CN101440547A - Terylene leisure sport fabric with elastic weft and warp - Google Patents
Terylene leisure sport fabric with elastic weft and warp Download PDFInfo
- Publication number
- CN101440547A CN101440547A CNA2007101904272A CN200710190427A CN101440547A CN 101440547 A CN101440547 A CN 101440547A CN A2007101904272 A CNA2007101904272 A CN A2007101904272A CN 200710190427 A CN200710190427 A CN 200710190427A CN 101440547 A CN101440547 A CN 101440547A
- Authority
- CN
- China
- Prior art keywords
- fabric
- warp
- terylene
- yarn
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses terylene sports fabric with elastic warp yarns and weft yarns. The fabric is characterized in that: at least one of the warp yarn and weft yarn is high-elasticity yarn prepared by the combination of polyethylene terephthalate(PET) and polypropylene terephthalate(PTT), the denier of the warp yarn and weft yarn is between 50 and 300D, and the denier per filament is between 0.5 and 3.2D. The fabric has the characteristics of loose texture, soft touch, good elasticity and drapability, good size stability, easy washing, no need of ironing, water resistance, stain resistant and the like.
Description
Technical field:
The present invention relates to a kind of production of elasticity textile product.
Background technology:
People require because of growth in the living standard the wearability of textiles, and more and more high.In recent years, elastic fabric is subjected to liking of people gradually, is a current class textiles with fastest developing speed.
The elastic fabric of indication now, major part are meant the latitude bullet or through bullet, based on the latitude bullet.The elastomer textiles mainly is divided into elastic spandex fiber, PBT fiber, ptt fiber, elastomer composite yarn etc. by kind and composition, and spandex is a kind of spandex, mainly is to carry out blending and produce the rubber-like yarn with other yarn; The fabric elasticity that is made into this kind yarn is bigger, but the shortcoming easy crimping that is fabric, fold and price comparison are expensive, and elasticity is difficult for controlled in process; With PTT or the pure short fiber elastomeric yarn that spins of PBT, though they can directly be weaved, also can satisfy the requirement of general textiles, their exist, and yielding, the easy firing of being heated, mechanical brute force are lower, fabric shape instability etc. lacks, so generally do not use separately.And the fabric that we are made into PTT and the compounded high elasticity complex yarn of PET just in time can be avoided the generation of above problem, and fabric elasticity is good, and recovery is strong, and DIMENSIONAL STABILITY is strong, and easily washing is dry, has overcome the bad problem of elastomeric polyurethane fiber fabric COLOR FASTNESS.
Summary of the invention:
The object of the present invention is to provide a kind of warp, the equal rubber-like terylene of broadwise outdoor activity fabric.
Technical solution of the present invention is:
A kind of longitude and latitude is rubber-like terylene outdoor activity fabric all, it is characterized in that: warp thread and weft yarn are at least a to be the high elasticity yarn that is composited by polyethylene terephthalate (PET) and polytrimethylene terephthalate (PTT), warp, weft yarn fiber number are between 50D-300D, and filament number is between 0.5D-3.2D.
Polyethylene terephthalate that described high-tension yarn is contained and polytrimethylene terephthalate mixed proportion are 1%:99%-99%:1%.
According to the JIS evaluation criterion, finished product warp-stretch rate is 5%-30%, and elastic recovery rate is more than 80%, and broadwise warp-stretch rate is 5%-30%, and elastic recovery rate is more than 80%.
Be organized as three foundation weave or multi-arm figured texture weave.
Also contain waterproof, grease proofing, antifouling resin composition in the fabric.
Product of the present invention has elastic effect, and all has high elasticity through broadwise, has alleviated the constraint sense of clothes to health in wearing process, thereby comfortable and easy to wear being convenient to of people moved.Product has that quality is fluffy, soft, elasticity is sufficient, drapability good, DIMENSIONAL STABILITY is good, easily washs, exempts from flatiron, characteristics such as waterproof, anti-soil.This lining is more comfortable in wearing motion process, and is convenient.
The invention will be further described below in conjunction with embodiment.
The specific embodiment:
Embodiment 1:
A kind of longitude and latitude is rubber-like terylene outdoor activity fabric all, be organized as 1/2 twill left to right, the 50D-24-DTY that it all adopts through weft yarn, be composited by polyethylene terephthalate (PET) and polytrimethylene terephthalate (PTT), polyethylene terephthalate (PET) accounts for 50%, and polytrimethylene terephthalate (PTT) accounts for 50%, and filament number is 2 DENIER, warp twist: S350T/M weaves at field, Tianjin coltfoal water spray dobbies.Weaving tension: 1500N, winding number 500RPM, pickwheel: 107T, grey cloth are through filling density: 168/inch*109 root/inch.
Above-mentioned grey cloth is by grey cloth typing → lax concise → middle typing → dyeing → drying → functional treatment (comprising dry resin) → hot blast stentering forming.Finally make finished product.Finished product is through filling density: 247/inch*168 root/inch.
Key process parameter
Grey cloth typing: temperature 130 degree, speed 50M/MIN, overfeeding+1.0%, wind speed 30HZ.
Lax concise: temperature 95 degree speed: 60m/min, the time of staying: 15 ~ 20 seconds.
Middle setting temperature: 180 degree, speed: 50m/min sets fabric width: 155cm, and fabric width is over: 154cm, wind speed: 30HZ, cropping adopts the mode of shaking and.
Dyeing maximum temperature: 120 degree * 30min, programming rate: 1.5 degree/min, cooling rate: 2.0 degree/min, bath raio: 1:20
The wire guide baking temperature: 130 degree, speed: 50m/min, cropping adopts the mode of shaking.
Functional treatment processing (dry resin): resin machine employing one is soaked one and is rolled method, water-sprinkling agent NDN-07 (trade name), isopropyl alcohol: 2.0G/L, acid: 2.0G/L, antistatic agent AG ACCEL700 (trade name): 1.0G/L, cloth speed: 50m/min, pick-up: 50%, cropping adopts the mode of shaking.
The width of cloth goes out typing: temperature 160 degree, and speed: 60m/min sets fabric width: 148cm, the fabric width 148cm that is over, wind speed: 30HZ, the overfeeding wheel: 3.5%, cropping adopts the mode of shaking
The product that makes by above step all has high elasticity through broadwise, and comfortable feel, gloss are soft, the fine and smooth softness of quality, drapability are good.Have the antifouling characteristics of waterproof and oilproof.
Assessment method: JIS standard.Finished product warp-stretch rate reaches 10%, and elastic recovery rate reaches 90%, and broadwise warp-stretch rate reaches 15%, and elastic recovery rate reaches 90%.
Embodiment 2:
A kind of longitude and latitude is rubber-like terylene outdoor activity fabric all, tissue adopts and changes plain weave, it all adopts 50D-32-DTY through weft yarn, be composited by polyethylene terephthalate (PET) and polytrimethylene terephthalate (PTT), polyethylene terephthalate (PET) accounts for 60%, polytrimethylene terephthalate (PTT) accounts for 40%, and filament number is 1.6D, weaves at field, Tianjin coltfoal water spray dobbies.Weaving tension: 1600N, winding number 530RPM, squeeze into number: 130/inch, grey cloth is through filling density: 120/inch*132 root/inch.
Above-mentioned grey cloth by grey cloth typing → lax refining → centre typing → dyeing → drying → arrangement typing → applying → after flood finalize the design on processing → bodyguard → cold rolling.Make product.Finished product is through filling density: 168/inch*152 root/inch.
Key process parameter
Grey cloth typing: temperature: 150 degree, speed: 45m/min sets fabric width: 175cm, and fabric width is over: 175cm, wind speed: 30HZ, cropping adopts the mode of shaking.
Lax concise temperature 95 degree speed: 60m/min, the time of staying: 15 ~ 20 seconds.
Middle setting temperature: 180 degree, speed: 30m/min sets fabric width: 160cm, and fabric width is over: 160cm, wind speed: 30HZ, cropping adopts the mode of shaking.
Dyeing maximum temperature: 120 degree * 30min, programming rate: 1.5 degree/min, cooling rate: 2.0 degree/min, bath raio: 1:20
The wire guide baking temperature: 130 degree, speed: 50m/min, cropping adopts the mode of shaking.
The width of cloth goes out typing: temperature 160 degree, and speed: 60m/min sets fabric width: 145cm, the fabric width 147cm that is over, wind speed: 30HZ, the overfeeding wheel: 3.5%, cropping adopts the mode of shaking.
Applying resin NH320, speed: 20m/min, the warp-wise tension force 1KG that curls.
After temperature 120 degree that floods, water-sprinkling agent NDN-07 (trade name): 10.0G/L, stiffening agent Sumitex Resin M-3 (trade name): 0.5G/L, bridging agent SumitexAccelerator ACX (trade name): 0.1G/L, isopropyl alcohol: 2.0G/L, acid: 2.0G/L, softener: 0.8G/L, softener: 0.3G/L, cloth speed: 15m/min, pick-up: 50%.The warp-wise tension force 1KG. that curls
Finalize the design on the bodyguard: temperature 160 degree, speed: 60m/min sets fabric width: 145cm, the fabric width 145cm that is over, wind speed: 30HZ, the overfeeding wheel: 2.0%, the warp-wise tension force 1KG. that curls
Cold rolling temperature: 30 degree, speed 25m/min, pressure: 60T/60T, the warp-wise tension force 1KG. that curls
The product that makes by above step all has high elasticity through broadwise, and comfortable feel, gloss are soft, the fine and smooth softness of quality, drapability are good.Have the antifouling characteristics of waterproof and oilproof.
Finished product warp-stretch rate reaches 15%, and elastic recovery rate reaches more than 90%, and broadwise warp-stretch rate reaches 20%, and elastic recovery rate reaches more than 90%.
Claims (4)
1, a kind of longitude and latitude rubber-like terylene outdoor activity fabric all, it is characterized in that: warp thread and weft yarn are at least a to be the high elasticity yarn that is composited by polyethylene terephthalate and polytrimethylene terephthalate, warp, weft yarn fiber number are between 50D-300D, and filament number is between 0.5D-3.2D.
2, longitude and latitude according to claim 1 rubber-like terylene outdoor activity fabric all, it is characterized in that: polyethylene terephthalate that described high-tension yarn is contained and polytrimethylene terephthalate mixed proportion are 1%:99%-99%:1%.
3, longitude and latitude according to claim 1 and 2 rubber-like terylene outdoor activity fabric all, it is characterized in that: according to the JIS evaluation criterion, finished product warp-stretch rate is 5%-30%, and elastic recovery rate is more than 80%, broadwise warp-stretch rate is 5%-30%, and elastic recovery rate is more than 80%.
4, longitude and latitude according to claim 1 and 2 rubber-like leisure terylene motion fabric all is characterized in that: be organized as three foundation weave or multi-arm figured texture weave.