CN103753656A - Flexible composite veneer and processing method thereof - Google Patents
Flexible composite veneer and processing method thereof Download PDFInfo
- Publication number
- CN103753656A CN103753656A CN201410013628.5A CN201410013628A CN103753656A CN 103753656 A CN103753656 A CN 103753656A CN 201410013628 A CN201410013628 A CN 201410013628A CN 103753656 A CN103753656 A CN 103753656A
- Authority
- CN
- China
- Prior art keywords
- decorative veneer
- veneer
- paint
- compound
- decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a flexible composite decorative veneer and a processing method thereof. The flexible composite decorative veneer is composed of a decorative veneer layer and a plastic film layer, the plastic film layer is composited onto the decorative veneer layer by means of heating and pressurizing and serves as a flexibility enhancement layer of the decorative veneer and a veneer and substrate composite bonding layer as well. The composited decorative veneer layer of the flexible composite decorative veneer can be coated with or without oil paint. The veneer layer is made of natural decorative veneer or recombined decorative veneer 0.06-0.3mm in thickness. The plastic film layer is composed of processed or unprocessed plastic films made of polyethylene, polypropylene or other materials 0.02-0.8mm in thickness. The paint coating is composed of polyurethane primer, ultraviolet curing primer, nitrocellulose primer or the like. The flexible composite decorative veneer can be used for surface decoration of curved and planar portions of various wood products, windows, doors and boards, and the problem that traditional nonwoven fabric or paper-base decorative veneers are prone to glue penetration during processing and utilization is avoided. In addition, the decorative veneer is high in water tolerance, flexibility and environment friendliness, and quality and attractiveness of the decorative veneer can be guaranteed.
Description
Technical field
The present invention relates to a kind ofly with paint film or flexible compound decorative veneer and processing method thereof with paint film, belong to wood working industry, is a kind of new technology adopting in decoration finishing, woodwork, furniture, door and window curved surface or plane surface decoration field.
Background technology
Timber has good native texture and color and luster, gives fresh and clean sensation, is therefore subject to more and more people's favor.
Along with the deficient of precious timber resource and the continuous research to woodwork processing technology, veneer material is in indoor furniture finishing, woodwork manufacture, as more and more in used in the edge sealing of wood furniture, door and window, lines and cabinet etc. and curved surface or plane facing.
In the current curved surface at woodwork and furniture finishing, right angle face portion veneer, conventionally adopt the back side to post the decorative veneer of nonwoven or backing paper (without covering with paint, lacquer, colour wash, etc.), to avoid producing wood grain, ftracture, break and problem on deformation.But nonwoven is take oil as raw material, be difficult to degradable, and veneer and non-woven fabric compoundedly often adopt all kinds of adhesives, environmental protection relatively not; Simultaneously, because veneer is relatively thin, in manufacturing process, easily produce strike-through phenomenon, and along with the impact of illumination, temperature and humidity variation, easily produce peeling off of wooden skin and nonwoven, wooden skin and backing paper, affected the decorative effect of its surperficial veneer, greatly shortened the service life of wood tegument veener goods, and its resistance to water has been poor; In addition, without covering with paint, lacquer, colour wash, etc. again after the nonwoven decorative veneer veneer of covering with paint, lacquer, colour wash, etc., its japanning, dry and all relative complex of bruting process, production efficiency is low.
Summary of the invention
In view of above-mentioned problems of the prior art, the object of the present invention is to provide a kind of flexible compound veneer and processing method thereof, the seep through problem of having avoided traditional nonwoven decorative veneer to be prone in processing and use procedure, the attractive in appearance and quality of assurance decorative veneer; Can be directly used in curved surface and right angle coated, reduce the complicated technologies such as japanning, dry, polishing.
A kind of flexible compound veneer of the present invention and processing method thereof, comprise following technical scheme:
A kind of band paint film flexible compound veneer, comprises decorative veneer layer, plastic film layers and skin of paint, and plastic film layers is pressurizeed and is compound on decorative veneer by heating, then is coated with last layer conventional oil paint or elasticity paint on compound decorative veneer surface; Described decorative veneer layer is natural finiss veneer or the recombinant decorative veneer that 0.06～0.3mm is thick, also can be the decorative veneer through modification; Described plastic film layers is treated or untreated polyethylene, polypropylene or other materials plastic sheeting, and thickness is 0.02～0.5mm; Described skin of paint is (face) paint etc. at the bottom of (face) paint or nitro at the bottom of (face) paint, ultraviolet light polymerization at the bottom of polyurethane.
As such scheme preferably, described decorative veneer layer is natural finiss veneer or the recombinant decorative veneer that 0.06～0.3mm is thick, also can be the decorative veneer through modifications such as softening, charings.Described decorative veneer layer and plastic film layers compound tense, can be added to all kinds of coupling agents such as silane coupling agent, maleic anhydride class coupling agent and polyurethanes coupling agent.Described coupling agent, can be applied to decorative veneer, or plastic sheeting.Also coupling agent or additive etc. can be added in plastic granulating, through extrusion molding and polyethylene, polypropylene etc., make plastic sheeting.
Another object of the present invention is to provide a kind of with paint film or flexible compound veneer and processing method thereof with paint film.
A kind of band paint film flexible compound veneer and processing method thereof, comprise the following steps:
A) wood-planing is cut into the decorative veneer of 0.06mm～0.3mm; B) on plastic sheeting, be coated with coupling agent (also can not be coated with as required), coupling agent coating weight is plastic sheeting 1%～20%, then displays 1～20min; C) decorative veneer described in step a is compound in advance on the decorating film described in step b and forms composite plate blanks, then on the upper and lower surface of composite plate blanks, add respectively Antisticking (film), bottom surface pading plate or industrial felt, play buffering, levelling effect; D) described composite plate blanks is carried out to hot pressing, 100～180 ℃ of hot pressing temperatures, hot pressing pressure 0.1～1.0MP, hot pressing time 1～6 minute, can adopt first low rear high sublevel heat pressing process of pressure in hot pressing; E) Antisticking (film) with compound good decorative veneer is sent into oil paint production line, on flexible compound decorative veneer surface, adopt spraying, roll coating model to varnish with lacquer, through one or multi-channel japanning, dry, sanding step is made satisfactory band paint film flexible compound decorative veneer.
As technique scheme preferably, step c), can be to upper lower bolster simultaneously or pressurization when different in d), and for fear of easily curling phenomenon of plastic foil compound decorative veneer, the both sides pressed temperature of upper lower bolster can difference.
As technique scheme preferably, the pressed temperature in step d) is 125 ℃～165 ℃, the time is 60～150s, pressure is 0.6～1.0Mpa.
As technique scheme preferably, for avoiding after plastic sheeting compound decorative veneer, easily curling phenomenon of flexible decorative veneer, antiadhesion barrier in step d) can be selected polyfluortetraethylene plate, after step d), can directly by sending into painted line with the polyfluortetraethylene plate of flexible compound decorative veneer, carry out paint finishing, to thinner poly tetrafluoroethylene, can be at the bonding MDF in its back side.
As technique scheme preferably, after step e), also comprise dyestripping step, described dyestripping step is that the compound decorative veneer through hot pressing is torn it down from Antisticking, is rolled into web-like for veneer.
Tool of the present invention has the following advantages:
1) than existing subsides nonwoven wood skin, subsides backing paper wood skin, do not need to add adhesive bonding, the feature of environmental protection is good, operating procedure is simple, be difficult for craze and transfiguration, good waterproof performance, has avoided the seep through problem of decorative veneer and nonwoven in production process, guarantees the attractive in appearance and quality of decorative veneer;
2) greatly improve water resistance and the flexility of decorative veneer, improved the feature of environmental protection of production environment and product, can be directly used in curved surface and right angle coated, reduced the techniques such as japanning in process of production of wood tegument veener goods, dry, polishing;
3) improve greatly production efficiency, saved production cost, guaranteed product quality, there is good application prospect.
Accompanying drawing explanation
Fig. 1 is a kind of structural representation with paint film flexible compound veneer of the present invention.
Fig. 2 is hot pressing assembly schematic diagram in the present invention.
Wherein, the 1st, skin of paint, the 2nd, decorative veneer layer, the 3rd, plastic film layers, the 4th, industrial felt, the 5th, liner plate, the 6th, Antisticking (film), the 7th, backing plate, the 8th, heating platen.
The specific embodiment
Below in conjunction with accompanying drawing, the present invention is described in further details.
This concrete embodiment; only that the invention will be further described; it is not limitation of the present invention; those skilled in the art are reading after this description and can to the present embodiment, make the modification that there is no creative contribution as required, but as long as in claim scope of the present invention inside, are all subject to the protection of Patent Law.
As shown in Figure 1, a kind of band paint film flexible compound veneer, comprises decorative veneer layer 2, plastic film layers 3 and skin of paint 1, and plastic film layers is pressurizeed and is compound on decorative veneer by heating, then is coated with last layer paint on compound decorative veneer surface.Specific practice comprises the steps:
A) wood-planing is cut into the decorative veneer of 0.06mm;
B) on the thick plastic sheeting of 0.08mm, be coated with silane coupler, coupling agent coating weight is plastic foil 3%, and the plastic foil that scribbles coupling agent is displayed to 10min;
C) as shown in Figure 2, decorative veneer described in step a) 2 is compound in advance on the decorating film 3 described in step b) and forms composite plate blanks, then under composite plate blanks, lower surface adds respectively the polyfluortetraethylene plate that 1mm is thick (film) 6, upper surface end face adds liner plate 5, bottom surface pad industrial felt 4 and steel plate 5, play buffering, levelling effect;
D) described composite plate blanks is carried out in heating platen 8 to hot pressing, hot pressing 2 times.Upper lower hot pressing board temperature is identical, is 125 ℃, and hot pressing time is 150s, and hot pressing pressure is 0.6Mpa.
E) will send into oil paint production line with the polyfluortetraethylene plate (film) of compound decorative veneer after hot pressing, at flexible compound decorative veneer surface roller coating ultraviolet light (UV) cured primer, through one or multi-channel japanning, dry, sanding step is made satisfactory band paint film flexible compound decorative veneer.
As shown in Figure 1, a kind of band paint film flexible compound veneer, comprises decorative veneer layer 2, plastic film layers 3 and skin of paint 1, and plastic film layers is pressurizeed and is compound on decorative veneer by heating, then is coated with last layer paint on compound decorative veneer surface.Specifically comprise the steps:
A) wood-planing is cut into the decorative veneer of 0.2mm;
B) as shown in Figure 2, decorative veneer described in step a) 2 is placed on the plastic sheeting 3 that 0.06mm is thick and forms composite plate blanks, then under composite plate blanks, the respectively thick PVF plate (film) 6 of addition polymerization four 1mm of lower surface, upper surface end face adds liner plate 5, bottom surface pad industrial felt 4 and steel plate 7, play buffering, levelling effect;
C) composite plate blanks of step b) is carried out in heating platen 8 to hot pressing, hot pressing 2 times.Upper lower hot pressing board temperature is identical, is 160 ℃, and hot pressing time is 120s, and hot pressing pressure is 0.6Mpa.
D) will send into oil paint production line with the polyfluortetraethylene plate (film) of compound decorative veneer after hot pressing, at flexible compound decorative veneer surface roller coating ultraviolet light (UV) cured primer, through one or multi-channel japanning, dry, sanding step is made satisfactory band paint film flexible compound decorative veneer.
As shown in Figure 1, a kind of band paint film flexible compound veneer, comprises decorative veneer layer 2, plastic film layers 3 and skin of paint 1, and plastic film layers is pressurizeed and is compound on decorative veneer by heating, then is coated with last layer paint on compound decorative veneer surface.Specifically comprise the steps:
A) wood-planing is cut into the decorative veneer of 0.16mm;
B) as shown in Figure 2, decorative veneer described in step a) 2 is placed on the plastic sheeting 3 that 0.05mm is thick and forms composite plate blanks, then under composite plate blanks, lower surface adds respectively the thick plastics antiadhesion barrier 6 of 0.02mm, antiadhesion barrier is adhered on MDF, upper surface end face adds liner plate 5, bottom surface pad industrial felt 4 and steel plate 7, play buffering, levelling effect;
C) composite plate blanks of step b is carried out in heating platen 8 to hot pressing, hot pressing 2 times.Upper lower hot pressing board temperature difference, lower hot pressing board temperature is 140 ℃, and upper hot pressboard temperature is 125 ℃, and hot pressing time is 150s, and hot pressing pressure is 0.8Mpa.
D) the polytetrafluoroethylene (PTFE) lamina membranacea with hot pressing compound decorative veneer is sent into oil paint production line, at flexible compound decorative veneer surface spraying polyurethane (PU), paint, through one or multi-channel japanning, dry, sanding step is made satisfactory band paint film flexible compound decorative veneer.
Embodiment 4
As shown in Figure 1, a kind of band paint film flexible compound veneer, comprises decorative veneer layer 2, plastic film layers 3 and skin of paint 1, and plastic film layers is pressurizeed and is compound on decorative veneer by heating, then is coated with last layer paint on compound decorative veneer surface.Specifically comprise the steps:
A) wood-planing is cut into the decorative veneer of 0.2mm;
B) by adding maleic anhydride grafted polyethylene particle in LLDPE particle, after extruding machine extrusion molding, form the plastic sheeting that 0.08mm is thick;
C) as shown in Figure 2, decorative veneer described in step a) 2 is placed on the plastic sheeting 3 that step b makes and forms composite plate blanks, then under composite plate blanks, the respectively thick PVF plate (film) 6 of addition polymerization four 1mm of lower surface, upper surface end face adds liner plate 5, bottom surface pad industrial felt 4 and steel plate 7, play buffering, levelling effect;
D) composite plate blanks of step b) is carried out in heating platen 8 to hot pressing, hot pressing 2 times.Upper lower hot pressing board temperature is identical, is 140 ℃, and hot pressing time is 150s, and hot pressing pressure is 1Mpa.
E) will send into oil paint production line with the polyfluortetraethylene plate (film) of compound decorative veneer after hot pressing, at flexible compound decorative veneer surface roller coating ultraviolet light (UV) cured primer, through one or multi-channel japanning, dry, sanding step is made satisfactory band paint film flexible compound decorative veneer.
Below only with silane coupler, make coupling agent, polyfluortetraethylene plate does Antisticking, the good polyurethane paint of ultraviolet-cured paint is that paint film material for example understands the preparation method with paint film flexible compound veneer, but person skilled discloses according to above embodiment, adopt other materials can realize equally object of the present invention, therefore belong to equally scope of the present invention.
Claims (7)
1. a flexible compound veneer, is characterized in that, comprises decorative veneer layer, plastic film layers, and plastic film layers is pressurizeed and is compound on decorative veneer layer by heating; Described veneer layer is natural finiss veneer or the recombinant decorative veneer that 0.06～0.3mm is thick; Described plastic film layers is treated or untreated polyethylene, polypropylene or other materials plastic sheeting, and thickness is 0.02～0.5mm.
2. flexible compound veneer according to claim 1, is characterized in that, described decorative veneer layer also can be the decorative veneer through modifications such as softening, charings.
3. flexible compound veneer as claimed in claim 1, described decorative veneer layer and plastic film layers compound tense, can add coupling agent.
4. flexible compound veneer as claimed in claim 3, is characterized in that, described coupling agent is for being silane coupling agent, maleic anhydride class coupling agent and polyurethanes coupling agent.
5. flexible compound veneer as claimed in claim 3, is characterized in that, described coupling agent can be applied to decorative veneer, or plastic sheeting, also coupling agent or additive etc. can be added in plastic granulating, through extrusion molding and polyethylene, polypropylene etc., makes plastic sheeting.
6. the flexible compound veneer as described in as arbitrary in claim 1 to 5, it is characterized in that, also comprise skin of paint, this skin of paint can be conventional oil enamelled coating or elasticity skin of paint, this skin of paint is coated on described decorative veneer surface, and described skin of paint is (face) paint etc. at the bottom of (face) paint or nitro at the bottom of (face) paint, ultraviolet light polymerization at the bottom of polyurethane.
7. a processing method for flexible compound decorative veneer, is characterized in that, comprises following step:
A) by timber slicing or be peeled into the decorative veneer of 0.06mm～0.3mm;
B) on plastic sheeting, be coated with coupling agent, coupling agent coated weight is 1%～20% of plastic sheeting weight, then displays 1～20min;
C) decorative veneer described in step a) is compound in advance on the decorative veneer described in step b) and forms composite plate blanks, then on the upper and lower surface of composite plate blanks, add respectively Antisticking (film), bottom surface pading plate or industrial felt;
D) described composite plate blanks is carried out to hot pressing, 100～180 ℃ of hot pressing temperatures, hot pressing pressure 0.1～1.0MP, can adopt single or multiple lift hot press, also can adopt roll squeezer pressurization compound.Adopt single or multiple lift hot press pressurization compound tense, hot pressing time 1～6 minute, can adopt first low rear high sublevel heat pressing process of pressure in hot pressing.Adopt roll squeezer pressurization compound tense, composite plate blanks need be through the pre-heat treatment;
E) send adding backing plate or do not add backing plate together with the Antisticking (film) through the compound good decorative veneer of hot pressing and plastic film layers one side into oil paint production line, on flexible compound decorative veneer surface, adopt the modes such as spraying, roller coat to coat common or elasticity paint, through one or multi-channel japanning, dry, sanding step is made satisfactory band paint film flexible compound decorative veneer.