CN106049042A - Preparing method for polyester fabric for leggings - Google Patents
Preparing method for polyester fabric for leggings Download PDFInfo
- Publication number
- CN106049042A CN106049042A CN201610373845.4A CN201610373845A CN106049042A CN 106049042 A CN106049042 A CN 106049042A CN 201610373845 A CN201610373845 A CN 201610373845A CN 106049042 A CN106049042 A CN 106049042A
- Authority
- CN
- China
- Prior art keywords
- fabric
- leggings
- bombax cotton
- terylene
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a preparing method for polyester fabric for leggings. By blending polyester fibers, kapok fibers and polyamide fabric, very good thermal insulation and antibacterial effects can be achieved, and meanwhile very good drapability and body shaping performance are achieved; environment-friendly treatment is carried out on kapok fibers, and thus kapok fibers are made to have good thermal insulation performance; no chemical preparation is used except food-grade glycerin, and the novel fiber preparing method is environmentally friendly.
Description
Technical field
The present invention relates to functional type garment material field, particularly relate to the preparation method of a kind of terylene leggings fabric.
Background technology
Polyster fibre is as most widely used chemical fibre, and it has good fibre-forming performance and mechanical performance, intensity
High, fast light, heat-resisting and resistance to acids and bases is good, there is good processability and Yi Fangxing, can pure spin, blending and intertexture.Polyester fabric
Washable and wearable, ironing and anti-crease, clothing, home textile, decoration and product with etc. field be widely used.But, polyster fibre is also deposited
, fabric not absorbing sweat poor in hygroscopicity, dress have feeling of oppression and heat, anti-static ability difference and easily stain the shortcomings such as dust, the most significantly make
The about application of polyster fibre and development.For improving the snugness of fit of polyster fibre, improve the application added value of polyster fibre,
It is typically polyster fibre is carried out the improvement of chemically or physically aspect, and then the moisture absorbing and sweat releasing property that endowing terylene fiber is higher, carries
High dacron wearing comfort.
Leggings, takes trousers also known as interior.It is to wear skirt and mini-skirt preventing exposure, cultivates one's moral character and the trousers that design, because of length
Different with materials and point a variety of, collocation that can be different from formal dress dress ornament.Because preventing exposure, cultivating one's moral character, so the position not only worn
Putting is bottoming, and the most also comparing has the end.General doll's shirt, long suspender belt, T-shirt and the company's body skirt slightly grown with upper body of leggings
The most reasonable.This pants type is mainly suitable for female consumer, is favored so comparing by women.
Along with improving constantly of people's quality of the life, warming, antibacterial, the slimming effect of fabric especially leggings in winter with
And drapability increasingly obtains thinking highly of of people, the fabric being currently known cannot take into account function above.
Summary of the invention
In view of this, it is an object of the invention to provide and a kind of there is the most warming, the terylene leggings fabric of anti-microbial property
Preparation method.
The preparation method of a kind of terylene leggings fabric, is carried out as steps described below:
A, by bombax cotton disperse after be placed in the environmental protection treatment liquid prepared dipping 2-3h, be then passed through washing and
40-50 DEG C of drying；
B, treated bombax cotton and polyster fibre and nylon fibre are carried out blending, obtain scribbled；
C, scribbled is weaved, obtain blending blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming
Trousers fabric.
Preferably, the environmental protection treatment liquid of described bombax cotton, including the composition of following percentage by weight:
Food grade glycerin 3-5%
Olive oil 1-3%
Vegetable colour 2-5%
Broussonetia papyrifera juice 0.5-0.8%
Guar gum 8-12%
Extract from fructus polygoni orientalis 1-2%
Deionized water surplus.
Chinese invention patent CN101982584A discloses the processing method of a kind of high hollow ratio kapok yarn, and the method is led to
Cross the surface-coated elastic film at bombax cotton to overcome traditional bombax cotton degree of hollowness after spinning process and cannot protect
The shortcoming held.
But the method is to have employed polyurethane, dimethylformamide, fluorine-containing anti-during the surface-coated of bombax cotton
The Organic substance such as water preparation, octadecanol, even across post processing, still has part residual human body can be had potential hazard, increases the weight of simultaneously
Burden to environment.The invention provides the bombax cotton processing method of a kind of environment protection health, the method uses guar gum conduct
Binding agent, food grade glycerin and olive oil are anti-as antibacterial and mixing as dispersant, Broussonetia papyrifera juice and extract from fructus polygoni orientalis
Water preparation, thus reach the effect that the degree of hollowness of bombax cotton is kept.
Polyster fibre and nylon fibre to blending dye in advance simultaneously, thus only need to enter fabric after blending
Row simple stamp and shaping, it is not necessary to through complicated dyeing and arrangement, reduce environmental pollution, simultaneously also mitigate right
The destruction of bombax cotton degree of hollowness, makes the blended yarn weaved fabric of preparation possess extraordinary thermal property.
Preferably, described polyster fibre and nylon fibre i.e. use vegetable colour to carry out it at the preparatory phase of fiber
Dyeing.
Preferably, in described blended yarn weaved fabric, the percentage by weight of polyster fibre, bombax cotton and nylon fibre is respectively
60-70%, 25-35% and 5-8%.
The preparation method of terylene leggings fabric provided by the present invention, has the advantage that
1, in addition to food grade glycerin, do not use chemicals, be the tencel preparation method of a kind of environmental protection；
2, add olive oil and food grade glycerin, strengthen the dispersion effect of bombax cotton treatment fluid；
3, blended yarn weaved fabric needs not move through dyeing and Final finishing stage, maintains the heat-insulating property that bombax cotton is good；
4, add Broussonetia papyrifera juice and extract from fructus polygoni orientalis and bombax cotton phase separation, make fabric possess good antibiotic property
Energy.
The good drapability of the terylene existing polyster fibre of leggings fabric 5, being made into, also possesses the guarantor that bombax cotton is good
Warm nature energy, also has the body shaping performance of nylon fibre, the most also has good anti-microbial property.
Detailed description of the invention
Embodiment 1
The preparation method of a kind of terylene leggings fabric, is carried out as steps described below:
A, by bombax cotton disperse after be placed in the environmental protection treatment liquid prepared dipping 2.5h, be then passed through washing and 45
DEG C dry；
B, treated bombax cotton and polyster fibre and nylon fibre are carried out blending, obtain scribbled；
C, scribbled is weaved, obtain blending blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming
Trousers fabric.
The environmental protection treatment liquid of described bombax cotton, including the composition of following percentage by weight:
Food grade glycerin 4%
Olive oil 2%
Vegetable colour 5%
Broussonetia papyrifera juice 0.7%
Guar gum 10%
Extract from fructus polygoni orientalis 2%
Deionized water surplus.
Described polyster fibre and nylon fibre i.e. use vegetable colour to dye it at the preparatory phase of fiber.
In described blended yarn weaved fabric the percentage by weight of polyster fibre, bombax cotton and nylon fibre be respectively 62%,
32% and 6%.
Embodiment 2
The preparation method of a kind of terylene leggings fabric, is carried out as steps described below:
A, by bombax cotton disperse after be placed in the environmental protection treatment liquid prepared dipping 2h, be then passed through washing and 50 DEG C
Dry；
B, treated bombax cotton and polyster fibre and nylon fibre are carried out blending, obtain scribbled；
C, scribbled is weaved, obtain blending blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming
Trousers fabric.
The environmental protection treatment liquid of described bombax cotton, including the composition of following percentage by weight:
Food grade glycerin 3%
Olive oil 3%
Vegetable colour 2%
Broussonetia papyrifera juice 0.8%
Guar gum 8%
Extract from fructus polygoni orientalis 1%
Deionized water surplus.
Described polyster fibre and nylon fibre i.e. use vegetable colour to dye it at the preparatory phase of fiber.
In described blended yarn weaved fabric the percentage by weight of polyster fibre, bombax cotton and nylon fibre be respectively 60%,
30% and 5%.
Embodiment 3
The preparation method of a kind of terylene leggings fabric, is carried out as steps described below:
A, by bombax cotton disperse after be placed in the environmental protection treatment liquid prepared dipping 3h, be then passed through washing and 40 DEG C
Dry；
B, treated bombax cotton and polyster fibre and nylon fibre are carried out blending, obtain scribbled；
C, scribbled is weaved, obtain blending blank, then carry out stamp, rear shaping and drying, obtain terylene bottoming
Trousers fabric.
The environmental protection treatment liquid of described bombax cotton, including the composition of following percentage by weight:
Food grade glycerin 5%
Olive oil 1%
Vegetable colour 2%
Broussonetia papyrifera juice 0.6%
Guar gum 12%
Extract from fructus polygoni orientalis 1.5%
Deionized water surplus.
Described polyster fibre and nylon fibre i.e. use vegetable colour to dye it at the preparatory phase of fiber.
In described blended yarn weaved fabric the percentage by weight of polyster fibre, bombax cotton and nylon fibre be respectively 67%,
25% and 8%.
Comparative example 1
Being removed by Broussonetia papyrifera juice in embodiment 1, remaining preparation condition is same as in Example 1.
Comparative example 2
Being removed by extract from fructus polygoni orientalis in embodiment 1, remaining preparation condition is same as in Example 1.
The anti-microbial property of embodiment and the fabric of comparative example is tested, obtains following data:
The examination criteria of biocidal property is GB/T20944.3-2008 " the evaluation third portion of antibacterial textile performance: vibration
Method ", use color fastness to washing testing machine washing methods, test to wash the bacteriostasis rate of fabric after 30 times.
By testing data above it is recognised that be individually added into Broussonetia papyrifera juice or extract from fructus polygoni orientalis, the antibiotic property of fabric
All can be simultaneously introduced two kinds of materials by ratio, antibacterial effect is far short of what is expected, therefore the antibacterial effect of fabric of the present invention is bombax cotton and Broussonetia papyrifera
Juice and the coefficient result of extract from fructus polygoni orientalis.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (5)
1. the preparation method of a terylene leggings fabric, it is characterised in that carry out as steps described below:
A, by bombax cotton disperse after be placed in the environmental protection treatment liquid prepared dipping 2-3h, be then passed through washing and 40-50
DEG C dry；
B, treated bombax cotton and polyster fibre and nylon fibre are carried out blending, obtain scribbled；
C, scribbled is weaved, obtain blending blank, then carry out stamp, rear shaping and drying, obtain terylene leggings face
Material.
The preparation method of terylene leggings fabric the most according to claim 1, it is characterised in that described bombax cotton
Environmental protection treatment liquid, including the composition of following percentage by weight:
Food grade glycerin 3-5%
Olive oil 1-3%
Vegetable colour 2-5%
Broussonetia papyrifera juice 0.5-0.8%
Guar gum 8-12%
Extract from fructus polygoni orientalis 1-2%
Deionized water surplus.
The preparation method of terylene leggings fabric the most according to claim 1, it is characterised in that described polyster fibre and
Nylon fibre i.e. uses vegetable colour to dye at the preparatory phase of fiber.
The preparation method of terylene leggings fabric the most according to claim 1, it is characterised in that in described blended yarn weaved fabric
The percentage by weight of polyster fibre, bombax cotton and nylon fibre is respectively 60-70%, 25-35% and 5-8%.
The preparation method of terylene leggings fabric the most according to claim 1, it is characterised in that enter as steps described below
OK:
A, by bombax cotton disperse after be placed in the environmental protection treatment liquid prepared dipping 2.5h, be then passed through washing and 45 DEG C of bakings
Dry；
B, treated bombax cotton and polyster fibre and nylon fibre are carried out blending, obtain scribbled；
C, scribbled is weaved, obtain blending blank, then carry out stamp, rear shaping and drying, obtain terylene leggings face
Material；
The environmental protection treatment liquid of described bombax cotton, including the composition of following percentage by weight:
Food grade glycerin 4%
Olive oil 2%
Vegetable colour 5%
Broussonetia papyrifera juice 0.7%
Guar gum 10%
Extract from fructus polygoni orientalis 2%
Deionized water surplus；
Described polyster fibre and nylon fibre i.e. use vegetable colour to dye it at the preparatory phase of fiber；
In described blended yarn weaved fabric, the percentage by weight of polyster fibre, bombax cotton and nylon fibre is respectively 62%, 32% and 6%.