CN101055258A - 一种水压焊缝快速检漏剂及其制备方法 - Google Patents
一种水压焊缝快速检漏剂及其制备方法 Download PDFInfo
- Publication number
- CN101055258A CN101055258A CN 200710017765 CN200710017765A CN101055258A CN 101055258 A CN101055258 A CN 101055258A CN 200710017765 CN200710017765 CN 200710017765 CN 200710017765 A CN200710017765 A CN 200710017765A CN 101055258 A CN101055258 A CN 101055258A
- Authority
- CN
- China
- Prior art keywords
- agent
- welding seam
- magnesium oxide
- hydraulic pressure
- sand mill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开的一种水压焊缝快速检漏剂,按质量百分比其组成为:乙醇65%~70%,聚乙烯醇缩丁醛0.13%~0.18%,轻质氧化镁28.5%~33.5%,百里香酚蓝0.10%~0.15%,抗沉剂1.22%~1.5%。将乙醇加入间歇式砂磨机中,开动砂磨机,先加入聚乙烯醇缩丁醛,使之溶解,然后依次加入轻质氧化镁,百里香酚蓝,抗沉剂,研磨至均匀无颗粒,即得。本发明涂层干燥快,附着力好,不容易从焊缝表面剥落;显色对比明显;可以区别焊缝内渗水和外部喷溅水变色,达到判断快速准确的效果。
Description
技术领域
本发明属于化工产品技术领域,涉及一种检漏剂,具体涉及一种判断穿透性焊缝缺陷的化学检漏剂,本发明还涉及该检漏剂的制备方法。
背景技术
目前的焊接技术中通常存在穿透性焊缝缺陷现象,因此有必要寻找一种穿透性焊缝缺陷的化学检漏剂。国内尚无涂覆在焊缝表面,通过注水打压来定性判断穿透性焊缝缺陷的化学检漏剂。日本技术主要加入无机粉体、显色剂、挥发或不挥发溶剂,通过颜色变化为变红或变绿来判断焊漏点,但是日本技术存在检漏剂易从表面脱落、显色不明显以及无法准确判断焊缝内渗水和外部喷溅水的问题。
发明内容
本发明的目的在于提供一种水压焊缝快速检漏剂,解决了现有检漏剂易从表面脱落、显色不明显以及无法准确判断焊缝内渗水和外部喷溅水的问题。
本发明的另一目的是提供上述检漏剂的制备方法。
本发明所采用的技术方案是,一种水压焊缝快速检漏剂,按质量百分比,其组成为:乙醇65%~70%,聚乙烯醇缩丁醛0.13%~0.18%,轻质氧化镁28.5~33.5%,百里香酚蓝0.1%~0.15%,抗沉剂1.22%~1.5%。
本发明所采用的另一技术方案是,上述检漏剂的制备方法,按以下步骤进行,
首先,将质量百分比65%~70%乙醇加入间歇式砂磨机中,开动砂磨机,按质量百分比加入0.13%~0.18%的聚乙烯醇缩丁醛,使之溶解;
然后,在上述混合物中依次加入28.5%~33.5%的轻质氧化镁、0.1%~0.15%的百里香酚蓝和1.22%~1.5%的抗沉剂,研磨30min~40min至均匀无颗粒,即得。
本发明的有益效果是,
A:本发明的检漏剂含有有机成膜物,涂层干燥快,附着力好,同国外单纯加入粉体相比,不容易从焊缝表面剥落。
B:涂层干态为黄色,遇水变深蓝色,同国外绿色相比,颜色明显;同红色相比,容易区分焊缝处的发兰处理的紫红色。
C:本发明的检漏剂遇水可以反复变色,可以区别焊缝内渗水和外部喷溅水变色,避免误判。
该水压焊缝快速检漏剂能达到显色明显,判断快速准确的效果。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
本发明水压焊缝快速检漏剂,按质量百分比,其组成为:乙醇65%~70%,聚乙烯醇缩丁醛0.13%~0.18%,轻质氧化镁28.5%~33.5%,百里香酚蓝0.1%~0.15%,抗沉剂1.22%~1.5%。
各组分在本检漏剂中的作用:
有机溶剂乙醇使本发明为液态,同时能溶解有机成膜物聚乙烯醇缩丁醛,当涂覆在焊缝表面后可以使涂层快速干燥。
无机粉体轻质氧化镁可以微溶于水。在水溶条件下,可以微量电离出氢氧根阴离子,使变色剂百里香酚蓝变蓝。
聚乙烯醇缩丁醛作为成膜物质,随乙醇挥发后在涂覆处干燥,较好的附着于焊缝表面。使涂层遇渗水不易冲掉脱落,造成判断遗漏。
变色剂百里香酚蓝,PH变色范围为8.0(黄)~9.6(蓝),因此使轻质氧化镁遇水变蓝,干燥后变黄。
抗沉剂可采用市场上化工产品常用的成品,使粉体轻质氧化镁悬浮于本发明体系中,不易沉淀板结。本发明提供了一种效果较好的产品,产自《德谦化学公司》,型号:923S。
以下是本发明提供的一种制备方法:
将质量百分比65%~70%乙醇加入间歇式砂磨机中,开动砂磨机,按质量百分比先加入0.13%~0.18%的聚乙烯醇缩丁醛,溶解,然后依次加入28.5%~33.5%的轻质氧化镁,0.1%~0.15%的百里香酚蓝,1.22%~1.5%的抗沉剂,研磨30min~40min至均匀无颗粒,即得。
实施例1
将质量百分比65%乙醇加入间歇式砂磨机中,开动砂磨机,按质量百分比先加入0.1 8%的聚乙烯醇缩丁醛,溶解,然后依次加入33.5%的轻质氧化镁,0.10%的百里香酚蓝,1.22%的抗沉剂,研磨30min至均匀无颗粒,即得。
实施例2
将质量百分比70%乙醇加入间歇式砂磨机中,开动砂磨机,按质量百分比先加入0.13%的聚乙烯醇缩丁醛,溶解,然后依次加入28.5%的轻质氧化镁,0.15%的百里香酚蓝,1.22%的抗沉剂,研磨40min至均匀无颗粒,即得。
实施例3
将质量百分比68.2%乙醇加入间歇式砂磨机中,开动砂磨机,按质量百分比先加入0.1 5%的聚乙烯醇缩丁醛,溶解,然后依次加入30%的轻质氧化镁,0.15%的百里香酚蓝,1.5%的抗沉剂,研磨35min至均匀无颗粒,即得。
本发明用于水压判定穿透性焊缝缺陷定性检查。将被测物注水打压后,将本发明涂覆于焊缝外表面,干膜呈黄色,涂层遇水变湿,湿膜呈蓝色,表示焊接处有裂缝,显色对比明显,可以快速准确判断焊缝缺陷。
Claims (2)
1.一种水压焊缝快速检漏剂,按质量百分比,其组成为:乙醇65%~70%,聚乙烯醇缩丁醛0.13%~0.18%,轻质氧化镁28.5%~33.5%,百里香酚蓝0.1%~0.15%,抗沉剂1.22%~1.5%。
2.一种权利要求1所述检漏剂的制备方法,其特征在于,包括下列步骤:
首先,将质量百分比65%~70%乙醇加入间歇式砂磨机中,开动砂磨机,按质量百分比加入0.13%~0.18%的聚乙烯醇缩丁醛,使之溶解;
然后,在上述混合物中依次加入28.5%~33.5%的轻质氧化镁、0.1%~0.15%的百里香酚蓝和1.22%~1.5%的抗沉剂,研磨30min~40min至均匀无颗粒,即得。