back, the non-coating article of making like this have higher water-fast pressure energy.The VHD lining of Polyester Yarns reaches soft, smooth, abundant feel through processing later.And compare with coating, pad pasting article, having certain advantage aspect cost, the ventilative and environmental protection, so have good market prospects.
Summary of the invention:
The object of the present invention is to provide a kind of higher density that has, have higher watertight non-coating CRUX facing fabric and production method thereof.
Technical solution of the present invention:
A kind of have a higher watertight non-coating CRUX facing fabric, and it is characterized in that: having a yarn kind in warp thread or the weft yarn at least is high-shrinkage yarn line or superfine fibre; The employing higher density is weaved, and when carrying out functional treatment after weaving, adds and crams the siliceous soft resin in space between fiber; Through calendering technology lining is made its dry heat treatment with plentiful soft hand feeling in arrangement setting back, but need not do coating processing.
With JIS is testing standard, and finished product initial stage and washing, 20 later water pressure resistances reached 800mmH
2The above level of O.
The tow fineness scope of said superfine fibre is 50~300 DENIERs; The filament number scope is: 0.2 DENIER~1.2 DENIERs.
The tow fineness scope of said high-shrinkage yarn line is 50~300 DENIERs; Boiling water shrinkage is more than 8%.
Fabric tissue adopts the plain weave of compact conformation or changes plain weave.
The scope of fabric compactness is: 75%~95%.
Said higher density is meant that grey cloth through close scope is: 100~300/inch; The filling density scope is: 80~150/inch.
A kind of have a higher watertight non-coating CRUX facing fabric manufacturing approach, comprise weave, step such as grey cloth is concise, lax, dyeing, functional treatment, it is characterized in that: grey cloth through close scope is: 100~300/inch; The filling density scope exists: 80~150/inch; The rate of sizing exists when weaving cotton cloth: 8%~12%; Lax leavening agent concentration is 1~2g/L, 100~120 ℃ of maximum temperatures, and the time 10min-20min that maximum temperature stops, heating rate are 1 ℃/Min~1.5 ℃/Min, rate of temperature fall is 2 ℃/Min~3 ℃/Min, bath raio: 1:10~1:20; When carrying out functional treatment, add and cram the siliceous soft resin in space between fiber.
Resin condition during functional treatment: resin adopts padding method, and the agent concentration that floods is at 4.0%-6.0%, and siliceous soft resina concentration is 1.0%~2.0%, and pick-up is at 30%-60%, and baking temperature is at 120 ℃-130 ℃, drying time 30S-120S.
Calendering condition: Taiwan calender, 140 ℃-160 ℃ of temperature, cloth speed 20m/min-30m/min, nip pressure 60/60N.
Product of the present invention has smooth and abundant feel, and production method is simple, need not do coating processing.Product has higher density, has higher water pressure resistance.
Below in conjunction with embodiment the present invention is further specified.
Embodiment 1:
A kind of have higher watertight non-coating CRUX facing fabric, a plain weave; The high-shrinkage yarn line that its warp thread adopts, its boiling water shrinkage is 14.4%; The superfine fibre that weft yarn adopts, its filament number is: 0.358 DENIER; Through the 24.3/cm of reed density that selects for use; The filling density wheel is used 102T; Sizing rate of yarn: 10%; The water spray dobbies is weaved, and weaving tension is 3000N; Revolution speed: 500PRM; 195/inch of grey cloth specification * 110/inch.
Above-mentioned grey cloth goes out typing → calendering engineering and makes finished product through concise → lax → drying → centre typing → dyeing → drying → functional treatment (comprising dried resin) → width of cloth.The tightness of finished product: 76%
The critical process condition:
Relaxation condition: 120 ℃ of flows are lax,
Swelling agent: 1g/L when lax, bath raio: 1:20, heating rate are at 1.5 ℃/Min, and the maximum temperature retention time: 120 ℃ * 15MIN, rate of temperature fall is at 2 ℃/Min.
The dried resin condition: resin adopts padding method.(one soaks one rolls)
The agent of flooding: 6.0% (as far as total liquid)
Siliceous soft resina: 2.0% (as far as total liquid)
Pick-up: 55%
Calendering condition: Taiwan calender, 160 ℃ of temperature, cloth speed 20m/min, pressure 60/60N.
Make the density that product has superelevation (209/inch*122 root/inch) through above step; JIS standard testing finished product initial stage water pressure resistance: 822mmH
2O;
Water pressure resistance: 968mmH after washing 20 times
2O
Embodiment 2:
A kind of have higher watertight CRUX facing fabric, a plain weave; It all adopts identical superfine fibre through weft yarn, and its filament number is: 0.5 DENIER; Through the 23.2/cm of reed density that selects for use; The filling density wheel is used 94T; Sizing rate of yarn: 12%; The water spray dobbies is weaved; Weaving tension: 2500N; Revolution speed: 547RPM; 183/inch*96 of grey cloth specification root/inch.Above-mentioned grey cloth goes out typing → calendering engineering through concise → dyeing → drying → functional treatment (comprising dried resin) → width of cloth and makes finished product.The tightness of finished product fabric is: 80%.
The critical process condition:
The dried resin condition: resin adopts padding method.(one soaks one rolls)
Siliceous soft resina: 1% (as far as total liquid)
The agent of flooding: 6.0% (as far as total liquid)
Pick-up: 50%
The calendering condition:
The Taiwan calender, 160 ℃ of temperature, cloth speed 20m/min, pressure 60/60N.
Making product through above step through filling density is: 206/inch * 110/inch.
JIS standard testing finished product initial stage water pressure resistance: 911mmH
2O;
Water pressure resistance: 1146mmH after washing 20 times
2O.
Claims (5)
1. one kind has higher watertight non-coating CRUX facing fabric, and it is characterized in that: having a yarn kind in warp thread or the weft yarn at least is the high-shrinkage yarn line; The employing higher density is weaved, and when carrying out functional treatment after weaving, adds and crams the siliceous soft resin in space between fiber; Make it have the dry heat treatment of plentiful soft hand feeling through calendering technology to lining in arrangement setting back; The tow fineness scope of said high-shrinkage yarn line is 50~300 DENIERs; Boiling water shrinkage is more than 8%; Said higher density is meant that grey cloth exists through close scope: 100~300/inch; The filling density scope exists: 80~150/inch.
2. according to claim 1 have a higher watertight non-coating CRUX facing fabric, it is characterized in that: be testing standard with JIS, water pressure resistances all reach 800mmH after finished product initial stage and the washing 20 times
2The above level of O.
3. a kind of higher watertight non-coating CRUX facing fabric that has according to claim 1 is characterized in that: fabric tissue adopts the plain weave of compact conformation or changes plain weave.
4. according to claim 1 have a higher watertight non-coating CRUX facing fabric, and it is characterized in that: the scope of fabric compactness is: 75%~95%.
5. one kind as claimed in claim 1ly has a higher watertight non-coating CRUX facing fabric manufacturing approach; Comprise weave, grey cloth is concise, lax, dyeing, functional treatment step, it is characterized in that: grey cloth through close scope is: 100~300/inch; The filling density scope is: 80~150/inch; The rate of sizing is: 8%~12%; Leavening agent concentration is 1~2g/L when lax, 100~120 ℃ of maximum temperatures, and the time 10min-20min that maximum temperature stops, heating rate are 1 ℃/Min~1.5 ℃/Min, rate of temperature fall is 2 ℃/Min~3 ℃/Min, bath raio: 1:10~1:20; When carrying out functional treatment, add the siliceous soft resin of cramming fibre space.