CN101109226A - Multi-layer wood composite flooring and manufacturing method therefor - Google Patents
Multi-layer wood composite flooring and manufacturing method therefor Download PDFInfo
- Publication number
- CN101109226A CN101109226A CNA2007100284431A CN200710028443A CN101109226A CN 101109226 A CN101109226 A CN 101109226A CN A2007100284431 A CNA2007100284431 A CN A2007100284431A CN 200710028443 A CN200710028443 A CN 200710028443A CN 101109226 A CN101109226 A CN 101109226A
- Authority
- CN
- China
- Prior art keywords
- layer
- wood composite
- solid wood
- composite floor
- veneer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multi-layer solid wooden compound floor board, which comprises from up to down an anti-wear layer, a decoration layer and a baseboard layer that are mutually glued. The baseboard layer comprises a plurality of mutually-glued single boards. The invention additionally discloses the method for making the floor board. The method comprises: selecting a plurality layers of single boards, coating glue on them, pressing the single boards to form the baseboard layer; coating glue between the baseboard layer and the decoration layer; pressing the decoration layer and the baseboard layer; sticking the anti-wear layer on the decoration layer; finally pressing the anti-wear layer, decoration layer and the baseboard layer to form a multi-layer solid wooden compound floor board. The multi-layer solid wooden compound floor board made by above method is furnished with appearance of a solid wood floorboard, is of steady structure, not liable to deformation, is of high surface strength, is wear and scraping proof, resistant to impact, burning and contamination, and is environmental friendly; the floorboard can be applicable for different environments, is economic, practical and durable.
Description
Technical field
The present invention relates to a kind of floor and manufacture method thereof, relate in particular to a kind of multi-layer solid wood composite floor and manufacture method thereof.
Background technology
The floor roughly is divided into wooden floor, multi-layer solid wood composite floor and strengthening composite floor on the market.
Wherein wooden floor has natural sex and wooden property, but raw material are in short supply, costs an arm and a leg and yielding.
Existing multi-layer solid wood composite floor, structure is crisscross, good stability, suction is made moist not yielding, and still, the multi-layer solid wood composite floor surface strength is poor, not wear-resisting, easily scratch, influence attractive in appearance, and for gaining in strength and stable, surface course often need be used thicker high-quality timber, because it is thicker to be in the high-quality timber on top layer,, cause timber to be wasted because of the saw crack so when cutting timber, can only obtain with the mode of saw blade cutting.
Strengthening composite floor generally adds decorative layer by substrate layer and adds surface wear-resistant layer and form, the surface strength height, wear-resisting, scratch resistance, anti-calcination, but substrate layer generally is to mix compacting with wood chip or wooden chaff by glue to form, its water proofing property is poor, and moisture-sensitive expands, torsional deformation, only be applicable to the arid region, certain limitation is arranged.
For overcoming the deficiency in the present technology, be necessary to provide a kind of and can adapt to various environment, surface strength height, the not floor of moisture-sensitive distortion.
Summary of the invention
The object of the present invention is to provide a kind of surface strength height, not the multi-layer solid wood composite floor of moisture-sensitive distortion.
A kind of multi-layer solid wood composite floor is characterized in that: comprise from top to bottom gluing wearing layer, decorative layer and substrate layer mutually, described substrate layer comprises gluing multilayer veneer mutually.
Described wearing layer is the alundum (Al abrasion-proof paper, and described decorative layer is wooden skin, by the slicing gained.
The grain direction of described multilayer veneer adjacent two layers is crisscross.
Another object of the present invention is to provide a kind of manufacture method of multi-layer solid wood composite floor.
A kind of method of making multi-layer solid wood composite floor comprises the steps:
1. select the multilayer veneer and to each veneer gluing;
2. at 15-20Mpa pressure, under 110 ℃-160 ℃ the temperature condition, suppress described multilayer veneer, synthetic substrate layer;
3. gluing between described substrate layer and described decorative layer;
4. at 15-20Mpa pressure, under 85 ℃-130 ℃ the temperature condition, suppress described decorative layer and substrate layer;
5. wearing layer is affixed on the decorative layer;
6. at 15-20Mpa pressure, under 120 ℃-170 ℃ the temperature condition, suppress described wearing layer, decorative layer and substrate layer, the synthesizing multilayer solid wood composite floor board.
By the multi-layer solid wood composite floor that said method is made, have following advantage:
1. Stability Analysis of Structures is not yielding.
2. the surface strength height is wear-resisting, and scratch resistance is shock-resistant, anti-calcination, anti-pollution, environmental protection.
3. has the wooden floor appearance effect.
4. can adapt to various environment, use wide.
5. the decorative layer on this floor adopts the mode of slicing to obtain, and the mode of avoiding adopting sawing causes waste to precious high-quality timber because of the saw crack in the process of cutting, can effectively save timber, makes floor economy, and material benefit is durable.
Description of drawings
Below in conjunction with accompanying drawing the specific embodiment of the present invention is described in further detail, wherein:
Fig. 1 is STRUCTURE DECOMPOSITION figure of the present invention;
Fig. 2 is a structural representation of the present invention.
The specific embodiment
With reference to Fig. 1, Fig. 2, a kind of multi-layer solid wood composite floor, comprise mutual gluing wearing layer 1, decorative layer 2 and substrate layer 3 from top to bottom, described wearing layer 1 is the alundum (Al abrasion-proof paper, decorative layer 2 is for selecting the wooden skin of high-quality timber by the slicing gained for use, precious high-quality timber can be effectively saved in the waste of avoiding adopting the mode of sawing to cause because of the saw crack in cutting the timber process; The use of this wearing layer 1 has in addition improved floor surface intensity, makes the floor wear-resisting, and scratch resistance is shock-resistant, anti-calcination, and anti-pollution, environmental protection makes floor economy, and material benefit is durable.Substrate layer 3 comprises that gluing thickness is the multilayer veneer 4 of 1mm-1.5mm mutually, and the grain direction of adjacent two layers is crisscross in the multilayer veneer 4, has improved the stability of flooring structure, prevents floor deformation, can adapt to various environment; Wherein said multilayer veneer 4 adjacent two layers can be selected unlike material veneers such as hard wood veneer and common wood veneer for use.
Fig. 1, a kind of multi-layer solid wood composite floor shown in Figure 2, can adopt following processing step to make: 1. select the multilayer veneer and to each veneer gluing, for example can select for use the thick hard wood veneer of 1-1.5mm to coat special Tai Er glue layer 2-3, and the thick common wood veneer of 1-1.5mm is coated the environmental protection urea-formaldehyde glue; 2. at 15-20Mpa pressure, under 110 ℃-160 ℃ the temperature condition, suppress described multilayer veneer, synthetic substrate layer, wherein at 17Mpa pressure, 130 ℃-140 ℃ temperature and 3-9 minute time conditions of compacting are down for good;
3. between described substrate layer and described decorative layer, coat the environmental protection urea-formaldehyde glue;
4. at 15-20Mpa pressure, under 85 ℃-130 ℃ the temperature condition, suppressing described decorative layer and substrate layer, with at 17Mpa pressure, is good under 105 ℃-110 ℃ temperature and 1-3 minute the time conditions of compacting wherein;
5. wearing layer is affixed on the decorative layer;
6. at 15-20Mpa pressure, under 120 ℃-170 ℃ the temperature condition, suppress described wearing layer, decorative layer and substrate layer, the synthesizing multilayer solid wood composite floor board, wherein at 17Mpa pressure, 140 ℃-150 ℃ temperature and suppressing under 30 seconds to 2 minutes the time conditions under the condition to good.
The preferred embodiment of above-mentioned steps 2 is at 17Mpa pressure, 130 ℃ temperature and suppress 6 minutes time conditions down or at 17Mpa pressure, 135 ℃ temperature and suppressing under 6 minutes the time conditions, and at 17Mpa pressure, 140 ℃ temperature and the time conditions of suppressing 6 minutes are suppressed described multilayer veneer down, synthetic substrate layer.
The preferred embodiment of above-mentioned steps 4 is at 17Mpa pressure, 105 ℃ temperature and suppress 2 minutes time conditions down or at 17Mpa pressure, 108 ℃ temperature and suppressing under 2 minutes the time conditions, and at 17Mpa pressure, 110 ℃ temperature and the time conditions of suppressing 2 minutes are suppressed described decorative layer and substrate layer down.
The preferred embodiment of above-mentioned steps 5 is at 17Mpa pressure, 140 ℃ temperature and suppress 1 minute time conditions down or at 17Mpa pressure, 145 ℃ temperature and suppressing under 1 minute the time conditions, and at 17Mpa pressure, 150 ℃ temperature and the time conditions of suppressing 1 minute are suppressed described wearing layer, decorative layer and substrate layer, synthesizing multilayer solid wood composite floor board down.
Get final product packing behind synthetic floor process health, the tongue and groove at last.
The multi-layer solid wood composite floor of being made by said method has the wooden floor appearance effect, and Stability Analysis of Structures is not yielding; Its surface strength height, wear-resisting, scratch resistance, shock-resistant, anti-calcination, anti-pollution, environmental protection; Can adapt to various environment, use wide; Have economy, material benefit, durability.
Claims (10)
1. multi-layer solid wood composite floor is characterized in that: comprise from top to bottom gluing wearing layer, decorative layer and substrate layer mutually, described substrate layer comprises gluing multilayer veneer mutually.
2. multi-layer solid wood composite floor according to claim 1 is characterized in that: described wearing layer is the alundum (Al abrasion-proof paper, and described decorative layer is wooden skin.
3. multi-layer solid wood composite floor according to claim 1 is characterized in that: the grain direction of described multilayer veneer adjacent two layers is crisscross.
4. multi-layer solid wood composite floor according to claim 1 is characterized in that: the thickness of described veneer is 0.5mm-2mm.
5. multi-layer solid wood composite floor according to claim 1 is characterized in that: described multilayer veneer adjacent two layers can be unlike material.
6. a method of making the described multi-layer solid wood composite floor of claim 1 is characterized in that it comprises the steps:
1). select the multilayer veneer and to each veneer gluing;
2). at 15-20Mpa pressure, under 110 ℃-160 ℃ the temperature condition, suppress described multilayer veneer, synthetic substrate layer;
3). gluing between described substrate layer and described decorative layer;
4). at 15-20Mpa pressure, under 85 ℃-130 ℃ the temperature condition, suppress described decorative layer and substrate layer;
5). wearing layer is affixed on the decorative layer;
6). at 15-20Mpa pressure, under 120 ℃-170 ℃ the temperature condition, suppress described wearing layer, decorative layer and substrate layer, the synthesizing multilayer solid wood composite floor board.
7. the method for making multi-layer solid wood composite floor as claimed in claim 6, it is characterized in that: in described selection multilayer veneer and the step each veneer gluing, select for use the thick hard wood veneer of 1-1.5mm to coat special Tai Er glue layer 2-3, and the thick common wood veneer of 1-1.5mm is coated the environmental protection urea-formaldehyde glue.
8. the method for making multi-layer solid wood composite floor as claimed in claim 6, it is characterized in that: the step of described synthetic substrate layer further is included in 17Mpa pressure, under 130 ℃-140 ℃ temperature and 3-9 minute the time conditions of compacting, suppress described multilayer veneer, synthetic substrate layer.
9. the method for making multi-layer solid wood composite floor as claimed in claim 6, it is characterized in that: the step of described compacting decorative layer and substrate layer further is included in 17Mpa pressure, under 105 ℃-110 ℃ temperature and 1-3 minute the time conditions of compacting, suppress described decorative layer and substrate layer.
10. the method for making multi-layer solid wood composite floor as claimed in claim 6, it is characterized in that: the step of described synthesizing multilayer solid wood composite floor board further is included in 17Mpa pressure, 140 ℃-150 ℃ temperature and suppressing under 30 seconds to 2 minutes the time conditions, suppress described wearing layer, decorative layer and substrate layer, the synthesizing multilayer solid wood composite floor board.