CN101173362A - 一种镁合金化学抛光处理工艺 - Google Patents

一种镁合金化学抛光处理工艺 Download PDF

Info

Publication number
CN101173362A
CN101173362A CNA2006101231812A CN200610123181A CN101173362A CN 101173362 A CN101173362 A CN 101173362A CN A2006101231812 A CNA2006101231812 A CN A2006101231812A CN 200610123181 A CN200610123181 A CN 200610123181A CN 101173362 A CN101173362 A CN 101173362A
Authority
CN
China
Prior art keywords
magnesium alloy
cleaning
chemical
chemical milling
chemical polishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006101231812A
Other languages
English (en)
Inventor
陈龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CNA2006101231812A priority Critical patent/CN101173362A/zh
Publication of CN101173362A publication Critical patent/CN101173362A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种镁合金化学抛光处理工艺，其步骤基本为：a.前处理，其用以将初始镁合金工件进行清洗、除油等表面清洁，可包括机械处理、碱洗、酸洗及清洗等步骤；b.化学抛光，进而将经上述处理后的镁合金工件浸渍于化学抛光溶液中；c.后处理，抛光完成后，则将该工件进行清洗、烘干等处理。其中，步骤b中所述化学抛光溶液其以水为溶剂，主要包括：硝酸40～100g/L、草酸0～50g/L、硫脲1～10g/L。因此，本发明通过采用一些普通酸和有机物的混合物配制成化学抛光液，其成分简单，便于管控，且所得到的化学抛光面光泽度好、表面平整，并且可以和其它化学处理环节混合使用，还可以作为镜面加工中的精细抛光液使用。

Description

一种镁合金化学抛光处理工艺
技术领域
本发明涉及一种金属表面处理工艺，特别是涉及一种镁合金表面处理工艺。
背景技术
镁合金具有重量轻、比强度高、弹性模量小、抗电磁干扰、屏蔽性好、减震能力强、加工性能好、导热性能好等优点，已经在国防、电子电器等方面得到广泛应用。但是在镁合金表面抛光工艺中，大多都采用铬酐、酚等进行处理，而且处理时间上较难掌握，药液消耗量也较大，实需开发一种不使用六价铬且稳定的镁合金化学抛光工艺。
发明内容
鉴于以上问题，本发明的主要目的在于提供一种镁合金化学抛光处理工艺，该工艺操作简单，所采用化学抛光液成分少，易于管控。
为达到上述目的，本发明提供的镁合金化学抛光处理工艺，其主要包括以下步骤：
a.前处理，其用以将初始镁合金工件进行清洗、除油等表面清洁，可包括机械处理、碱洗、酸洗及清洗等步骤；
b.化学抛光，进而将经上述处理后的镁合金工件浸渍于化学抛光溶液中，其中温度控制在20～50℃之间，浸渍时间为1～5分钟；
c.后处理，抛光完成后，则将该工件进行清洗、烘干等处理。
其中，步骤b中所述化学抛光溶液主要包括以下组分，其以水为溶剂：
硝酸              40～100g/L；
草酸              10～50g/L；
硫脲              1～10g/L。
而所述清洗则优选为用去离子水超声波清洗。
所述硝酸为工业常用硝酸，其浓度一般为66～68％(体积比)。
所谓化学抛光，其即为针对金属表面不平整而不光亮，利用酸或碱的作用，对凹凸点的腐蚀速度的不同而使凸点处腐蚀较快，凹点处腐蚀较慢，从而达到不同速度的腐蚀，使金属表面平整而出现了光亮效果。
因此，本发明通过采用一些普通酸和有机物的混合物配制成化学抛光液，其成分简单，便于管控，且所得到的化学抛光面光泽度好、表面平整，并且可以和其它化学处理环节混合使用，还可以作为镜面加工中的精细抛光液使用。
具体实施方式
实施例1
依下述组分配制化学抛光溶液：
硝酸         60g/L；
草酸         30g/L；
硫脲         5g/L。
取一AZ31B镁合金样品依此进行水洗、喷砂、碱洗、酸洗、超声波清洗，然后再将该样品浸渍于上述化学抛光溶液中，稳定控制为室温，浸渍时间为3分钟，到时间后取出样品先水洗再烘干，则得到抛光产品，该所得产品表面平整，出现了光亮效果且光泽度较好。
实施例2
依下述组分配制化学抛光溶液：
硝酸         50g/L；
草酸         45g/L；
硫脲         5g/L。
取一AZ31B镁合金样品依此进行水洗、喷砂、碱洗、酸洗、超声波清洗，然后再将该样品浸渍于上述化学抛光溶液中，稳定控制为室温，浸渍时间为5分钟，到时间后取出样品先水洗再烘干，则得到抛光产品，该所得产品表面平整，出现了光亮效果且光泽度较好。
实施例3
依下述组分配制化学抛光溶液：
硝酸         70g/L；
草酸         30g/L；
硫脲         10g/L。
取一AZ31B镁合金样品依此进行水洗、喷砂、碱洗、酸洗、超声波清洗，然后再将该样品浸渍于上述化学抛光溶液中，稳定控制为室温，浸渍时间为2分钟，到时间后取出样品先水洗再烘干，则得到抛光产品，该所得产品表面平整，出现了光亮效果且光泽度较好。
以上具体实施方式，是对本发明所作的详细说明。注意这些实施方式并非用以限定本发明，对于本领域的熟练技术人员，在不背离本发明精神的情况下所做出的改进和补充，应该视为在本发明的保护范围之内。

Claims (7)

1.一种镁合金化学抛光溶液，其特征在于，以水为溶剂，其每升溶液中包括：
硝酸                   40～100g/L；
草酸                   10～50g/L；
硫脲                   1～10g/L。
2.根据权利要求1所述的镁合金化学抛光溶液，其特征在于，所述硝酸为工业常用硝酸，其浓度一般为66～68％(体积比)。
3.一种镁合金化学抛光工艺，其特征在于，主要包括以下步骤：
a.前处理，其用以将初始镁合金工件进行清洗、除油等表面清洁；
b.化学抛光，进而将经上述处理后的镁合金工件浸渍于如权利要求1或2所述的化学抛光溶液中；
c.后处理，抛光完成后，则将该工件进行清洗、烘干等处理。
4.根据权利要求3所述镁合金化学抛光工艺，其特征在于，所述前处理可包括机械处理、碱洗、酸洗及清洗等步骤。
5.根据权利要求3所述镁合金化学抛光工艺，其特征在于，所述化学抛光其温度控制在20～50℃之间。
6.根据权利要求3所述镁合金化学抛光工艺，其特征在于，所述化学抛光其浸渍时间为1～5分钟。
7.根据权利要求3所述镁合金化学抛光工艺，其特征在于，所述清洗优选为用去离子水超声波清洗。
CNA2006101231812A 2006-10-31 2006-10-31 一种镁合金化学抛光处理工艺 Pending CN101173362A (zh)