CN208072873U - A kind of soft solid wooden compound floor of ground heating - Google Patents
A kind of soft solid wooden compound floor of ground heating Download PDFInfo
- Publication number
- CN208072873U CN208072873U CN201820314112.8U CN201820314112U CN208072873U CN 208072873 U CN208072873 U CN 208072873U CN 201820314112 U CN201820314112 U CN 201820314112U CN 208072873 U CN208072873 U CN 208072873U
- Authority
- CN
- China
- Prior art keywords
- layer
- cork
- solid wood
- composite
- wooden compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of ground heating composite wood substrate layers on soft solid wooden compound floor, including cork balance layer；Composite cork substrate layer on the solid wood base material layer；Composite wood dash board decorative layer on the cork substrate layer；Composite wear-resistant layer in the solid wood dash board decorative layer.It is combined together as a result of by the function of the cork performance compound with solid wood, can make it is a can reach geothermal heating more be applicable in, mute noise reduction, regenerated environment protecting, stability are strong, it saves the forest reserves, improve the characteristics such as floor service life, family can not only be widely used in, and the public places such as kindergarten, theater, library are may be also used in, while can realize Fast Installation, improve installation effectiveness.
Description
Technical field
The utility model is related to technical field of construction and decoration materials, and in particular to a kind of ground heating is compound with soft solid wood
Plate.
Background technology
With economic continuous development, ground surface finishing is increasingly particular about, and cork is process using cork, and cork is
Renewable resource, cork granulocyte are cellular, and interior to be full of air, mainly ingredient suberin is that a kind of chemical composition is suitable
Stablize, fat-free and protein of going bail for, so cork products have sound-absorbing feature, meets the requirement of mankind's energy conservation and environmental protection.
Solid wood composite base material is that juggle is peeled into veneer or by flitch slicing at veneer, then three made of adhesive gluing
The board-like material of layer or multilayer, and the orthogonal gluing of the machine direction of adjacent layer veneer is made to form.By the plank of different tree species
Crosswise lamination forms, the shortcomings that overcoming solid wooden floor board moisture expansion and drying shrinkage to a certain extent；
Although above-mentioned floor all has the advantage that but when needing heating in winter or particular surroundings, since the temperature difference is larger, on
It states floor and will appear moisture resistance and stability difference and than heavier problem.
Utility model content
The utility model provides a kind of soft solid wooden compound floor of ground heating, and when logical heating for solving the prior art is laid with
The moisture resistance and the poor problem of stability that general floorings generate have and do not generate deformation and impermeable technology effect because of heating
Fruit.
To overcome the shortcomings of the prior art, the embodiment of the present application to provide a kind of soft solid wooden compound floor of ground heating,
Including wearing layer, solid wood dash board decorative layer, cork substrate layer, solid wood composite base material layer, cork balance layer；
Composite wood substrate layer on the cork balance layer；
Composite cork substrate layer on the solid wood base material layer；
Composite wood dash board decorative layer on the cork substrate layer；
Composite wear-resistant layer in the solid wood dash board decorative layer.
Further, the thickness of the wearing layer is 0.01-3mm.
Further, the thickness of the solid wood dash board decorative layer is 0.03-5mm.
Further, the thickness of the cork substrate layer is 0.5-6mm.
Further, the thickness of the solid wood base material layer is 1-20mm.
Further, the thickness of the cork balance layer is 0.1-5mm.
Further, cork balance layer, solid wood composite base material layer, cork substrate layer, solid wood dash board decorative layer use successively
Environment-protecting and non-poisonous water-borne polyurethane bond is bonded, and will be compound after complex carry out thermocompression forming.
The technical solution provided in the embodiment of the present application, at least has the following technical effect that or advantage：
In the embodiment of the present application, composite wood substrate layer on the cork balance layer；It is compound soft on the solid wood base material layer
The wooden substrate layer；Composite wood dash board decorative layer on the cork substrate layer；Composite wear-resistant layer in the solid wood dash board decorative layer.By
The function of the cork performance compound with solid wood is combined together in using, can make a can reach geothermal heating more
It is applicable in, mute noise reduction, regenerated environment protecting, stability are strong, save the forest reserves, improve the characteristics such as floor service life, can not only
It is widely used in family, and may be also used in the public places such as kindergarten, theater, library, while can realize quickly peace
Dress improves installation effectiveness.
Description of the drawings
Fig. 1 is the structural schematic diagram of the embodiment of the present application.
Specific implementation mode
It elaborates below in conjunction with the accompanying drawings to the utility model.
Embodiment
Referring to Fig.1, in the embodiment of the present application, the embodiment of the present application provides a kind of soft solid wooden compound floor of ground heating, packet
Include wearing layer 5, solid wood dash board decorative layer 4, cork substrate layer 3, solid wood composite base material layer 2, cork balance layer 1；
Composite wood substrate layer 2 on the cork balance layer 1；
Composite cork substrate layer 3 on the solid wood base material layer 2；
Composite wood dash board decorative layer 4 on the cork substrate layer 3；
Composite wear-resistant layer 5 in the solid wood dash board decorative layer 4.
Further, the wearing layer 5, cork substrate layer 3 have waterproof and dampproof anti abrasive effect.The solid wood
Dash board decorative layer 4 has the decorative effect of solid wood texture, can use pure solid wood dash board, can also use scientific and technological wood skin, have and save
The characteristic of resource.The solid wood composite base material layer 2 can otch, bayonet type can be split into, and can be from the precision of specification
Fast Installation between two pieces of floors of upper realization, can enhance the globality on ground.The cork balance layer 1 has flat well
Weigh internal stress, noise reduction, waterproof, anti-skidding, damping, increase feel, characteristic not easy to crack, free from environmental pollution.
In the embodiment of the present application, the function of the cork performance compound with solid wood is combined together, a energy can be made
Reach geothermal heating to be more applicable in, mute noise reduction, regenerated environment protecting, stability are strong, save the forest reserves, improve floor service life
Etc. characteristics, family can not only be widely used in, and may be also used in the public places such as kindergarten, theater, library, together
When can realize Fast Installation, improve installation effectiveness.
Further, the thickness of the wearing layer 5 is 0.01-3mm.
Further, the thickness of the solid wood dash board decorative layer 4 is 0.03-5mm.
Further, the thickness of the cork substrate layer 3 is 0.5-6mm.
Further, the thickness of the solid wood base material layer 2 is 1-20mm.
Further, the thickness of the cork balance layer 1 is 0.1-5mm.
Further, cork balance layer 1, solid wood composite base material layer 2, cork substrate layer 3, solid wood dash board decorative layer 4 be successively
Bonded using environment-protecting and non-poisonous water-borne polyurethane bond, and will be compound after complex carry out thermocompression forming.
The preparation method of soft solid wooden compound floor in the embodiment of the present application, includes the following steps：
Cork balance layer is carried out thermal finalization processing by step 1；
Cork balance is carried out fixed thick sanding processing by step 2；
Solid wood composite base material layer is carried out thermal finalization processing by step 3；
Solid wood composite base material layer is carried out fixed thick sanding processing by step 4；
Cork substrate layer is carried out thermal finalization processing by step 5；
Step 6, by solid wood composite base material layer, fixed thick sand after thermal finalization treated cork substrate layer, fixed thick sanding processing
Cork balance layer after light processing is compounded to form soft solid wooden compound floor blank flat successively；
Soft solid wooden compound floor blank flat is carried out fixed thick sanding processing by step 7；
Step 8, will fixed thick sanding treated the compound upper solid wood dash board decoration in soft solid wooden compound floor blank flat upper surface
Layer, forms soft solid wooden compound floor element plate；
Step 9 applies wear-resistant primer top coat layer above after soft solid wooden compound floor element plate is carried out fixed thick sanding processing, is formed
The mute soft solid wooden compound floor of complete heating；
Step 10 slots mute soft solid wooden compound floor.
The cork balance layer uses fine grained cork sheet material of the density between 0.25-0.32kg/cm3, in temperature control
It makes and carries out thermal finalization processing in Celsius≤130 DEG C of environment；
The fixed thick sanding processing of the cork balance layer determines thickness, sand paper mesh number last time using what sand paper carried out 2 times or more
Using 180 mesh, thickness error is strict controlled within ± 0.3mm；
Solid wood between 0.55-0.99kg/cm3 of the solid wood composite base material layer thermal finalization processing selection is compound, in temperature
It controls and carries out thermal finalization processing in Celsius≤130 DEG C of environment；
The fixed thick sanding processing of the solid wood composite base material layer is to carry out two-sided fixed thick sanding processing to solid wood composite base material layer,
Sand paper mesh number last time uses 180 mesh, thickness error to be strict controlled within ± 0.2mm；
The solid wood composite base material layer is applied water-base cement and is bonded using environment-protecting and non-poisonous water-borne polyurethane bond, multiple to solid wood
It closes substrate layer and carries out double spread processing, glue-spread must be controlled in every square metre of 200g ± 20g；
The cork substrate layer uses high density cork sheet of the density between 0.45-0.7kg/cm3, density necessary
More than or equal to 0.45kg/cm3, thermal finalization processing is carried out in Celsius≤130 DEG C of environment in temperature control；
The cork balance layer, solid wood composite base material layer, cork substrate layer three are compound：Refer to by cork balance layer, reality
It is multiple to carry out short-cycle hot-pressing again for the wooden composite base material layer, cork substrate layer after being bonded with environment-protecting and non-poisonous water-borne polyurethane bond
Close, recombination time at 5-8 minute, temperature control it is Celsius≤130 DEG C；
The fixed thick sanding processing of the compound blank flat of soft solid wood is that first with 80 mesh abrasive bands, board bottom face carries out fixed thick sanding over the ground；
Then fixed thick coarse sand is carried out to floor surface with 100 mesh, 180 mesh, 240 mesh abrasive bands respectively, then respectively with 320 mesh, the sand of 600 mesh
Band carries out fixed thick washed ore.
Composite wood dash board decorative layer on the compound blank flat of soft solid wood：Refer to by the compound blank flat of soft solid wood and solid wood
Dash board decorative layer is bonded with environment-protecting and non-poisonous water-borne polyurethane bond and carries out that short-cycle hot-pressing is compound, and recombination time is in 5-8 again
Minute, temperature control it is Celsius≤130 DEG C, formed the soft solid wooden compound floor element plate of ground heating；
The fixed thick sanding processing of the soft solid wooden compound floor element plate is to solid wood complexin plate first with 80 mesh abrasive bands to floor
Bottom surface carries out fixed thick sanding；Then fixed thick coarse sand is carried out to floor surface with the abrasive band of 100 mesh, 180 mesh, 240 mesh respectively, then divided
Fixed thick washed ore is not carried out with 320 mesh, 600 mesh abrasive bands；
It is to use roller coating or showering using aqueous priming paint that the soft solid wooden compound floor upper surface, which applies wear-resistant primer top coat layer,
Mode is coated, and at least to be coated 3 times, and each coated weight will be maintained at 35g/m2 or more or use roller coating using aqueous finish paint
Or showering mode is coated, and at least to be coated 2 times, each coated weight will be maintained at 25g/m2 or more；
The soft solid wooden compound floor fluting is to carry out bayonet type precision to the composite floor board for being painted with surface layer abrasion-proof paint
Slot treatment, can realize Fast Installation between two pieces of floors from the precision of specification, and the belt speed of groover used must when fluting
It must control in 50~70m/min.
Further include carrying out hand to the soft solid wooden compound floor for ending slot to touch inspection；Floor to ending notch carries out
Certified products is examined, due to the natural different property on cork surface layer, it is necessary to be increased assembly line hand and be touched inspection, otherwise be easy to out surface layer and lack
Fall into substandard products；Further include to the soft solid wooden compound floor carton after inspection and carrying out heat-sealing plastics package, due to monolithic floor ratio
It is heavier, it is less than 7 per case packing the piece number, when otherwise can exceed the normal load of people, personal injury can be caused in the handling process.
The function of the cork performance compound with solid wood is combined together by the embodiment of the present application, and can make a can reach
Geothermal heating is more applicable in, and mute noise reduction, regenerated environment protecting, stability are strong, is saved the forest reserves, is improved the spies such as floor service life
Property, it can not only be widely used in family, and may be also used in the public places such as kindergarten, theater, library, while energy
It realizes Fast Installation, improves installation effectiveness.
Finally it should be noted that the above specific implementation mode is only to illustrate the technical solution of the utility model rather than limit
System, although the utility model is described in detail in reference implementation example, it will be understood by those of ordinary skill in the art that, it can
To be modified or replaced equivalently to the technical solution of the utility model, without departing from the spirit of technical solutions of the utility model
And range, it should all cover in the right of the utility model.
Claims (6)
1. a kind of soft solid wooden compound floor of ground heating, which is characterized in that including wearing layer, solid wood dash board decorative layer, cork base
Material layer, solid wood composite base material layer, cork balance layer；
Composite wood substrate layer on the cork balance layer；
Composite cork substrate layer on the solid wood base material layer；
Composite wood dash board decorative layer on the cork substrate layer；
Composite wear-resistant layer in the solid wood dash board decorative layer.
2. the soft solid wooden compound floor of ground heating as described in claim 1, which is characterized in that the thickness of the wearing layer is
0.01—3mm。
3. the soft solid wooden compound floor of ground heating according to claim 1, which is characterized in that the solid wood dash board decoration
The thickness of layer is 0.03-5mm.
4. the soft solid wooden compound floor of ground heating as described in claim 1, which is characterized in that the thickness of the cork substrate layer
Degree is 0.5-6mm.
5. the soft solid wooden compound floor of ground heating as described in claim 1, which is characterized in that the thickness of the solid wood base material layer
Degree is 1-20mm.
6. the soft solid wooden compound floor of ground heating as described in claim 1, which is characterized in that the thickness of the cork balance layer
Degree is 0.1-5mm.