CN101113634A - Large grade composite floor and method for making same - Google Patents
Large grade composite floor and method for making same Download PDFInfo
- Publication number
- CN101113634A CN101113634A CNA2007100560056A CN200710056005A CN101113634A CN 101113634 A CN101113634 A CN 101113634A CN A2007100560056 A CNA2007100560056 A CN A2007100560056A CN 200710056005 A CN200710056005 A CN 200710056005A CN 101113634 A CN101113634 A CN 101113634A
- Authority
- CN
- China
- Prior art keywords
- veneer
- composite floor
- base plate
- paddle
- dash board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A large size composite floor relates to the technology field of floor processing, comprising the following preparation process of surface plate choosing and processing, paddle choosing and processing, bottom plate choosing and processing, hot pressing, balance and health preserving, etc. By the choosing of base materials, the invention can produce overlong, overwide and large size composite floor, thereby greatly improving the stability and integrity of the floors, effectively solves the warping problem of large size composite floor; besides, the floor gives people the natural and generous feeling and harmonious and elegant visual enjoyment, thus being especially suitable for large palaces.
Description
Technical field:
The present invention relates to the floor processing technique field, the present invention relates to a kind of composite floor board specifically, the invention still further relates to the preparation method of this composite floor board.
Background technology:
The essential structure of common composite floor board is: dash board, paddle, base plate are glued together.Manufacturing process is: behind selected base material gluing, use common hot-press equipment to press together, through after the sanding, be processed into normal specifications semiproduct plate with common mortise equipment, carry out deep processing according to different requirements again.
1. common composite floor board base material is chosen:
1.. dash board: length 400-2300MM; Width: 80-270MM; Thickness 3.0-4.0MM
2.. paddle and base plate:, mostly be the rotary cut venner of monolithic or multi-disc overlap joint according to selected specification of dash board and the selection of equipment processing limit.
2. common composite floor board equipment is chosen:
1.. hot-press equipment: general processing length 1000-2500MM;
2.. mortise equipment: general processing length: 400-2500MM.
3. common composite floor board specification is set:
1.. length: 400-2200MM
2.. width: 90-260MM
3.. thickness: 10-15MM
4.. the compound number of plies: 3-7 layer.
No matter be to produce base material, the equipment that needs, still the floor of being processed into all exists very big traditional, generality and randomness, the floor of adopting the big specification of said method production, and warpage issues is serious.Simultaneously, because common composite floor board specification is limit, make its less stable, the third dimension of overall appearance and visual effect are all outstanding inadequately.
Summary of the invention:
The technical problem to be solved in the present invention is the composite floor board that discloses a kind of big specification.
The present invention also discloses the preparation method of the composite floor board of big specification.
Composite floor board of the present invention is made of dash board, paddle and base plate, and dash board is former plank, paddle is a veneer, is formed by 6 layers of thick veneer compacting of 2.0MM, and base plate is a sliced veneer, two forward overlapping placements, paddle is between dash board and base plate, and is bonding by floor glue between each laminate.
The preparation method of above-mentioned composite floor board is for may further comprise the steps:
1, dash board is chosen processing: choose plate side, sawing becomes dash board, and balance is gone into drying kiln, and temperature is controlled at 90-70 ℃, and after dry processing in 12 days, moisture content reaches 7.0-9.0%, and saw is cut into the dash board woolen cloth again.
2, paddle is chosen processing: choosing moisture content is the 7-8.5% veneer, and wherein veneer is that 6 layers of thick veneer compacting of 2.0MM form, and chooses after sanding is fixed thick.
3, base plate is chosen processing: choose two of sliced veneers, forward overlapping placement, base plate moisture content 1-5%.
4, with the overlapping placement behind the gluing one by one of dash board, paddle and base plate, adopt hot-press method to carry out hot pressing, make flooring blank, pressure is 12-14MPA, and the time is 12-14 minute, and temperature is the 95-100 degree.
5, balance health-preserving: with the health 48 hours under airtight condition of the flooring blank after the hot pressing.
6 sandings, mortise: identical with general composite floor board processing technology, guarantee during sanding that sheet is at 200MM ± 0.2MM, the dash board THICKNESS CONTROL is more than 5.5MM simultaneously, base plate Baidu is controlled at 1.6-2.0MM, described mortise, guarantee that in the difference of height 0.3MM between the plate, laterally squareness is controlled in the 0.1MM.
7, surfacing: refer to that dash board is scratched trace, hand is drawn together or cigarette is coated with true qualities oil after smoking or has the oil of color, promptly cooperate the composite floor board of plate face modelled after an antique to handle, perhaps directly oil as required or coat with lacquer.
Wherein the dash board dry run adopts following conditional effect even more ideal in the step 1:
The temperature humidity time
Initial stage is handled 90 ℃ of 28-30.5% 8-12H
Dry 70 ℃ of 22-23.5% 22-24H
72℃ 19-21.5% 22-24H
74℃ 16-18.5% 22-24H
78℃ 13-15.5% 24-26H
Handle 90 ℃ of 28-30.5% 12-14H mid-term
Dry 78 ℃ of 11-13.5% 22-24H
82℃ 8-10.5% 22-24H
86℃ 6.5-8.5% 22-24H
End and handle 90 ℃ of 15-18.5% 24-26H
Cooling detects moisture content, airtight health 3 days.
In order to save big specification paddle, can adopt two veneer butt joints to make in the step 2.
In order to save big specification base plate, the 2-5 that forward tiles on whole veneer opens width and the thickness short veneer identical with whole veneer and replaces whole veneer in the step 3, and the length sum of short veneer is identical with whole veneer, lacks veneer between veneer and whole veneer.
The production on conventional composite floor, improve stability and associative perception method often abutment surface be coated with that jewelry solves, and to not doing particular processing in the aspects such as specification of base material, the present invention chooses by base material, the boundary line of floor specification medelling breaks traditions, produce the novel floor of overlength, super wide whole large format, greatly strengthened floor stability and associative perception, solved warpage issues effectively at the specification composite floor board.
Composite floor board of the present invention can be rated as " giant " in the composite floor board series products, whole generous naturally, of tremendous momentum, be particularly suitable for large-scale palace class finishing, the property of its overlength, super wide, ultra firmly, the breath performance ground that the emperor is defiant incisively and vividly, " whole the tree " particularly selected for use is as base material, the dash board base material must be the timber that the age of tree is felled at the virgin forest more than 300 years, form through special processes, the plate face nature of producing, coherent and long, give the visual enjoyment of people's harmony, elegance.Its unitary construction has reached artistry and has manifested the perfect unity of noble makings.
Description of drawings:
Accompanying drawing is the sectional view on floor of the present invention.
The specific embodiment:
Composite floor board of the present invention is made of dash board 1, paddle 2 and base plate 3, at first chooses 4000X360MM plate side, and sawing becomes the thick dash board of 4000X360X7.0MM, balance is gone into drying kiln, after dry processing in 12 days, moisture content reaches 8.0%, and saw is cut into 3700X320X6.9MM dash board 1 woolen cloth; Choose the 3700X325X10MM veneer as paddle 2, moisture content 8%, wherein veneer is that 6 layers of thick veneer compacting of 2.0MM form, and chooses after sanding is fixed thick; Choose two of 3720X330X2.2MM sliced veneers, forward overlapping placement, base plate moisture content 3% is as base plate 3.With the overlapping placement behind the gluing one by one of dash board 1, paddle 2 and base plate 3, adopt hot-press method to carry out hot pressing, make flooring blank, pressure is 13MPA, and the time is 13 minutes, and temperature is 98 degree.With the health 48 hours under airtight condition of the flooring blank after the hot pressing.Sanding is identical with general composite floor board processing technology with mortise, guarantee during sanding that sheet is at 200MM ± 0.2MM, the dash board THICKNESS CONTROL is more than 5.5MM simultaneously, base plate Baidu is controlled at 1.6-2.0MM, described mortise, guarantee that in the difference of height 0.3MM between the plate, laterally squareness is controlled in the 0.1MM.The composite floor board manufacturing process is finished in surfacing.Wherein dash board 1 dry run is:
The temperature humidity time
Initial stage handle 90 ℃ 30.% 10 hours
Dry 70 ℃ 23.% 24 hours
72 ℃ 20% 23 hours
74 ℃ 17% 23 hours
78 ℃ 14% 25 hours
Handle mid-term 90 ℃ 9% 13 hours
Dry 78 ℃ 12% 24 hours
82 ℃ 9% 24 hours
86 ℃ 7.5% 24 hours
End to handle 90 ℃ 17% 26 hours
Cooling detects moisture content, airtight health 72 hours.
Claims (5)
1. the composite floor board of a big specification, it is characterized in that: it is made of dash board, paddle and base plate, dash board is former plank, paddle is a veneer, formed by 6 layers of thick veneer compacting of 2.0MM, base plate is a sliced veneer, two forward overlapping placements, paddle is between dash board and base plate, and is bonding by floor glue between each laminate.
2. the composite floor board preparation method of big specification according to claim 1 is characterized in that adopting following steps to finish:
(1), dash board is chosen processing: choose plate side, sawing becomes dash board, and balance is gone into drying kiln, and temperature is controlled at 90-70 ℃, and after dry processing in 12 days, moisture content reaches 7.0-9.0%, and saw is cut into the dash board woolen cloth again;
(2), paddle is chosen processing: choosing moisture content is the 7-8.5% veneer, and wherein veneer is that 6 layers of thick veneer compacting of 2.0MM form, and chooses after sanding is fixed thick;
(3), base plate is chosen processing: choose two of sliced veneers, forward overlapping placement, base plate moisture content 1-5%;
(4), with the overlapping placement behind the gluing one by one of dash board, paddle and base plate, adopt hot-press method to carry out hot pressing, make flooring blank, pressure is 12-14MPA, the time is 12-14 minute, temperature is the 95-100 degree;
(5), balance health-preserving: with the health 48 hours under airtight condition of the flooring blank after the hot pressing;
(6), sanding, mortise: identical with general composite floor board processing technology, guarantee during sanding that sheet is at 200MM ± 0.2MM, the dash board THICKNESS CONTROL is more than 5.5MM simultaneously, base plate Baidu is controlled at 1.6-2.0MM, described mortise, guarantee that in the difference of height 0.3MM between the plate, laterally squareness is controlled in the 0.1MM;
(7), surfacing.
3. composite floor board preparation method according to claim 2 is characterized in that: dash board dry run condition is in the step 1:
The temperature humidity time
Initial stage is handled 90 ℃ of 28-30.5% 8-12H
Dry 70 ℃ of 22-23.5% 22-24H
72℃ 19-21.5% 22-24H
74℃ 16-18.5% 22-24H
78℃ 13-15.5% 24-26H
Handle 90 ℃ of 28-30.5% 12-14H mid-term
Dry 78 ℃ of 11-13.5% 22-24H
82℃ 8-10.5% 22-24H
86℃ 6.5-8.5% 22-24H
End and handle 90 ℃ of 15-18.5% 24-26H
Cooling detects moisture content, airtight health 3 days.
4. composite floor board preparation method according to claim 2 is characterized in that: the paddle of step 2 adopts two veneer butt joints to make.
5. composite floor board preparation method according to claim 2, it is characterized in that: the base plate described in the step 3, be that the 2-5 that forward tiles on whole veneer opens width and the thickness short veneer identical with whole veneer and replaces whole veneer, the length sum of short veneer is identical with whole veneer, lacks veneer between veneer and whole veneer.