CN108312690A - The preparation method of multi-functional furniture composite plate - Google Patents
The preparation method of multi-functional furniture composite plate Download PDFInfo
- Publication number
- CN108312690A CN108312690A CN201810205095.9A CN201810205095A CN108312690A CN 108312690 A CN108312690 A CN 108312690A CN 201810205095 A CN201810205095 A CN 201810205095A CN 108312690 A CN108312690 A CN 108312690A
- Authority
- CN
- China
- Prior art keywords
- fire
- proof plate
- substrate
- plate
- upper substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of multi-functional furniture composite plate, include the following steps：Step 1：Substrate is cut into upper substrate and lower substrate in composite plate by cutting machine；Fireproof wood is cut into the fire-proof plate in composite plate by cutting machine again；Step 2：Upper substrate, lower substrate and fire-proof plate are first subjected to wet grinding with Plane surface grinding machine；Then upper substrate, lower substrate and fire-proof plate three are dried respectively with dryer；Step 3：Distinguish even spread gluing oxidant layer on the two sides of fire-proof plate, upper substrate and lower substrate are fitted in the two sides of fire-proof plate respectively；Step 4：By the hot pressing at high temperature of upper substrate, fire-proof plate and lower substrate；Step 5：In coated on one side waterproof layer of the upper substrate with respect to fire-proof plate；In coated on one side antibiotic layer of the lower substrate with respect to fire-proof plate；Step 6：The plank that step 5 is obtained carries out surface UV.The present invention can solve the problems, such as that existing wood plank is non-moistureproof, not prevent fires, antibiotic property is poor, and preparation method is simple, production easy to spread.
Description
Technical field
The invention belongs to technical field of furniture, more particularly to a kind of preparation method of multi-functional furniture composite plate.
Background technology
With the improvement of living standards, people are also higher and higher to the environmental requirement of indoor inhabitation, including furniture
Workmanship.Make furniture and ornamental plate and substantially use the plate based on timber, as solid slab, clamping plate, fiberboard,
Decoration panel, fire-proof plate and particieboard etc., 105058519 A of Chinese patent CN are disclosed a kind of " furniture composite plate ", including
Bottom plate, glued board and panel, bottom plate and panel are solid wood sheet, but wood plank is non-watertight, are easy water swelling, easily mildew
Bacterium, the long green hair of humidity cause swollen plank, contracting, warpage, phenomena such as cracking, shorter so as to cause the service life of product；In addition wood plank
Anti-microbial property it is poor, the bacterial reproduction of timber plate surface cannot be inhibited, reduce the living environment quality of user.
Therefore, those skilled in the art actively research and develop a kind of composite plate of making furniture newly to solve the above problems.
Invention content
The invention mainly solves the technical problem of providing a kind of preparation methods of multi-functional furniture composite plate, can solve
Existing wood plank is non-moistureproof, does not prevent fires, the problem of antibiotic property difference, and preparation method is simple, production easy to spread.
In order to solve the above technical problems, one aspect of the present invention is：A kind of multi-functional furniture composite plate
Preparation method, including waterproof layer, upper substrate, fire-proof plate, lower substrate and antibiotic layer, the upper substrate, fire-proof plate and lower substrate
It is fixedly connected by adhesive, the waterproof layer is located at one side of the upper substrate relative to fire-proof plate, and the antibiotic layer is located at
One side of the lower substrate relative to fire-proof plate；
The preparation method of the composite plate includes the following steps：
Step 1：Plate cutting
Substrate is cut into the substrate of two pieces of 4-7mm thickness by laser cutting machine, as the upper substrate in composite plate under
Substrate；Fireproof wood is cut into the substrate of 2-4mm thickness by laser cutting machine again, as the fire-proof plate in composite plate；
Step 2：Plank is polished, is dried
The surface of upper substrate, lower substrate and fire-proof plate is first subjected to wet grinding with Plane surface grinding machine, ODS sensors is used in combination to distinguish
Detect the flatness of upper substrate, lower substrate and fire-proof plate three；Then with dryer respectively to upper substrate, lower substrate and fire-proof plate
Three is dried, and detects the moisture content of upper substrate, lower substrate and fire-proof plate three respectively；
Step 3：Plank is glued
Distinguish even spread gluing oxidant layer on the two sides of fire-proof plate, upper substrate and lower substrate are then fitted in into fire prevention respectively
The coating weight on the two sides of plate, the gluing oxidant layer is 100-160g/m2；
Step 4：Hot pressing
By upper substrate, fire-proof plate and lower substrate at a high temperature of 100-150 DEG C hot pressing 10-20s, make upper substrate, fire-proof plate
It is 7-12mm with the overall thickness after lower substrate hot pressing；
Step 5：It is coated with waterproof layer and antibiotic layer
In coated on one side waterproof layer of the upper substrate with respect to fire-proof plate, the waterproof layer is to contain acrylic resin, melamine
The coating weight of the glue-line of amine and sodium metasilicate, the waterproof layer is 30-60g/m2；It is anti-with respect to the coated on one side of fire-proof plate in lower substrate
Bacterium layer, the antibiotic layer are the glue-line containing Nano metal powder and adhesive resin, and the coating weight of the antibiotic layer is 40-70g/
m2；
Step 6：Surface treatment
The plank that step 5 is obtained carries out surface UV, is placed in thermostatic chamber after being cooled to room temperature.
It further says, the substrate in the step 1 is PPC substrates or PVC substrates.
It further says, the moisture content in the step 2 is in 5-7%.
It further says, the fire-proof plate is flame-retarded gypsum plank, ca silicate fibre plate or chlorine oxygen magnesium fire-proof plate.
It further says, the adhesive is phenolic resin glue, urea-formaldehyde resin adhesive, hot melt adhesive or lignin stick.
It further says, the urea-formaldehyde resin adhesive includes vinyl alcohol and ammonium chloride.
It further says, the adding proportion of acrylic resin, melamine and sodium metasilicate in the waterproof layer is (by weight
Number meter) it is 1：3：1.
It further says, the adding proportion of Nano metal powder and the adhesive resin in the antibiotic layer is (by weight
Number meter) it is 3：1.
Beneficial effects of the present invention at least have the following：
1, the present invention is made of waterproof layer, upper substrate layer, fire-proof plate layer, lower substrate layer and antibiotic layer, reasonable in design,
The making material of any plate fitment is can be used as, and its manufacturing method is simple, production easy to spread；
2, the overall thickness after upper substrate layer of the present invention, fire-proof plate layer and lower substrate layer hot pressing be 7-12mm, and upper substrate,
Fire-proof plate and lower substrate first pass through Plane surface grinding machine flattened surface using drying machine drying before hot pressing, and it is 5-7% to make its moisture content,
Compactness between layers is preferable, effectively improves the hardness of composite plate, sturdy and durable；And the moisture content of each plate is relatively low,
Reduce the probability of plank craze and transfiguration；
3, waterproof layer is the glue-line containing acrylic resin, melamine and sodium metasilicate, can avoid moisture in external environment
Erosion to composite plate of the present invention further decreases the probability of composite plate craze and transfiguration, improves the service life of composite plate；
4, antibiotic layer is the glue-line containing Nano metal powder and adhesive resin, and Nano metal powder is selected from nano-silver powder,
Have the function of antibacterial sterilization, to make the surface of composite plate of the present invention have the function of antibiosis and self-cleaning, and then composite plate is made to reach
The purpose self-cleaning to long-term hygienic, safety, improves the living environment quality of user；
5, the sandwich layer of composite plate is fire-proof plate layer, which is selected from flame-retarded gypsum plank, ca silicate fibre plate or chlorine oxygen
Magnesium fire-proof plate adds the fire-proof function of composite plate, improves the safety that furniture uses.
Description of the drawings
Fig. 1 is the structural schematic diagram of the present invention；
Each section label is as follows in attached drawing：
Waterproof layer 1, upper substrate 2, fire-proof plate 3, lower substrate 4 and antibiotic layer 5.
Specific implementation mode
The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that advantages and features of the invention energy
It is easier to be readily appreciated by one skilled in the art, so as to make a clearer definition of the protection scope of the present invention.
Embodiment：A kind of preparation method of multi-functional furniture composite plate, as shown in Figure 1, including waterproof layer 1, upper substrate
2, fire-proof plate 3, lower substrate 4 and antibiotic layer 5, the upper substrate, fire-proof plate and lower substrate are fixedly connected by adhesive, described anti-
Water layer is located at one side of the upper substrate relative to fire-proof plate, and the antibiotic layer is located at one of the lower substrate relative to fire-proof plate
Face；
The preparation method of the composite plate includes the following steps：
Step 1：Plate cutting
Substrate is cut into the substrate of two pieces of 4-7mm thickness by laser cutting machine, as the upper substrate in composite plate under
Substrate；Fireproof wood is cut into the substrate of 2-4mm thickness by laser cutting machine again, as the fire-proof plate in composite plate；
Step 2：Plank is polished, is dried
The surface of upper substrate, lower substrate and fire-proof plate is first subjected to wet grinding with Plane surface grinding machine, ODS sensors is used in combination to distinguish
Detect the flatness of upper substrate, lower substrate and fire-proof plate three；Then with dryer respectively to upper substrate, lower substrate and fire-proof plate
Three is dried, and detects the moisture content of upper substrate, lower substrate and fire-proof plate three respectively；
Step 3：Plank is glued
Distinguish even spread gluing oxidant layer on the two sides of fire-proof plate, upper substrate and lower substrate are then fitted in into fire prevention respectively
The coating weight on the two sides of plate, the gluing oxidant layer is 100-160g/m2；
Step 4：Hot pressing
By upper substrate, fire-proof plate and lower substrate at a high temperature of 100-150 DEG C hot pressing 10-20s, make upper substrate, fire-proof plate
It is 7-12mm with the overall thickness after lower substrate hot pressing；
Step 5：It is coated with waterproof layer and antibiotic layer
In coated on one side waterproof layer of the upper substrate with respect to fire-proof plate, the waterproof layer is to contain acrylic resin, melamine
The coating weight of the glue-line of amine and sodium metasilicate, the waterproof layer is 30-60g/m2；It is anti-with respect to the coated on one side of fire-proof plate in lower substrate
Bacterium layer, the antibiotic layer are the glue-line containing Nano metal powder and adhesive resin, and the coating weight of the antibiotic layer is 40-70g/
m2；
Step 6：Surface treatment
The plank that step 5 is obtained carries out surface UV, is placed in thermostatic chamber after being cooled to room temperature.
Substrate in the step 1 is PPC substrates or PVC substrates.
Moisture content in the step 2 is in 5-7%.
The fire-proof plate is flame-retarded gypsum plank, ca silicate fibre plate or chlorine oxygen magnesium fire-proof plate.
The adhesive is phenolic resin glue, urea-formaldehyde resin adhesive, hot melt adhesive or lignin stick.
The urea-formaldehyde resin adhesive includes vinyl alcohol and ammonium chloride.
The adding proportion (counting in parts by weight) of acrylic resin, melamine and sodium metasilicate in the waterproof layer is 1：
3：1.
The adding proportion (counting in parts by weight) of Nano metal powder and the adhesive resin in the antibiotic layer is 3：
1。
Working principle of the present invention is as follows：The present invention is by waterproof layer, upper substrate layer, fire-proof plate layer, lower substrate layer and antibacterial
Layer composition, it is reasonable in design, the making material of any plate fitment is can be used as, and its manufacturing method is simple, it is easy to spread
Production；
Overall thickness after upper substrate layer, fire-proof plate layer and lower substrate layer hot pressing is 7-12mm, and upper substrate, fire-proof plate and
Lower substrate first passes through Plane surface grinding machine flattened surface using drying machine drying before hot pressing, its moisture content is made to be 5-7%, layer and layer it
Between compactness it is preferable, effectively improve the hardness of composite plate, it is sturdy and durable；And the moisture content of each plate is relatively low, reduces plank
The probability of craze and transfiguration；
Waterproof layer is the glue-line containing acrylic resin, melamine and sodium metasilicate, can avoid moisture pair in external environment
The erosion of composite plate of the present invention further decreases the probability of composite plate craze and transfiguration, improves the service life of composite plate；
Antibiotic layer is the glue-line containing Nano metal powder and adhesive resin, and Nano metal powder is selected from nano-silver powder, tool
There is antibacterial sterilization, to make the surface of composite plate of the present invention have the function of antibiosis and self-cleaning, and then composite plate is made to reach
The self-cleaning purpose of long-term hygienic, safety, improves the living environment quality of user；
The sandwich layer of composite plate is fire-proof plate layer, which is selected from flame-retarded gypsum plank, ca silicate fibre plate or chlorine oxygen magnesium
Fire-proof plate adds the fire-proof function of composite plate, improves the safety that furniture uses.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure transformation made by bright specification and accompanying drawing content is applied directly or indirectly in other relevant technical fields,
Similarly it is included within the scope of the present invention.
Claims (8)
1. a kind of preparation method of multi-functional furniture composite plate, it is characterised in that：Including waterproof layer, upper substrate, fire-proof plate, under
Substrate and antibiotic layer, the upper substrate, fire-proof plate and lower substrate are fixedly connected by adhesive, and the waterproof layer is located on described
One side of the substrate relative to fire-proof plate, the antibiotic layer are located at one side of the lower substrate relative to fire-proof plate；
The preparation method of the composite plate includes the following steps：
Step 1：Plate cutting
Substrate is cut into the substrate of two pieces of 4-7mm thickness by laser cutting machine, as the upper substrate and lower substrate in composite plate；
Fireproof wood is cut into the substrate of 2-4mm thickness by laser cutting machine again, as the fire-proof plate in composite plate；
Step 2：Plank is polished, is dried
The surface of upper substrate, lower substrate and fire-proof plate is first subjected to wet grinding with Plane surface grinding machine, ODS sensors is used in combination to detect respectively
The flatness of upper substrate, lower substrate and fire-proof plate three；Then with dryer respectively to upper substrate, lower substrate and fire-proof plate three
It is dried, and detects the moisture content of upper substrate, lower substrate and fire-proof plate three respectively；
Step 3：Plank is glued
Distinguish even spread gluing oxidant layer on the two sides of fire-proof plate, upper substrate and lower substrate are then fitted in into fire-proof plate respectively
The coating weight on two sides, the gluing oxidant layer is 100-160g/m2；
Step 4：Hot pressing
By upper substrate, fire-proof plate and lower substrate at a high temperature of 100-150 DEG C hot pressing 10-20s, make upper substrate, fire-proof plate and under
Overall thickness after substrate hot pressing is 7-12mm；
Step 5：It is coated with waterproof layer and antibiotic layer
Upper substrate with respect to fire-proof plate coated on one side waterproof layer, the waterproof layer be containing acrylic resin, melamine and
The coating weight of the glue-line of sodium metasilicate, the waterproof layer is 30-60g/m2；In coated on one side antibacterial of the lower substrate with respect to fire-proof plate
Layer, the antibiotic layer are the glue-line containing Nano metal powder and adhesive resin, and the coating weight of the antibiotic layer is 40-70g/
m2；
Step 6：Surface treatment
The plank that step 5 is obtained carries out surface UV, is placed in thermostatic chamber after being cooled to room temperature.
2. the preparation method of multi-functional furniture composite plate according to claim 1, it is characterised in that：In the step 1
Substrate be PPC substrates or PVC substrates.
3. the preparation method of multi-functional furniture composite plate according to claim 1, it is characterised in that：In the step 2
Moisture content in 5-7%.
4. the preparation method of multi-functional furniture composite plate according to claim 1, it is characterised in that：The fire-proof plate is
Flame-retarded gypsum plank, ca silicate fibre plate or chlorine oxygen magnesium fire-proof plate.
5. the preparation method of multi-functional furniture composite plate according to claim 1, it is characterised in that：The adhesive is
Phenolic resin glue, urea-formaldehyde resin adhesive, hot melt adhesive or lignin stick.
6. the preparation method of multi-functional furniture composite plate according to claim 5, it is characterised in that：The Lauxite
Glue includes vinyl alcohol and ammonium chloride.
7. the preparation method of multi-functional furniture composite plate according to claim 1, it is characterised in that：In the waterproof layer
Acrylic resin, melamine and sodium metasilicate adding proportion (counting in parts by weight) be 1：3：1.
8. the preparation method of multi-functional furniture composite plate according to claim 1, it is characterised in that：In the antibiotic layer
Nano metal powder and the adding proportion (in parts by weight count) of the adhesive resin be 3：1.