CN100549069C - 一种单速催化酚醛树脂凝胶驱油剂 - Google Patents
一种单速催化酚醛树脂凝胶驱油剂 Download PDFInfo
- Publication number
- CN100549069C CN100549069C CNB2005101279605A CN200510127960A CN100549069C CN 100549069 C CN100549069 C CN 100549069C CN B2005101279605 A CNB2005101279605 A CN B2005101279605A CN 200510127960 A CN200510127960 A CN 200510127960A CN 100549069 C CN100549069 C CN 100549069C
- Authority
- CN
- China
- Prior art keywords
- oil
- polyacrylamide
- displacing agent
- hydro
- phenol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种单速催化酚醛树脂凝胶驱油剂，在0.06～0.6%水解聚丙烯酰胺、0.06～0.12%苯酚和0.06～0.12%甲醛体系中加入0.01～0.06%单组分的加速成胶的催化剂，其余量为水；催化剂是草酸、氢氧化钠、碳酸氢钠、氢氧化钾中的一种；凝胶形成的时间可根据油田的需要控制，满足驱油和堵水的不同功能的需要，作为驱油剂使用成本低，作为堵水剂使用，形成凝胶的时间大幅缩短，提高成功率，稳定时间在6个月以上。
Description
技术领域
本发明涉及一种石油开发中用于提高石油采收率的单速催化酚醛树脂凝胶驱油剂。
背景技术
(1)水解聚丙烯酰胺与苯酚-甲醛形成酚醛树脂凝胶用于油田高温油藏的堵水作业，没有作为驱油剂使用。
(2)苯酚-甲醛-聚合物形成凝胶的时间与温度相关，温度越高，形成凝胶的时间缩短，对于80℃左右的油藏，苯酚-甲醛-水解聚丙烯酰胺形成凝胶的时间在120h以上，形成凝胶的时间过长，不利于现场应用。
(3)过去研究的水解聚丙烯酰胺与苯酚-甲醛形成酚醛树脂凝胶聚合物浓度高，成本高。
(4)苯酚常温下(40℃以下)为固体，存在施工的加药的困难。
发明内容
本发明的目的是把用于油田高温油藏堵水作业的水解聚丙烯酰胺、苯酚和甲醛形成的酚醛树脂凝胶经过改进，作为驱油剂用于油田高温油藏采油，提高石油采收率；根据驱油剂的需要，研究出单速催化的酚醛凝胶驱油体系，将形成弱凝胶的时间缩短到24h以内。
本技术方案是这样实现的：
在水解聚丙烯酰胺、苯酚和甲醛体系中加入单组分或多组分的加速成胶的催化剂，可以作为油田驱油剂或堵水剂的需要，调整形成凝胶的时间，催化剂包括碱类或除苯酚以外的多酚类化学制剂，如草酸、氢氧化钠、碳酸氢钠、氢氧化钾、间苯二酚化学制剂，单速催化可以是其中的任一种，多速催化可以是其中两种或三种的混合物，为提高体系的钙、镁等抗二价离子的高矿化度的能力，聚丙烯酰胺选择：阴离子性、复合离子性、非离子性，体系在矿化度8％的油田水中形成驱油或堵水用凝胶。
酚醛树脂凝胶做驱油剂，按下面重量百分比配方：
水解聚丙烯酰胺0.06％～0.6％、
苯酚0.06％～0.12％、
甲醛0.06％～0.12％、
催化剂0.01％～0.06％、
其余量为水。
使用方法：
先溶解水解聚丙烯酰胺，然后把苯酚、甲醛和催化剂直接加入已经溶好的水解聚丙烯酰胺的容器中，搅拌均匀后，用注聚泵注入水井或油井中。
本多速催化酚醛树脂凝胶作为驱油剂使用，已在新疆油田的80℃以上的中、低渗透砂岩油藏推广使用4年，使用油藏两个，增油5000吨以上，对油田的稳产起到重要作用，增加了聚丙烯酰胺与苯酚-甲醛凝胶体系的使用功能，根据油田的需要分三个速度控制形成的凝胶的时间，满足驱油和堵水的不同功能的需要，作为驱油剂使用成本低，作为堵水剂使用，形成凝胶的时间大幅缩短，提高成功率，用于80℃以上的高温油藏，稳定时间在6个月以上。
具体实施方式
实施例1
按下面重量百分比例配料制备多速催化酚醛树脂凝胶驱油剂：
0.06％水解聚丙烯酰胺+0.06％苯酚+0.06％甲醛+0.04％氢氧化钠+余量水
凝胶粘度100mPa.s，80℃，成胶时间40h。
实施例2
本实施例以碱催化的体系为例。
0.6％、阴离子性水解聚丙烯酰胺+0.12％苯酚+0.12％甲醛+0.01％碳酸氢钠+余量水
凝胶粘度100mPa.s，80℃，成胶时间40h。
实施例3
本实施例以碱催化的体系为例。
0.06％非离子性水解聚丙烯酰胺+0.06％苯酚+0.06％甲醛+0.06％氢氧化钾+余量水
凝胶粘度100mPa.s，80℃，成胶时间40h。
实施例4
本实施例以多酚催化的体系为例。
0.06％阴离子性水解聚丙烯酰胺+0.06％苯酚+0.06％甲醛+0.01％间苯二酚+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例5
本实施例以多酚催化的体系为例。
0.5％复合离子性水解聚丙烯酰胺+0.1％苯酚+0.08％甲醛+0.01％二酚+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例6
本实施例以多酚催化的体系为例。
0.4％复合离子水解聚丙烯酰胺+0.06％苯酚+0.06％甲醛+0.06％多酚+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例7
本实施例以多酚催化的体系为例。
0.5％阴离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.05％间苯二酚和二酚两种的混合+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例8
本实施例以多酚催化的体系为例。
0.08％非离子性水解聚丙烯酰胺+0.09％苯酚+0.09％甲醛+0.01％间苯二酚和多酚两种的混合+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例9
本实施例以多酚催化的体系为例。
0.09％水解聚丙烯酰胺+0.1％苯酚+0.06％甲醛+0.02％二酚和多酚两种的混合+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例10
本实施例以多酚催化的体系为例。
0.06％阴离子性水解聚丙烯酰胺+0.06％苯酚+0.06％甲醛+0.01％草酸+余量水
凝胶粘度80mPa.s，80℃，成胶时间20h。
实施例11
0.08％复合离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.01％氢氧化钠+0.01％间苯二酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例12
0.08％非离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.01％碳酸氢钠、+0.01％二酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例13
0.08％复合离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.02％氢氧化钾+0.02％多酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例14
0.08％阴离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.03％氢氧化钠+0.03％多酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例15
0.08％复合离子聚合物+0.08％苯酚+0.08％甲醛+0.01％氢氧化钾+0.01％间苯二酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例16
0.08％非离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.01％碳酸氢钠+0.01％间苯二酚和二酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例17
0.08％非离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.01％氢氧化钠+0.01％间苯二酚和多酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
实施例18
0.08％阴离子性水解聚丙烯酰胺+0.08％苯酚+0.08％甲醛+0.01％氢氧化钾+0.01％二酚和多酚+余量水
凝胶粘度140mPa.s，80℃，成胶时间20h。
Claims (2)
1.一种单速催化酚醛树脂凝胶驱油剂，其特征在于：按重量百分比，在0.06～0.6％水解聚丙烯酰胺、0.06～0.12％苯酚和0.06～0.12％甲醛体系中加入0.01～0.06％单组分的加速成胶的催化剂，余量为水；催化剂是草酸、氢氧化钠、碳酸氢钠、氢氧化钾中的一种。
2.根据权利要求1所述的一种单速催化酚醛树脂凝胶驱油剂，其特征在于：聚丙烯酰胺是阴离子性、复合离子性或非离子性。