CN109680355A - A kind of vapor-permeable type Yoga takes fabric and preparation method thereof - Google Patents
A kind of vapor-permeable type Yoga takes fabric and preparation method thereof Download PDFInfo
- Publication number
- CN109680355A CN109680355A CN201811490628.9A CN201811490628A CN109680355A CN 109680355 A CN109680355 A CN 109680355A CN 201811490628 A CN201811490628 A CN 201811490628A CN 109680355 A CN109680355 A CN 109680355A
- Authority
- CN
- China
- Prior art keywords
- fiber
- vapor
- preparation
- fabric
- permeable type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the preparation methods that a kind of vapor-permeable type Yoga takes fabric, antibiotic polyester fiber and pearl fiber and cocoon fiber progress is blended, dandelion, Herba Epimedii, safflower and the mulberry leaf being added in antibiotic polyester fiber preparation process, cheap, effect is good;Antibacterial plant mixture and conch meal is added simultaneously, antibacterial effect is more preferably;Natural plants coloring agent is added, dyeing effect is good;After addition safflower and pearl fiber are used cooperatively, under conditions of moving perspiration more preferably to the health-care efficacy of women.
Description
Technical field
The present invention relates to functional form garment material fields, take fabric and its preparation side more particularly to a kind of vapor-permeable type Yoga
Method.
Background technique
Polyester fiber is as most widely used chemical fibre, with good fibre-forming performance and mechanical performance, intensity
High, fast light, heat-resisting and resistance to acid and alkali is good, has good processability and Yi Fangxing, pure can spin, blended and intertexture.Polyester fabric
Washable and wearable, ironing and anti-crease, clothes, home textile, decoration and product with etc. fields be widely used.However, polyester fiber is also deposited
Hygroscopicity is poor, absorbing sweat, dress do not have the shortcomings that feeling of oppression and heat, anti-static ability difference and easily stain dust fabric, therefore make significantly
The about application and development of polyester fiber.For the snugness of fit for improving polyester fiber, the application added value of polyester fiber is improved,
The improvement of chemically or physically aspect, and then the higher moisture absorbing and sweat releasing property of endowing terylene fiber are usually carried out to polyester fiber, are mentioned
High dacron wearing comfort.
Requirement with people to fabric is higher and higher, and the other performance of polyester fiber is also gradually valued by people,
Especially have the chemical fibre product of anti-microbial property, there are good market prospects.
Underwear fabric is due to wearing next to the skin, therefore it is required that comfortable and easy to wear, soft, elasticity is good.Present people have underwear
New requirement, such as antibacterial performance are increasingly valued by people.
Summary of the invention
In view of this, the object of the present invention is to provide the preparation methods that a kind of vapor-permeable type Yoga takes fabric.
A kind of vapor-permeable type Yoga takes fabric, is formed by polyester fiber, pearl fiber, cocoon fiber hybrid woven, described
The weight percentage of each component of blended yarn weaved fabric is as follows:
Pearl fiber 65-75%
Polyester fiber 12-20%
Cocoon fiber surplus.
A kind of vapor-permeable type Yoga takes the preparation method of fabric, carries out as steps described below:
A, antibacterial plant mixture and distilled water are added in flask, the quality of distilled water is plant mixture quality
20-30 times;
B, it is heated to 35-40 DEG C, and is evaporated under reduced pressure, distillate is collected;
C, gained distillate is filtered and concentrated to after solid content is 50-60% and obtains plant antimicrobial;
D, under the preparation condition not higher than 40 DEG C, gelatin and Arabic gum is used to coat plant antimicrobial as softgel shell,
Form microcapsules;
E, microcapsules and micron order calcined shell powder are sufficiently mixed, are then quantitatively adding molten condition by measuring turntable
Polyester slice in, and within the 3-5s time, by polyester slice, as-spun fibre, concrete technology is made in high speed spinning on spinning machine
Condition are as follows: 300-320 DEG C of spinning temperature, spinning speed 1300-1400m/min;
F, as-spun fibre is carried out shaping using parallel drafting machine, finished product polyester fiber, drafting multiple 3-4 can be obtained
Times;
G, polyester fiber and pearl fiber and cocoon fiber progress is blended, and by dyeing, final finishing, obtain blended face
Material.
Preferably, the antibacterial plant mixture in the step A includes the ingredient of following weight percent:
Dandelion 15-20%
Herba Epimedii 8-15%
Safflower 3-5%
Mulberry leaf surplus.
Preferably, in the step E microcapsules, micron order calcined shell powder and polyester slice weight percent are as follows:
Microcapsules 3-5%
Micron order calcined shell powder 1-2%
Polyester slice surplus.
Preferably, natural plants coloring agent and microcapsules and micron order calcined shell powder can be added in the step E
It is added in polyester slice after common mixing.
Preferably, the amount of the natural plants coloring agent of addition is the 3-10% of polyester slice weight.
Preferably, in the step G, in order to reduce influence of the high temperature to polyester fiber anti-microbial property, the dyeing
It is combined into one with finishing process, and by temperature control between 70-80 DEG C, the control of processing time is within 5min.
Dandelion herbaceos perennial.Root is coniform, surface sepia, shrinkage, limb edge have sometimes wave-formed mouth or
Pinniform drastic crack, base portion is gradually narrow at petiole, and often band reddish violet, scape top aubergine are close long by spider's thread shape white for petiole and master pulse
Pubescence;Capitulum, involucre mitriform, achene crineous, long pappus white, 4~October of flowering fruit bearing stage.Dandelion has certain resist
Bacterium effect: there is stronger bactericidal effect to staphylococcus aureus resistance bacterial strain, hemolytic streptococcus in the product injection test tube.
Also have one to Diplococcus pneumopniae, meningococcus, corynebacterium diphtheriae, Pseudomonas aeruginosa, shigella dysenteriae, typhoid bacillus etc. and micrococcus catarrhalis
Determine bactericidal effect.This product alcohol extract 1:400 can inhibit tulase, but decoction 1:100 is invalid.The water decoction of its 1:80 can delay
ECHO11 viral cytopathic, alcohol extract (31mg/kg) can kill Leptospira, also have inhibiting effect to certain fungies.It is right
Campylobacter pylori has good killing effect.
Herba Epimedii is Berberidaceae plant Herba Epimedii Epimedium brevicornum Maxim., Epimedium sagittatum
Epimedium sagittatum (Sieb.et Zucc.) Maxim., E. Pubescens Epimedium pubescens
Or the dried leaf of korean epimedium herb Epimedium koreanum Nakai Maxim..Summer, autumn cauline leaf are tapped when luxuriant, are removed
Slightly stalk and impurity are removed, dries or dries in the shade.There is significant inhibiting effect to poliovirus in Herba Epimedii decoction test tube, in medicine
In object and viruses contact 1 hour, i.e. performance deactivation can also inhibit other enteroviruses;To staphylococcus albus, golden yellow
Color staphylococcus has significant bacteriostasis, has slight inhibition to make Nai Shi micrococcus catarrhalis, Diplococcus pneumopniae, haemophilus influenzae
With.1% concentration has inhibitory effect to Bacillus tuberculosis.
Mulberry leaf, (Mulberry Leaf), scientific name: Folium Mori.Chinese medicine name is the dried leaf of moraceae plants mulberry, is
The conventional food also known as mulberry of silkworm, thorn mulberry, mulberry fruit tree, yellow wood leaf etc., mulberry tree, mulberry yield are planted in China, various regions, north and south extensively
It is abundant.The Major Foods of silkworm.Intact leaf is in or width egg shape that blade base is heart-shaped, and the micro- point in top, there are sawtooth, vein in edge
Dense white pubescence.The thicker dirty-green of old leaf.Tender leaf is relatively thin, yellow green.Matter is crisp easily, holds prick the hand.Gas is light, and mildly bitter flavor is puckery.
It is medicinal it is generally acknowledged that frost after the person's of adopting matter it is good.Mulberry leaf have dispelling wind and heat from the body, clearing away the lungheat and moisturizing, the effect of clearing liver and improving vision.And have
Treat anemopyretic cold, lung-heat type cough, dizziness headache, the effect of red eyes and dim-sighted.By 2014, the bud head of mulberry leaf was made by someone
Cuisine, and mulberry leaf is made to have the value of dietotherapy, liked due to the bud head nutritive value of its mulberry leaf is abundant by masses, referred to as mulberry bud
Dish.The mulberry tree bud in the village Xun Jili on the south again, state's silk Cultural Park is the most outstanding, it is contemplated that the irrigation of Zhu Wanshui is worn, mulberry leaf bud
Microelement than general mulberry bud than be higher by it is very much.
Conch meal is by natural seashell by being made after high-temperature calcination, crushing.Its constituent be calcium carbonate, calcium oxide,
The calcified materials such as calcium hydroxide, this has the function of that absorption, decomposition (formaldehyde, benzene, ammonia) etc. and adjusting air are wet as cellular
The functions such as degree, while the conch meal fired is to a variety of thin including Escherichia coli, salmonella, staphylococcus aureus etc.
Bacterium has extremely strong antibacterial and bactericidal effect, and has the function of anti-corrosion, mould proof.Conch meal is added in coating, it is manufactured interior
Wall coating will have good absorption pernicious gas and fungistatic effect.
Conch meal and antibacterial plant mixture are used in conjunction with, and antibacterial effect is more preferably.
In the preparation process of entire antibiotic polyester fiber of the invention, conch meal and antibacterial plant mixture are added to poly-
In ester slice, due to preparation process only simple mixing, conch meal and antibacterial plant mixture are mainly distributed on washing for generation
Synthetic fibre fiber surface, therefore conch meal and antibacterial plant mixture usage amount are less;After natural plants coloring agent is added, coloring agent is same
It is distributed in terylene surface, dyeing effect is good.
A kind of vapor-permeable type Yoga provided by the present invention takes the preparation method of fabric, has the advantages that
1, chemicals is not used in antibiotic polyester fiber preparation process, is a kind of tencel preparation side of environmental protection
Method.
2, the antibacterial plant mixture being added, cheap, effect is good, using low temperature preparation early period and uses microcapsule coated
Mode can be to contained by antibacterial plant mixture when in the polyester slice that 300 DEG C or so of molten state is added in the later period
The effectively antimicrobial component such as phenols, alcohols, lipid be not destroyed as far as possible.
3, antibacterial plant mixture and conch meal is added simultaneously, antibacterial effect is more preferably.
4, after addition safflower and pearl fiber are used cooperatively, under conditions of moving perspiration more to the health-care efficacy of women
It is good.
Specific embodiment
A kind of vapor-permeable type Yoga takes the preparation method of fabric, carries out as steps described below:
A, antibacterial plant mixture and distilled water are added in flask, the quality of distilled water is plant mixture quality
20-30 times;
B, 38 DEG C are heated to, and is evaporated under reduced pressure, distillate is collected;
C, gained distillate is filtered and concentrated to after solid content is 55% and obtains plant antimicrobial;
D, under the preparation condition not higher than 20-35 DEG C, gelatin and Arabic gum is used to coat plants antimicrobial as softgel shell
Agent forms microcapsules;
E, microcapsules and micron order calcined shell powder are sufficiently mixed, are then quantitatively adding molten condition by measuring turntable
Polyester slice in, and within the 3-5s time, by polyester slice, as-spun fibre, concrete technology is made in high speed spinning on spinning machine
Condition are as follows: 305 DEG C of spinning temperature, spinning speed 1350m/min;
F, as-spun fibre is carried out shaping using parallel drafting machine, finished product polyester fiber, drafting multiple 3.5 can be obtained
Times;
G, polyester fiber and pearl fiber and cocoon fiber progress is blended, and by dyeing, final finishing, obtain blended face
Material.
The weight percentage of each component of the blended yarn weaved fabric is as follows:
Pearl fiber 72%
Polyester fiber 15%
Cocoon fiber surplus.
Antibacterial plant mixture in the step A, the ingredient including following weight percent:
Dandelion 18%
Herba Epimedii 10%
Safflower 4%
Mulberry leaf surplus.
The weight percent of microcapsules, micron order calcined shell powder and polyester slice in the step E are as follows:
Microcapsules 4%
Micron order calcined shell powder 1.5%
Polyester slice surplus.
Table one: the weight percentage of each component of antibacterial plant mixture is see following table in each specific embodiment:
Dandelion | Herba Epimedii | Safflower | Mulberry leaf | |
Embodiment 1 | 18 | 10 | 4 | Surplus |
Embodiment 2 | 15 | 12 | 4 | Surplus |
Embodiment 3 | 16 | 12 | 5 | Surplus |
Embodiment 4 | 16 | 8 | 5 | Surplus |
Embodiment 5 | 18 | 15 | 3 | Surplus |
Embodiment 6 | 20 | 15 | 3 | Surplus |
Embodiment 7 | 20 | 10 | 3 | Surplus |
Table two: the weight percentage of each component of polyester fiber is see following table in each specific embodiment:
Table three: in each specific embodiment in blended yarn weaved fabric each fiber weight percentage see following table:
Pearl fiber | Polyester fiber | Cocoon fiber | |
Embodiment 1 | 72 | 15 | Surplus |
Embodiment 2 | 70 | 20 | Surplus |
Embodiment 3 | 68 | 12 | Surplus |
Embodiment 4 | 65 | 15 | Surplus |
Embodiment 5 | 65 | 20 | Surplus |
Embodiment 6 | 75 | 12 | Surplus |
Embodiment 7 | 72 | 15 | Surplus |
Test the anti-microbial property of blended yarn weaved fabric:
Table four: the bacteriostasis property (%) of blended yarn weaved fabric:
Staphylococcus aureus | Candida albicans | Escherichia coli | |
Embodiment 1 | 95 | 92 | 97 |
Embodiment 2 | 94 | 91 | 95 |
Embodiment 3 | 94 | 91 | 95 |
Embodiment 4 | 94 | 90 | 96 |
Embodiment 5 | 95 | 91 | 96 |
Embodiment 6 | 92 | 90 | 96 |
Embodiment 7 | 92 | 92 | 95 |
As shown in Table 4, blended yarn weaved fabric is non-to the fungistatic effect of staphylococcus aureus, Candida albicans and Escherichia coli
Chang Hao.
Embodiment 8
A kind of vapor-permeable type Yoga takes the preparation method of fabric, carries out as steps described below:
A, antibacterial plant mixture and distilled water are added in flask, the quality of distilled water is plant mixture quality
20-30 times;
B, 40 DEG C are heated to, and is evaporated under reduced pressure, distillate is collected;
C, gained distillate is filtered and concentrated to after solid content is 57% and obtains plant antimicrobial;
D, under the preparation condition not higher than 20-35 DEG C, gelatin and Arabic gum is used to coat plants antimicrobial as softgel shell
Agent forms microcapsules;
E, microcapsules, micron order calcined shell powder and natural plants coloring agent are sufficiently mixed, then pass through metering turntable
It is quantitatively adding in the polyester slice of molten condition, and within the 3-5s time, by polyester slice, high speed spinning is made on spinning machine
As-spun fibre, concrete technology condition are as follows: 310 DEG C of spinning temperature, spinning speed 1300m/min;
F, as-spun fibre is carried out shaping using parallel drafting machine, finished product polyester fiber, drafting multiple 4 can be obtained
Times;
G, polyester fiber and pearl fiber and cocoon fiber progress is blended, and by dyeing, final finishing, obtain blended face
Material.
The weight percentage of each component of the blended yarn weaved fabric is as follows:
Pearl fiber 70%
Polyester fiber 17%
Cocoon fiber surplus.
Antibacterial plant mixture in the step A, the ingredient including following weight percent:
Dandelion 15%
Herba Epimedii 12%
Safflower 3%
Mulberry leaf surplus.
The weight percent of microcapsules, micron order calcined shell powder and polyester slice in the step E are as follows:
Microcapsules 3.5%
Micron order calcined shell powder 2%
Natural plants coloring agent 3.5%
Polyester slice surplus.
The natural plants coloring agent is natural mulberries extract coloring agent.
Polyester fiber dyes in advance during the preparation process, increases the dyeing effect of fiber, the color jail of soaping of polyester fiber
Degree reaches 4 grades or more, while also reducing the dosage of coloring agent in subsequent dyeing, reduces costs.The above, only this hair
Bright preferable specific embodiment, but scope of protection of the present invention is not limited thereto, any technology for being familiar with the art
Personnel in the technical scope disclosed by the present invention, are subject to equivalent replacement according to the technical scheme of the invention and its inventive conception or change
Become, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of vapor-permeable type Yoga takes fabric, formed by polyester fiber, pearl fiber, cocoon fiber hybrid woven, feature exists
In the weight percentage of each component of the blended yarn weaved fabric is as follows:
Pearl fiber 65-75%
Polyester fiber 12-20%
Cocoon fiber surplus.
2. the preparation method that a kind of vapor-permeable type Yoga takes fabric, which is characterized in that carry out as steps described below:
A, antibacterial plant mixture and distilled water are added in flask, the quality of distilled water is the 20-30 of plant mixture quality
Times;
B, it is heated to 35-40 DEG C, and is evaporated under reduced pressure, distillate is collected;
C, gained distillate is filtered and concentrated to after solid content is 50-60% and obtains plant antimicrobial;
D, under the preparation condition not higher than 40 DEG C, gelatin and Arabic gum is used to coat plant antimicrobial as softgel shell, is formed
Microcapsules;
E, microcapsules and micron order calcined shell powder are sufficiently mixed, are then quantitatively adding the poly- of molten condition by measuring turntable
In ester slice, and within the 3-5s time, by polyester slice, as-spun fibre, concrete technology condition is made in high speed spinning on spinning machine
Are as follows: 300-320 DEG C of spinning temperature, spinning speed 1300-1400m/min;
F, as-spun fibre is carried out shaping using parallel drafting machine, finished product polyester fiber can be obtained, drafting multiple is 3-4 times;
G, polyester fiber and pearl fiber and cocoon fiber progress is blended, and by dyeing, final finishing, obtain blended yarn weaved fabric.
3. the preparation method that vapor-permeable type Yoga as claimed in claim 2 takes fabric, which is characterized in that in the step A
Antibacterial plant mixture, the ingredient including following weight percent:
Dandelion 15-20%
Herba Epimedii 8-15%
Safflower 3-5%
Mulberry leaf surplus.
4. the preparation method that vapor-permeable type Yoga as claimed in claim 2 takes fabric, which is characterized in that micro- in the step E
The weight percent of capsule, micron order calcined shell powder and polyester slice are as follows:
Microcapsules 3-5%
Micron order calcined shell powder 1-2%
Polyester slice surplus.
5. the preparation method that vapor-permeable type Yoga as claimed in claim 2 takes fabric, which is characterized in that can in the step E
It is added in polyester slice with being added after natural plants coloring agent mixes jointly with microcapsules and micron order calcined shell powder.
6. the preparation method that vapor-permeable type Yoga as claimed in claim 2 takes fabric, which is characterized in that in the step G, dye
Color and finishing process are combined into one, and by temperature control between 70-80 DEG C, the control of processing time is within 5min.
7. the preparation method that vapor-permeable type Yoga as claimed in claim 5 takes fabric, which is characterized in that the natural plants of addition contaminate
The weight of toner is the 3-10% of polyester slice weight.