CN101205632A - 一种熔体直纺生产中强涤纶长丝的工艺 - Google Patents

一种熔体直纺生产中强涤纶长丝的工艺 Download PDF

Info

Publication number
CN101205632A
CN101205632A CNA2007101913318A CN200710191331A CN101205632A CN 101205632 A CN101205632 A CN 101205632A CN A2007101913318 A CNA2007101913318 A CN A2007101913318A CN 200710191331 A CN200710191331 A CN 200710191331A CN 101205632 A CN101205632 A CN 101205632A
Authority
CN
China
Prior art keywords
fdy
roller temperature
polyester filament
technology
hot
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007101913318A
Other languages
English (en)
Inventor
辛婷芬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenghong Group Co Ltd
Original Assignee
Shenghong Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenghong Group Co Ltd filed Critical Shenghong Group Co Ltd
Priority to CNA2007101913318A priority Critical patent/CN101205632A/zh
Publication of CN101205632A publication Critical patent/CN101205632A/zh
Pending legal-status Critical Current

Abstract

本发明的目的在于提供一种利用熔体直纺生产方式生产中等强度涤纶长丝(FDY)的加工工艺。本发明采取的技术路线与常规品种相同，但采取高于普能民用丝的第一、第二热辊温度及较高的牵伸倍数，同时对卷绕设备上进行了一些改进。从而在不增加很大设备投资的前提下，可生产出了满足要求的涤纶中强FDY长丝。该FDY长丝具备强力较高，断裂伸长率较低的特点。主要应用于涤纶缝纫线和纸包装袋加强筋用织造领域。

Description

一种熔体直纺生产中强涤纶长丝的工艺
技术领域
本发明涉及一种涤纶长丝的加工工艺，属化纤技术领域。
背景技术
一般的涤纶长丝，生产方法无外乎两种：切片纺及熔体纺。对于熔体纺丝方法来说，由于存在着连续化、大容量的特点，因此在民用丝领域有着广泛的应用。但由于在聚合阶段，其熔体的各种特性基本定型，包括粘度、水份、DEG含量及色度均有严格的限制，因此，利用熔体直接纺进行生产的FDY或POY产品，其理化性能几乎没有大的可供改变的可能性。
现阶段，在一步法生产方式的模式下加工涤纶中强丝(FDY)，为了满足纤度为50-300D，断裂强度≥6.0g/d断裂伸长率12±2％的要求，只能在纺丝卷绕工艺上下工夫。据检索，目前国内还没有具体的采用熔体直纺方式生产中等强度涤纶FDY长丝的相关实践，也没见正式的报道或论文或专利出现。
发明内容
本发明的目的在于提供一种利用熔体直纺生产方式生产中等强度涤纶长丝(FDY)的加工工艺。
本发明采取的技术路线与常规品种相同，包括：聚酯熔体→熔体输送→纺丝箱体→计量泵→组件→侧吹风冷却→集束上油→甬道→第一热辊→第二热辊→主网络→卷绕→平衡→摇袜→染色判色→外观分级→包装。
本发明主要采用有别于普通品种的热盘温度与牵伸倍数。具体如下：
1、第一热辊温度选择：100～115℃。(民用低强丝一般小于100℃)
2、第二热辊温度选择：150～165℃。(民用低强丝一般小于135℃)
3、设定牵伸倍数为3.2～4.0，以此为依据来设定GR1、GR2的转速。(民用低强丝牵伸倍数一般小于2.5)
本发明同时对卷绕设备上进行了一些改进，包括在一、二热辊之间增加一道导丝装置。另外，使用工业丝油剂对丝束进行上油，将油架高度适当降低，由1200mm降为700～900mm等等。
本发明在不增加很大设备投资的前提下，生产出了纤度为50～300D，断裂强度≥6.0g/d，  断裂伸长率12±2％的涤纶中强FDY长丝。该FDY长丝具备强力较高，断裂伸长率较低的特点。其主要应用于涤纶缝纫线和纸包装袋加强筋用织造领域，因其产品条干均匀度好，强伸纤度不匀率低，产品成本低廉，而广受客户欢迎。
具体实施方式
以下是在江苏盛虹化纤有限公司一期A区生产50D/36F细旦中强FDY长丝的实施例子。
纺丝卷绕设备均为德国巴马格公司提供，聚合采用美国杜邦的三釜工艺流程。具体工艺见下表：
    生产线/位 L18线1#   产量：Kg/h     规格：dtex/f     55/36
    纸管颜色： 大红   用量：Kg/24h     批号：
    纤度 卷绕纤度(中心值)     55     dtex
    熔体系统 计量泵泵前压力     ≥35     Kg/C m2
箱体热媒炉设定温度A1     289     ℃
管道热媒炉设定温度A2     289     ℃
箱体热媒炉设定温度B1     ℃
管道热媒炉设定温度B2     ℃
    组件 砂配比     40-60目     填满     g
    60-80目     50     g
喷丝板规格     PRB-56-18-0.20*0.58
侧吹风 侧吹风风压     600±10     pa
侧吹风风速     0.4     m/s
侧吹风风温     22     ℃
侧吹风湿度     80±5     ％
    油嘴位置 距喷丝板距离     900mm 距风网距离     160     mm
    油剂 型号     F-1619
原油浓度     90     ％
配制浓度     13     ％
含油率     0.8     ％
 防腐剂   300     ppm
油泵(辊)转速  油泵规格： 0.08  ccm/rev   22.00     r.p.m
卷绕  预网络表压 bar  主网络表压   3.0     bar
 GR1温度 103  GR1速度   1195     m/min
 GR2温度 142  GR2速度   4542     m/min
 卷绕速度   4500     m/min
 卷绕重量   5     Kg
 落筒时间   202.02     min
卷绕角  启动   5.2   防重叠方式A：SPW
 130mm 卷绕角1   5.3   防重叠方式B：SPW
 135mm 卷绕角2   5.5   接触压力(N)
 140mm 卷绕角3   5.7   140mm     120
 150mm 卷绕角4   5.9   200mm     120
 170mm 卷绕角5   5.8   280mm     120
 190mm 卷绕角6   5.7   320mm     120
 210mm 卷绕角7   5.6   360mm     120
 285mm 卷绕角8   5.4   400mm     120
 切换   5.3   430mm     120
产品经江苏盛虹化纤有限公司检测中心进行各项物理指标的测试后，性能可达到设定要求，具体物性指标如下表：
  项目 产品规格55dtex/36f
  线密度(dtex)     55.2
  线密度变异系数(cv％)     0.12
  断裂强度(cN/dtex)     6.12
  断裂强度变异系数(％)     2.21
  断裂伸长(％)     12.2
  断裂伸长变异系数(％)     1.36
  条干均匀度(cv％)     1.32
  染色均匀度(级)     4.5
  含油率(％)     0.96
  沸水收缩率(％)     2.3
  网络度(个/米)     15
特别说明：江苏盛虹化纤有限公司纤维检测中心是具有国家认证认可委员会标志的检测单位，其测试报告具有较大的权威性，可等效于政府间相关检测机构。

Claims (3)

1.本发明的目的在于提供一种利用熔体直纺生产方式生产中等强度涤纶长丝(FDY)的加工工艺，该工艺采取的技术路线与常规品种相同，其特征在于：在普通民用丝加工工艺的基础上，采取高于普能民用丝的第一、第二热辊温度及较高的牵伸倍数，同时对卷绕设备上进行了一些改进。
2.根据权利要求1所述的中等强度涤纶长丝(FDY)的加工工艺，其特征在于采取的技术路线与常规品种相同，包括：聚酯熔体→熔体输送→纺丝箱体→计量泵→组件→侧吹风冷却→集束上油→甬道→第一热辊→第二热辊→主网络→卷绕→平衡→摇袜→染色判色→外观分级→包装。
3.根据权利要求1所述的中等强度涤纶长丝(FDY)的加工工艺，其特征在于，具体工艺参数包括：①第一热辊温度选择100～115℃；②第二热辊温度选择150～165℃；③设定牵伸倍数为3.2～4.0，以此为依据来设定GR1、GR2的转速。
CNA2007101913318A 2007-12-18 2007-12-18 一种熔体直纺生产中强涤纶长丝的工艺 Pending CN101205632A (zh)