CN106049042B - A kind of preparation method of terylene leggings fabric - Google Patents

A kind of preparation method of terylene leggings fabric Download PDF

Info

Publication number
CN106049042B
CN106049042B CN201610373845.4A CN201610373845A CN106049042B CN 106049042 B CN106049042 B CN 106049042B CN 201610373845 A CN201610373845 A CN 201610373845A CN 106049042 B CN106049042 B CN 106049042B
Authority
CN
China
Prior art keywords
bombax cotton
terylene
leggings
fabric
polyester fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610373845.4A
Other languages
Chinese (zh)
Other versions
CN106049042A (en
Inventor
包新姐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huizhou Sheng Xing Industrial Co., Ltd.
Original Assignee
CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd filed Critical CHANGXING ZHIHENG CLOTHING MATERIAL Co Ltd
Priority to CN201610373845.4A priority Critical patent/CN106049042B/en
Publication of CN106049042A publication Critical patent/CN106049042A/en
Application granted granted Critical
Publication of CN106049042B publication Critical patent/CN106049042B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention provides a kind of preparation methods of terylene leggings fabric, blended by carrying out polyester fiber and bombax cotton and nylon fibre, can reach extraordinary heat preservation, antibacterial effect, while being also equipped with extraordinary drapability and body shaping performance；Environmental protection treatment is carried out to bombax cotton, bombax cotton is made to have good heat-insulating property；Chemicals is not used in addition to food grade glycerin, is a kind of tencel preparation method of environmental protection.

Description

A kind of preparation method of terylene leggings fabric
Technical field
The present invention relates to functional form garment material fields, more particularly to a kind of preparation method of terylene leggings fabric.
Background technology
Polyester fiber is as most widely used chemical fibre, with good fibre-forming performance and mechanical performance, intensity High, fast light, heat-resisting and resistance to acid and alkali is good, has good processability and Yi Fangxing, pure can spin, blended and intertexture.Polyester fabric Washable and wearable, ironing and anti-crease, clothes, home textile, decoration and product with etc. fields be widely used.However, polyester fiber is also deposited Hygroscopicity is poor, absorbing sweat, dress do not have the shortcomings that feeling of oppression and heat, anti-static ability difference and easily stain dust fabric, therefore make significantly The about application and development of polyester fiber.For the snugness of fit of raising polyester fiber, the application added value of polyester fiber is improved, The improvement of chemically or physically aspect, and then the higher moisture absorbing and sweat releasing property of endowing terylene fiber are typically carried out to polyester fiber, are carried High dacron wearing comfort.
Leggings, it is also known as interior to take trousers.It is in order to wear the trousers that skirt and mini-skirt are wardrobe-malfunction-proof, cultivate one's moral character and design, because of length And point many kinds, collocation that can from formal dress dress ornament different different with materials.Because it is wardrobe-malfunction-proof, cultivate one's moral character, the position not only worn It is bottoming to set, and also compare has bottom at heart.Leggings generally slightly long doll's shirt, long suspender belt, T-shirt and even body skirt with upper body It is more reasonable.This pants type is mainly suitable for female consumer, is favored by women so comparing.
With the continuous improvement of people's quality of the life, fabric especially the warming of winter leggings, antibacterial, slimming effect with And drapability increasingly obtains thinking highly of for people, the fabric being currently known can not take into account above functions.
Invention content
In view of this, there is good warming, anti-microbial property terylene leggings fabric the object of the present invention is to provide a kind of Preparation method.
A kind of preparation method of terylene leggings fabric, carries out as steps described below：
A, be placed on after disperseing bombax cotton in prepared environmental protection treatment liquid and impregnate 2-3h, then by washing and 40-50 DEG C of drying；
B, treated bombax cotton and the progress of polyester fiber and nylon fibre is blended, obtain scribbled；
C, scribbled is weaved, obtains blended blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming Trousers fabric.
Preferably, the environmental protection treatment liquid of the bombax cotton, includes the ingredient of following weight percent：
Food grade glycerin 3-5%
Olive oil 1-3%
Vegetable colour 2-5%
Paper mulberry juice 0.5-0.8%
Guar gum 8-12%
Extract from fructus polygoni orientalis 1-2%
Deionized water surplus.
Chinese invention patent CN101982584A discloses a kind of processing method of high hollow ratio kapok yarn, and this method is logical It crosses and overcomes traditional bombax cotton degree of hollowness after spinning process in the surface of bombax cotton coating elastic film and can not protect The shortcomings that holding.
But this method is to using polyurethane, dimethylformamide, fluorine-containing anti-in the surface coating procedure of bombax cotton The organic matters such as aqua, octadecyl alcolol still have part residual that can have potential hazard to human body, while aggravating even across post-processing To the burden of environment.The present invention provides a kind of bombax cotton processing method of environment protection health, this method uses guar gum conduct Binder, food grade glycerin and olive oil are anti-as antiseptic and mixing as dispersant, paper mulberry juice and extract from fructus polygoni orientalis Aqua, to achieve the effect that the degree of hollowness to bombax cotton is kept.
Simultaneously blended polyester fiber and nylon fibre are dyed in advance, to only needed after blended to fabric into The simple stamp of row and sizing, need not move through complicated dyeing and arrangement, reduce environmental pollution while also mitigating pair The destruction of bombax cotton degree of hollowness makes the blended yarn weaved fabric of preparation have extraordinary thermal property.
Preferably, the polyester fiber and nylon fibre carry out it using vegetable colour in the preparatory phase of fiber Dyeing.
Preferably, the weight percent of polyester fiber, bombax cotton and nylon fibre is respectively in the blended yarn weaved fabric 60-70%, 25-35% and 5-8%.
The preparation method of terylene leggings fabric provided by the present invention, has the following advantages that：
1, chemicals is not used in addition to food grade glycerin, is a kind of tencel preparation method of environmental protection；
2, olive oil and food grade glycerin is added, reinforces the dispersion effect of bombax cotton treatment fluid；
3, blended yarn weaved fabric needs not move through dyeing and final finishing stage, maintains the good heat-insulating property of bombax cotton；
4, paper mulberry juice and extract from fructus polygoni orientalis and bombax cotton phase separation is added, fabric is made to have good antibiotic property Energy.
5, the good drapability for the existing polyester fiber of terylene leggings fabric being made into, also has the good guarantor of bombax cotton Warm nature energy, also the body shaping performance with nylon fibre, while also there is good anti-microbial property.
Specific implementation mode
Embodiment 1
A kind of preparation method of terylene leggings fabric, carries out as steps described below：
A, it is placed on after disperseing bombax cotton in prepared environmental protection treatment liquid and impregnates 2.5h, then by washing and 45 DEG C drying；
B, treated bombax cotton and the progress of polyester fiber and nylon fibre is blended, obtain scribbled；
C, scribbled is weaved, obtains blended blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming Trousers fabric.
The environmental protection treatment liquid of the bombax cotton, includes the ingredient of following weight percent：
Food grade glycerin 4%
Olive oil 2%
Vegetable colour 5%
Paper mulberry juice 0.7%
Guar gum 10%
Extract from fructus polygoni orientalis 2%
Deionized water surplus.
The polyester fiber and nylon fibre dyes it using vegetable colour in the preparatory phase of fiber.
In the blended yarn weaved fabric weight percent of polyester fiber, bombax cotton and nylon fibre be respectively 62%, 32% and 6%.
Embodiment 2
A kind of preparation method of terylene leggings fabric, carries out as steps described below：
A, it is placed on after disperseing bombax cotton in prepared environmental protection treatment liquid and impregnates 2h, then by washing and 50 DEG C Drying；
B, treated bombax cotton and the progress of polyester fiber and nylon fibre is blended, obtain scribbled；
C, scribbled is weaved, obtains blended blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming Trousers fabric.
The environmental protection treatment liquid of the bombax cotton, includes the ingredient of following weight percent：
Food grade glycerin 3%
Olive oil 3%
Vegetable colour 2%
Paper mulberry juice 0.8%
Guar gum 8%
Extract from fructus polygoni orientalis 1%
Deionized water surplus.
The polyester fiber and nylon fibre dyes it using vegetable colour in the preparatory phase of fiber.
In the blended yarn weaved fabric weight percent of polyester fiber, bombax cotton and nylon fibre be respectively 60%, 30% and 5%.
Embodiment 3
A kind of preparation method of terylene leggings fabric, carries out as steps described below：
A, it is placed on after disperseing bombax cotton in prepared environmental protection treatment liquid and impregnates 3h, then by washing and 40 DEG C Drying；
B, treated bombax cotton and the progress of polyester fiber and nylon fibre is blended, obtain scribbled；
C, scribbled is weaved, obtains blended blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming Trousers fabric.
The environmental protection treatment liquid of the bombax cotton, includes the ingredient of following weight percent：
Food grade glycerin 5%
Olive oil 1%
Vegetable colour 2%
Paper mulberry juice 0.6%
Guar gum 12%
Extract from fructus polygoni orientalis 1.5%
Deionized water surplus.
The polyester fiber and nylon fibre dyes it using vegetable colour in the preparatory phase of fiber.
In the blended yarn weaved fabric weight percent of polyester fiber, bombax cotton and nylon fibre be respectively 67%, 25% and 8%.
Comparative example 1
By the paper mulberry juice removal in embodiment 1, remaining preparation condition is same as Example 1.
Comparative example 2
By the extract from fructus polygoni orientalis removal in embodiment 1, remaining preparation condition is same as Example 1.
The anti-microbial property of the fabric of embodiment and comparative example is tested, following data are obtained：
The examination criteria of biocidal property is GB/T20944.3-2008《The evaluation third portion of antibacterial textile performance：Oscillation Method》, using color fastness to washing testing machine washing methods, the bacteriostasis rate of fabric after test is washed 30 times.
By the above test data it is recognised that being individually added into paper mulberry juice or extract from fructus polygoni orientalis, the antibiotic property of fabric Can be than two kinds of substances be added simultaneously, antibacterial effect is far short of what is expected, therefore the antibacterial effect of fabric of the present invention is bombax cotton and paper mulberry Juice and the coefficient result of extract from fructus polygoni orientalis.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto, Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.

Claims (4)

1. a kind of preparation method of terylene leggings fabric, which is characterized in that carry out as steps described below：
A, it is placed on after disperseing bombax cotton in prepared environmental protection treatment liquid and impregnates 2-3h, then by washing and 40-50 DEG C drying；
B, treated bombax cotton and the progress of polyester fiber and nylon fibre is blended, obtain scribbled；
C, scribbled is weaved, obtains blended blank, then carry out stamp, rear shaping and drying, obtain terylene leggings face Material；
The environmental protection treatment liquid of the bombax cotton, includes the ingredient of following weight percent：
Food grade glycerin 3-5%
Olive oil 1-3%
Vegetable colour 2-5%
Paper mulberry juice 0.5-0.8%
Guar gum 8-12%
Extract from fructus polygoni orientalis 1-2%
Deionized water surplus.
2. the preparation method of terylene leggings fabric according to claim 1, which is characterized in that the polyester fiber and Nylon fibre is dyed using vegetable colour in the preparatory phase of fiber.
3. the preparation method of terylene leggings fabric according to claim 1, which is characterized in that in the blended yarn weaved fabric The weight percent of polyester fiber, bombax cotton and nylon fibre is respectively 60-70%, 25-35% and 5-8%.
4. the preparation method of terylene leggings fabric according to claim 1, which is characterized in that as steps described below into Row：
A, it is placed on after disperseing bombax cotton in prepared environmental protection treatment liquid and impregnates 2.5h, then by washing and 45 DEG C of bakings It is dry；
B, treated bombax cotton and the progress of polyester fiber and nylon fibre is blended, obtain scribbled；
C, scribbled is weaved, obtains blended blank, then carry out stamp, rear shaping and drying, obtain terylene leggings face Material；
The environmental protection treatment liquid of the bombax cotton, includes the ingredient of following weight percent：
Food grade glycerin 4%
Olive oil 2%
Vegetable colour 5%
Paper mulberry juice 0.7%
Guar gum 10%
Extract from fructus polygoni orientalis 2%
Deionized water surplus；
The polyester fiber and nylon fibre dyes it using vegetable colour in the preparatory phase of fiber；
The weight percent of polyester fiber, bombax cotton and nylon fibre is respectively 62%, 32% and 6% in the blended yarn weaved fabric.
CN201610373845.4A 2016-05-31 2016-05-31 A kind of preparation method of terylene leggings fabric Active CN106049042B (en)