CN101224885A - 蒲绒活性炭的制备工艺 - Google Patents

蒲绒活性炭的制备工艺 Download PDF

Info

Publication number
CN101224885A
CN101224885A CNA2007101162253A CN200710116225A CN101224885A CN 101224885 A CN101224885 A CN 101224885A CN A2007101162253 A CNA2007101162253 A CN A2007101162253A CN 200710116225 A CN200710116225 A CN 200710116225A CN 101224885 A CN101224885 A CN 101224885A
Authority
CN
China
Prior art keywords
cattail wool
cattail
wool
activated carbon
active carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007101162253A
Other languages
English (en)
Other versions
CN100582000C (zh
Inventor
张成禄
张建
丁瑾
史倩倩
李燕
邹红艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong University
Original Assignee
Shandong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong University filed Critical Shandong University
Priority to CN200710116225A priority Critical patent/CN100582000C/zh
Publication of CN101224885A publication Critical patent/CN101224885A/zh
Application granted granted Critical
Publication of CN100582000C publication Critical patent/CN100582000C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种蒲绒活性炭的制备工艺。该制备工艺是：剪取香蒲上的肉穗状花序，取花序上的蒲绒，将蒲绒在120℃下烘干，去除水分，按重量比1∶1.6－1∶2.0的比例浸泡于浓度为25％－35％的磷酸中；在60℃－80℃水浴加热浸渍30－50分钟；置于马福炉或炭化炉中升温至260℃－300℃进行炭化活化40－80分钟，停止加热后在炉内焖2小时后取出；然后用80℃－100℃的蒸馏水或去离子水洗涤至pH值为6.5－7.0，烘干即可。本发明采用化学法制备蒲绒活性炭纤维，制备过程简单，制备速度快，制备成本较低，且不破坏纤维组织，能够获得吸附量大(较一般的活性炭高2－4倍)、比表面积大、微孔丰富、机械强度高的蒲绒活性炭纤维。

Description

蒲绒活性炭的制备工艺
技术领域
本发明涉及一种采用化学方法制备蒲绒活性炭纤维的工艺。
背景技术
制备活性炭纤维，常用的前躯体有：纤维素基，PAN基，酚醛基，聚乙烯醇基，苯乙烯/烯烃共聚物等，目前使用较广的主要是前四种。但利用上述有机前躯体制备活性炭纤维的工艺方法复杂且成本高，对环境污染严重。
近年来，将纤维素作为天然高分子材料用来作吸附剂使用，已得到人们的关注，有关的开发利用愈来愈多。其中有研究者用棉花作为原料制取活性炭纤维，但制取成本较高。
发明内容
本发明针对现有活性炭纤维制备方法的不足，提供一种制备过程简单、速度快、成本低、纤维组织性能好的蒲绒活性炭纤维的制备工艺。
本发明的蒲绒活性炭纤维的制备工艺是：
剪取香蒲上的肉穗状花序，取花序上的蒲绒，将蒲绒在120℃下烘干，去除水分，按重量比1∶1.6-1∶2.0的比例浸泡于浓度为25％-35％的磷酸中；在60℃-80℃水浴加热浸渍30-50分钟；置于马福炉或炭化炉中升温至260℃-300℃进行炭化活化40-80分钟，停止加热后在炉内焖2小时后取出；然后用80℃-100℃的蒸馏水或去离子水洗涤至pH值为6.5-7.0，烘干，即可制得蒲绒活性炭纤维。
本发明采用化学法制备蒲绒活性炭纤维，制备过程简单，制备速度快，制备成本较低，且不破坏纤维组织，能够获得吸附量大(较一般的活性炭高2-4倍)、比表面积大、微孔丰富、机械强度高的蒲绒活性炭纤维。
具体实施方式
实施例1
剪取香蒲上的肉穗状花序，取花序上的蒲绒。将蒲绒在120℃烘干，去除水份，按重量比1∶2.0的比例浸泡于25％的磷酸中，在60℃-80℃水浴加热浸渍30分钟。置于马福炉(或炭化炉)待程序升温至260℃时，进行炭化活化80分钟，关闭电源后在炉内焖2小时后取出。然后用80℃-100℃的蒸馏水(或去离子水)洗涤至pH值为6.5-7.0，烘干，即可制得蒲绒活性炭纤维。
实施例2
剪取香蒲上的肉穗状花序，取花序上的蒲绒。将蒲绒在120℃烘干，去除水份，按重量比1∶1.8的比例浸泡于30％的磷酸中，在60℃-80℃水浴加热浸渍40分钟。置于马福炉(或炭化炉)待程序升温至在280℃时，进行炭化活化60分钟，关闭电源后在炉内焖2小时后取出。然后用80℃-100℃的蒸馏水(或去离子水)洗涤至pH值为6.5-7.0，烘干，即可制得蒲绒活性炭纤维。
实施例3
剪取香蒲上的肉穗状花序，取花序上的蒲绒。将蒲绒在120℃烘干，去除水份，按重量比1∶1.6的比例浸泡于35％的磷酸中，在60℃-80℃水浴加热浸渍50分钟。置于马福炉(或炭化炉)待程序升温至300℃时，进行炭化活化40分钟，关闭电源后在炉内焖2小时后取出。然后用80℃-100℃的蒸馏水(或去离子水)洗涤至pH值为6.5-7.0，烘干，即可制得香蒲绒活性炭纤维。

Claims (1)

1.一种蒲绒活性炭的制备工艺，其特征在于，该制备工艺是：
剪取香蒲上的肉穗状花序，取花序上的蒲绒，将蒲绒在120℃下烘干，去除水分，按重量比1∶1.6-2.0的比例浸泡于浓度为25％-35％的磷酸中；在60℃-80℃水浴加热浸渍30-50分钟；置于马福炉或炭化炉中升温至260℃-300℃进行炭化活化40-80分钟，停止加热后在炉内焖2小时再取出；然后用80℃-100℃的蒸馏水或去离子水洗涤至pH值为6.5-7.0，烘干，即制得蒲绒活性炭纤维。
CN200710116225A 2007-12-27 2007-12-27 蒲绒活性炭纤维的制备工艺 Expired - Fee Related CN100582000C (zh)