CN103300515B - A kind of multilamellar windproof fabric and application thereof - Google Patents
A kind of multilamellar windproof fabric and application thereof Download PDFInfo
- Publication number
- CN103300515B CN103300515B CN201210068578.1A CN201210068578A CN103300515B CN 103300515 B CN103300515 B CN 103300515B CN 201210068578 A CN201210068578 A CN 201210068578A CN 103300515 B CN103300515 B CN 103300515B
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- multilamellar
- windproof
- denier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of multilamellar windproof fabric and application thereof, this fabric is three-decker, and precoat is containing cotton fabrics;Intermediate layer is nonporous polyurethane film;Lining layer is pure fluffing WARP-KNITTING of washing, and in yarn be the terylene single thread of 10~30 Denier, table yarn be 20~90 Denier, the polyester multifilament of 12~100.The fabric of the present invention has the feel of plentiful softness, a high fissility, superior poisture-penetrability, water pressure resistance and wind-proof performance, thermal property, is suitable for making the trousers of dress in winter.
Description
Technical field
The present invention relates to a kind of multilamellar windproof fabric and application thereof, be specifically related to that a kind of to be particularly well-suited to make trousers many
Layer windproof fabric.
Background technology
In the winter environments such as severe cold, humidity, high wind, sleet, people select dress folder cotton-padded trousers or down wadded trousers.
Although wherein folder cotton-padded trousers protection effect is preferable, but relatively heavy and also unsightly, be not easy to action;And down wadded trousers in order to
Meet people's demand to clothing light weight sense, mostly use the fabric of superfine fibre and reduce down filler, but accordingly its
Windproof, warmth retention property is lowered by the most significantly, and wind can quickly enter in clothes thus take away the heat of human body, and people will feel more
Come the coldest.
In order to solve the windproof of fabric, major part product is all to have employed the membrane materials such as PU, TPU, PTFE to pass through at present
The chemical fibre series products that coating, laminating processing obtain.It is as a kind of for outdoor activity in Chinese patent CN101892598A discloses
Multilamellar fabric, use polyamide false twist yarn particular by precoat and lining layer, intermediate layer uses waterproof humidity-permeant film, by
Have employed polyamide false twist processing yarn in contact coldness and the mobility in view of fabric, its heat insulating ability is the most bad, so not
It is suitable for making the trousers of dress in winter;Although mentioning waterproof humidity-permeant film used in this patent can be non-porous film, but
Non-porous film the most unavoidably there will be the problems such as breathability is the best.
For the heat insulating ability of windproof fabric, people is the most also had to propose employing cotton fabric in underwear field, such as China
The ectonexine of the multilamellar windproof fabric disclosed in patent CN2422131Y uses bafta, and intermediate layer uses micro-cellular polyurethane bullet
Property thin film, although this type of bafta comfortableness is good, warmth retention property have also been obtained improvement simultaneously, but owing to being to use in underwear field,
And use micro-porous film, the water pressure resistance of fabric, windproof also a bit deficient in.
As the trousers fabric of dress in winter, it is desirable to develop a kind of outward appearance and look advanced, be suitable for severe cold, tide
The dress of the special adverse circumstances such as wet, high wind, has the fabric of the function such as warm and windproof.
Summary of the invention
It is an object of the invention to provide a kind of special adverse circumstances such as severe cold, humidity, high wind that are suitable for wear, have superior
Poisture-penetrability, water pressure resistance and thermal property and soft multilamellar windproof fabric and application thereof.
The technical solution of the present invention is as follows:
The multilamellar windproof fabric of present invention definition refers to that finished textile product at least includes two or more tissue layer, and these layers lead to
Cross to be fitted and connected and formed together.
The multilamellar windproof fabric of the present invention is three-decker, is made up of precoat, intermediate layer and lining layer, wherein precoat
For the woven fabric containing cotton fiber;Intermediate layer is nonporous polyurethane film;Lining layer is pure fluffing WARP-KNITTING of washing, and in yarn be 10~
The terylene single thread of 30 Denier, table yarn is 20~90 Denier, the polyester multifilament of 12~100.
Since it is considered that the problem such as water pressure resistance and warmth retention property, intermediate layer of the present invention uses nonporous polyurethane film;And nothing
Although hole polyurethane film can improve the warmth retention property of fabric, but can affect the water vapour permeability of fabric also simultaneously.Knit to improve
The poisture-penetrability of thing, lining layer of the present invention is pure to wash fluffing WARP-KNITTING, and in it, yarn is the terylene single thread of 10~30 Denier, table yarn
It is 20~90 Denier, the polyester multifilament of 12~100, the single fiber fiber number of the single fiber fiber number of table yarn≤inner yarn.Wherein lining layer
Selecting the double-layered structure of WARP-KNITTING, more preferably through the flat tissue of floss, putting down tissue through floss is double-layered structure, and its positive and negative can use
Different yarns, front uses the polyester multifilament of many radicals, and stringer is clear, and coil arranges in " V " type;Reverse side uses single washing
Synthetic fibre single thread, the long underlap of the front comb of fabric backing cover on the short underlap of rear comb, it can be ensured that fabric have soft,
The feature that good-extensibility, laddering are little, can improve the overall feel of finished product, stretching when being easy to laminating, fabric add carrying out fluffing
It is difficult to de-yarn man-hour.In yarn select single thread can ensure that yarn strength and the moisture permeability of fabric and fabric are windproof, simultaneously will not
Affect the water pressure resistance performance of fabric, the resistance to ag(e)ing of peel strength especially peel strength and washing resistance;Table yarn is 20
~90 Denier, the polyester multifilament fabric of 12~100 carry out fluffing processing after not only can improve fabric feeling but also fabric can be improved
Heat insulating ability, reduces fabric breathability;If radical is less than 12, feel is hardened;And higher than 100, fluffing adds yarn in man-hour
Line is easily broken, and difficulty of processing increases.Wherein table yarn more preferably 20~50 Denier, the polyester multifilament of 24~72, is so constituted
The gross weight of treble cloths can control between 280~350g, relatively light weight.If in, yarn fiber number is higher than 30 pellet Buddhist nuns
You, the fiber number of table yarn are higher than 90 Denier, and fabric can become heavy;If in, yarn fiber number is less than 10 Denier, the fiber number of table yarn
Less than 20 Denier, the intensity of fabric can be the lowest, and weaves difficulty, improves cost.
Precoat of the present invention is preferably the raising machine fabric formed by the cotton content yarn containing cotton staple more than 35%, more
Preferably textile raising machine fabric.Here in woven fabric, yarn count is at more than 32s, preferably 32~16s.If yarn count is thick
In 16s, it will ensure the performance balance of fabric by reducing density, the style of such fabric face can be the most rough, and fabric
Density is too low also will cause fabric seam, windproof lower degradation problem occur;If yarn count is narrower than 32s, fabric face
Style by preciosity, weaving cost also can improve, and fabric intensity also can reduce.
In the present invention, the density of precoat woven fabric is at 150~260/inch, and density is if above 260/inch's
Words, the space between yarn is too small, and fabric moisture transmission degree understands step-down and cost also can improve;And if being less than 150/inch, yarn
Space between line becomes big, the easy exposing surface of non-porous film in intermediate layer, and peel strength and heat insulating ability reduce, the windproof meeting of fabric
Reduce, particularly can affect resistance to ag(e)ing and the washing resistance of peel strength.
Woven fabric after precoat woven fabric is fluffing processing in the present invention.Precoat after fluffing processing on the one hand feel
Soft, surface has velvet and improves heat insulating ability and reduce the breathability of fabric simultaneously and improve windproof, on the other hand fluffing
Easily carrying out laminating processing after processing and can improve the peel strength of finished product, and the resistance to ag(e)ing of peel strength and wash durable
Property.
The intermediate layer of the present invention uses nonporous polyurethane elastica, owing to thin film itself does not has hole, therefore can ensure finished product
Water proofing property, windproof, heat insulating ability.The nonporous polyurethane film preferred hydrophilic nonporous polyurethane film of the present invention, by the parent of film
Water characteristic relies on the difference of vapour pressure inside and outside clothes, and from the place that pressure is high, steam is transferred to low place, it is achieved thereby that
Moisture-inhibiting function.In view of feel and the lightweight of finished product, present invention preferably employs grammes per square metre at 350g/cm2Following hydrophilic without
Hole elastic polyurethane film.Above-mentioned thickness preferably between 5~15um, more preferably 6~10um.If the thickness of film is less than 5um, raw
Producing difficulty, water pressure resistance, the performance such as windproof are difficult to ensure that;But thickness is more than 15um, the grammes per square metre of film will improve, and not only can
Damage the flexibility of film, also can affect peel strength resistance to ag(e)ing and washing resistance especially to peel strength, and
The clothing made can be the heaviest.
The concrete production method of multilamellar windproof fabric of the present invention:
Precoat:
Grey cloth singes → and cold dome → boil drift → tentering → mercerising → surface sanding → dyeing → finished product sizing → preshrinking;
Lining layer:
Concise → middle sizing → fluffing processing → dyeing → wet resin sizing;
Laminating processing:
Precoat and waterproof humidity-permeant film once fit engineering → maturation engineering → lining layer and waterproof humidity-permeant film secondary laminating
Engineering → calendering engineering, prepares the fabric of three-decker.
The moisture permeability of multilamellar windproof fabric of the present invention is at 10000g/m2More than 24h, heat insulating ability clo value more than 0.8,
The breathability of fabric is at 1cm3/cm2Below s, water pressure resistance is at 20000mmH2More than 0;After washing 24 hours strong through the stripping of broadwise
Degree is all at more than 300gf/cm, through the peel strength of broadwise all at more than 300gf/cm after ageing-resistant three weeks.It is suitable for making winter
Dress trousers, appearance style is rough, feel is fine and smooth.
Detailed description of the invention
The method of testing of each performance in the present invention is as follows:
(1) thickness
Tekurokku company 1/1000mm thickness gauge is used to measure;
(2) grammes per square metre
Test according to JIS L 1096 method;
(3) hand valuation
About the evaluation of the feel such as loftiness, soft feeling, the general evaluation result using 10 practicians (has 4 etc.
Level), ◎: excellent zero: good △: general ×: poor;
(4) water pressure resistance test
Test according to JIS L 1092 " water repellency test method of fibre ";
(5) moisture permeability test
Test according to JIS L 1099 " the moisture permeability test method of fibre ";
(6) peel strength test
Test according to JIS L 1089 " the peeling strength test method of fibre ";
(7) heat insulating ability test
Use KES Fabric Style instrument, test;
(8) air penetrability test
Test according to JIS L 1096 method;
(9) washing resistance
The washing machine using JIS L 1096 standard to specify, washs 24h continuously;
(10) ageing-resistant
Constant temperature and humidity machine, temperature 70 degree, humidity 90%RH, 3 weeks standing times.
Below in conjunction with embodiment and comparative example, the invention will be further described.
Embodiment 1
Precoat: all use 20s cotton yarn through weft yarn, weaves on air-jet loom, then through following processing: grey cloth is singed
(80m/min) → cold dome → boil drift → tentering (room temperature) → mercerising (70m/min) → surface sanding (15m/min) → continuous dyeing
→ finished product sizing (180 DEG C) → preshrinking (140 DEG C), prepares the textile raising machine fabric of 200/inch of finished product gross density;
Lining layer: in employing, yarn is the terylene single thread of 20 Denier, table yarn is 30 Denier, the polyester multifilament of 24, adopts
Braiding it is organized on tricot machine with putting down through floss, then through following processing: concise → middle → fluffing processing → dye of shaping (190 DEG C)
Color (125 DEG C) → wet resin is shaped, and prepares and pure washs fluffing WARP-KNITTING;
Laminating: selecting thickness is that the non-porous hydrophilic polyurethane film of 7.5um uses as intermediate layer, first by precoat and waterproof
Moisture permeable membrane is once fitted engineering (120 DEG C, 12m/min) → maturation engineering (40 DEG C, humidity 70%, 48h);Again by lining layer with anti-
Water moisture permeable membrane secondary is fitted, and actual conditions is with engineering of once fitting, final multilamellar windproof fabric specific performance such as table 1 institute prepared
Show.
Embodiment 2
Precoat be formed as weft yarn as warp thread, 16s cotton staple yarn by 20s cotton staple yarn finished product density 180/
The textile raising machine fabric of inch;Intermediate layer is the non-porous hydrophilic polyurethane film of thickness 6.0um;Lining layer is by 15 Denier
Terylene single thread is as inner yarn, and 50 Denier, the polyester multifilament of 48 pure wash fluffing WARP-KNITTING as what table yarn was formed, remaining work
Skill is with embodiment 1, and the final multilamellar windproof fabric specific performance prepared is as shown in table 1.
Embodiment 3
Precoat be formed as weft yarn as warp thread, 21s cotton staple yarn by 32s cotton staple yarn finished product density 240/
The textile raising machine fabric of inch;Intermediate layer is the non-porous hydrophilic polyurethane film of thickness 8.0um;Lining layer is by 20 Denier
Terylene single thread is as inner yarn, and 30 Denier, the polyester multifilament of 12 pure wash fluffing WARP-KNITTING as what table yarn was formed, remaining work
Skill is with embodiment 1, and the final multilamellar windproof fabric specific performance prepared is as shown in table 1.
Embodiment 4
Precoat for by through weft yarn all use finished product gross density 160 that 21s polyester-cotton blend yarn (T/C=35:65) formed/
The textile raising machine fabric of inch;Intermediate layer is the non-porous hydrophilic polyurethane film of thickness 8.5um;Lining layer is by 30 Denier
Terylene single thread is as inner yarn, and 50 Denier, the polyester multifilament of 36 pure wash fluffing WARP-KNITTING as what table yarn was formed, remaining work
Skill is with embodiment 1, and the final multilamellar windproof fabric specific performance prepared is as shown in table 1.
Embodiment 5
Precoat for by through weft yarn all use finished product gross density 250 that 32s polyester-cotton blend yarn (T/C=35:65) formed/
The textile raising machine fabric of inch;Intermediate layer is the non-porous hydrophilic polyurethane film of thickness 12um;Lining layer is by 30 Denier
Terylene single thread fluffs through oblique flat sennit fabric as inner yarn, pure the washing that 70 Denier, the polyester multifilament of 72 are formed as table yarn, its
Remaining technique is with embodiment 1, and the final multilamellar windproof fabric specific performance prepared is as shown in table 1.
Embodiment 6
Precoat is that the cotton textiles fluffing of the 220/inch of finished product gross density all using 30s cotton to be formed through weft yarn is woven
Thing;Intermediate layer is the non-porous hydrophilic polyurethane film of thickness 10um;Lining layer is as inner yarn by the terylene single thread of 20 Denier, 50
Denier, the polyester multifilament of 96 pure wash fluffing WARP-KNITTING as what table yarn was formed, and remaining technique, with embodiment 1, is finally made
The multilamellar windproof fabric specific performance obtained is as shown in table 1.
The multilamellar windproof fabric that embodiment 1-6 prepares is for making the trousers of dress in winter.
Comparative example 1
Precoat all use 20s cotton staple through weft yarn, air-jet loom is weaved, formed finished product density be 200/
The pure cotton woven fabric of inch;The nonporous polyurethane film that the waterproof humidity-permeant film in intermediate layer selects thickness to be 20um;Lining layer uses 50
Denier, the Polyester Yarns of 12, be knitted to form pure circle of washing on circle volume machine and compile thing;The exterior and the interior layer does not the most carry out fluffing processing, remaining
Technique is with embodiment 1, and the final multilamellar windproof fabric specific performance prepared is as shown in table 1.
Comparative example 2
Precoat all use 16s cotton staple through weft yarn, air-jet loom is weaved, formed finished product density be 120/
The pure cotton woven fabric of inch;The nonporous polyurethane film that the waterproof humidity-permeant film in intermediate layer selects thickness to be 40um;Precoat is not carried out
Fluffing processing, remaining technique is with embodiment 1, and the final windproof fabric specific performance prepared is as shown in table 1.
Comparative example 3
The Polyester Yarns all using 150 Denier through weft yarn of precoat, weaves on air-jet loom, by following processing:
Concise → dyeing → middle sizing (170 DEG C) → cylinder is dried → resin processing (resin that floods processing) → arrangement sizing → calendering
(160 DEG C), obtaining finished product density is that the pure of 280/inch washs woven fabric;2 conventional padding process are used to be starched by polyurethane again
Material forms the micro-porous film of thickness 50um, the final windproof fabric specific performance prepared in above-mentioned base fabric by wet-process coating
As shown in table 1.
Claims (4)
1. a multilamellar windproof fabric, is characterized in that: this fabric is three-decker, and precoat is containing cotton fabrics;Intermediate layer is
Thickness hydrophilic non-porous polyurethane film between 5~15um;Lining layer is pure fluffing WARP-KNITTING of washing, and in yarn be 10~30
The terylene single thread of Denier, table yarn is 20~90 Denier, the polyester multifilament of 12~100;This fabric washing is warp after 24 hours
Broadwise peel strength is all at more than 300gf/cm, through broadwise peel strength all at more than 300gf/cm after ageing-resistant three weeks.
The most according to claim 1, multilamellar windproof fabric, is characterized in that: described precoat be by cotton content more than 35%
The raising machine fabric that the yarn containing cotton staple is formed.
The most according to claim 1, multilamellar windproof fabric, is characterized in that: the moisture permeability of this fabric is at 10000g/m224h with
On, air penetrability is at 1cm3/cm2Below s, heat insulating ability clo value is more than 0.8, and water pressure resistance is at 20000mmH2More than 0.
4. one kind have employed the winter trousers of multilamellar windproof fabric described in claim 1.