CN103741306A - Blended yarn made of dacron, mulberry silk and pearl fiber - Google Patents
Blended yarn made of dacron, mulberry silk and pearl fiber Download PDFInfo
- Publication number
- CN103741306A CN103741306A CN201410054260.7A CN201410054260A CN103741306A CN 103741306 A CN103741306 A CN 103741306A CN 201410054260 A CN201410054260 A CN 201410054260A CN 103741306 A CN103741306 A CN 103741306A
- Authority
- CN
- China
- Prior art keywords
- mulberry silk
- pearl fiber
- blended yarn
- dacron
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a blended yarn made of dacron, mulberry silk and pearl fiber. The blended yarn comprises the following components in parts by weight: 65 to 75 parts of the dacron, 10 to 20 parts of the mulberry silk and 10 to 20 parts of the pearl fiber. The blended yearn provided by the invention can complement the characteristics of the dacron, the mulberry silk and the pearl fiber and has the advantages of the dacron, the mulberry silk and the pearl fiber.
Description
Technical field
the present invention relates to the blended yarn of a kind of terylene, mulberry silk, pearl fiber, belong to Functional Chemical Fibers technical field.
Background technology
Blended yarn is the yarn being spun into by two or more fiber, as fiber crops/cotton, hair/cotton, hair/fiber crops/thin,tough silk, wash/cotton, wash/hair etc., broken the boundary between original cotton, fiber crops, hair, silk, chemical fibre, can make up the deficiency of single certain textile material, embody the superiority of each component fibre, to improve the einnehmen function of fabric, expand the scope of application.Existing blended yarn function is complete not enough.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art part, the blended yarn of a kind of terylene, mulberry silk, pearl fiber is provided.
The blended yarn of terylene of the present invention, mulberry silk, pearl fiber, comprises following ingredients: terylene 65-75 weight portion, mulberry silk 10-20 weight portion and pearl fiber 10-20 weight portion.
Preferably,
The blended yarn of described terylene, mulberry silk, pearl fiber, comprises following ingredients: terylene 70 weight portions, mulberry silk 15 weight portions and pearl fiber 15 weight portions.
The present invention has following technique effect: the terylene in blended yarn has following performance: intensity is high.Staple fibre intensity is 2.6~5.7cN/dtex, and high-tenacity fiber is 5.6~8.0cN/dtex.Because hygroscopicity is lower, its wet strength and dry strength are basic identical.Impact strength is higher 4 times than polyamide fibre, higher 20 times than viscose.Good springiness.Elasticity approaches wool, when extending 5%~6%, almost can recover completely.Crease resistance surpasses other fibers, i.e. fabric wrinkle not, good stability of the dimension.Modulus of elasticity is 22~141cN/dtex, higher 2~3 times than polyamide fibre.Good water absorption.ABRASION RESISTANCE is good.ABRASION RESISTANCE is only second to the best polyamide fibre of ABRASION RESISTANCE, all better than other natural fabrics and synthetic fiber.Light resistance is good.Light resistance is only second to acrylic fibers.Corrosion-resistant.Can bleach tolerant, oxidant, hydro carbons, ketone, oil product and inorganic acid.Resistance to diluted alkaline, is not afraid of mouldly, but thermokalite can make its decomposition.Dyeability is poor.Dacron hygroscopicity is poor, and dress has feeling of oppression and heat, and simultaneously easy static electrification, contamination dust, affect attractive in appearance and comfortableness.Very easily dry after but washing, and wet decline hardly by force, indeformable, there is good wash and wear performance.Terylene is to close the best fabric of heat resistance in fine fabric, and fusing point is at 260 ℃, and ironing temperature can be at 180 ℃.Have thermoplasticity, can manufacture accordion-pleated skirt, rivel is lasting.Meanwhile, the melt resistance of dacron is poor, is meeting cigarette ash, Mars etc. and is easily forming hole.While therefore, wearing, should avoid the contact of cigarette end, spark etc. as far as possible.The light resistance of dacron is better, and except poorer than acrylic fibers, its sun-proof ability surpasses natural fabric.Especially the sun-proof ability after glass is fine, almost equally matched with acrylic fibers.The resistance to various chemicals of dacron are functional.Acid, alkali is all little to its destructiveness, is not afraid of mould simultaneously, is not afraid of and damages by worms.Dacron wrinkle resistance and conformality are fine, therefore, are applicable to makeing overcoat clothes.
Silk has following characteristic: be the lightest the thinnest the most soft natural fabric of occurring in nature, can easily restore to the original state after cancelling external force, the inner tube of a tyre is molding not, not stuffy, and purse up, evenly not soft, can forever exempt to turn over use.Cocoon silk quilt, adopts first-class silk, and the fine footpath between fields structure with novel, makes steam free flow.Add distinctive ventilative, the water vapour permeability of silk itself, make cocoon silk quilt feel more sliding, refreshing not warm, warm and not dry.Mulberry silk is mainly comprised of animal protein, is rich in 18 kinds of necessary amino acid of human body, can promote Skin Cell vigor, anti-vascular sclerosis, long-term use can anti-skin senescence, and some skin disease is had to special antipruritic effect, to arthritis, scapulohumeral periarthritis, asthma has certain health-care function.Have " human body the second skin ", " fiber queen's " good reputation.
The existing pearl face skin-care effect of pearl fiber, has again ventilative, the comfortable and easy to wear characteristic of viscose moisture absorption.The pearl fiber surface uniform pearl micro-particle that distributing, for a long time in skin contact, there is pearl face skin care, relieve inflammation or internal heat relieve internal heat, tender white muscle skin, anti-ultraviolet effect.Pearl fiber contains several amino acids and trace element, and fiber surface is smooth nice and cool, has gloss as pearl.Blended yarn of the present invention can be complementary by the feature of three kinds of fibers, performance three's advantage.
The specific embodiment
embodiment 1
The blended yarn of the terylene of the present embodiment, mulberry silk, pearl fiber, comprises following ingredients: terylene 75 weight portions, mulberry silk 10 weight portions and pearl fiber 20 weight portions.
embodiment 2
The blended yarn of the terylene of the present embodiment, mulberry silk, pearl fiber, comprises following ingredients: terylene 65 weight portions, mulberry silk 20 weight portions and pearl fiber 10 weight portions.
embodiment 3
The blended yarn of the terylene of the present embodiment, mulberry silk, pearl fiber, comprises following ingredients: terylene 70 weight portions, mulberry silk 15 weight portions and pearl fiber 15 weight portions.
Claims (2)
1. a blended yarn for terylene, mulberry silk, pearl fiber, is characterized in that: comprise following ingredients: terylene 65-75 weight portion, mulberry silk 10-20 weight portion and pearl fiber 10-20 weight portion.
2. the blended yarn of terylene according to claim 1, mulberry silk, pearl fiber, is characterized in that, comprises following ingredients: terylene 70 weight portions, mulberry silk 15 weight portions and pearl fiber 15 weight portions.