CN101058901A - 纳米珍珠聚丙烯超细旦纤维及其制备方法 - Google Patents

纳米珍珠聚丙烯超细旦纤维及其制备方法 Download PDF

Info

Publication number
CN101058901A
CN101058901A CN 200710091025 CN200710091025A CN101058901A CN 101058901 A CN101058901 A CN 101058901A CN 200710091025 CN200710091025 CN 200710091025 CN 200710091025 A CN200710091025 A CN 200710091025A CN 101058901 A CN101058901 A CN 101058901A
Authority
CN
China
Prior art keywords
pearl
nano
superfine denier
polypropylene
polypropylene superfine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200710091025
Other languages
English (en)
Other versions
CN101058901B (zh
Inventor
马永梅
范家起
江雷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing Tongdao Hecheng Technology Development Co., Ltd.
Original Assignee
Xietong Rongchuang Sci & Tech Development Co Ltd Beijing
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xietong Rongchuang Sci & Tech Development Co Ltd Beijing filed Critical Xietong Rongchuang Sci & Tech Development Co Ltd Beijing
Priority to CN2007100910257A priority Critical patent/CN101058901B/zh
Publication of CN101058901A publication Critical patent/CN101058901A/zh
Application granted granted Critical
Publication of CN101058901B publication Critical patent/CN101058901B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于纺织品领域，特别涉及纳米珍珠聚丙烯超细旦纤维及其制备方法。所述的纳米珍珠聚丙烯超细旦纤维是由纳米珍珠粉与聚丙烯超细旦纤维复合而成，其中纳米珍珠粉占纳米珍珠聚丙烯超细旦纤维总重量的0.1％～15％，纳米珍珠聚丙烯超细旦纤维的单丝纤度为0.1～0.5旦，抗张强度6～8克/旦，断裂伸长率为25～70％。这种纤维具有纳米珍珠所含有的十余种氨基酸和多种微量元素，既有珍珠养颜护肤功效，又有超细旦纤维服用舒适的特性；使用本发明的纤维加工成织物对人体具有良好的营养、保健作用。

Description

纳米珍珠聚丙烯超细旦纤维及其制备方法
技术领域
本发明涉及一种超细旦纤维，尤其涉及一种将纳米珍珠与聚丙烯超细旦纤维复合而成的一种超细旦纤维及其制备方法，属于纺织品领域。
背景技术
通常单丝纤度为0.5旦左右的化学纤维为超细旦纤维，而聚丙烯超细旦纤维可制成手感柔软、穿着舒适的高档纺织物，有着很高的经济价值，而珍珠养颜护肤、清火败毒、嫩白肌肤、抗紫外线的功效，珍珠含有多种氨基酸和微量元素。因而纳米珍珠超细旦纤维制造技术的开发是几年来功能性纤维都很重视的高新技术。
珍珠功能性纤维由于具有良好的经济价值，研究类似产品的企业很多，珍珠纤维是由东华大学和上海新型纺纱中心合作共同研发的一种新型纤维，专利申请号CN200410067962.2所公开的珍珠纤维技术方案是将纳米级珍珠粉在粘胶纤维纺丝时加入纤维内，而粘胶纤维本身具有很多难以克服的缺点。故开发新的纳米珍珠复合材料在聚丙烯超细旦纤维的应用开发有着重要作用。
发明内容
为了解决上述存在的问题，本发明的目的是提供一种具有珍珠良好性能的纳米珍珠聚丙烯超细旦纤维。
本发明的技术方案是这样实现的：纳米珍珠聚丙烯超细旦纤维是由纳米珍珠粉与聚丙烯超细旦纤维复合而成，其中纳米珍珠粉占纳米珍珠聚丙烯超细旦纤维总重量的0.1％～15％，纳米珍珠聚丙烯超细旦纤维的单丝纤度为0.1～0.5旦，抗张强度6～8克/旦，断裂伸长率为25％～70％。
本发明的纤维具有纳米珍珠所含有的十余种氨基酸和多种微量元素。
所述的聚丙烯是熔融指数为35～100的超细旦聚丙烯树脂。
所述的纳米珍珠粉的粒径是50～100纳米。
本发明的另一个目的是针对纳米珍珠聚丙烯超细旦纤维制造中的技术困难，提供一种纳米珍珠聚丙烯超细旦纤维的制备方法。
本发明的纳米珍珠聚丙烯超细旦纤维的制备方法包括以下步骤：
(1).纳米珍珠粉复合物的制备
珍珠进行高速机械粉碎等物理处理后获得粗珍珠粉，然后将粗珍珠粉与水按重量1∶10～100的比例混合，经过高压粉碎，得到粒径为50～100纳米的珍珠粉的水分散液，加入为珍珠粉重量1％～5％的稳定剂，和为珍珠粉重量1％～10％的乳化剂，干燥处理，得到纳米珍珠粉复合物；
(2).纳米珍珠聚丙烯超细旦切片的制备
将步骤(1)得到的纳米珍珠粉复合物与相容剂按重量1∶0.1～8的比例在常温下混合均匀后，再将上述混合物加入到聚丙烯超细旦切片中，上述混合物在聚丙烯超细旦切片中的重量含量为0.2％～30％，经双螺杆挤出机造粒，得到纳米珍珠聚丙烯超细旦切片；
(3).纳米珍珠聚丙烯超细旦纤维的制备
将步骤(2)得到的纳米珍珠聚丙烯超细旦切片，按照纺丝的工艺要求，进行高速复合纺丝，纺丝的熔体温度控制在185～230℃之间，卷绕速度控制在500～3500米/分，热定型温度为60～100℃，牵引倍数一般可控制在3～6倍之间。
在所述的步骤(2)中的混合物中可进一步加入加工助剂。
本发明在采用稳定的工艺制作单丝纤度为0.1～0.5旦的纳米珍珠聚丙烯超细旦纤维时，设法减小纺丝过程中各种参数的波动，尽可能的抑制纳米珍珠聚丙烯超细旦纤维生产过程中的不稳定因素，调整纳米珍珠与聚丙烯超细旦纤维复合物的比例，可以抑制在纺丝过程中因降解而引起熔体粘度变化和相容的不均匀，纺丝的熔体温度瞬间控制在185～230℃之间，卷绕速度控制在500～3500米/分，热定型温度为60～100℃，牵引倍数一般可控制在3～6倍之间。
所述的双螺杆挤出机造粒温度是190～230℃。
所述的稳定剂是羧甲基纤维素钠、黄原胶、瓜尔豆胶、卡拉胶、海藻酸钠等或它们的任意混合物。
所述的乳化剂是蔗糖脂肪酸酯、聚甘油脂肪酸酯、大豆磷脂、山梨醇酐单硬脂酸酯等或它们的任意混合物。
所述的相容剂是接枝率不小于0.5％的马来酸酐接枝聚丙烯、丙烯酸接枝聚丙烯等或它们的任意混合物。
所述的加工助剂是润滑剂和/或抗氧剂等。
所述的润滑剂是硬脂酸钙、乙撑双硬脂酰胺(EBS)、油酸酰胺等或它们的任意混合物。
所述的抗氧剂是抗氧剂1010(汽巴嘉基公司Irganox1010)、抗氧剂1076(汽巴嘉基公司Irganox1076)、抗氧剂168(汽巴嘉基公司Irganox168)等或它们的任意混合物。
与现有技术相比，本发明的有益效果是：本发明的纤维具有纳米珍珠所含有的十余种氨基酸和多种微量元素，既有珍珠养颜护肤功效，又有超细旦纤维吸湿透气、服用舒适的特性；本发明的纳米珍珠聚丙烯超细旦纤维表面均匀分布着珍珠微粒，长期与皮肤接触，具有珍珠养颜护肤、清火败毒、嫩白肌肤、抗紫外线的功效；同时纳米珍珠聚丙烯超细旦纤维还含有多种氨基酸和微量元素，纤维表面光滑凉爽，有珍珠般光泽。使用本发明的纳米珍珠聚丙烯超细旦纤维加工成织物对人体具有良好的营养和保健作用。
具体实施方式
下面结合具体实施例，对本发明作进一步详细描述，但不作为对本发明的限定。
实施例1.
(1).纳米珍珠粉复合物的制备
将1重量份珍珠用清水洗净干燥后，以高频振动磨加工至300目，然后与9重量份去离子水、0.1重量份羧甲基纤维素钠、0.1重量份蔗糖脂肪酸酯混合，配制成悬浮液，把高压均质机的压强设定为100MPa，将悬浮液加入到高压均质机的进料池，自动进料，经高压粉碎后得到粒径为50～100纳米的珍珠粉的悬浮液，加热干燥后得到粒径为50～100纳米的珍珠粉复合物；
(2).纳米珍珠聚丙烯超细旦切片的制备
将步骤(1)得到的5重量份纳米珍珠粉复合物与5重量份接枝率为0.5％的丙烯酸接枝聚丙烯混合，再将混合物与90重量份聚丙烯超细旦切片混合，并加入0.2重量份的润滑剂硬脂酸钙和0.2重量份的抗氧剂1010，以双螺杆挤出机在200℃下造粒，得到纳米珍珠聚丙烯超细旦切片；
(3).纳米珍珠聚丙烯超细旦纤维的制备
将步骤(2)得到的纳米珍珠聚丙烯超细旦切片，按照纺丝的工艺要求，进行高速复合纺丝。纺丝的熔体温度控制在185～230℃之间，卷绕速度控制在500～3500米/分，热定型温度为60～100℃，牵引倍数一般可控制在3～6倍之间。
步骤(2)中所述的配比可根据表1和表2的配方变化，按照纺丝工艺：纺丝的温度控制在185～230℃之间，卷绕速度控制在500～2500米/分进行纺丝，按照3进行后加工测试，纤维的可纺性非常好。
表1列出了纳米珍珠超细旦聚丙烯纤维切片成份配比：
表1
 纳米珍珠超细旦聚丙烯纺丝树脂   重量份数
 超细旦聚丙烯树脂(MI＝35，Q＝1.27)纳米珍珠复合物丙烯酸接枝聚丙烯硬脂酸钙抗氧剂1010   90550.10.2
表2列出了纳米珍珠超细旦聚丙烯纤维切片成份配比：
表2
  编号   超细旦聚丙烯树脂(MI＝35，Q＝1.27)   纳米珍珠复合物   丙烯酸接枝聚丙烯
  1-2-11-2-21-2-31-2-41-2-5   90重量份92重量份94重量份96重量份98重量份   5重量份4重量份3重量份2重量份1重量份   5重量份4重量份3重量份2重量份1重量份
本系列添加的其它的加工助剂和表1相同。
表3列出了纳米珍珠超细旦纤维卷绕丝和成品丝的性质
表3
  纺丝切片   卷绕机的最   成品纤维的性质
  编号   大牵引倍数   单丝纤度(旦)   抗张强度(克/旦)   断裂伸长率(％)
  1-2-11-2-21-2-31-2-41-2-5   4.14.14.14.14.1   0.430.450.430.470.46   5.96.06.16.05.9   5035455557
按照表1配比进行纺丝后，并对于不同配方的纳米珍珠超细旦纤维的氨基酸含量见表4，微量元素含量见表5；
表4
 氨基酸   1-2-1g/100g样品   1-2-2g/100g样品   1-2-3g/100g样品  1-2-4g/100g样品  1-2-5g/100g样品
 ASP天门东氨酸THR苏氨酸SER丝氨酸GLU谷氨酸GLY甘氨酸   0.0270.0070.0170.0180.035   0.0230.0060.0130.0140.030   0.0190.0050.010.0120.025  0.0100.0020.0050.0050.009  0.0050.0010.0020.0020.004
  ALA丙氨酸VAL缬氨酸MET蛋氨酸ILE异亮氨酸LEU亮氨酸TYR酪氨酸PHE苯丙氨酸LYS赖氨酸   0.0420.0080.0020.0080.020.0070.0120.008   0.0350.0070.0020.0070.0180.0060.010.007   0.0300.0060.0020.0060.0160.0060.010.006   0.0140.0030.0010.0020.0080.0040.0070.003   0.0050.0010.0010.0010.0020.0010.0030.001
表5
  微量元素   1-2-1mg/100g样品   1-2-2mg/100g样品   1-2-3mg/100g样品   1-2-4mg/100g样品   1-2-5mg/100g样品
  钙钾钠镁铜铁锰锌   4.50.099201.460.0373.347.430.05   3.90.077161.20.0303.016.610.04   2.70.05110.80.0181.714.90.03   1.90.0380.50.090.912.50.02   0.90.0130.020.0450.511.10.01
由表4和表5列出的数据可以看出：纳米珍珠纤维中含有大量的微量元素和高级蛋白质，为纤维的服装提供了高级蛋白质和微量元素。

Claims (10)

1.一种纳米珍珠聚丙烯超细旦纤维，其特征是：所述的纳米珍珠聚丙烯超细旦纤维是由纳米珍珠粉与聚丙烯超细旦纤维复合而成，其中纳米珍珠粉占纳米珍珠聚丙烯超细旦纤维总重量的0.1％～15％，纳米珍珠聚丙烯超细旦纤维的单丝纤度为0.1～0.5旦，抗张强度6～8克/旦，断裂伸长率为25～70％。
2.根据权利要求1所述的纳米珍珠聚丙烯超细旦纤维，其特征是：所述的聚丙烯是熔融指数为35～100的超细旦聚丙烯树脂。
3.根据权利要求1所述的纳米珍珠聚丙烯超细旦纤维，其特征是：所述的珍珠粉的粒径是50～100纳米。
4.一种根据权利要求1～3任一项所述的纳米珍珠聚丙烯超细旦纤维的制备方法，其特征是，所述的方法包括以下步骤：
(1).纳米珍珠粉复合物的制备
将珍珠进行物理处理后获得粗珍珠粉，然后将粗珍珠粉与水按重量1∶10～100的比例混合，经过高压粉碎，得到粒径为50～100纳米的珍珠粉的水分散液，加入为珍珠粉重量1％～10％的稳定剂，和为珍珠粉重量1％～10％的乳化剂，干燥处理，得到纳米珍珠粉复合物；
(2).纳米珍珠聚丙烯超细旦切片的制备
将步骤(1)得到的纳米珍珠粉复合物与相容剂按重量1∶0.1～8的比例在常温下混合均匀后，再将上述混合物加入到聚丙烯超细旦切片中，上述混合物在聚丙烯超细旦切片中的重量含量为0.2％～30％，经双螺杆挤出机造粒，得到纳米珍珠聚丙烯超细旦切片；
(3).纳米珍珠聚丙烯超细旦纤维的制备
将步骤(2)得到的纳米珍珠聚丙烯超细旦切片进行高速复合纺丝，纺丝的熔体温度控制在185～230℃之间，卷绕速度控制在500～3500米/分，热定型温度为60～100℃，牵引倍数控制在3～6倍之间。
5.根据权利要求4所述的方法，其特征是：所述的双螺杆挤出机造粒温度是190～230℃。
6.根据权利要求4所述的方法，其特征是：所述的稳定剂是羧甲基纤维素钠、黄原胶、瓜尔豆胶、卡拉胶、海藻酸钠或它们的任意混合物。
7.根据权利要求4所述的方法，其特征是：所述的乳化剂是蔗糖脂肪酸酯、聚甘油脂肪酸酯、大豆磷脂、山梨醇酐单硬脂酸酯或它们的任意混合物。
8.根据权利要求4所述的方法，其特征是：所述的相容剂是接枝率不小于0.5％的马来酸酐接枝聚丙烯、丙烯酸接枝聚丙烯或它们的任意混合物。
9.根据权利要求4所述的方法，其特征是：所述的步骤(2)用于造粒的混合物中加入有加工助剂。
10.根据权利要求9所述的方法，其特征是：所述的加工助剂是润滑剂和/或抗氧剂。
CN2007100910257A 2006-04-07 2007-04-05 纳米珍珠聚丙烯超细旦纤维及其制备方法 Expired - Fee Related CN101058901B (zh)