CN100383206C - 胶带用离型涂层组成物 - Google Patents
胶带用离型涂层组成物 Download PDFInfo
- Publication number
- CN100383206C CN100383206C CNB2004100572079A CN200410057207A CN100383206C CN 100383206 C CN100383206 C CN 100383206C CN B2004100572079 A CNB2004100572079 A CN B2004100572079A CN 200410057207 A CN200410057207 A CN 200410057207A CN 100383206 C CN100383206 C CN 100383206C
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- release coating
- coating constituent
- tape according
- alkyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明是关于一种胶带用离型涂层组成物，此胶带用离型涂层组成物包括：(a)80～95重量份的丙烯酸烷基酯类单体，(b)5～10重量份的丙烯酸羟烷基酯类单体，(c)1～5重量份的不饱和羧酸单体，(d)0.1～3.0重量份的界面活性剂以及(e)5～20重量份的保护胶体。其中，(a)、(b)及(c)合计为100重量份，而(d)与(e)的重量份是相对于总和为100重量份的(a)、(b)及(c)的来计算。
Description
技术领域
本发明涉及一种胶带用的离型涂层组成物，特别是涉及一种环保的胶带用离型涂层组成物。
背景技术
在日常生活中，胶带常用以粘合或固定物体，而因应不同的用途，市面上有许多不同种类的胶带。其中遮蔽胶带(masking tape)又称美纹胶带(crepe tape)，已在工业上被广泛地使用，例如，在汽车工业中进行钣金喷漆、烤漆时，使用美纹胶带可以遮蔽其他不需喷漆或烤漆的车体部份。在电子业中亦使用美纹胶带以进行电子元件(如电阻、电容)接脚的贴合，以便于电子元件的运输及自动化操作。
此外，为了使美纹胶带操作方便，除了在胶带基材底面涂覆有粘胶层外，往往还会在胶带的表面涂上一层离型涂层(release coating)，使其具有适当的剥离力(release force)。且因为美纹胶带的操作环境常常需曝露在高温及含有挥发性溶剂中，所以胶带表面上的离型涂层需具备耐溶剂性、耐高温及耐老化等特性，尤其是在胶带的耐老化特性方面。此外，若离型涂层成份转移(migration)至胶带底面的粘胶层的表面上，将会造成胶带的剥离力变高以及粘着力衰退等现象，而此现象会影响到胶带的品质与使用寿命。所以，美纹胶带的需求为在长时间高温以及高湿度的环境下，其胶带表面上的离型涂层成份不会转移(migration)到胶带底面的粘胶层的表面上。
现有习知的涂覆于美纹胶带表面的离型涂层，大都是由压克力单体(丙烯酸酯树脂)经聚合反应而组成的组成物，且为使其达到耐溶剂性，通常还会加入丙烯腈(acrylonitrile)单体参与反应。然而，此单体为具有毒性的管制品，使用其单体不仅会增加制程中的处理费用，且亦有害于人体健康与生态环境。
由此可见，上述现有的胶带用离型涂层组成物在使用上，显然仍存在有不便与缺陷，而亟待加以进一步改进。为了解决胶带用离型涂层组成物存在的问题，相关厂商莫不费尽心思来谋求解决之道，但长久以来一直未见适用的设计被发展完成，而一般产品又不能够解决上述问题，此显然是相关业者急欲解决的问题。
有鉴于上述现有的胶带用离型涂层组成物存在的缺陷，本发明人基于从事此类产品设计制造多年丰富的实务经验及专业知识，并配合学理的运用，积极加以研究创新，以期创设一种新型的胶带用离型涂层组成物，能够改进一般现有的胶带用离型涂层组成物，使其更具有实用性。经过不断的研究、设计，并经反复试作样品及改进后，终于创设出确具实用价值的本发明。
发明内容
本发明的目的在于，克服现有的胶带用离型涂层组成物存在的缺陷，而提供一种新的胶带用离型涂层组成物，所要解决的技术问题是使其可以解决现有习知的离型涂层组成物中含有有毒化学品的问题，并且此离型涂层组成物亦同时具有耐溶剂、耐高温及耐老化等特性，从而更加适于实用。
本发明的目的及解决其技术问题是采用以下技术方案来实现的。依据本发明提出的一种胶带用离型涂层组成物，其特征在于其包括：(a)80～95重量份(part per hundred，phr)的丙烯酸烷基酯类单体；(b)5～10重量份的丙烯酸羟烷基酯类单体；(c)1～5重量份的不饱和羧酸单体(unsaturated carboxylic acids)；(d)0.1～3.0重量份的界面活性剂(surfactant)；以及(e)5～20重量份的保护胶体，其中(a)、(b)及(c)合计为100重量份，而(d)与(e)的重量份是相对于总和为100重量份的(a)、(b)及(c)来计算。
本发明的目的及解决其技术问题还可采用以下技术措施进一步实现。
前述的胶带用离型涂层组成物，其中所述的丙烯酸烷基酯类单体的烷基含1～20个碳原子。
前述的胶带用离型涂层组成物，其中所述的丙烯酸烷基酯类单体的烷基含1～10个碳原子。
前述的胶带用离型涂层组成物，其中所述的丙烯酸烷基酯类单体包括丙烯酸烷基酯(alkyl acrylates)单体或甲基丙烯酸烷基酯(alkylmethacrylates)单体。
前述的胶带用离型涂层组成物，其中所述的丙烯酸烷基酯单体包括丙烯酸乙酯(ethyl acrylate)、丙烯酸丁酯(n-butyl acrylate)、丙烯酸-2乙基己酯(2-ethylhexyl acrylate)或丙烯酸癸酯(decyl acrylate)。
前述的胶带用离型涂层组成物，其中所述的甲基丙烯酸烷基酯单体包括甲基丙烯酸甲酯(methyl methacrylate，MMA)或甲基丙烯酸丁酯(butylmethacrylate)。
前述的胶带用离型涂层组成物，其中所述的丙烯酸羟烷基酯类单体的烷基含1～10个碳原子。
前述的胶带用离型涂层组成物，其中所述的丙烯酸羟烷基酯类单体的烷基含1～5个碳原子。
前述的胶带用离型涂层组成物，其中所述的丙烯酸羟烷基酯类单体包括丙烯酸羟烷基酯(hydroxy alkyl acrylates)单体或甲基丙烯酸羟烷基酯(hydroxy alkyl methacrylates)单体。
前述的胶带用离型涂层组成物，其中所述的丙烯酸羟烷基酯单体包括丙烯酸羟乙基酯(hydroxy ethyl acrylate)或丙烯酸羟丙基酯(hydroxypropyl acrylate)。
前述的胶带用离型涂层组成物，其中所述的甲基丙烯酸羟烷基酯单体包括甲基丙烯酸羟乙基酯(hydroxy ethyl methacrylate)或甲基丙烯酸羟丙基酯(hydroxy propyl methacrylate)。
前述的胶带用离型涂层组成物，其中所述的不饱和羧酸单体包括甲基丙烯酸(methacrylic acid，MAA)、丙烯酸(acrylate acid)、衣康酸(itaconic acid)、顺式丁烯二酸(maleic acid)或反式丁烯二酸(allomaleic acid)。
前述的胶带用离型涂层组成物，其中所述的界面活性剂是选自一非离子界面活性剂与一阴离子界面活性剂所组成的族群。
前述的胶带用离型涂层组成物，当该(a)、(b)及(c)的总和为100重量份时，该非离子界面活性剂的使用量为0.1～1.0重量份。
前述的胶带用离型涂层组成物，其中所述的非离子界面活性剂包括聚氧乙烯壬基苯基醚(polyoxethyene nonyl phenyl ether)、聚氧乙烯辛基苯基醚、聚乙二醇烷基酚醚、脂肪酸山梨酯或聚乙二醇脂肪酸山梨酯。
前述的胶带用离型涂层组成物，当该(a)、(b)及(c)的总和为100重量份时，该阴离子界面活性剂的使用量为0.4～3.0重量份。
前述的胶带用离型涂层组成物，其中所述的阴离子界面活性剂包括十二烷基苯磺酸钠(sodium dodecyl benzene sulphonate)、十二烷基磺酸钠(sodium dodecyl sulfonate)、磺酸基-十二烷苯基醚二钠、磺酸基琥珀酸-n-十八酯二钠或聚氧乙烯壬基苯基醚硫酸胺(ammonium polyoxethyenenonyl phenyl ether sulfate)。
前述的胶带用离型涂层组成物，其中所述的保护胶体包括聚乙烯醇(polyvinyl alcohol，PVA)或卵磷脂(lecithin)。
前述的胶带用离型涂层组成物，其更包括一交联剂(cross-linker)。
前述的胶带用离型涂层组成物，当该(a)、(b)及(c)的总和为100重量份时，该交联剂的使用量为0.1～5.0重量份。
前述的胶带用离型涂层组成物，其中所述的交联剂包括金属螯合剂(metal chelating agent)、缩水甘油基甲基丙烯酸酯(glycidylmethacrylate)、硅烷(silane)、丙烯基酰胺(acrylamide)或羟甲基丙烯基酰胺(methylol acrylamide)。
前述的胶带用离型涂层组成物，其更包括一引发剂(initiator)。
前述的胶带用离型涂层组成物，当该(a)、(b)及(c)的总和为100重量份时，该引发剂的使用量为0.1～2.0重量份。
前述的胶带用离型涂层组成物，其中所述的引发剂包括过硫酸钠、过硫酸铵或过硫酸钾。
前述的胶带用离型涂层组成物，其更包括一缓冲剂(buffer)。
前述的胶带用离型涂层组成物，当该(a)、(b)及(c)的总和为100重量份时，该缓冲剂的使用量为0.1～0.5重量份。
前述的胶带用离型涂层组成物，其中所述的缓冲剂包括碳酸氢钠(sodium bicarbonate)或醋酸钠(sodium acetate)。
前述的胶带用离型涂层组成物，其中所述的胶带用离型涂层组成物为乳液状，且乳液中的粒子的平均粒径是介于0.1至0.5微米。
前述的胶带用离型涂层组成物，其中所述的胶带用离型涂层组成物的玻璃转化温度(Tg)是介于摄氏0至70度。
前述的胶带用离型涂层组成物，其中所述的胶带用离型涂层组成物的固体成分是介于20至60重量百分比。
前述的胶带用离型涂层组成物，其适用于美纹胶带(crepe tape)、聚丙烯膜胶带、玛拉胶带、保护胶带或双面胶带等。
借由上述技术方案，本发明胶带用离型涂层组成物至少具有下列优点：
1、本发明胶带用离型涂层组成物以丙烯酸羟烷基酯类单体替代丙烯腈单体参与反应，因此可以避免对人体健康与生态环境造成影响。
2、此外，藉由上述特举的实验例与比较例可知，本发明胶带用离型涂层组成物具有耐溶剂性、耐高温以及耐老化等特性。
3、本发明胶带用离型涂层组成物可以适用于各种不同的胶带例如是美纹胶带、聚丙烯膜胶带、玛拉胶带、保护胶带或双面胶带等，当然本发明的胶带用离型涂层组成物亦可应用于其他合适的物体上，而不仅限于胶带的应用。
综上所述，本发明提供一种胶带用离型涂层组成物，而可解决现有习知的离型涂层组成物中含有有毒化学品的问题，并且此离型涂层组成物亦同时具有耐溶剂、耐高温及耐老化等特性。其具有上述诸多的优点及实用价值，并在同类产品中未见有类似的产品公开发表或使用而确属创新，其在功能上有较大的改进，在技术上有较大的进步，并产生了好用及实用的效果，且较现有的胶带用离型涂层组成物具有增进的多项功效，从而更加适于实用，诚为一新颖、进步、实用的新设计。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，而可依照说明书的内容予以实施，并且为了让本发明的上述和其他目的、特征和优点能更明显易懂，以下特举多个较佳实验例，详细说明如下。
具体实施方式
为更进一步阐述本发明为达成预定发明目的所采取的技术手段及功效，以下结合较佳实验例，对依据本发明提出的胶带用离型涂层组成物其具体实施方式、特征及其功效，详细说明如后。
本发明提供了一种对人体健康、生态环境有益，同时具有耐溶剂、耐高温及耐老化的胶带用离型涂层组成物，其是以乳化聚合方法制成的，而其组成包括(a)80～95重量份的丙烯酸烷基酯类单体，(b)5～10重量份的丙烯酸羟烷基酯类单体，(c)1～5重量份的不饱和羧酸单体，(d)0.1～3.0重量份的界面活性剂以及(e)5～20重量份的保护胶体。其中，(a)、(b)及(c)合计为100重量份，而(d)与(e)的重量份是相对于总和为100重量份的(a)、(b)及(c)的来计算。
其中，上述的(a)丙烯酸烷基酯类单体较佳是包含1～20个碳原子的烷基，而更佳的是含有1～10个碳原子的烷基。在又一更佳实验例中，丙烯酸烷基酯类单体例如是丙烯酸烷基酯单体或甲基丙烯酸烷基酯单体。其中，丙烯酸烷基酯单体例如是丙烯酸乙酯、丙烯酸丁酯、丙烯酸-2乙基己酯或丙烯酸癸酯，而甲基丙烯酸烷基酯单体例如是甲基丙烯酸甲酯或甲基丙烯酸丁酯。
此外，上述的(b)丙烯酸羟烷基酯类单体较佳是含1～10个碳原子的烷基，而更佳是含1～5个碳原子的烷基。在又一更佳实验例中，丙烯酸羟烷基酯类单体例如是丙烯酸羟烷基酯单体或甲基丙烯酸羟烷基酯单体。其中，丙烯酸羟烷基酯单体例如是丙烯酸羟乙基酯或丙烯酸羟丙基酯，而甲基丙烯酸羟烷基酯单体例如是甲基丙烯酸羟乙基酯或甲基丙烯酸羟丙基酯。
另外，上述的(c)不饱和羧酸单体例如可以是甲基丙烯酸、丙烯酸、衣康酸、顺式丁烯二酸或反式丁烯二酸。
此外，上述的(d)界面活性剂是选自非离子界面活性剂与阴离子界面活性剂所组成的族群，而其作用为在进行乳化聚合反应时，可使反应达到乳化安定性以及可使最终产物具有优异的耐溶剂及耐老化特性。在一较佳实验例中，当(a)、(b)及(c)的总和为100重量份时，非离子界面活性剂的使用量例如是0.1～1.0phr。而非离子界面活性剂例如可以是聚氧乙烯壬基苯基醚、聚氧乙烯辛基苯基醚、聚乙二醇烷基酚醚、脂肪酸山梨酯或聚乙二醇脂肪酸山梨酯。另外，在又一较佳实验例中，当(a)、(b)及(c)的总和为100重量份时，阴离子界面活性剂的使用量例如是0.4～3.0phr。而阴离子界面活性剂例如是十二烷基苯磺酸钠、十二烷基磺酸钠、磺酸基-十二烷苯基醚二钠、磺酸基琥珀酸-n-十八酯二钠或聚氧乙烯壬基苯基醚硫酸铵。
另外，上述(e)保护胶体的使用量是相对于总合为100重量份的(a)、(b)及(c)来计算的，而保护胶体可例如是聚乙烯醇(polyvinyl alcohol，PVA)或卵磷脂(lecithin)。
除此之外，本发明离型涂层组成物更佳地是可包括至少一个以上的交联剂(cross-linker)、引发剂(initiator)、缓冲剂(buffer)及去离子水参与反应。在一较佳实验例中，当(a)、(b)及(c)的总和为100重量份时，则交联剂的使用量为0.1～1.0重量份，引发剂的使用量为0.1～2.0重量份，缓冲剂的使用量为0.1～0.5重量份。其中交联剂可例如是金属螯合剂、缩水甘油基甲基丙烯酸酯、硅烷、丙烯基酰胺或羟甲基丙烯基酰胺。而引发剂可例如是过硫酸钠、过硫酸铵或过硫酸钾，且缓冲剂可例如是碳酸氢钠或醋酸钠。
本发明是在反应槽中进行乳化聚合反应，其为将上述离型涂层组成物(a)、(b)及(c)三种单体与(d)及(e)在反应槽中混合，并且添加适量的引发剂、交联剂、缓冲剂以及去离子水在反应槽中一起参与反应。然后，对反应槽进行升温加热以开始进行反应，其中，反应槽的温度例如是介于50～90℃之间，而反应时间例如是5～10小时。接着，在反应完成后，可在反应槽中得到乳化溶液，其即为本发明的离型涂层组合物。
特别是，藉由上述方法所得的本发明的离型涂层组成物中乳液的粒子的平均粒径例如是介于0.1～0.5微米(μm)，而玻璃转移温度(Tg)例如是介于摄氏0至70度，而固体成份例如是介于20至60重量百分比。
以下，特举数个实验例与比较例说明本发明，然非用以限定本发明。
[实验例1]
首先，将80g的去离子水与3.0g的聚氧乙烯壬基苯基醚及3.0g的聚氧乙烯壬基苯基醚硫酸铵均匀搅拌制备成A溶液。
另取67.5g的丙烯酸丁酯单体、60.0g甲基丙烯酸甲酯单体、15.0g甲基丙烯酸羟乙基酯单体与4.5g的甲基丙烯酸单体均匀搅拌制备成B溶液。
再另取300g的去离子水及22.5g的卵磷脂均匀搅拌制备成C溶液。
又另取37.4g的去离子水、1.5g的过硫酸钾及0.8g的碳酸氢钠均匀搅拌制备成D溶液。
然后，将A溶液及B溶液倒入预乳化槽中，并快速搅拌以制备成预乳化液(pre-emulsion)。
接着，将C溶液及D溶液倒入反应槽中。其中该反应槽设备是由搅拌器、温度计、加热器、回流冷凝管、五颈瓶盖及一公升容量的圆底瓶所组成的。
之后，使用加热器对反应槽进行加热。当反应槽内溶液温度升至摄氏70～75时，将10％的预乳化溶液滴入反应槽中以进行反应，且在进行此反应时，需在20-30分钟内将预乳化溶液喂入(慢慢滴入)完毕且此时反应槽内的温度需维持在70～75℃。
接着，再将反应槽内的温度升温至80～85℃，并维持此温度，然后将其余90％的预乳化溶液在240分钟喂入完毕。之后，维持反应条件在约90分钟后，将反应槽冷却至室温。而反应槽内所得的乳胶即为本发明的离型涂层组合物。
[实验例2]
实验例2中的成分与反应步骤皆与实验1相同，二者的差异仅为实验例2是在上述实验例1的B溶液中加入羟甲基丙烯基酰胺以参与反应。亦即是实验例2的B溶液中包括67.5g的丙烯酸丁酯单体、60.0g的甲基丙烯酸甲酯单体、15.0g甲基丙烯酸羟乙基酯单体、4.5g的甲基丙烯酸单体与3.0g羟甲基丙烯基酰胺。
[比较例]
比较例是依照实验例1的方法进行，但其中在配制C溶液时，比较例不使用卵磷脂(保护胶体)以参与反应。
上述的实验例1、实验例2与比较例中所得的离型涂层组合物为乳化溶液，其乳化溶液中的乳胶粒子会因组成物或实验条件不同而具有不同的高分子物性。因此是藉由下述的测试方法来了解其物性，其中测试方法包括固体成份测试、粘度测试、T形剥离力测试、钢板粘着力测试、耐溶剂测试以及耐高温测试。
其中，上述的固体成份测试的方法为取一称盘并记录此称盘重量(此重量值以a表示)。另取适量的实验例所得的产物(此重量值以b表示)置于称盘中。然后，将称盘移置烘箱内，并设定烘箱的温度为150℃，并使其烘烤时间为1小时。之后，将称盘取出并称其重量(此重量值以c表示)。接着利用下述公式即可计算出固体成份。
固体成份(％)＝{(c-a)/b}×100
此外，上述的粘度测试的方法是使用Brook field粘度计以测粘度，其测试条件为用4号转速棒(Spindle)，并且设定转速为30rpm，在25℃下进行。而所得粘度的结果，以cps(centi poise)来表示。
另外，上述的T形(T-Peel)剥离力测试的方法为先利用CM35美纹胶带(四维公司产品)以贴合本发明的离型涂层试片。然后再使用2kgw的辊轮在试片进行来回一次压辊。接着，将试片置于条件设定为23℃、65％相对湿度的环境中3天。之后，截取宽度25mm，长度150mm的试片，解开胶带的离型涂层试片长约50mm夹在下夹头，并将CM35美纹胶带夹在上夹头，以300mm/min的速度连续剥离，剥离期间离型涂层与CM35美纹胶带维持T字形，并观察其荷重，单位为g/25mm。
此外，上述的钢板粘着力测试是依照ASTM D-1000标准为测试方法，而ASTM D-1000即为美国材料与检验协会于1999年发布的电气和电子设备用压敏粘结涂覆带的试验方式。
另外，上述的耐溶剂测试为取一试片，该试片尺寸为宽度25mm，长度100mm，将试片浸入甲苯溶剂30分钟后，再取出试片并置于100℃的环境中10分钟，随后将试片取出并使其冷却至室温后，观察离型涂层是否被溶掉。
此外，上述的耐高温测试为取一试片，该试片尺寸为宽度25mm，长度100mm，然后，将试片置放在150℃烘箱中1小时后，再取出试片并以离型涂层面对搓6次，观察其是否脱弱或脆化。
本发明的实验例1、实验例2和比较例的离型涂层组合物依上述的测试方法进行后，其测试结果列在下表1中。其中上述测试中所使用的试片的制造方法为以64g美纹纸做为基材，并将适量的离型涂层组成物涂布在基材上形成的。离型涂层组成物的涂布量为将适量的离型涂层组成物涂布在基材，并置于温度设定为135℃的烘箱中烘烤5分钟后其干量为10±2g/m2即可。
表1
○：表示可达标准
由上述表1可知，实验例1与实验例2的固成份为30％，而实验例1的粘度为12cps，实验例2的粘度为25cps。另外，在上述的实验例2中加入交联剂参与反应可调整离型涂层组合物的粘度，并使其较实验例1的黏度略高。
另外，本发明的实验例1、实验例2和比较例的离型涂层组合物经老化后，分别依前述测试方法进行测试，其结果列于是表2中。老化条件为将离型涂层组合物置于烘箱中3天，烘箱的设定条件为65℃及80％相对湿度，之后再将其取出并置于条件设定为23℃、65％相对湿度的烘箱中1个小时。
表2
○：表示可达标准
由上述表1及表2的数据显示，实验例1与实验例2的离型涂层组合物经由室温测试后，可发现其T形剥离力及钢板粘着力二者测试的物性皆为稳定，且其离型涂层组合物经老化后所做的测试数据与未经老化的测试数据比较，也无明显上升或下降的趋势，其表示实验例1与实验例2的离型涂层组合物皆具有耐老化性质。另外，由测试结果可知实验例1与实验例2的离型涂层组合物皆保有其耐溶剂及耐热性。
因此，在胶带的一面上胶，而另一面以本发明离型涂层组成物处理，除了在制作中可免除环境污染的问题外，同时所制作出来的胶带也可具有耐溶剂性、耐高温以及耐老化等特性。且本发明的离型涂层组成物可适用于各种不同的胶带例如是美纹胶带、聚丙烯膜胶带、玛拉胶带、保护胶带或双面胶带等。
另外，以下是对实验例1、实验例2和比较例的离型涂层组成物做了实用性的比较，包括试验组与对照组的比较。试验组为美纹胶带基材一面涂胶，另一面涂上实验例1、2或比较例所得的离型涂层组成物，而对照组为美纹胶带基材一面涂胶，另一面不做处理(即未涂离型涂层组成物)。而比较的结果为试验组中比较例的离型涂层组成物在制程后，其T型剥离力太高，且经老化处理后其T型剥离力上升太高，因此不符合使用标准。另外，对照组是分别在室温及经过老化条件下做比较，结果为T形剥离力皆太高，而无法剥离。所以，由此实用性的比较可知实验例1与实验例2的涂离型涂层组成物皆可适用于使用标准。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (30)
1.一种胶带用离型涂层组成物，其特征在于其包括：
(a)80～95重量份的丙烯酸烷基酯类单体；
(b)5～10重量份的丙烯酸羟烷基酯类单体；
(c)1～5重量份的不饱和羧酸单体；
(d)0.1～3.0重量份的界面活性剂；以及
(e)5～20重量份的卵磷脂，
其中(a)、(b)及(c)合计为100重量份，而(d)与(e)的重量份是相对于总和为100重量份的(a)、(b)及(c)来计算。
2.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸烷基酯类单体的烷基含1～20个碳原子。
3.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸烷基酯类单体的烷基含1～10个碳原子。
4.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸烷基酯类单体包括丙烯酸烷基酯单体或甲基丙烯酸烷基酯单体。
5.根据权利要求4所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸烷基酯单体包括丙烯酸乙酯、丙烯酸丁酯、丙烯酸-2乙基己酯或丙烯酸癸酯。
6.根据权利要求4所述的胶带用离型涂层组成物，其特征在于其中所述的甲基丙烯酸烷基酯单体包括甲基丙烯酸甲酯或甲基丙烯酸丁酯。
7.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸羟烷基酯类单体的烷基含1～10个碳原子。
8.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸羟烷基酯类单体的烷基含1～5个碳原子。
9.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸羟烷基酯类单体包括丙烯酸羟烷基酯单体或甲基丙烯酸羟烷基酯单体。
10.根据权利要求9所述的胶带用离型涂层组成物，其特征在于其中所述的丙烯酸羟烷基酯单体包括丙烯酸羟乙基酯或丙烯酸羟丙基酯。
11.根据权利要求9所述的胶带用离型涂层组成物，其特征在于其中所述的甲基丙烯酸羟烷基酯单体包括甲基丙烯酸羟乙基酯或甲基丙烯酸羟丙基酯。
12.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的不饱和羧酸单体包括甲基丙烯酸、丙烯酸、衣康酸、顺式丁烯二酸或反式丁烯二酸。
13.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的界面活性剂是选自一非离子界面活性剂与一阴离子界面活性剂所组成的族群。
14.根据权利要求13所述的胶带用离型涂层组成物，其特征在于当该(a)、(b)及(c)的总和为100重量份时，该非离子界面活性剂的使用量为0.1～1.0重量份。
15.根据权利要求13所述的胶带用离型涂层组成物，其特征在于其中所述的非离子界面活性剂包括聚氧乙烯壬基苯基醚、聚氧乙烯辛基苯基醚、聚乙二醇烷基酚醚、脂肪酸山梨酯或聚乙二醇脂肪酸山梨酯。
16.根据权利要求13所述的胶带用离型涂层组成物，其特征在于当该(a)、(b)及(c)的总和为100重量份时，该阴离子界面活性剂的使用量为0.4～3.0重量份。
17.根据权利要求13所述的胶带用离型涂层组成物，其特征在于其中所述的阴离子界面活性剂包括十二烷基苯磺酸钠、十二烷基磺酸钠、磺酸基-十二烷苯基醚二钠、磺酸基琥珀酸-n-十八酯二钠或聚氧乙烯壬基苯基醚硫酸铵。
18.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其更包括一交联剂。
19.根据权利要求18所述的胶带用离型涂层组成物，其特征在于其中当该(a)、(b)及(c)的总和为100重量份时，该交联剂的使用量为0.1～5.0重量份。
20.根据权利要求18所述的胶带用离型涂层组成物，其特征在于其中所述的交联剂包括金属螯合剂、缩水甘油基甲基丙烯酸酯、硅烷、丙烯基酰胺或羟甲基丙烯基酰胺。
21.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其更包括一引发剂。
22.根据权利要求21所述的胶带用离型涂层组成物，其特征在于当该(a)、(b)及(c)的总和为100重量份时，该引发剂的使用量为0.1～2.0重量份。
23.根据权利要求21所述的胶带用离型涂层组成物，其特征在于其中所述的引发剂包括过硫酸钠、过硫酸铵或过硫酸钾。
24.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其更包括一缓冲剂。
25.根据权利要求24所述的胶带用离型涂层组成物，其特征在于当该(a)、(b)及(c)的总和为100重量份时，该缓冲剂的使用量为0.1～0.5重量份。
26.根据权利要求24所述的胶带用离型涂层组成物，其特征在于其中所述的缓冲剂包括碳酸氢钠或醋酸钠。
27.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的胶带用离型涂层组成物为乳液状，且乳液中的粒子的平均粒径是介于0.1至0.5微米。
28.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的胶带用离型涂层组成物的玻璃转化温度是介于摄氏0至70度。
29.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其中所述的胶带用离型涂层组成物的固体成分是介于20至60重量百分比。
30.根据权利要求1所述的胶带用离型涂层组成物，其特征在于其适用于美纹胶带、聚丙烯膜胶带、玛拉胶带或双面胶带。