CN105908329A - Anti-bacterial shirt fabric and making method thereof - Google Patents
Anti-bacterial shirt fabric and making method thereof Download PDFInfo
- Publication number
- CN105908329A CN105908329A CN201610322711.XA CN201610322711A CN105908329A CN 105908329 A CN105908329 A CN 105908329A CN 201610322711 A CN201610322711 A CN 201610322711A CN 105908329 A CN105908329 A CN 105908329A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- fibre
- preparation
- fabric
- polyester slice
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for preparing an anti-bacterial shirt fabric. Anti-bacterial polyester fibers, silk fibers and vinylon fibers are blended, and an anti-bacterial plant mixture is added in the making process of anti-bacterial polyester fibers, so that the price is low, and the effect is good. Meanwhile, the anti-bacterial plant mixture and shell powder are added, so that the anti-bacterial effect is better. A natural plant coloring agent is added, so that the dyeing effect is good.
Description
Technical field
The present invention relates to functional type garment material field, particularly relate to a kind of antibacterial shirt fabric and preparation thereof
Method.
Background technology
Polyster fibre is as most widely used chemical fibre, and it has good fibre-forming performance and mechanical performance,
Intensity is high, fast light, heat-resisting and resistance to acids and bases is good, has good processability and Yi Fangxing, can pure spin, blending
And intertexture.Polyester fabric washable and wearable, ironing and anti-crease, at field quilts such as clothing, home textile, decoration and product use
Extensively application.But, polyster fibre there is also that hygroscopicity is poor, fabric not absorbing sweat, dress have feeling of oppression and heat, anti-quiet
The shortcomings such as power difference and easily contamination dust, constrain application and the development of polyster fibre the most significantly.For improving
The snugness of fit of polyster fibre, improves the application added value of polyster fibre, it is common that to polyster fibre
Improvement in terms of or physics, and then the moisture absorbing and sweat releasing property that endowing terylene fiber is higher, improve dacron dress
Comfort level.
Along with people are more and more higher to the requirement of fabric, other performance of polyster fibre is the most gradually by the weight of people
Depending on, especially possess the chemical fibre product of anti-microbial property, there is good market prospect.
Shirt can be divided into combing cotton shirt, silk shirt, crepe de Chine shirt, polyester-cotton shirt etc. by bed material, typically
Focus on light, thin, soft, refreshing, very, the performance such as good permeability, and anti-microbial property is the most increasingly by the weight of people
Depending on.
Summary of the invention
In view of this, it is an object of the invention to provide the preparation method of a kind of antibacterial shirt fabric.
A kind of antibacterial shirt fabric, is formed by polyster fibre, silk fiber, vinylon fibre hybrid woven, described
Each weight percentages of components of blended yarn weaved fabric as follows:
Silk fiber 10-15%
Vinylon fibre 15-25%
Polyster fibre surplus.
The preparation method of a kind of antibacterial shirt fabric, is carried out as steps described below:
A, antibacterial plant mixture and distilled water being added in flask, the quality of distilled water is plant mixture matter
20-30 times of amount;
B, it is heated to 35-40 DEG C, and distillation of reducing pressure, collect distillate;
C, gained distillate is filtered and concentrated to solid content is to obtain plant antimicrobial after 50-60%;
D, under the preparation condition of not higher than 40 DEG C, use gelatin and arabic gum to be coated with Genes For Plant Tolerance as softgel shell
Microbial inoculum, forms microcapsule;
E, microcapsule and micron order calcined shell powder are sufficiently mixed, are then quantitatively adding molten by metering rotating disk
Melt in the polyester slice of state, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made
As-spun fibre, concrete technology condition is: spinning temperature 300-320 DEG C, and spinning speed is 1300-1400m/min;
F, as-spun fibre uses parallel drafting machine shape, i.e. can get finished product polyster fibre, drawing-off times
Number is for 3-4 times;
G, polyster fibre and silk fiber and vinylon fibre are carried out blending, and through dyeing, Final finishing,
To blended yarn weaved fabric.
Preferably, the antibacterial plant mixture in described step A includes the composition of following percentage by weight:
Herba Taraxaci 15-20%
Flos Chrysanthemi Indici 8-15%
Aloe 3-5%
Flagger surplus.
Preferably, microcapsule, micron order calcined shell powder and the weight percent of polyester slice in described step E
Than being:
Microcapsule 3-5%
Micron order calcined shell powder 1-2%
Polyester slice surplus.
Preferably, described step E can add natural plants stain and microcapsule and micron order calcining shellfish
Shell powder adds in polyester slice after jointly mixing.
Preferably, the 3-10% that amount is polyester slice weight of the natural plants stain of addition.
Preferably, in described step G, in order to reduce the high temperature impact on polyster fibre anti-microbial property, described
Dyeing and finishing process unite two into one, and temperature is controlled between 70-80 DEG C, the process time controls
Within 5min.
Dandelion herbaceos perennial.Root is coniform, surface sepia, shrinkage, and limb edge has ripple sometimes
Shape tooth or pinniform drastic crack, base portion the narrowest one-tenth petiole, petiole and master pulse normal band reddish violet, scape top aubergine,
Close by the spider's thread shape long pubescence of white;Head inflorescence, involucre mitriform, achene crineous, long pappus white, flowers and fruits
Phase 4~October.Herba Taraxaci possesses certain antibacterial action: to staphylococcus aureus in this product injection test tube
Resistant strain, Hemolytic streptococcus have stronger bactericidal action.To Diplococcus pneumoniae, meningococcus, diphtheria
Bacillus, bacillus pyocyaneus, dysentery bacterium, Bacillus typhi etc. and micrococcus catarrhalis also have certain bactericidal action.This product alcohol
Extract 1:400 can suppress tulase, but decoct 1:100 is invalid.The water decoction of its 1:80 can delay
ECHO11 viral cytopathic, ethanol extract (31mg/kg) can kill leptospira, also have some fungus
Inhibitory action.Campylobacter pylori is had good killing action.
Flos Chrysanthemi Indici is Compositae herbaceos perennial, and the capitate profile of Flos Chrysanthemi Indici is similar to Flos Chrysanthemi, in class ball
Shape, diameter 0.3~1cm, brown color.Involucre is made up of 4~5 layers of bract.Ligulate flower one is taken turns, yellow, wrinkle
Crinkle is bent;Tubular flower is most, buff.Body is light.Gas is pungent, bitter in the mouth, slightly poisonous.Wild in patana,
The wild area such as Tian Bian, roadside.It is preferred without stalk, complete, toil, the non-standard-sized sheet person of flower with yellow skin.The leaf of Herba Dendranthematis indici,
Flower and all herbal medicine.Bitter in the mouth, pungent, cool, heat-clearing and toxic substances removing, wind-dispelling heat-dissipating, dissipating blood stasis, improving eyesight, blood pressure lowering.Anti-
Control epidemic cerebrospinal meningitis, prevent influenza, flu, treat hypertension, hepatitis, dysentery, carbuncle furuncle
Treat skin ulcer and have positive effect.The immersion of Flos Chrysanthemi Indici is to killing wriggler and fly larvae is the most highly effective.Flos Chrysanthemi Indici is to summer
Red and swollen pustule after mosquito bite has the effect that sterilization goes to swell.
Aloe is Liliaceae perennial evergreen herbaceous plant, and leafage is raw, big and plump, in seat shape or be born in stem top,
The normal lanceolar of leaf or the short width of leaf, edge has sharp tooth to sting.Inflorescence is umbrella shape, total shape, spike, cone etc.,
Color is red, yellow or tool redness of the skin or complexion speckle, six, petal, gynoecium six pieces.The many Colaesces of perianth base portion become tubular.Aloe
In Aloin A, wound hormone and the polysaccharide peptide manna etc. that contain there is viral infection resisting, promote that wound healing is multiple
Former effect, has anti-inflammation and sterilization, heat absorption detumescence, softening skin, the function of holding cell viability, curdlan
Combine with 1-decene-1 and also there is healing wounds activity.
Flagger is Iridaceae, iris, perennial thicket draft.Root stock is sturdy, wooden, tiltedly stretches,
It is surrounded by outward Lao Ye residual sheath and trichoid fiber that a large amount of fine and close reddish violet fractures;Fibrous root is thick and grows, yellow
White, few branch.[1] spending big novelty, pattern is gorgeous, dazzlingly beautiful.Flower has indigo plant, white, yellow, lilac
Isochrome.The month at florescence 5-6, each flower can bloom 7-10 days, the most resistance to views and admires;Flagger happiness sunlight, suitable plant in
Leeward in sandy soil.Cure mainly laryngopharynx swelling and pain, spit blood, epistaxis, spitting of blood, dysuria, sick, ulcerative carbuncle furuncle
Swollen.
The antibacterial plant mixture of the present invention uses flagger to be main component, is simultaneously introduced Herba Taraxaci, Flos Chrysanthemi Indici
And Aloe, wherein flagger is grown on wasteland, roadside, patana, especially with the salinization of soil grassland overgrazed
Upper growth is more, and raw material is extensive, and price is low;And the higher Aloe addition of price is considerably less.Various plants is mixed
After conjunction, antibacterial effect is more a lot of than single plant.
Conch meal is by making after high-temperature calcination, pulverizing by natural seashell.Its constituent is calcium carbonate, oxygen
Changing the calcified material such as calcium, calcium hydroxide, this is as cellular, has absorption, decomposes (formaldehyde, benzene, ammonia)
Deng effect and the function such as adjusting air humidity, the conch meal simultaneously fired to include escherichia coli, Salmonella,
Staphylococcus aureuses etc. have extremely strong antibacterial and bactericidal action in interior various bacteria, and have anticorrosion, prevent
Mould function.In coating add conch meal, the interior wall coating made by have good absorption harmful gas and
Fungistatic effect.
Conch meal and antibacterial plant mixture are used in conjunction with, and antibacterial effect is more preferably.
In the preparation process of the whole antibiotic polyester fiber of the present invention, conch meal and antibacterial plant mixture are added
In polyester slice, due to the simplest mixing of preparation technology, conch meal and antibacterial plant mixture mainly divide
Cloth is in the PET fiber surface generated, therefore conch meal and antibacterial plant mixture usage amount are less;Add natural planting
After thing stain, stain is distributed in terylene surface equally, and Color is good.
The preparation method of a kind of antibacterial shirt fabric provided by the present invention, has the advantage that
1, in antibiotic polyester fiber preparation process, do not use chemicals, be the tencel system of a kind of environmental protection
Preparation Method.
2, the antibacterial plant mixture added, cheap, effective, uses early stage low temperature prepare and use micro-
The mode of capsule cladding, time in the polyester slice of the molten state of later stage addition about 300 DEG C, can be to antibacterial
The effectively antimicrobial component such as contained phenols in plant mixture, alcohols, lipid is not destroyed as far as possible.
3, being simultaneously introduced antibacterial plant mixture and conch meal, antibacterial effect is more preferably.
4, by polyster fibre and silk fiber and vinylon fibre blending, the most farthest ensure that fabric
Soft, lubricious, the hygroscopicity of fabric can be increased again, antibacterial bacteriostatic is effective, simultaneously the addition of silk fiber
Not higher than 15%, compare traditional silk and greatly reduce cost.
Detailed description of the invention
The preparation method of a kind of antibacterial shirt fabric, is carried out as steps described below:
A, antibacterial plant mixture and distilled water being added in flask, the quality of distilled water is plant mixture matter
20-30 times of amount;
B, it is heated to 38 DEG C, and distillation of reducing pressure, collect distillate;
C, gained distillate is filtered and concentrated to solid content is to obtain plant antimicrobial after 55%;
D, under the preparation condition of not higher than 20-35 DEG C, use gelatin and arabic gum to plant as softgel shell cladding
Thing antibacterial, forms microcapsule;
E, microcapsule and micron order calcined shell powder are sufficiently mixed, are then quantitatively adding molten by metering rotating disk
Melt in the polyester slice of state, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made
As-spun fibre, concrete technology condition is: spinning temperature 305 DEG C, and spinning speed is 1350m/min;
F, as-spun fibre uses parallel drafting machine shape, i.e. can get finished product polyster fibre, drawing-off times
Number is 3.5 times;
G, polyster fibre and silk fiber and vinylon fibre are carried out blending, and through dyeing, Final finishing,
To blended yarn weaved fabric.
Each weight percentages of components of described blended yarn weaved fabric is as follows:
Silk fiber 12%
Vinylon fibre 18%
Polyster fibre surplus.
Antibacterial plant mixture in described step A, including the composition of following percentage by weight:
Herba Taraxaci 18%
Flos Chrysanthemi Indici 10%
Aloe 4%
Flagger surplus.
In described step E, the percentage by weight of microcapsule, micron order calcined shell powder and polyester slice is:
Microcapsule 4%
Micron order calcined shell powder 1.5%
Polyester slice surplus.
Table one: in each specific embodiment, each weight percentages of components of antibacterial plant mixture please see table:
Herba Taraxaci | Flos Chrysanthemi Indici | Aloe | Flagger | |
Embodiment 1 | 18 | 10 | 4 | Surplus |
Embodiment 2 | 15 | 12 | 4 | Surplus |
Embodiment 3 | 16 | 12 | 5 | Surplus |
Embodiment 4 | 16 | 8 | 5 | Surplus |
Embodiment 5 | 18 | 15 | 3 | Surplus |
Embodiment 6 | 20 | 15 | 3 | Surplus |
Embodiment 7 | 20 | 10 | 3 | Surplus |
Table two: in each specific embodiment, each weight percentages of components of polyster fibre please see table:
Table three: in each specific embodiment, in blended yarn weaved fabric, each fiber weight percentage please see table:
Silk fiber | Vinylon fibre | Polyster fibre | |
Embodiment 1 | 12 | 18 | Surplus |
Embodiment 2 | 10 | 20 | Surplus |
Embodiment 3 | 12 | 25 | Surplus |
Embodiment 4 | 12 | 25 | Surplus |
Embodiment 5 | 13 | 22 | Surplus |
Embodiment 6 | 15 | 20 | Surplus |
Embodiment 7 | 15 | 18 | Surplus |
The anti-microbial property of test blended yarn weaved fabric:
Table four: the bacteriostasis property (%) of blended yarn weaved fabric:
Staphylococcus aureus | Candida albicans | Escherichia coli | |
Embodiment 1 | 98 | 95 | 97 |
Embodiment 2 | 97 | 95 | 95 |
Embodiment 3 | 97 | 94 | 95 |
Embodiment 4 | 98 | 93 | 96 |
Embodiment 5 | 97 | 94 | 96 |
Embodiment 6 | 97 | 95 | 96 |
Embodiment 7 | 97 | 93 | 95 |
As shown in Table 4, blended yarn weaved fabric is to staphylococcus aureus, Candida albicans and colibacillary antibacterial
Effect is the best.
Embodiment 8
The preparation method of a kind of antibacterial shirt fabric, is carried out as steps described below:
A, antibacterial plant mixture and distilled water being added in flask, the quality of distilled water is plant mixture matter
20-30 times of amount;
B, it is heated to 40 DEG C, and distillation of reducing pressure, collect distillate;
C, gained distillate is filtered and concentrated to solid content is to obtain plant antimicrobial after 57%;
D, under the preparation condition of not higher than 20-35 DEG C, use gelatin and arabic gum to plant as softgel shell cladding
Thing antibacterial, forms microcapsule;
E, microcapsule, micron order calcined shell powder and natural plants stain are sufficiently mixed, then by meter
Amount rotating disk is quantitatively adding in the polyester slice of molten condition, and within the 3-5s time, by polyester slice in spinning
On machine, high speed spinning makes as-spun fibre, and concrete technology condition is: spinning temperature 310 DEG C, and spinning speed is
1300m/min;
F, as-spun fibre uses parallel drafting machine shape, i.e. can get finished product polyster fibre, drawing-off times
Number is 4 times;
G, polyster fibre and silk fiber and vinylon fibre are carried out blending, and through dyeing, Final finishing,
To blended yarn weaved fabric.
Each weight percentages of components of described blended yarn weaved fabric is as follows:
Silk fiber 10%
Vinylon fibre 17%
Polyster fibre surplus.
Antibacterial plant mixture in described step A, including the composition of following percentage by weight:
Herba Taraxaci 15%
Flos Chrysanthemi Indici 12%
Aloe 3%
Flagger surplus.
In described step E, the percentage by weight of microcapsule, micron order calcined shell powder and polyester slice is:
Microcapsule 3.5%
Micron order calcined shell powder 2%
Natural plants stain 3.5%
Polyester slice surplus.
Described natural plants stain is natural Fructus Mori extracting solution stain.
Polyster fibre dyes in preparation process in advance, adds the Color of fiber, soaping of polyster fibre
Color fastness reaches more than 4 grades, also reduces the consumption of stain in follow-up dyeing simultaneously, reduces cost.
The impact on blended yarn weaved fabric anti-microbial property of each composition is analyzed below with concrete comparative example:
Comparative example 1-7
Compared with Example 1, the content of each composition, other preparation condition in antibacterial plant mixture is only adjusted
Constant, the performance of test blended yarn weaved fabric:
Table five: in each specific embodiment, each weight percentages of components of antibacterial plant mixture please see table:
Herba Taraxaci | Flos Chrysanthemi Indici | Aloe | Flagger | |
Comparative example 1 | 0 | 10 | 12 | Surplus |
Comparative example 2 | 12 | 0 | 10 | Surplus |
Comparative example 3 | 10 | 12 | 0 | Surplus |
Comparative example 4 | 0 | 22 | 0 | Surplus |
Comparative example 5 | 22 | 0 | 0 | Surplus |
Comparative example 6 | 0 | 0 | 22 | Surplus |
Comparative example 7 | 0 | 0 | 0 | Surplus |
Table six: the bacteriostasis property (%) of blended yarn weaved fabric:
By comparative example 1-7 it is recognised that only add flagger or add in antibacterial plant mixture
Two or three is all unable to reach optimal antibacterial effect.
Comparative example 8, compared with Example 1, are added without micron order calcined shell powder, other preparation condition
Constant, the performance of test blended yarn weaved fabric:
Table seven: the bacteriostasis property (%) of blended yarn weaved fabric:
Staphylococcus aureus | Candida albicans | Escherichia coli | |
Embodiment 1 | 98 | 95 | 97 |
Comparative example 8 | 82 | 75 | 89 |
By comparative example 8 it is recognised that be added without the micron order calcined shell powder antibacterial effect to blended yarn weaved fabric
Fruit impact is bigger.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art is in the technical scope that the invention discloses, according to the technology of the present invention
Scheme and inventive concept equivalent or change in addition thereof, all should contain within protection scope of the present invention.
Claims (7)
1. an antibacterial shirt fabric, is formed by polyster fibre, silk fiber, vinylon fibre hybrid woven, it is characterised in that each weight percentages of components of described blended yarn weaved fabric is as follows:
Silk fiber 10-15%
Vinylon fibre 15-25%
Polyster fibre surplus.
2. the preparation method of an antibacterial shirt fabric, it is characterised in that carry out as steps described below:
A, antibacterial plant mixture and distilled water being added in flask, the quality of distilled water is 20-30 times of plant mixture quality;
B, it is heated to 35-40 DEG C, and distillation of reducing pressure, collect distillate;
C, gained distillate is filtered and concentrated to solid content is to obtain plant antimicrobial after 50-60%;
D, under the preparation condition of not higher than 40 DEG C, use gelatin and arabic gum to be coated with plant antimicrobial as softgel shell, form microcapsule;
E, microcapsule and micron order calcined shell powder are sufficiently mixed, then it is quantitatively adding in the polyester slice of molten condition by metering rotating disk, and within the 3-5s time, polyester slice high speed spinning on spinning-drawing machine is made as-spun fibre, concrete technology condition is: spinning temperature 300-320 DEG C, and spinning speed is 1300-1400m/min;
F, as-spun fibre using parallel drafting machine shape, i.e. can get finished product polyster fibre, drafting multiple is 3-4 times;
G, polyster fibre and silk fiber and vinylon fibre are carried out blending, and through dyeing, Final finishing, obtain blended yarn weaved fabric.
The preparation method of antibacterial shirt fabric the most as claimed in claim 2, it is characterised in that the antibacterial plant mixture in described step A, including the composition of following percentage by weight:
Herba Taraxaci 15-20%
Flos Chrysanthemi Indici 8-15%
Aloe 3-5%
Flagger surplus.
The preparation method of antibacterial shirt fabric the most as claimed in claim 2, it is characterised in that in described step E, the percentage by weight of microcapsule, micron order calcined shell powder and polyester slice is:
Microcapsule 3-5%
Micron order calcined shell powder 1-2%
Polyester slice surplus.
The preparation method of antibacterial shirt fabric the most as claimed in claim 2, it is characterised in that can add in described step E and add in polyester slice after natural plants stain mixes jointly with microcapsule and micron order calcined shell powder.
The preparation method of antibacterial shirt fabric the most as claimed in claim 2, it is characterised in that in described step G, dyes and finishing process unites two into one, and temperature is controlled between 70-80 DEG C, and the process time controls within 5min.
The preparation method of antibacterial shirt fabric the most as claimed in claim 5, it is characterised in that the 3-10% that weight is polyester slice weight of the natural plants stain of addition.