CN101195940A - Regenerated cellulose fibre blending yarn and method for producing the same - Google Patents
Regenerated cellulose fibre blending yarn and method for producing the same Download PDFInfo
- Publication number
- CN101195940A CN101195940A CNA2006101191143A CN200610119114A CN101195940A CN 101195940 A CN101195940 A CN 101195940A CN A2006101191143 A CNA2006101191143 A CN A2006101191143A CN 200610119114 A CN200610119114 A CN 200610119114A CN 101195940 A CN101195940 A CN 101195940A
- Authority
- CN
- China
- Prior art keywords
- speed
- regenerated cellulose
- fiber
- yarn
- operating condition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The utility model discloses regenerated cellulose fiber blended yarn and the preparation method, the components and the content of weight percentage: cellulose fiber occupies 25 to 70 percent, and the other fibers occupy 75 to 30 percent. The regenerated cellulose fiber is the fiber processed by adopting no less than one kind of the raw material from wood, bamboo, pearl, and wood pulp. For the regenerated cellulose fiber blended yarn provided by the invention, because the speed is controlled, each main technical gage is adjusted, each process quantification is adjusted, the rowan pick-up coefficient is reduced, the temperature control range is adjusted, thus, the level of yarn evenness is obviously improved, the details are reduced, and the yarn reached the requirement for subsequent weaving. The textile weaved by the regenerated cellulose fiber blended yarn of the invention has the moisture absorbing and sweat discharging performance, the health function for reducing the bacterial reproduction, the antistatic function, the appearance of silk like, the wearing is comfortable and handsome, also the textile is cool and dry, which is very soft for the skin, and the textile has no pollution and no poison to the human body, which is deeply favored by people.
Description
Technical field
The present invention relates to a kind of blended yarn and preparation method thereof, particularly have the moisture absorbing and sweat releasing performance and reduce vegetative health care blended yarn with health care.
Background technology
Along with the raising of people's living standard, require more and more higher, particularly particularly outstanding to clothes interest with health care to dress.In recent years, along with the continuous appearance of new fiber, the requirement of functional yarn and fabric thereof is also mentioned on the schedule of Textile Engineering, special reproduction cellulose fibre blended yarn is exactly an example.Regenerated celulose fibre utilizes the environmental protection means exactly, and through being processed into regenerated fiber, these fibers have the moisture absorbing and sweat releasing performance and reduce vegetative health care, and have the function of antistatic with raw materials such as wood, bamboo, pearls.But because these fiber itselfs have strong, the smooth characteristics of fiber rigidity, make that it brings in spinning process between fiber that obvolvent is poor, problem such as flat low, the details height of bar solid carbon dioxide.
Summary of the invention
The technical issues that need to address of the present invention are to disclose a kind of regenerated cellulose fibre blending yarn and preparation method thereof, to overcome the above-mentioned defective that prior art exists.
Regenerated cellulose fibre blending yarn of the present invention is characterized in that, its component and weight percent content are: regenerated celulose fibre is 25%-70%, other fiber 75%-30%.
Said regenerated celulose fibre is for being the fiber that raw material is processed into in wood, bamboo, pearl or the wood pulp more than one, processing method has detailed description in the cotton textile technology document, this processing method does not belong to scope of the present invention, the relevant personnel can be prepared with reference to the method for above-mentioned document, the regenerated celulose fibre that the present invention uses, derive from the commercially available prod, the trade mark of producing as Lenzin company is the product of Lenzin, and its main component is a beech.
Said other fiber is selected from more than one in string, regenerated celulose fibre, synthetic fiber or the azelon.When other fiber adopts regenerated celulose fibre, select for use and the different types of regenerated celulose fibre of above-mentioned regenerated celulose fibre.
The preferred wood pulp fibre of said string, bamboo pulp fiber, pearl fiber;
The preferred polyster fibre of said synthetic fiber, acrylic fiber, bright and beautiful fine fiber;
The preferred wool fibre of said azelon, exempt from wool fibre, silk flock;
The preparation method of above-mentioned regenerated cellulose fibre blending yarn comprises the steps:
Distribute cotton according to above-mentioned ratio, carry out blowing, comb and parallel cotton fibers prior to spinning, drafting, rove and spun yarn then successively;
The temperature of each step is controlled at 23 ℃～32 ℃;
The relative humidity of each step is:
The comb and parallel cotton fibers prior to spinning step is 60%～65%, and drafting and rove step are 60%～65%, spun yarn step 55%～60%, winder step 70%～75%
Further, according to preferable methods of the present invention, the operating condition of said blowing step is: griping cotton machine hired roughneck speed is 650～710r/min, mixing and blowing machine hired roughneck speed is 650～750 * 800～900r/min, opener hired roughneck speed is 450～510r/min, lapper hired roughneck speed is 700～815r/min, and fan speed is 1150～1300/min;
Said griping cotton machine, mixing and blowing machine, opener and lapper are the general equipment in this area.
The operating condition of said comb and parallel cotton fibers prior to spinning step is:
Cylinder speed is 330～350r/min, licker-in speed is 750～850r/min, doffer speed is 19～22r/min, is cover plate speed? it is 9～12/1000 that 80～120r/min, cotton feeder～licker-in space ", it is 5～7/1000 that licker-in～cylinder spaces ", it is 4～6/1000 that cylinder～doffer is spaced "; it is 14～11/1000 that preceding securing cover plate～cylinder spaces ", it is 17～15/1000 that back stationary plate～cylinder spaces ", it is 8～117～107～107～108～11/1000 that cover plate～cylinder spaces "; The operating condition of said drafting step is:
Adopt 3 also, 8 * 8 * 8～6 * 8 * 8 of number of doubling, ratch 44～47 * 49～52, roller speed 200～220r/min;
The operating condition of said rove step is:
Ratch is 51～54 * 58～61mm, roller speed 180～200r/min, twist coefficient 68～72;
The operating condition of said spun yarn step is:
Ratch 43～45 * 58～62m/m, roller speed 180～210r/min, twist coefficient 340～360.
The inventor finds, the mixture of said ratio needs the specific operating procedure condition of control, the blended yarn that can obtain to conform to quality requirements, regenerated celulose fibre blended yarn provided by the invention, owing to controlled speed, adjusted each main technique and spaced, it is quantitative to have adjusted each operation, having reduced rove picks up coefficient and adjusts Temperature and Humidity Control scope etc., it is flat obviously to have improved one-tenth sliver solid carbon dioxide, reduces details, makes yarn reach follow-up woven requirement.
Use the woven fabric of special reproduction cellulose fibre blended yarn of the present invention's spinning, have the moisture absorbing and sweat releasing performance and reduce vegetative health care, the function of antistatic, has the outward appearance as the silk, aesthetic feeling comfortable and easy to wear, pleasantly cool dry and comfortable again, very gentle to skin,, nonhazardous pollution-free to human body are favored by people deeply.
The specific embodiment
Embodiment 1
Regenerated celulose fibre is: J14.7tex, 40
sThe preparation spinning step of C50/ days silks 50 is as follows:
1, distribute cotton (weight):
Tencel fiber 50% 11.3dtex * 38mm, Lenzin company provides;
5800 of the cotton 229 50% length 29mm fineness in cotton Xinjiang, mature coefficient 0.86 uniformity 86.5.
2, blowing:
A002 is the equipment of Zhengzhou Textile Machinery Co., Ltd preparation, and A035 is the equipment of Jintan textile machinery factory preparation, and FA106 is the equipment of Zhengzhou Textile Machinery Co., Ltd preparation, and A076C is the equipment of Zhengzhou Textile Machinery Co., Ltd preparation.
3, comb and parallel cotton fibers prior to spinning:
4, drafting:
Employing 3 and technology, 6 * 8 * 8 of number of doubling, ratch 46 * 50mm, roller speed 200r/min.
5, rove:
Ratch 51.5 * 58m/m, roller speed 185r/min, twist coefficient 68.
6, spun yarn:
Ratch 43 * 60mm, front roller speed 205r/min, twist coefficient 360.
In the above-mentioned technology, temperature is controlled at 30 ℃, and relative humidity: comb and parallel cotton fibers prior to spinning is controlled at 62%, and thick 62%, spun yarn 57%, winder 75%.
Adopt company standard to detect, quality index is as follows:
| Weight CV% | 1.5 | This does crow | 12.47 |
| Deviation of weight | +0.2 | Details | 2.0 |
| Ultimate strength | 288 | Slubbing | 10 |
| Fracture strength | 19.61 | Cotton knot | 26.5 |
| Fracture CV% | 9.36 | Filoplume | 3.6 |
| Twist | 94.2 | Ten myriametre yarn defects | 1.1 |
| Pick up irregular | 3.2 | The blackboard cotton knot | 0 |
| Pick up coefficient | 361 |
This shows that special reproduction fiber provided by the invention and cotton blending yarn reach follow-up woven requirement.
Use the woven fabric of above-mentioned regenerated cellulose fibre blending yarn of the present invention's spinning, have the moisture absorbing and sweat releasing performance and reduce vegetative health care, electrostatic-proof function, has the outward appearance as the silk, aesthetic feeling comfortable and easy to wear, pleasantly cool dry and comfortable again, very gentle to skin,, nonhazardous pollution-free to human body are favored by people deeply.
Embodiment 2
Proportioning following (weight):
Bamboo cellulose fibre 20% 10.1dtex * 38mm, Ji Gao company provides;
Polyster fibre 80%1.56dtex * 38mm, Lian Ji FCFC provides;
Adopt the method for embodiment 1 to be prepared, testing result is as follows:
| Weight CV% | 1.4 | This does crow | 12.43 |
| Deviation of weight | +0.8 | Details | 1.0 |
| Ultimate strength | 341.5 | Slubbing | 11.5 |
| Fracture strength | 18.46 | Cotton knot | 22 |
| Fracture CV% | 7.96 | Filoplume | 1.09 |
| Twist | 84.6 | Ten myriametre yarn defects | 1.5 |
| Pick up irregular | 3.7 | The blackboard cotton knot | 1/2 |
| Pick up coefficient | 364 |
Claims (10)
1. regenerated cellulose fibre blending yarn, component and weight percent content are: regenerated celulose fibre is 25%-70%, other fiber 75%-30%.
Said regenerated celulose fibre is for being the fiber that raw material is processed into in wood, bamboo, pearl or the wood pulp more than one;
Said other fiber is selected from more than one in string, regenerated celulose fibre, synthetic fiber or the azelon.
2. regenerated cellulose fibre blending yarn according to claim 1 is characterized in that, the preferred wood pulp fibre of said string, bamboo pulp fiber, pearl fiber.
3. regenerated cellulose fibre blending yarn according to claim 1 is characterized in that, said synthetic fiber are polyster fibre, acrylic fiber, bright and beautiful fine fiber.
4. regenerated cellulose fibre blending yarn according to claim 1 is characterized in that, said azelon is wool fibre, exempt from wool fibre, silk flock.
5. according to the preparation method of each described regenerated cellulose fibre blending yarn of claim 1～4, it is characterized in that, comprise the steps:
Distribute cotton according to above-mentioned ratio, carry out blowing, comb and parallel cotton fibers prior to spinning, drafting, rove and spun yarn then successively;
The temperature of each step is controlled at 23 ℃～32 ℃;
The relative humidity of each step is:
The comb and parallel cotton fibers prior to spinning step is 60%～65%, and drafting and rove step are 60%～65%, spun yarn step 55%～60%, winder step 70%～75%.
6. method according to claim 5, it is characterized in that, the operating condition of said blowing step is: griping cotton machine hired roughneck speed is 650～710r/min, mixing and blowing machine hired roughneck speed is 650～750 * 800～900r/min, opener hired roughneck speed is 450～510r/min, lapper hired roughneck speed is 700～815r/min, and fan speed is 1150～1300/min.
7. method according to claim 5, it is characterized in that, the operating condition of said comb and parallel cotton fibers prior to spinning step is: cylinder speed is 330～350r/min, licker-in speed is 750～850r/min, doffer speed is 19～21r/min, cover plate speed is 80～120r/min, it is 9～12/1000 that cotton feeder～licker-in spaces "; it is 5～7/1000 that licker-in～cylinder spaces ", it is 4～6/1000 that cylinder～doffer is spaced "; it is 14～11/1000 that preceding securing cover plate～cylinder spaces ", it is 17～15/1000 that back stationary plate～cylinder spaces ", it is 8～11 7～10 7～10 7～10 8～11/1000 that cover plate～cylinder spaces ".
8. method according to claim 5 is characterized in that, the operating condition of said blowing step is: the operating condition of said drafting step is:
Adopt 3 also, 8 * 8 * 8～6 * 8 * 8 of number of doubling, ratch 45～48 * 49～53mm, roller speed 200～220r/min.
9. method according to claim 5 is characterized in that, the operating condition of said blowing step is: the operating condition of said rove step is:
Ratch 51～54 * 58～61mm, roller speed 180～200r/min, twist coefficient 68～72.
10. method according to claim 5 is characterized in that, the operating condition of said blowing step is: the operating condition of said spun yarn step is:
Ratch 43～45 * 58～62m/m, roller speed 180～210r/min, twist coefficient 340～360.