CN109719807A - A kind of wood skin and aluminium alloy compound finishing coat plate manufacture craft - Google Patents
A kind of wood skin and aluminium alloy compound finishing coat plate manufacture craft Download PDFInfo
- Publication number
- CN109719807A CN109719807A CN201811460702.2A CN201811460702A CN109719807A CN 109719807 A CN109719807 A CN 109719807A CN 201811460702 A CN201811460702 A CN 201811460702A CN 109719807 A CN109719807 A CN 109719807A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- gluing
- natural veneer
- manufacture craft
- finishing coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wood skins and aluminium alloy compound finishing coat plate manufacture craft, it is characterised in that: the following steps are included: (1) mold: the prototype structure according to various product is opened in aluminium alloy length；(2) it is surface-treated: aluminium alloy blank material surface polishing machine is handled into smooth, burr removing；(3) gluing: carrying out a gluing on aluminium alloy, and Special coating glue machine gluing is used on natural veneer, guarantees glue dosage and viscosity；(4) compound with natural veneer: successively to be set, enabled aluminum alloy to more docile with natural veneer with dedicated electric iron fixed bit；(5) it is put into relevant device: being put into positive and negative press；(6) it pressurizes: being pressurizeed with air pump, pressure is controlled in 3Mpa.The present invention has the advantage that technical flow design is reasonable, moulding can carry out customized according to the requirement of oneself；With the form of assembling, the workload of master carpenter is reduced, it is only necessary to on-site install, reduce manpower and material resources, reduce cost.
Description
Technical field
The present invention relates to house ornamentation and tooling technical field, in particular to a kind of wood skins and aluminium alloy compound finishing coat plate
Manufacture craft.
Background technique
It is all currently on the market that melamine faced chipboard is commonly called as finishing coat plate, pvc veneer and Recombinant Wood class furniture what is sold.Benefit
All kinds of wooden skin texture overlay film on multi-layer board either density board is imitated with computer technology scanning production.Such production method is quick
But have certain limitation because it is 2.5 meters that the size of plate, which has limitation longest, if with finger-jointed plate the superelevation the case where lower plate
Material, which expands with heat and contract with cold, to be easily deformed.
Summary of the invention
In order to solve the above technical problems, technical solution provided by the invention is a kind of wood skin and aluminium alloy compound face
Paint plate manufacture craft, it is characterised in that: the following steps are included:
(1) mold: the prototype structure according to various product is opened in aluminium alloy length；
(2) it is surface-treated: aluminium alloy blank material surface polishing machine is handled into smooth, burr removing；
(3) gluing: carrying out a gluing on aluminium alloy, and Special coating glue machine gluing is used on natural veneer, guarantees glue
Dosage and viscosity；
(4) compound with natural veneer: successively to be set with dedicated electric iron fixed bit, enable aluminum alloy to more add with natural veneer
Patch；
(5) it is put into relevant device: being put into positive and negative press；
(6) it pressurizes: being pressurizeed with air pump, pressure is controlled in 3Mpa；
(7) it heats: being heated using the electrothermal tube in machine, temperature is controlled at 140 degrees Celsius to 160 degrees Celsius；
(8) form: material is integrally formed after heating；
(9) it polishes: veneer surface is processed by shot blasting, to be ready in next step；
(10) japanning: upper paint vehicle processing is carried out according to the requirement predefined, the effect of presentation has the skin texture of solid wood to imitate
Fruit；
(11) it combines: being assembled into all kinds of furniture.
Preferably, the type of the natural veneer includes red acid branch, rosewood, teak, black walnut and cherry.
The invention has the following advantages over the prior art: technical flow design is reasonable, moulding can be wanted according to oneself
Ask progress customized；With the form of assembling, the workload of master carpenter is reduced, it is only necessary to on-site install, reduces manpower and material resources,
Reduce cost；Manufactured plate not modification, does not crack, moisture-proof, high temperature-proof, the element of honest dense pure handicraft in terms of appearance
Much higher than other similar machine molded products.
Detailed description of the invention
Fig. 1 is a kind of process flow chart of wood skin and aluminium alloy compound finishing coat plate manufacture craft of the present invention.
Specific embodiment
Present invention will be described in further detail below with reference to the accompanying drawings.
In conjunction with attached drawing, a kind of wood skin and aluminium alloy compound finishing coat plate manufacture craft, it is characterised in that: including following
Step:
(1) mold: the prototype structure according to various product is opened in aluminium alloy length；
(2) it is surface-treated: aluminium alloy blank material surface polishing machine is handled into smooth, burr removing；
(3) gluing: carrying out a gluing on aluminium alloy, and Special coating glue machine gluing is used on natural veneer, guarantees glue
Dosage and viscosity；
(4) compound with natural veneer: successively to be set with dedicated electric iron fixed bit, enable aluminum alloy to more add with natural veneer
Patch；
(5) it is put into relevant device: being put into positive and negative press；
(6) it pressurizes: being pressurizeed with air pump, pressure is controlled in 3Mpa；
(7) it heats: being heated using the electrothermal tube in machine, temperature is controlled at 140 degrees Celsius to 160 degrees Celsius；
(8) form: material is integrally formed after heating；
(9) it polishes: veneer surface is processed by shot blasting, to be ready in next step；
(10) japanning: upper paint vehicle processing is carried out according to the requirement predefined, the effect of presentation has the skin texture of solid wood to imitate
Fruit；
(11) it combines: being assembled into all kinds of furniture.
The type of the natural veneer includes red acid branch, rosewood, teak, black walnut and cherry.
The present invention does base with aluminium alloy, and natural solid wood veneer is covered on surface, and wood skin is natural wood by machine
Slicing, the type of wood skin have red acid branch, rosewood, teak, black walnut, cherry；Thickness can be adjusted arbitrarily, last painting on surface
Material, the effect finally presented have the textural effect of solid wood, and there is the environmental protection again that can achieve the effect that prevent fires in the base of aluminium alloy.Accomplish not
Modification is not cracked, moisture-proof, high temperature-proof, and the element of honest dense pure handicraft is much higher than other similar machines in terms of appearance
Molded product.Technical flow design is reasonable, and moulding can carry out customized according to the requirement of oneself.In the side of all kinds of house ornamentation companies operation
Formula is that carpenter master worker is allowed to visit production, and the duration is very long, and does not have smart, can not arbitrarily be replaced.And we use the shape of assembling
Formula reduces the workload of master carpenter, it is only necessary to on-site install.Natural resources is gradually rare, the selling at exorbitant prices of natural wood, I
With existing aluminium alloy environment-friendly materials carry out innovation make new material, it appears that the appearance for possessing solid wood is the common people's
Price.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., is all included in the scope of protection of the present invention.
Claims (2)
1. a kind of wood skin and aluminium alloy compound finishing coat plate manufacture craft, it is characterised in that: the following steps are included:
(1) mold: the prototype structure according to various product is opened in aluminium alloy length；
(2) it is surface-treated: aluminium alloy blank material surface polishing machine is handled into smooth, burr removing；
(3) gluing: carrying out a gluing on aluminium alloy, and Special coating glue machine gluing is used on natural veneer, guarantees glue dosage
And viscosity；
(4) compound with natural veneer: successively to be set, enabled aluminum alloy to more docile with natural veneer with dedicated electric iron fixed bit；
(5) it is put into relevant device: being put into positive and negative press；
(6) it pressurizes: being pressurizeed with air pump, pressure is controlled in 3Mpa；
(7) it heats: being heated using the electrothermal tube in machine, temperature is controlled at 140 degrees Celsius to 160 degrees Celsius；
(8) form: material is integrally formed after heating；
(9) it polishes: veneer surface is processed by shot blasting, to be ready in next step；
(10) japanning: upper paint vehicle processing is carried out according to the requirement predefined, the effect of presentation has the textural effect of solid wood；
(11) it combines: being assembled into all kinds of furniture.
2. a kind of wood skin according to claim 1 and aluminium alloy compound finishing coat plate manufacture craft, it is characterised in that:
The type of the natural veneer includes red acid branch, rosewood, teak, black walnut and cherry.