CN103088278B - 一种镀层中不含铅的镀覆网的制造方法 - Google Patents

一种镀层中不含铅的镀覆网的制造方法 Download PDF

Info

Publication number
CN103088278B
CN103088278B CN201210478898.4A CN201210478898A CN103088278B CN 103088278 B CN103088278 B CN 103088278B CN 201210478898 A CN201210478898 A CN 201210478898A CN 103088278 B CN103088278 B CN 103088278B
Authority
CN
China
Prior art keywords
zinc
coating
nickel
lead
manufacture method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210478898.4A
Other languages
English (en)
Other versions
CN103088278A (zh
Inventor
孙长志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANCHANG FEILONG BRAND STEEL GRID CO Ltd
Original Assignee
TIANCHANG FEILONG BRAND STEEL GRID CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANCHANG FEILONG BRAND STEEL GRID CO Ltd filed Critical TIANCHANG FEILONG BRAND STEEL GRID CO Ltd
Priority to CN201210478898.4A priority Critical patent/CN103088278B/zh
Publication of CN103088278A publication Critical patent/CN103088278A/zh
Application granted granted Critical
Publication of CN103088278B publication Critical patent/CN103088278B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种镀层中不含铅的镀覆网的制造方法，包括如下步骤：提供金属；在所述金属上镀覆锌镀层；在所述锌镀层上镀覆锌镍层，其中，所述锌镍层中包含（按重量计算）0.025～0.05％的镍；在所述锌镍层表面镀覆多元金属层，其中，所述多元金属层包含（按重量计算）镍：0.025～0.04％；铬：0．01～0.025％；余量的锌。制造方法中不采用铅，对环境友好，由此方法生产出的镀覆网具有更好的耐腐蚀性能。

Description

一种镀层中不含铅的镀覆网的制造方法
技术领域
本发明涉及一种镀层中不含铅的镀覆网的制造方法。
背景技术
采用分批处理方法，通过将制品浸在锌熔体镀液中对钢制品进行镀锌，镀液通常含有重量比高达1.5％的铅，以避免形成浮渣和降低锌的表面张力。然而，作为重金属，铅的使用，不仅对自然环境造成破坏，还对生物体造成极大损害，在许多国家的许多行业，被明令禁止，亟待改进。
发明内容
针对现有技术存在的问题，本发明的目的在于提出一种镀层中不含铅的镀覆网的制造方法，制造方法中不采用铅，对环境友好，由此方法生产出的镀覆网具有更好的耐腐蚀性能。
为达到上述目的，本发明采用如下技术方案：
一种镀层中不含铅的镀覆网的制造方法，包括如下步骤：
提供金属；
在所述金属上镀覆锌镀层；
在所述锌镀层上镀覆锌镍层，其中，所述锌镍层中包含（按重量计算）0.025～0.05％的镍；
在所述锌镍层表面镀覆多元金属层，其中，所述多元金属层包含（按重量计算）镍：0.025～0.04％；铬：0.01～0.025％；余量的锌。
所述金属为网状。
所述锌镍层中包含重量比为0.04％的镍。
所述多元金属层包含（按重量计算）镍：0.025％；铬：0.025％；余量的锌。
所述金属为钢。
基于以上技术方案的公开，本发明具备如下有益效果：
通过采用本发明提出的一种镀层中不含铅的镀覆网的制造方法制造出的镀覆网，由于锌镀层、锌镍层、多元金属层中均不含铅，不仅对环境友好，同时，由于锌镀层、锌镍层、多元金属层的存在，钢网的耐腐蚀性能得到显著提高。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案：
实施例1
提出一种镀层中不含铅的镀覆网的制造方法，包括如下步骤：
Ｓ11、提供金属。
Ｓ12、在所述金属上镀覆锌镀层。
Ｓ13、在所述锌镀层上镀覆锌镍层。
其中，所述锌镍层中包含（按重量计算）0.025～0.05％的镍。
Ｓ14、在所述锌镍层表面镀覆多元金属层。
其中，所述多元金属层包含（按重量计算）镍：0.025～0.04％；铬：0．01～0.025％；余量的锌。
实施例2
Ｓ21、提供钢网。
Ｓ22、在钢网上镀覆锌镀层。
Ｓ23、在锌镀层上镀覆锌镍层。
其中，锌镍层中包含重量比为0.04％的镍。
Ｓ24、在所述锌镍层表面镀覆多元金属层。
其中，多元金属层包含（按重量计算）镍：0.025％；铬：0.025％；余量的锌。
在本发明中，锌镀层、锌镍层、多元金属层中均不含铅，对环境友好，同时，由于锌镀层、锌镍层、多元金属层的存在，钢网的耐腐蚀性能得到显著提高。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (4)

1.一种镀层中不含铅的镀覆网的制造方法，其特征在于，包括如下步骤：
提供金属；
在所述金属上镀覆锌镀层；
在所述锌镀层上镀覆锌镍层，其中，所述锌镍层中包含(按重量计算)0.025～0.05％的镍；
在所述锌镍层表面镀覆多元金属层，其中，所述多元金属层包含(按重量计算)镍：0.025～0.04％；铬：0.01～0.025％；余量的锌；
所述金属为钢。
2.根据权利要求1所述的镀层中不含铅的镀覆网的制造方法，其特征在于，所述金属为网状。
3.根据权利要求1所述的镀层中不含铅的镀覆网的制造方法，其特征在于，所述锌镍层中包含重量比为0.04％的镍。
4.根据权利要求1所述的镀层中不含铅的镀覆网的制造方法，其特征在于，所述多元金属层包含(按重量计算)镍：0.025％；铬：0.025％；余量的锌。
CN201210478898.4A 2012-11-22 2012-11-22 一种镀层中不含铅的镀覆网的制造方法 Active CN103088278B (zh)