CN101323767A - 一种环保粘合剂 - Google Patents
一种环保粘合剂 Download PDFInfo
- Publication number
- CN101323767A CN101323767A CNA2007100286598A CN200710028659A CN101323767A CN 101323767 A CN101323767 A CN 101323767A CN A2007100286598 A CNA2007100286598 A CN A2007100286598A CN 200710028659 A CN200710028659 A CN 200710028659A CN 101323767 A CN101323767 A CN 101323767A
- Authority
- CN
- China
- Prior art keywords
- solvent
- high molecular
- molecular polymer
- environment
- friendly adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种环保粘合剂，主要由高分子聚合物、溶剂和增塑剂组成。所述的高分子聚合物为聚乙烯醇类树脂，所述的增塑剂为苯二甲酸酯类化合物，所述的溶剂选自酯类、酮类和醇类中的至少1～2种。本发明无杂质，粘度稳定性好，主要用于生产高叠层片式多层陶瓷电容器，与陶瓷粉球磨后瓷粉分散均匀，流延后所得到的超薄电子陶瓷膜片均匀、平整光滑、无针孔、无气泡、不自动脱膜和剥落，并且流延后所挥发出来的气体对大气污染小。
Description
技术领域
本发明涉及一种粘合剂，尤其是指一种用于生产高叠层片式多层陶瓷电容器的粘合剂。
背景技术
近年来，电子陶瓷元件得到广泛的应用。在电子陶瓷元件的流延成膜工艺中，为了得到均匀、致密的膜层，除了必不可少的优质陶瓷粉外，同时还必需具备使陶瓷粉成膜的优质粘合剂。粘合剂的性能、质量直接影响成膜后陶瓷电子元件的质量。
目前，许多陶瓷电子元件企业所使用的粘合剂，主要由高分子聚合物、溶剂、增塑剂等组成，其中溶剂采用有毒性的芳香族有机物，如甲苯和二甲苯。中国ZL00131765.2提出了一种用于陶瓷浆糊组合物，其中就采用了甲苯或二甲苯作为溶剂使用；该粘合剂虽能达到良好地分散陶瓷粉的效果，保证了流延膜片的致密度，并且能使成膜后的膜片不自动脱膜和剥落，但是由于其中的溶剂在流膜后要全部挥发掉，不残留于产品中，对空气造成了严重的污染。
发明内容
本发明所需解决的问题是提供一种对大气无污染或污染极少，且性能良好的环保粘合剂。
根据上述需解决的问题设计了一种环保粘合剂，主要由高分子聚合物、溶剂、增塑剂及助剂等组成，所述的高分子聚合物为聚乙烯类树脂，所述的增塑剂为苯二甲酸酯类化合物，所述的溶剂选自酯类、酮类和醇类中的至少1～2种。
本发明所述的环保粘合剂为一种混合物，其中：高分子的含量为10～20重量％；溶剂的含量为60～85重量％；增塑剂的含量为3～6重量％；助剂的含量为3～9重量％。
本发明中溶剂要在电子元件流膜过程中保证流膜作用，并且在流膜后要全部挥发掉，不残剩留于产品中。因此，所述的溶剂必须考虑其溶解能力、粘度、沸点，同时还有考虑化学性质，毒性，气味等各种因素。为此，本发明的溶剂选自酯类、醇类和酮类中的至少1～2中，替代有毒的甲苯类芳香族溶剂。
本发明粘合剂无杂质，粘度稳定性好，与瓷粉球磨后瓷粉分散均匀，流延后所得到的膜片均匀、平整光滑、无针孔、无气泡、不自动脱膜和剥落，并且不会对大气造成污染。
具体实施方式
下面结合实施例对本发明的进行更详细的说明。
本发明主要由高分子聚合物、溶剂、增塑剂等组成，还可根据需要在其中加入助剂。其中高分子聚合物为聚乙烯醇类树脂，而聚乙烯醇类树脂为聚乙烯醇缩丁醛。增塑剂为苯二邻甲酸酯类化合物，而苯二甲酸酯类化合物为邻苯二甲酸二辛酯。溶剂选自酯类、酮类和醇类中的至少1～2种。作为溶剂的酯类为醋酸正丙酯，酮类为正丁酮，醇类为乙醇。所述的助剂具有润滑、脱模、消泡、分散等作用，助剂的含量以重量百分比计可占到总量的3～9。所述的助剂是常规的润滑剂、脱模剂、消泡剂、分散剂的组合，对本发明仅有如其名述的辅助性作用。
本发明是一种混合物，其中：高分子的含量为10～22重量％；溶剂的含量为60～90重量％；增塑剂的含量为3～8重量％。
实施例一
将作为溶剂使用的醋酸正丙酯与乙醇按照1∶1的比例混合均匀，抽取79份备用。再在备用的溶剂中分别缓慢加入作为高分子聚合物使用的聚乙烯醇缩丁醛树脂粉16份，在加入过程中进行搅拌直至聚乙烯醇缩丁醛树脂粉充分溶解。然后再加入作为增塑剂使用的5份邻苯二甲酸二辛酯(DOP)，搅拌均匀，并放入防尘室静置除泡处理4小时。所得的混合物即为本发明环保性粘合剂。
实施例二
将作为溶剂使用的正丁酮与乙醇按照1∶1的比例混合均匀，抽取79份备用。再在备用的溶剂中分别缓慢加入作为高分子聚合物使用的聚乙烯醇缩丁醛树脂粉16份，在加入过程中进行搅拌直至聚乙烯醇缩丁醛树脂粉充分溶解。然后再加入作为增塑剂使用的5份邻苯二甲酸二辛酯(DOP)，搅拌均匀，并放入防尘室静置除泡处理4小时。所得的混合物即为本发明环保性粘合剂。
实施例三
将作为溶剂使用的正丁酮∶醋酸正丙酯∶乙醇为1∶1∶1的比例混合均匀，抽取79份备用。再在备用的溶剂中分别缓慢加入作为高分子聚合物使用的聚乙烯醇缩丁醛树脂粉16份，在加入过程中进行搅拌直至聚乙烯醇缩丁醛树脂粉充分溶解。然后再加入作为增塑剂使用的5份邻苯二甲酸二辛酯(DOP)，搅拌均匀，并放入防尘室静置除泡处理4小时。所得的混合物即为本发明环保性粘合剂。
实施例四
将作为溶剂使用的醋酸正丙酯，抽取79份备用。再在备用的溶剂中分别缓慢加入作为高分子聚合物使用的聚乙烯醇缩丁醛树脂粉16份，在加入过程中进行搅拌直至聚乙烯醇缩丁醛树脂粉充分溶解。然后再加入作为增塑剂使用的5份邻苯二甲酸二辛酯(DOP)，搅拌均匀，并放入防尘室静置除泡处理4小时。所得的混合物即为本发明环保性粘合剂。
本发明粘合剂无杂质，粘度稳定性好。主要用于生产高叠层片式多层陶瓷电容器，与陶瓷粉球磨后瓷粉分散均匀，流延后所得到的超薄电子陶瓷膜片均匀、平整光滑、无针孔、无气泡、不自动脱膜和剥落，并且流延后所挥发出来的气体对大气污染小。
以上所述的仅是本发明的非限定性实施方式，组份含量的变化对本发明导出的粘合剂产品的特性无实质性影响，故未多次举例。另外，应当指出，本发明还可添加一些具有润滑、脱模、消泡、分散等作用的助剂。这些都属于发明的保护范围。
Claims (4)
1、一种环保粘合剂，由高分子聚合物、溶剂、增塑剂组成，
所述的高分子聚合物为聚乙烯醇类树脂，含量以重量百分比计占10～22；
所述的增塑剂为苯二甲酸酯类化合物，含量以重量百分比计占3～8；
所述的溶剂选自酯类、酮类和醇类中的至少1～2种，含量以重量百分比计占60～90。
2、根据权利要求1所述的环保粘合剂，其特征在于：所述的聚乙烯醇类树脂为聚乙烯醇缩丁醛。
3、根据权利要求2所述的环保粘合剂，其特征在于：作为溶剂的酯类为醋酸正丙酯，酮类为正丁酮，醇类为乙醇。
4、根据权利要求1或2所述的环保粘合剂，其特征在于：苯二甲酸酯类化合物为邻苯二甲酸二辛酯。