CN100523268C - 锌镍镀层 - Google Patents

锌镍镀层 Download PDF

Info

Publication number
CN100523268C
CN100523268C CNB038259982A CN03825998A CN100523268C CN 100523268 C CN100523268 C CN 100523268C CN B038259982 A CNB038259982 A CN B038259982A CN 03825998 A CN03825998 A CN 03825998A CN 100523268 C CN100523268 C CN 100523268C
Authority
CN
China
Prior art keywords
zinc
coating layer
nickel coating
net
plating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB038259982A
Other languages
English (en)
Other versions
CN1742108A (zh
Inventor
P·埃蒂安
A·罗达迪奥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bekaert NV SA
Original Assignee
Bekaert NV SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bekaert NV SA filed Critical Bekaert NV SA
Publication of CN1742108A publication Critical patent/CN1742108A/zh
Application granted granted Critical
Publication of CN100523268C publication Critical patent/CN100523268C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种包含金属线材的网。该网采用锌镍镀层镀覆。该锌镍镀层包含0.01-0.1重量%Ni，并且不含铅。本发明还涉及一种采用这种锌镍镀层镀覆的线材。

Description

锌镍镀层
发明领域
本发明涉及包含锌镍镀层的网以及这种网的制造方法。本发明还涉及采用锌镍镀层镀覆的线材。
发明背景
本领域一般都知道采用分批处理方法通过将制品浸渍在锌熔体镀液中对钢制品进行镀锌。镀液通常含有最高达1.5重量％铅，以避免形成浮渣和降低锌的表面张力。
但是，由于立法缘故，许多国家禁止使用铅。
发明概述
本发明的一个目的是提供具有无铅镀层的网和提供使用无铅镀液制造镀覆网的方法。
本发明的另一个目的是提供包含耐腐蚀性能优异的锌镍镀层的网。
本发明的又一个目的是提供具有锌镍镀层的线材。
本发明的再一个目的是提供借助连续镀覆工艺制造镀覆网的方法。
根据本发明的第一个方面，提供采用锌镍镀层镀覆的网。该网包括金属线材。
锌镍镀层含有0.01-0.1重量％Ni。更优选锌镍镀层含有0.035-0.065重量％Ni。
该锌镍镀层无铅。所谓“无铅”指的是镀层不含铅(不可避免的痕量除外)。
如上所述，锌镀液中一般添加铅，以避免形成浮渣。根据本发明，已令人惊奇地发现可以镀覆锌镍镀层而无需添加铅。
锌镍镀层优选采用连续镀覆方法使网通过热浸镀(galvanising)工艺中的锌镍镀液进行镀覆。
在一个优选实施方案中，在金属线材与锌镍镀层界面处，形成了金属线材的金属与锌镍镀层的合金层。该合金层厚度为0.1-10μm，例如8μm。
与采用锌镀层镀覆的网相比，采用根据本发明的锌镍镀层镀覆的网具有改善的耐腐蚀性。
网可以包括焊接网，例如包含许多在交叉点处电焊在一起的线材的网。网还可以包括一种包含金属线材的编织结构。
网的筛孔可以为矩形、方形、六角形或者菱形的开孔。网可以为平面状，或者可以进行弯曲或变形。
线材优选是钢线材或者采用锌或锌合金镀层镀覆的钢线材。
线材横截面可以为圆形、椭圆形、矩形或者其它任何形状。
在一个优选实施方案中，线材横截面为圆形，直径为0.1-5mm，如0.4-1mm。
在一个优选实施方案中，网在采用锌镍镀层镀覆之前，优选采用锌或锌合金镀层镀覆。
网的线材可以在成型为网之前采用锌或锌合金镀层镀覆。
或者，包含金属线材的网采用锌或锌合金镀层镀覆。
根据本发明的第二个方面，提供采用镍锌镀层镀覆的线材。该线材优选包括钢线材。更优选该线材包括具有锌或锌合金镀层镀覆的钢线材。
根据本发明的又一个方面，提供制造镀覆网的方法。
该方法包括如下步骤：
-提供网；
-通过热浸镀在所述网上镀覆锌镍镀层，所述锌镍镀层含有0.01-0.1重量％Ni，所述锌镍镀层无铅。
所述方法还可以包括如下步骤：在镀覆所述锌镍镀层之前，在所述网上镀覆锌镀层。
所述锌镍镀层采用连续镀覆方法镀覆。
本发明优选实施方案描述
一个优选实施方案包括一种具有钢线材的焊接网。
锌镍镀层采用连续热浸镀工艺镀覆。热浸镀镀液含有0.048-0.053重量％Ni。
焊接网在热浸镀液中的浸渍时间为10秒至5分钟。
镀覆在网上的锌镍镀层含有0.035-0.065重量％Ni，并且无铅。
在金属线材与锌镍镀层的界面处，形成了钢与锌镍镀层的合金层。合金层厚度为0.1-10μm。
为了评价耐腐蚀性，对采用锌镍镀层镀覆的网进行盐雾试验。表1列出了当5％表面为深褐色锈(DBR)覆盖时的时间长度。第2列示出的是采用锌镍镀层镀覆的网的耐腐蚀性；第3列示出的是采用锌镀层镀覆的网的耐腐蚀性。
表1
 
Zn-Ni镀覆网 Zn镀覆网
直到5％DBR时的盐雾试验小时数 ±400 ±200

Claims (9)

1.一种包含金属线材的网，所述网采用锌镍镀层镀覆，所述锌镍镀层无铅并且所述锌镍镀层含有0.01-0.1重量％Ni，其中，所述网在镀覆所述锌镍镀层之前，采用锌或锌合金镀层镀覆。
2.根据权利要求1的网，其中，所述锌镍镀层含有0.035-0.065重量％Ni。
3.根据权利要求1或2的网，其中，在金属线材与锌镍镀层界面处，形成了厚0.1-10μm的合金层。
4.根据权利要求1或2的网，其中，所述网包括焊接网或者编织网。
5.根据权利要求1或2的网，其中，所述网包含钢线材。
6.根据权利要求1或2的网，其中，所述网包含镀锌钢线材。
7.一种采用锌镍镀层镀覆的金属线材，所述锌镍镀层无铅，其中，所述线材在镀覆所述锌镍镀层之前，采用锌或锌合金镀层镀覆。
8.根据权利要求7的金属线材，所述金属线材包括钢线材或者镀有锌或锌合金镀层的钢线材。
9.一种制造镀覆网的方法，所述方法包括如下步骤：
-提供网；
-通过热浸镀在所述网上镀覆锌镍镀层，所述锌镍镀层无铅并且所述锌镍镀层含有0.01-0.1重量％Ni，其中，所述网在镀覆所述锌镍镀层之前，采用锌镀层镀覆。
CNB038259982A 2003-03-07 2003-03-07 锌镍镀层 Expired - Fee Related CN100523268C (zh)