CN106217506A - A kind of board and preparation method thereof - Google Patents
A kind of board and preparation method thereof Download PDFInfo
- Publication number
- CN106217506A CN106217506A CN201610628260.2A CN201610628260A CN106217506A CN 106217506 A CN106217506 A CN 106217506A CN 201610628260 A CN201610628260 A CN 201610628260A CN 106217506 A CN106217506 A CN 106217506A
- Authority
- CN
- China
- Prior art keywords
- veneer
- board
- central layer
- dash
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of board, including two pieces of dash boards and one piece of central layer, between two pieces of dash boards, be provided with one piece of central layer；The grain direction of described dash board is that longitudinally the grain direction of described central layer is horizontal；Every piece of described dash board includes that more than two-layer the first veneer is obtained by identical grain direction stacking glued hot pressing, and described first veneer uses rotary cutting process to prepare；Described central layer includes that more than two-layer the second veneer is obtained by identical grain direction stacking glued hot pressing, and described second veneer uses rotary cutting process to prepare.The invention also discloses the preparation method of board.Using the present invention, keep good fracture resistance after can be used for depiction, and engraving, the most easy to crack, insect protected is mothproof, environmental and durable, can be used for making floor, furniture-plates and decorative panel.
Description
Technical field
The present invention relates to wooden building materials, particularly relate to a kind of board, correspondingly, further relate to the system of a kind of board
Preparation Method.
Background technology
Along with the raising day by day of level of consumption, market is for such as woods such as solid wood door plate, solid wood furniture, solid wood decorative product
A great variety of models for product, stability and service life all propose higher requirement.The multi-layer sheet that tradition is commonly used has thin wood
Work plate and plywood, core-board is made up of glue laminated Wood block floor in the middle of two panels veneer, and plywood is by three layers or multilamellar one
Veneer or the thin plate sticker hot pressing of millimeters thick form, and are to make the material that furniture is the most commonly used at present by hand.But joiner
Plate is because its face ply is thin and the problem of plate construction causes the resistance to deformation of sheet material, cracking resistance after plate surface depiction
Performance reduce；Plywood is then arranged alternately with wood grain transverse and longitudinal due to its veneer, and engraving machinery need to be carved along wood grain, and wood grain is horizontal
Vertical structure alternately is unfavorable for engraving.Therefore, core-board and plywood all cannot be used for rag pattern.
Nowadays the monoblock plank that timber is log sawing of rag it is generally used for, yet with the limitation of log
Property, the size of its plank is restricted, it is impossible to make significantly product.Some ornamental composite wood boards occur on market plane,
First the veneer to surface carries out rag process, then carries out pasting thickening, to strengthen the thickness of sheet material, but, this type of is ornamental
Plank can only be produced by the size being pre-designed, and the pattern on plank can not be changed, and motility is poor, and fracture resistance is deteriorated,
Easy to crack, it is not durable.
Therefore, needing the shortcoming providing a kind of novel sheet material to overcome existing sheet material badly, filling up on market about can be used for carving
The blank of the plank carved.
Summary of the invention
The technical problem to be solved is, it is provided that a kind of board, after can be used for depiction, and engraving
Keeping good fracture resistance, the most easy to crack, insect protected is mothproof, environmental and durable.
In order to solve above-mentioned technical problem, the invention provides a kind of board, including two pieces of dash boards and one piece of central layer,
One piece of central layer it is provided with between two pieces of dash boards；The grain direction of described dash board is that longitudinally the grain direction of described central layer is horizontal；
Every piece of described dash board includes that more than two-layer the first veneer is prepared by identical grain direction stacking hot-press gluing, described the
One veneer uses rotary cutting process to prepare；
Described central layer includes that more than two-layer the second veneer is prepared by identical grain direction stacking hot-press gluing, and described second is single
Plate uses rotary cutting process to prepare.
As the improvement of such scheme, the thickness of described first veneer and the second veneer is 1-4mm.
As the improvement of such scheme, described central layer is made up of lignum cinnamomi camphorae.
As the improvement of such scheme, the thicker function with depiction of the dash board of sheet material.
As the improvement of such scheme, the thickness of described central layer is less than the summation thickness of two pieces of dash boards.
As the improvement of such scheme, described dash board and central layer use glued heat pressing process bonding.
As the improvement of such scheme, described first veneer and the second veneer first carry out the pretreatment dried before bonding,
The moisture content of described first veneer and the second veneer is less than 10%.
Correspondingly, invention additionally discloses the preparation method of a kind of board, comprise the following steps:
(1) log is carried out rotary-cut and processes prepared first veneer and the second veneer；
(2) the first veneer and the second veneer carry out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；
(3) if being bonded by dried layer the first veneer in the same direction by the technique of glued hot pressing, dash board is prepared；
(4) if being bonded by dried layer the second veneer in the same direction by the technique of glued hot pressing, central layer is prepared；
(5) dash board is stacked according to vertical-horizontal-vertical wood grain order with central layer；
(6) use the technique of glued hot forming that dash board is bonded with central layer, prepare described board.
Additionally, invention additionally discloses the preparation method of a kind of board, comprise the following steps:
(1) log is carried out rotary-cut and processes prepared first veneer and the second veneer；
(2) the first veneer and the second veneer carry out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；
(3) if by the technique of glued hot pressing successively by the first veneer that dried layer is longitudinal, if horizontal the second veneer of dried layer and
If the first veneer of dried layer longitudinal direction stacks bonding in order, prepare described board.
Implement the embodiment of the present invention, have the advantages that
Board of the present invention is provided with three layers and includes that two pieces of dash boards and one piece of central layer are vertical-horizontal-vertical side with grain direction
Formula stacking, and dash board is glued by the first veneer stacking in the same direction of polylith wood grain, and central layer is by polylith wood grain the second veneer in the same direction
Stacking is glued.Owing in dash board, the grain direction of the first veneer is all that longitudinally identical with log board is the wood grain side of dash board
To being also in the same direction, its processability is suitable with the processability of log, sheet material of the present invention in the performance of engraving effect also with former
Wooden is suitable.Three ply board direction according to wood grain when stacking bonds according to vertical-horizontal stroke-longitudinal order, can strengthen composite board
Rupture strength, the present invention makes sheet material can show relatively at vertical and horizontal by above-mentioned crisscross overlapped way
Good rupture strength, the most easy to crack.And through detecting board of the present invention Form aldehyde release Limited Doses before and after engraving
Low, bending strength meets national standard, Environmental Safety.
Additionally, central layer of the present invention can also use lignum cinnamomi camphorae to make so that described board have insect protected mothproof,
The advantage driving mould damp proof insulation.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, make to retouch the most in detail to the present invention below
State.
After there is depiction for the composite board being currently used for engraving, the resistance to deformation of sheet material, the performance of cracking resistance reduce
And the problem such as the plank size of log sawing is little, the present invention provides a kind of board to overcome the problems referred to above.
The present invention provides a kind of board, including two pieces of dash boards and one piece of central layer, is provided with one piece of core between two pieces of dash boards
Plate；The grain direction of described dash board is that longitudinally the grain direction of described central layer is horizontal；
Every piece of described dash board includes that more than two-layer the first veneer is obtained by identical grain direction stacking glued hot pressing, described the
One veneer uses rotary cutting process to prepare；
Described central layer includes that more than two-layer the second veneer is obtained by identical grain direction stacking glued hot pressing, and described second is single
Plate uses rotary cutting process to prepare.
Existing core-board and plywood are conventional selections.Wherein core-board is to be spelled by glue laminated in the middle of two panels veneer
Grafting plate is made, and the two panels veneer thickness being located at surface is generally 1-2mm, once after rag, when the rag degree of depth is more than
During veneer thickness, the wood fiber of veneer is completely severed, and resistance to tension weakens significantly.Core-board flexural capacity after rag is bright
Aobvious decline, easily ftractures, poor product quality.
And plywood is the veneer thick by three layers or multilamellar 1-3mm or thin plate stacking glue in the way of wood grain transverse and longitudinal replaces
Patch hot pressing forms, but engraving machinery need to be carved along wood grain, and wood grain transverse and longitudinal structure alternately is unfavorable for engraving.Even if it is glued
After plate rag, sheet material is unlikely to deform, but owing to sheet material top layer is relatively thin, its processability is not so good as core-board, and particularly engraving milling is made
The effect of type is undesirable.
Additionally, splice again after the compound sheet material many employings sawing of tradition three ply board, need repeatedly slicing, repair and straight wait processing
Sliceable, volume recovery is relatively low.
Therefore, the present invention changes the design of existing composite board, and existing monoblock sheet material has the wood grain transverse and longitudinal of multilamellar hand over
For the mode of stacking, change three layers into and include two pieces of dash boards and one piece of central layer stacking in the way of grain direction is vertical-horizontal-vertical, and
Dash board is glued by the first veneer stacking in the same direction of polylith wood grain, and central layer is glued by the second veneer stacking in the same direction of polylith wood grain.
Owing in dash board, the grain direction of the first veneer is all longitudinally, identical with log board is the grain direction of dash board is also with
Suitable with the processability of log to, its processability, sheet material of the present invention also suitable with log in the performance of engraving effect.
Due to timber there is anisotropy, timber is along crackle (i.e. slash grain) the more vertical trunk of intensity in trunk direction
Transversal crack (i.e. laterally wood grain) intensity is much greater, three ply board when stacking direction according to wood grain according to vertical-horizontal stroke-longitudinal feed row
Bonding, can strengthen the horizontal rupture strength of composite board, and the present invention makes plate by above-mentioned crisscross overlapped way
Material all can show preferable rupture strength at vertical and horizontal.
Preferably, the thickness of described first veneer and the second veneer is 1-4mm.
Wherein, dash board can be by the first veneer laminate adhesive of 2,3,4 or 5 pieces, and its thickness can be 4mm, 4.5mm,
5mm, 5.5mm, 6mm, 7mm or 8mm, wait and be not limited to the example above.
Central layer can be by the first veneer laminate adhesive of 2,3,4 or 5 pieces, and its thickness can be 2mm, 2.5mm, 2.8mm,
3mm, 3.5mm, 4mm or 5mm, wait and be not limited to the example above.
Preferably, core thickness is less than the summation thickness of two pieces of dash boards.
It is prepared from, relative to conventional sawing additionally, dash board of the present invention and core are all the modes using rotary-cut
The dash board becoming isometric uniform thickness carries out being spliced into significantly dash board again, and the present invention not only technique is simpler, and volume recovery is higher, raw
Produce cost lower.According to calculating that this technique is 1.6 times of volume recovery of traditional handicraft and cost is the 50% of traditional handicraft.
It should be noted that log wide material sources of the present invention, as Lignum seu Ramulus Cunninghamiae Lanceolatae, Masson Pine, poplar, Cortex Fraxini mandshuricae, birch,
Basswoods etc., above timber all can be used for manufacturing dash board of the present invention and central layer.
Preferably, core of the present invention uses lignum cinnamomi camphorae to make, and lignum cinnamomi camphorae is traditional famous and precious timber, it is possible to give out
Special strong fragrance, does not wanes year in year out, and this fragrance makes lignum cinnamomi camphorae furniture have unique utilitarian function: insect protected is prevented
Eat into, drive mould damp proof insulation.Insect protected is mothproof, drive the excellent of mould damp proof insulation to be applied to make monoblock sheet material also have on core of the present invention
Point, is the first-selection preparing high-end product.
Described first veneer and the second veneer first carry out the pretreatment dried, described first veneer and the second list before bonding
The moisture content of plate is less than 10%.Wherein, the moisture content of the first veneer and the second veneer preferably differs less than 1%, to guarantee plate
Material there is preferable stability.
Correspondingly, the present invention also provides for the preparation method of a kind of board, comprises the following steps:
(1) log is carried out rotary-cut and processes prepared first veneer and the second veneer；
(2) the first veneer and the second veneer carry out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；
(3) if being bonded by dried layer the first veneer in the same direction by the technique of glued hot pressing, dash board is prepared；
(4) if being bonded by dried layer the second veneer in the same direction by the technique of glued hot pressing, central layer is prepared；
(5) dash board is stacked according to vertical-horizontal-vertical wood grain order with central layer；
(6) use the technique of glued hot forming that dash board is bonded with central layer, prepare described board.
The method first prepares dash board and central layer, stacks glued hot-forming according still further to vertical-horizontal-vertical wood grain order.
Additionally, invention additionally discloses the preparation method of a kind of board, comprise the following steps:
(1) log is carried out rotary-cut and processes prepared first veneer and the second veneer；
(2) the first veneer and the second veneer carry out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；
(3) if by the technique of glued hot pressing successively by the first veneer that dried layer is longitudinal, if horizontal the second veneer of dried layer and
If the first veneer of dried layer longitudinal direction stacks bonding in order, prepare described board.
The most previously prepared dash board of the method and central layer, but the most glued hot pressing one-shot forming.
Below using board of the present invention, core-board and plywood as experimental subject, before and after contrasting its rag
The situation of change of each performance.
Embodiment 1
Cortex Fraxini mandshuricae is carried out rotary-cut and processes the first veneer and the second veneer of 1mm thickness preparing 1mm thickness；To the first veneer and second
Veneer carries out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；Same by 5 layers by the technique of glued hot pressing
To first veneer bonding, prepare dash board；By the technique of glued hot pressing, 5 layers of second veneer in the same direction are bonded, prepare central layer；
Dash board is stacked according to vertical-horizontal-vertical wood grain order with central layer；The technique using glued hot forming makes dash board glue with central layer
Closing, prepared thickness is the described board A of 15mm.
Carving out required pattern with automatic carving machine on described board A, carving depth, up to 5mm, makes described
Producing on board A in concave-convex grain carbonization, easy sanding, and plate face has surface fiber to occur, finally reaches required
Till pattern.
After deep complete concave-convex grain, accurate sander is used to select 100-180 sand paper by the surface carbon on backing material plate face
Chemical fibre dimension carries out sanding process, speed 10-15m/min, and required pattern is clearly showed in sanding back plate face, prepares the rag degree of depth
Rag sheet material A1 for 5mm.
Embodiment 2
Masson Pine is carried out rotary-cut and processes the first veneer preparing 1mm thickness, Cortex cinnamomi camphorae is carried out rotary-cut process and prepares 1mm thick second
Veneer, carries out drying and processing and makes the moisture content of the first veneer and the second veneer less than 10% the first veneer and the second veneer；Pass through
The technique of glued hot pressing is by the first veneer of 4 layers of longitudinal direction, and 4 layers of second horizontal veneer, the first veneer of 4 layers of longitudinal direction stacks gradually
Bonding；The technique using glued hot forming makes dash board bond with central layer, and prepared thickness is the described board B of 12mm.
On described board B, required pattern, pattern and embodiment 1 is gone out deeply with the speed of 5-8m/s with rolling ironing machine
Identical, deep thickness is up to 2mm, and time deep, bowl temperature controls at 320 DEG C；Make to produce concave-convex on described board B
Surface fiber is had to occur in stricture of vagina carbonization, easy sanding, and plate face, till finally reaching required pattern.
After deep complete concave-convex grain, accurate sander is used to select 100-180 sand paper by the surface carbon on backing material plate face
Chemical fibre dimension carries out sanding process, speed 10-15m/min, and required pattern is clearly showed in sanding back plate face, prepares the rag degree of depth
Rag sheet material B1 for 2mm.
Reference example 1
Cortex Fraxini mandshuricae log carries out rotary-cut processing prepared two panels thickness is the veneer of 1mm, utilizes sawing machine that log is made flitch,
Conventional preparation techniques is used to prepare the core-board C that thickness is 15mm.
Going out required pattern on core-board C deeply with automatic carving machine, pattern is identical with embodiment 1, and engraving is deep
Degree is up to 5mm, and time deep, bowl temperature controls at 320 DEG C；Make to produce on core-board C concave-convex grain carbonization, easy sanding,
And there is surface fiber to occur on plate face, till finally reaching required pattern.
After deep complete concave-convex grain, accurate sander is used to select 100-180 sand paper by the surface carbon on backing material plate face
Chemical fibre dimension carries out sanding process, speed 10-15m/min, and required pattern is clearly showed in sanding back plate face, prepares the rag degree of depth
Rag sheet material C1 for 5mm.
Reference example 2
Using conventional preparation techniques to prepare the plywood D that thickness is 15mm, plywood totally 6 layers, every layer thickness is 2.5mm.
On plywood D, required pattern is gone out deeply with the speed of 5-8m/s, the phase of pattern and embodiment 1 with rolling ironing machine
With, deep thickness is up to 2mm, and time deep, bowl temperature controls at 320 DEG C；Make to produce on plywood D concave-convex grain carbonization, appearance
Easily surface fiber is had to occur, till finally reaching required pattern in sanding, and plate face.
After deep complete concave-convex grain, accurate sander is used to select 100-180 sand paper by the surface carbon on backing material plate face
Chemical fibre dimension carries out sanding process, speed 10-15m/min, and required pattern is clearly showed in sanding back plate face, prepares the rag degree of depth
Rag sheet material D1 for 5mm.
Test mode:
1, " Form aldehyde release limitation in GB/T18580-2001 indoor decorating and refurnishing materials wood-based plate and goods thereof " test is used
A, A1, B and B1 in above-described embodiment, and the Form aldehyde release Limited Doses of C, C1, D and the D1 in reference example.
2, " GB/T 17657-2013 test methods of evaluating the properties of wood-based panels and surface decorated wood-based panels " is used to test above-mentioned reality
Execute A, A1, B and the B1 in example, and the bending strength of C, C1, D and the D1 in reference example.
Table 1 embodiment and reference example physicochemical property contrast table
As seen from Table 1, before and after sheet material B and the B1 engraving of sheet material A and A1 of the embodiment of the present invention 1 and embodiment 2, formaldehyde is released
Put Limited Doses to increase, but impact is little, though the bending strength carving figuratum sheet material A1 and B1 is in a slight decrease, but
Still conform to the requirement of national standard.And sheet material C and C1 of reference example 1 and sheet material D and D1 of reference example 2, the thin wood after engraving
The Form aldehyde release Limited Doses of work plate C1 and plywood D1 increases, and bending strength is decreased obviously, and does not even meet state
Family's standard, its flexural capacity is not enough.
Last institute is it should be noted that, the present invention is only protected by above example in order to technical scheme to be described
Protecting the restriction of scope, although being explained in detail the present invention with reference to preferred embodiment, those of ordinary skill in the art should
Understand, technical scheme can be modified or equivalent, without deviating from the essence of technical solution of the present invention
And scope.
Claims (9)
1. a board, it is characterised in that include two pieces of dash boards and one piece of central layer, be provided with one piece of core between two pieces of dash boards
Plate；The grain direction of described dash board is that longitudinally the grain direction of described central layer is horizontal；
Every piece of described dash board includes that more than two-layer the first veneer is obtained by identical grain direction stacking glued hot pressing, described the
One veneer uses rotary cutting process to prepare；
Described central layer includes that more than two-layer the second veneer is obtained by identical grain direction stacking glued hot pressing, and described second is single
Plate uses rotary cutting process to prepare.
2. board as claimed in claim 1, it is characterised in that the thickness of described first veneer and the second veneer is 1-4mm.
3. board as claimed in claim 1, it is characterised in that described central layer is made up of lignum cinnamomi camphorae.
4. as claimed in claim 1 board, it is characterised in that the dash board of sheet material is thicker, and have can the function of depiction.
5. board as claimed in claim 1, it is characterised in that the thickness of described central layer is thick less than the summation of two pieces of dash boards
Degree.
6. board as claimed in claim 1, it is characterised in that described dash board and central layer use glued heat pressing process bonding.
7. board as claimed in claim 1, it is characterised in that described first veneer and the second veneer are first carried out before bonding
The pretreatment dried, the moisture content of described first veneer and the second veneer is less than 10%.
8. a preparation of plates method as claimed in claim 1, it is characterised in that comprise the following steps:
(1) log is carried out rotary-cut and processes prepared first veneer and the second veneer；
(2) the first veneer and the second veneer carry out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；
(3) if being bonded by dried layer the first veneer in the same direction by the technique of glued hot pressing, dash board is prepared；
(4) if being bonded by dried layer the second veneer in the same direction by the technique of glued hot pressing, central layer is prepared；
(5) dash board is stacked according to vertical-horizontal-vertical wood grain order with central layer；
(6) use the technique of glued hot forming that dash board is bonded with central layer, prepare described board.
9. a preparation of plates method as claimed in claim 1, it is characterised in that comprise the following steps:
(1) log is carried out rotary-cut and processes prepared first veneer and the second veneer；
(2) the first veneer and the second veneer carry out drying and processing makes the moisture content of the first veneer and the second veneer less than 10%；
(3) if by the technique of glued hot pressing successively by the first veneer that dried layer is longitudinal, if horizontal the second veneer of dried layer and
If the first veneer of dried layer longitudinal direction stacks bonding in order, prepare described board.