CN1140646A - Multi-layer overlaid decoration board - Google Patents
Multi-layer overlaid decoration board Download PDFInfo
- Publication number
- CN1140646A CN1140646A CN 95108206 CN95108206A CN1140646A CN 1140646 A CN1140646 A CN 1140646A CN 95108206 CN95108206 CN 95108206 CN 95108206 A CN95108206 A CN 95108206A CN 1140646 A CN1140646 A CN 1140646A
- Authority
- CN
- China
- Prior art keywords
- veneer
- layer
- decoration board
- thick china
- machine direction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The said multi-layer board consists of several layers of turned base plate and overlaid layer of planed plate adhered with waterproof glue. The several layers have properly arranged fibre orientation and the prodn process adopts optimal temp, pressure and other technological parameters. The said board may be used in indoor decoration of building, vehicle and ship.
Description
A kind of multi-layer overlaid decoration board comprises its product configurations and production technology, and this decorative panel is applicable to building and car, the ship inside fitting building decorative plates as purposes such as furred ceiling, wallboard, floors.
In modern building, particularly buildings such as hotel, office building, commercial building mostly are reinforced concrete frame structure greatly, and are inner with high-strength, lightweight body of wall partition, cover with dalle.In existing ornament materials, wood decoration plate material belongs to the flawless finish material, except that to its intensity and some function is for example prevented fires, waterproof etc. has the specific (special) requirements, also its top layer decorative effect is had higher requirements.Though wood decoration plate material has many kinds, it is perfect that the structure of its product and production technology are more attained, and keeps on improving.
The product configurations and the production technology that the purpose of this invention is to provide a kind of multi-layer overlaid decoration board make its structure more reasonable, and intensity increases, and better decorative effect is arranged.Technology advanced person ensures the quality of products.
Used technical scheme, the product configurations of multi-layer overlaid decoration board of the present invention is bondd successively by several layers base material veneer and top layer thick china and to form.Basic unit is the several layers rotary cut venner, and the top layer thick china is a sliced veneer, the arrangement that intermeshes of the machine direction of each layer of base material veneer, with eliminate timber vertically with laterally, breathing between sapwood and the core and strength difference reduce distortion, gain in strength.The top layer thick china is parallel with the machine direction of base material first floor veneer, keeping product two sides machine direction unanimity, and make the top layer lines clear, increase decorative effect.Between each veneer and between veneer and the thick china all with the marine glue pressing that bonds, make it to meet water indeformable, do not come unglued; The wood grain pinhole is filled and led up in first Puttying on its top layer thick china, in case, scribble two-layer above resin again with incrustation in the line of back, and to obtain the decorative effect of light; With its mass-impregnation fire prevention, waterproof, anticorrisive agent material, can obtain functions such as fire-resistant, water-fast, corrosion resistant.
The multi-layer overlaid decoration board of present technique can the side's of making plate or stripe board, and when making long narrow stripe board, the machine direction of the machine direction of its top layer thick china (sliced veneer) and base material first floor rotary cut venner in the same way and parallel with the length direction of stripe board.
The production technology of multi-layer overlaid decoration board of the present invention, its technological process and main technologic parameters are:
Log cut-out boiling (water temperature 50-80 ℃) → be peeled into veneer (the thick 1-2mm of veneer) → oven dry (moisture content is controlled at 6-10%) → veneer shearing shaping → piece (veneer pieces together big plate up to specification) → gluing (on veneer, to be coated with melamine glue, glue consumption 250-300g/m
2(each veneer texture is vertical mutually in) → hot pressing, hot pressing temperature 100-130 ℃, pressure 1-1.8MPa, 1 minute time/mm) → (thick china is the veneer that slicing is in strip to fixed thick sanding → veneer, the first plate texture of its texture and base material in the same way and parallel with the length direction of stripe board) → saw limit (size 915 * 915 or 915 * 1830 or 1220 * 2440, the mm of unit) → polish (playing putty, polishing) → mortice opening (to open horizontal tongue-and-groove earlier, be cut into bar shaped, open vertical tongue-and-groove again) → (priming paint, finish paint) sprays paint.
Multi-layer overlaid decoration board of the present invention, compare with the like product of prior art, its structure is more reasonable, can save timber to greatest extent, very strong water-fast, weather-resistant property are arranged, have higher intensity and the smooth decorative effect of light, and specification assembling rationally is simple, is suitable as the senior building ornament materials of the purposes such as furred ceiling, wallboard, floor of the indoor and compartment of building, steamer.Its production technology advanced person is feasible, can produce with conventional equipment, can guarantee product quality, improves timber utilization rate.
Now be described further in conjunction with the accompanying drawings.
Fig. 1 is the profile schematic diagram of multi-layer overlaid decoration board of the present invention.
Fig. 2 is the 2-2 partial cross-section of Fig. 1, shows its structure.
Multi-layer overlaid decoration board is made standard-sized sheet material, uses for the buildings decoration engineering, and its frame is that tenon groove structure is seen Fig. 1.Its upper surface 1 and bottom surface 2 are different structure and different brightness, to reduce manufacturing cost.Its interior laminate layer structure sees Fig. 2 for details, and the base material 3 of multiple layer decorative compound sheet of the present invention is several layers rotary cut venner 4, reaches first floor rotary cut venner 5, for example has 15 layers.The top layer is a slicing thick china 6, each layer veneer 4 and 4 and the arrangement that intermeshes of the machine direction of first floor veneer 5, and best for adjacent two layers becomes 90 ° of arranged verticals, its top layer thick china 6 is sliced veneers, and is parallel with the machine direction of first floor rotary cut venner 5.Between each layer veneer 4,4 and between the veneer 4,5,5, make it to become one with Waterproof glue line 7 bonding pressings between 6, scribble on the upper surface of top layer thick china 6 two-layer more than (for example three layers) putty and resin 8, (can be coloured or colourless) have formed bright smooth upper surface 1.Its bottom surface 2 be base material veneer 4 except that mass-impregnation, can not remake specially treated.
Decorative panel integral body of the present invention can flood that fire prevention, waterproof, anti-corrosion material are fire-resistant to obtain, waterproof, performance such as anticorrosion.
Decorative panel of the present invention, the best use is shaped as strip.
The production technology of multi-layer overlaid decoration board of the present invention, its main technique flow process and technological parameter see the following form:
| Sequence number | The operation title | The operation content | Capital equipment | Technological parameter |
| 1 | Boiling | Log cuts off boiling | The boiling pond | Water temperature 50-80 |
| 2 | Rotary-cut | Well-done rounding is become veneer | Rotary veneer machine | The thick 1-2mm of veneer |
| 3 | Oven dry | Rotary cut venner is dried | Jet-propelled mesh dryer | Moisture content 6-10% |
| 4 | Shear | Veneer is sheared and is shaped | Veneer clipper | |
| 5 | Piece | Veneer is pieced together big plate up to specification | No paper tape sewing machine | |
| 6 | Gluing | On veneer, be coated with melamine glue | Glue spreader | Glue consumption 250-300g/m 2 |
| 7 | Hot pressing | On chopping board, carry out assembly by the mutual vertical pile of the grain of wood, be placed on the bonding of exerting pressure on the hot press then. | Hot press | 1. hot pressing temperature 100-130 ℃ of 2. 3. time 1 minute/mm of pressure 1～1.8MPa |
| 8 | Fixed thick sanding | Fixed thick sanding makes thick line unanimity, bright and clean. | Contact calibrating machine | Thickness deviation ± 0.1 |
| 9 | Veneer | The thick china hot pressing that slicing is in strip is fitted on the first plate of base material, leaves the processing seam in the middle of every sliced veneer. | Four rollers glue spreader veneer hot press (technology and hot pressing are together) | 1. the parallel 2. thick china of the first plate lines of thick china and base material width specifications have 60,75,90mm |
| 10 | The saw limit | To cut into semi-finished product through the decorative panel after the hot pressing veneer is shaped. | Sawing machine | Size 915 * 915 or 915 * 1830, or 1220 * 2440, the mm of unit |
| 11 | Polishing | The Puttying polishing | ||
| 12 | Mortice opening | Open horizontal tongue-and-groove earlier, be split into strip with multiple blade saw along centre processing seaming and cutting then and open vertical both sides tongue-and-groove again. | The horizontal vertical edge milling machines of edge milling machines multiple blade saw | |
| 13 | Japanning | The primer spray finish paint | Spray gun, curtain coater coating roller all can |
Claims (5)
1. multi-layer overlaid decoration board, its structure is bondd successively by several layers base material veneer and top layer thick china and forms, and it is characterized in that:
A. base material is the several layers rotary cut venner, the arrangement that intermeshes of the machine direction of each layer veneer;
B. the top layer thick china is a sliced veneer, and its machine direction is parallel with first floor rotary cut venner machine direction;
C. between each veneer and between veneer and the thick china with the marine glue pressing that bonds.
2. multi-layer overlaid decoration board according to claim 1, it is characterized in that: described decorative panel is a strip, its top layer thick china is the veneer that slicing is in strip, and the machine direction of its machine direction and base material first floor rotary cut venner in the same way, and is and parallel with the length direction of stripe board.
3. multi-layer overlaid decoration board according to claim 1 is characterized in that: scribble resin more than two-layer again scraping twice putty on the thick china of top layer earlier.
4. multi-layer overlaid decoration board according to claim 1 is characterized in that: the fire prevention of described decorative panel mass-impregnation, waterproof, anticorrisive agent.
5. the production technology of a multi-layer overlaid decoration board, it is characterized in that: main technique flow process and technological parameter are:
Log cut-out boiling (water temperature 50-80 ℃) → be peeled into veneer (the thick 1-2mm of veneer) → oven dry (moisture content is controlled at 6-10%) → veneer shearing shaping → piece (veneer pieces together big plate up to specification) → gluing (on veneer, to be coated with melamine glue, glue consumption 250-300g/m
2(each veneer texture is vertical mutually in) → hot pressing, hot pressing temperature 100-130 ℃, pressure 1-1.8MPa, 1 minute time/mm) → (thick china is the veneer that slicing is in strip to fixed thick sanding → veneer, its texture and base material first floor veneer texture in the same way and parallel with the length direction of stripe board) → saw limit (size 915 * 915 or 915 * 1830 or 1220 * 2440, the mm of unit) → polish (playing putty, polishing) → mortice opening (to open horizontal tongue-and-groove earlier, be cut into bar shaped, open vertical tongue-and-groove again) → (priming paint, finish paint) sprays paint