CN101323195A - Surface recombination technique of veneer and metal - Google Patents
Surface recombination technique of veneer and metal Download PDFInfo
- Publication number
- CN101323195A CN101323195A CNA200710041998XA CN200710041998A CN101323195A CN 101323195 A CN101323195 A CN 101323195A CN A200710041998X A CNA200710041998X A CN A200710041998XA CN 200710041998 A CN200710041998 A CN 200710041998A CN 101323195 A CN101323195 A CN 101323195A
- Authority
- CN
- China
- Prior art keywords
- wooden skin
- metal
- wood
- metal surface
- gluing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a surface recombination technology of wood skin and metal, including wood skin preparation, surface treatment of the metal and the wood skin, rubber coating, laminating, painting and other steps. In the invention, the wood skin is pasted on the surface of the metal, which can not only embody the special texture of wood and the function of heat insulation and sound attenuation typical of wood, and meet the vision and touch requirements of people, but also improve fire resistance rating of the whole dalle to reach the higher standards for fire fighting materials as inside of the wood is the metal plate with excellent fire retardancy. At last, the wood veneer is low in cost, thus the decoration cost can be reduced. Through detection, the adhesion strength of the wood skin can reach 0.5MPa.
Description
Technical field
The present invention relates to a kind of preparation method of composite decorative building material, concrete wooden skin and the metal surface combination process of relating to.
Background technology
Along with the development of society, people more and more tend to adopt the material with natural texture to carry out building decoration, and wood materials becomes wherein a kind of quite general selection.Timber itself has the sensation of warm nature, and can coordinate collocation with most family products.Therefore it is inflammable that but the fatal shortcoming of timber is, if use timber as finishing material then there is hidden danger in the fire-fighting in large area.Particularly, use the finishing mode of timber not meet its fireproof requirement in a large number for the demanding building of fire-fighting rank.And because the minimizing day by day of virgin forest resource, the growth cycle of timber is longer again, and the price of pure timber-work grows to even greater heights, and using timber to fit up has in a large number increased the cost of finishing undoubtedly.
At present composite material for decoration begins to be applied to the finishing in various places, and as pasting facing paper etc. on wood substrate, but the ornament materials of this class exists fire-protection rating and the not high shortcoming of intensity.Also have a kind of ornament materials that on ceramic base material, pastes all kinds of facing papers, but its toughness is bad, fragile.
Chinese patent CN1475374 discloses " the wooden leather jacket decorations technology on a kind of metallic door, case, cabinet surface "; this technology is when the wooden leather jacket decorations work of carrying out metallic door, case, cabinet metal surface; elder generation is according to the dimensional requirement of doing product; wooden skin is cut into different specifications; then; wooden skin up to specification is sticked with glue on bed course, and bed course adopts pliability better and pull resistance cloth and paper preferably, its objective is when protecting wooden skin to stick on metal level not to be damaged.After wood skin and bed course paste, just it is sticked with glue at the metal surface of the metallic door of having made, case, cabinet, get final product with clear finish at last.Metallic door, case, cabinet must the brushing antirusting paints before pasting wooden skin.But this method is not suitable for serialization production.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of wooden skin and metal surface combination process, to solve the existing in prior technology weak point.
The technical scheme that technical problem to be solved by this invention adopted is such:
A kind of wooden skin and metal surface combination process comprise the steps:
1, wooden leather is equipped with
Adopt the round log or the lumps of wood to come out with the slicing of carpenter's plane cutter, its thickness is between the 0.2mm-3mm, and length and width are decided according to the product of being produced; The moisture content of controlling wooden skin is below 12%;
2, the processing on metal and wooden skin surface
The metal surface is handled, polish with emery cloth during processing, with acetone soln the metal surface after polishing is handled, and use the hot blast drying Rough Metal Surface; Handle the gluing surface of wooden skin clean equally;
3, gluing
Uniform gluing on the gluing surface of the matsurface of metal and wooden skin, glue-spread is 80～140g/m
2, the adhesive of employing is a LK-140 aqueous, environmental protective glue, the viscosity of adhesive is 60000CP/20 ℃～100000CP/20 ℃; Behind the gluing airing 3-4 minute,
4, fit
The one side that wooden skin is scribbled adhesive is bonded at metal and scribbles on the one side of adhesive, drives bubble out of, carries out hot pressing, curing, 10～15kg/cm then
2, 100 ℃～110 ℃ of hot pressing temperatures, hot pressing time 5～7 minutes, solidification temperature is more than 5 ℃, be 6～8 hours hardening time;
5, japanning
Brush varnish 30-60 μ m on wooden skin and metal surface, the varnish of employing is zapon.
In above-mentioned combination process, metal is preferably aluminium sheet.This mainly be because aluminium sheet to have an antirust corrosion good, the advantage that weight is lighter can alleviate the decoration working strength of workers at decoration process like this.
The wooden skin that adopts is a kind of in Chinese hemlock spruce, dragon spruce, walnut, cherry, Chinese toon wood, the wooden skin of Beech.
The present invention posts wooden skin on the metal surface, can either embody the special quality of timber, satisfy the requirement in people's vision and the sense of touch, and effect such as the distinctive heat preserving sound deadening of timber, can be again metallic plate because of the inboard of wooden skin with excellent flame retardancy energy, and improve the fire resistance rating of whole dalle, reach very high fire-fighting requirement.At last, the cost of this wood veneer is lower, can reduce decoration cost.Through detecting, the bonding strength of wooden skin reaches 0.5MPA.
Description of drawings
Describe the present invention in detail below in conjunction with the drawings and specific embodiments;
Fig. 1 is the structural representation of the dalle of the present invention's preparation.
The specific embodiment
For technological means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with concrete diagram, further set forth the present invention.
A kind of wooden skin and metal surface combination process comprise the steps:
1, wooden leather is equipped with
Adopt the round log or the lumps of wood to come out with the slicing of carpenter's plane cutter, its thickness is between the 0.2mm-3mm, and length and width are decided according to the product of being produced; The moisture content of controlling wooden skin is below 12%; The wooden skin that adopts is a kind of in Chinese hemlock spruce, dragon spruce, walnut, cherry, Chinese toon wood, the wooden skin of Beech.
2, the processing on metal and wooden skin surface
Surface of aluminum plate is handled, polished with emery cloth during processing, with acetone soln the surface of aluminum plate after polishing is handled, and used the hot blast drying surface of aluminum plate; Handle the gluing surface of wooden skin clean equally;
3, gluing
Uniform gluing on the gluing surface of the matsurface of aluminium sheet and wooden skin, glue-spread is 100g/m
2, the adhesive of employing is a LK-140 aqueous, environmental protective glue, the viscosity of adhesive is 60000CP/20 ℃～100000CP/20 ℃; Airing is 1 minute behind the gluing;
4, fit
The one side that wooden skin is scribbled adhesive is bonded at aluminium sheet and scribbles on the one side of adhesive, drives bubble out of, applies certain pressure then and is cured, and force value is 12Kg/cm
2, hot pressing temperature is 100 ℃, and hot pressing time is 5 minutes, and solidification temperature is more than 5 ℃, and be 6 hours hardening time;
5, japanning
Brush varnish 30～60 μ m on wooden skin and surface of aluminum plate, the varnish of employing is zapon.
The Woodveneer structure of preparation can be referring to Fig. 1.Install and use in the process, wooden skin 1 is exposed to the outside that can observe directly, that is to say wooden skin 1 one sides outwardly and aluminium sheet 2 one sides inwardly.This wood veneer can be installed in all places such as ceiling, wall facade, floor, can form extraordinary decorative effect.Because all outer surfaces of wood veneer of the present invention all is sealed with paint, promptly wood veneer having been carried out the paint sealing handles, therefore can guarantee wood veneer stable performance of the present invention, not bonding not easily separated between wood skin and the metallic plate, and can effectively avoid the wooden facing change color that causes because of making moist and the distortion of wood veneer.
More than show and described basic principle of the present invention, principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification just illustrates principle of the present invention; the present invention also has various changes and modifications without departing from the spirit and scope of the present invention, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1, a kind of wooden skin and metal surface combination process is characterized in that, comprise the steps:
(1), wooden leather is equipped with
Adopt the round log or the lumps of wood to come out with the slicing of carpenter's plane cutter, its thickness is between the 0.1mm-2mm, and length and width are decided according to the product of being produced; The moisture content of controlling wooden skin is below 12%;
(2), the processing on metal and wooden skin surface
The metal surface is handled, polishes with emery cloth during processing,, with acetone soln the metal surface after polishing is handled, and use the hot blast drying Rough Metal Surface; Handle the gluing surface of wooden skin clean equally;
(3), gluing
Uniform gluing on the gluing surface of the matsurface of metal and wooden skin, glue-spread is 100～180g/m
2, the adhesive of employing is a LK-140 aqueous, environmental protective glue, the viscosity of adhesive is 60000CP/20 ℃～100000CP/20 ℃; Behind the gluing airing 1-2 minute;
(4), fit
The one side that wooden skin is scribbled adhesive is bonded at metal and scribbles on the one side of adhesive, drives bubble out of, carries out hot pressing, curing, 10～15kg/cm then
2, 100 ℃～110 ℃ of hot pressing temperatures, hot pressing time 5～7 minutes, solidification temperature is more than 5 ℃, be 6～8 hours hardening time;
(5), japanning
Brush varnish 30-60 μ m on wooden skin and metal surface, the varnish of employing is zapon.
2, wooden skin according to claim 1 and metal surface combination process is characterized in that, described metal is an aluminium sheet.
3, wooden skin according to claim 1 and metal surface combination process is characterized in that, the wooden skin of employing is a kind of in Chinese hemlock spruce, dragon spruce, walnut, cherry, Chinese toon wood, the wooden skin of Beech.