CN100376626C - 一种香味抗菌降解聚烯烃组合物及其制造方法及用途 - Google Patents
一种香味抗菌降解聚烯烃组合物及其制造方法及用途 Download PDFInfo
- Publication number
- CN100376626C CN100376626C CNB02136687XA CN02136687A CN100376626C CN 100376626 C CN100376626 C CN 100376626C CN B02136687X A CNB02136687X A CN B02136687XA CN 02136687 A CN02136687 A CN 02136687A CN 100376626 C CN100376626 C CN 100376626C
- Authority
- CN
- China
- Prior art keywords
- perfume
- agent
- antibacteria
- degradation
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种香味抗菌降解聚烯烃组合物及其制造方法及用途，该组合物包括以下组分与含量(重量份)：聚烯烃20～80份，生物降解料20～80份，抗菌剂0.3～8份，香味剂1～9份，分散剂3～5份，偶联剂3～5份，交联剂0.5～3份；该组合物的制造方法包括香味抗菌降解聚烯烃母料的制备及组合物的制备等工艺步骤；该组合物可用于制作各种保鲜膜、保鲜袋等膜制品以及一次性餐具、无纺布等。与现有技术相比，本发明方法简单、工艺合理，产品具有可持续飘香、抗菌及可降解等特点。
Description
技术领域
本发明涉及功能性化学组合物及其制造方法及用途，尤其涉及一种香味抗菌降解聚烯烃组合物及其制造方法及用途。
背景技术
随着科学技术的不断发展，聚合物塑料的应用越来越广泛，尤其是一次性使用的日用品领域，如一次性饭盒、食品袋、保鲜膜等等，一般用量都很大，然而，环保问题也越来越突出。因此，市场上出现了可降解一次性饭盒、塑料袋等产品，但是，由于配方及工艺方面的原因，这种可降解产品不是降解率很低，就是产品强度不够，在实际应用时受到很大限制。此外，随着人们生活水平的提高，人们对一次性塑料产品的抗菌功能和香味都有需求，但这类产品极少，除了有少量抗菌塑料问世以外，在一次性使用的可降解塑料中同时具有抗菌和可持续飘香功能的产品尚未见报导。
发明内容
本发明的目的就是为了克服上述现有技术存在缺陷而提供一种可持续飘香、具有抗菌及可降解功能的聚烯烃组合物及其制造方法及用途。
本发明的目的可以通过以下技术方案来实现：
一种香味抗菌降解聚烯烃组合物，其特征在于，该组合物包括以下组分与含量(重量份)：
聚烯烃 20～80份
生物降解料 20～80份
抗菌剂 0.3～8份
香味剂 1～9份
分散剂 3～5份
偶联剂 3～5份
交联剂 0.5～3份
所述的聚烯烃选自高密度聚乙烯(HDPE)、线性低密度聚乙烯(LLDPE)、低密度聚乙烯(LDPE)、茂金属聚乙烯(MPE)、聚丙烯(PP)、聚苯乙烯(PS)、乙烯醋酸乙烯共聚物(EVA)中的一种，所述的生物降解料选自覆羟改性变性淀粉(变性淀粉SMA)、丙烯腈接枝变性淀粉、丙烯酸酯接枝变性淀粉、甲基丙烯酸酯接枝变性淀粉、苯乙烯接枝变性淀粉、玉米糊精、生态利(Starate)中的一种或几种，所述的抗菌剂选自沸石、磷酸复盐、托勃莫来石、碘伏、百里酚、双胍类、醇类、酰基苯胺类、咪唑、吡啶、噻唑、异噻唑酮中的一种或几种，所述的香味剂选自乙酸乙酯、风梨醛、玫瑰醛、丁酸戊酯、柠檬醛、戊酸戊酯、丁香油、沉香醛、人造苦杏仁油十八醛中的一种或几种，所述的分散剂选自低分子聚乙烯蜡，所述的偶联剂选自钛酸酯类或硅烷类偶联剂，所述的交联剂选自过氧化二异丙苯。
该组合物还包括促降剂0.5～1.5重量份，该促降剂选自乙酰丙酮铁、二硫代氨基甲酸铁、二茂铁、市购低温热氧化促降剂中的一种或几种。
该组合物还包括助熔剂1～3重量份，该助熔剂选自硬脂酸、氧化聚乙烯中的一种。
该组合物还包括增塑剂0.5～3重量份，该增塑剂选自邻苯二甲酸酯、间苯二甲酸二辛酯、磷酸酯、油酸酯中的一种或几种。
一种香味抗菌降解聚烯烃组合物的制造方法，其特征在于，该方法包括以下工艺步骤：
(1).抗菌降解聚烯烃母料的制备
A.原料混合：首先将生物降解料20～80重量份、抗菌剂0.3～8重量份进行混合，并进行细化处理，使其粒度达到10μ以下，然后将该混合物加入另一高速混合机中，同时加入分散剂3～5重量份，偶联剂3～5重量份、交联剂0.5～3重量份进行高速混合，混合时间为15～20分钟，将该混合物冷却至常温，再加入聚烯烃5～20重量份进行混合，混合时间为10～15分钟，得到备料供造粒用；
B.挤出造粒：将上述备料用双螺杆挤出机或往复式螺杆挤出机挤出造粒，螺杆温度控制在130～210℃，得到抗菌降解聚烯烃母料；
(2).香味抗菌降解聚烯烃组合物的制备
将聚烯烃15～60重量份、香味剂1～9重量份加入上述抗菌降解聚烯烃母料中进行混合，混合温度为130～210℃，混合时间为10～20分钟，得到香味抗菌降解聚烯烃组合物。
所述的步骤(1)A中还可加入包括促降剂0.5～1.5重量份、助熔剂1～3重量份、增塑剂0.5～3重量份中的一种或几种。
所述的步骤(2)中的香味剂1～9重量份也可以提前在步骤(1)A中加入，该步骤(2)成为单纯的聚烯烃15～60重量份与母料混合。
一种香味抗菌降解聚烯烃组合物的用途，其特征在于，该组合物用于制作膜制品，包括保鲜膜、保鲜袋、食品包装袋、透气膜。
一种香味抗菌降解聚烯烃组合物的用途，其特征在于，该组合物用于制作餐具制品，包括餐盒、杯、刀、叉、食品托盘。
一种香味抗菌降解聚烯烃组合物的用途，其特征在于，该组合物用于制作无纺布制品，包括妇女用卫生巾、婴儿用尿布以及台布、围裙、内衣、内裤。
与现有技术相比，本发明很好地解决了生物降解料与聚烯烃的相容性问题，因此，制品致密性好，机械强度高，可满足各种制品的需要；且本发明组合物的生物降解料含量最高可达80％，因此，产品降解容易，其成本远远低于普通聚烯烃组合物。此外，本发明所使用的抗菌剂细度低，抗菌广谱，对包括金色葡萄球菌、白葡萄球菌、乙型链球菌、甲类链球菌、肺炎球菌、脑膜炎球菌、大肠杆菌、绿脓杆菌、痢痪志贺氏菌、伤寒杆菌、淋病球菌、白念珠菌等都有良好抑杀作用。本发明制得的组合物加入吹塑机、注塑机、压延机、浇注机等塑料加工机械，即可制作各种膜制品、餐具制品以及无纺布制品，包括保鲜膜、保鲜袋、食品包装袋、透气膜、餐盒、杯、刀、叉、食品托盘、妇女用卫生巾、婴儿用尿布以及台布、围裙、内衣、内裤等等。这些制品具有持久清香、增加了产品趣味性，提高了产品的附加值。
具体实施方式
下面将结合具体实施例对本发明作进一步说明：
| 实施例编号 | 1 | 2 | 3 | |
| 乙酸乙酯(公斤)风梨醛(公斤)玫瑰醛(公斤)沸石(公斤)磷酸复盐(公斤)托勃莫来石(公斤)变性淀粉SMA(公斤)丙烯腈接枝变性淀粉(公斤)市购生态利(公斤)乙酰丙酮铁(公斤)二硫代氨基甲酸铁(公斤)二茂铁(公斤) | 1598200.5 | 8524401 | 150.3801.5 | |
| 聚烯烃 | LDPE(公斤)PP(公斤)PS(公斤) | 80 | 60 | 20 |
| 低分子聚乙烯蜡(公斤)钛酸酯(公斤)硅烷(公斤)过氧化二异丙苯(公斤)硬脂酸(公斤)氧化聚乙烯(公斤)邻苯二甲酸酯(公斤)间苯二甲酸二辛酯(公斤)磷酸酯(公斤) | 330.510.2 | 44221 | 55333 | |
上述实施例1的制造方法如下：
一种香味抗菌降解聚乙烯组合物的制造方法，该方法包括以下工艺步骤：
(1).抗菌降解聚乙烯母料的制备
A.原料混合：首先将变性淀粉SMA80公斤、沸石8公斤进行混合，并进行细化处理，使其粒度达到10μ以下，然后将该混合物加入另一高速混合机中，同时加入低分子聚乙烯蜡3公斤，钛酸酯偶联剂3公斤、过氧化二异丙苯0.5公斤进行混合，混合时间为15～20分钟，将该混合物冷却至常温，再加入低密度聚乙烯20公斤混合10～15分钟，得到备料供造粒用；
B.挤出造粒：将上述备料用双螺杆挤出机或往复式螺杆挤出机挤出造粒，螺杆温度控制在130～210℃，得到抗菌降解聚乙烯母料；
(2).香味抗菌降解聚乙烯组合物的制备
将低密度聚乙烯60公斤、乙酸乙酯1公斤、风梨醛5公斤、玫瑰醛9公斤加入上述抗菌降解聚乙烯母料中进行混合，混合温度为130～210℃，混合时间为10～20分钟，得到香味抗菌降解聚乙烯组合物。所述的步骤(2)中的乙酸乙酯1公斤、风梨醛5公斤、玫瑰醛9公斤也可以提前在步骤(1)A中加入，该步骤(2)成为单纯的聚乙烯60公斤与母料混合。
上述方法制得的香味抗菌降解聚乙烯组合物可以用于制作膜制品，包括保鲜膜、保鲜袋、食品包装袋、透气膜等等。
上述实施例2的制造方法除了配料之外，其余与实施例1相同。所制得的香味抗菌降解聚丙烯组合物可以用于制作无纺布等一次性用品，包括妇女用卫生巾、婴儿用尿布以及台布、围裙、内衣、内裤等等。
上述实施例3的制造方法除了配料之外，其余与实施例1相同。所制得的香味抗菌降解聚苯乙烯组合物可以用于制作餐具，包括餐盒、杯、刀、叉、食品托盘等等。
上述实施例1、2、3的产品部分性能如下：
| 实施例编号 | 1 | 2 | 3 |
| 降解率(45天) | ＞20％ | ＞30％ | ＞40％ |
| 曝露空气中香味保持时间(月) | ＞3 | ＞3 | ＞3 |
| 杀菌率 | 90～100％ | 90～100％ | 90～100％ |
Claims (10)
1.一种香味抗菌降解聚烯烃组合物，其特征在于，该组合物包括以下组分与重量份：
聚烯烃 20～80份
生物降解料20～80份
抗菌剂 0.3～8份
香味剂 1～9份
分散剂 3～5份
偶联剂 3～5份
交联剂 0.5～3份
所述的聚烯烃选自高密度聚乙烯、线性低密度聚乙烯、低密度聚乙烯、茂金属聚乙烯、聚丙烯、聚苯乙烯、乙烯醋酸乙烯共聚物中的一种，所述的生物降解料选自覆羟改性变性淀粉、丙烯腈接枝变性淀粉、丙烯酸酯接枝变性淀粉、甲基丙烯酸酯接枝变性淀粉、苯乙烯接枝变性淀粉、玉米糊精、生态利中的一种或几种，所述的抗菌剂选自沸石、磷酸复盐、托勃莫来石、碘伏、百里酚、双胍类、醇类、酰基苯胺类、咪唑、吡啶、噻唑、异噻唑酮中的一种或几种，所述的香味剂选自乙酸乙酯、风梨醛、玫瑰醛、丁酸戊酯、柠檬醛、戊酸戊酯、丁香油、沉香醛、人造苦杏仁油十八醛中的一种或几种，所述的分散剂选自低分子聚乙烯蜡，所述的偶联剂选自钛酸酯类或硅烷类偶联剂，所述的交联剂选自过氧化二异丙苯。
2.根据权利要求1所述的一种香味抗菌降解聚烯烃组合物，其特征在于，该组合物还包括促降剂0.5～1.5重量份，该促降剂选自乙酰丙酮铁、二硫代氨基甲酸铁、二茂铁中的一种或几种。
3.根据权利要求1所述的一种香味抗菌降解聚烯烃组合物，其特征在于，该组合物还包括助熔剂1～3重量份，该助熔剂选自硬脂酸、氧化聚乙烯中的一种。
4.根据权利要求1所述的一种香味抗菌降解聚烯烃组合物，其特征在于，该组合物还包括增塑剂0.5～3重量份，该增塑剂选自邻苯二甲酸酯、间苯二甲酸二辛酯、磷酸酯、油酸酯中的一种或几种。
5.一种权利要求1所述的香味抗菌降解聚烯烃组合物的制造方法，其特征在于，该方法包括以下工艺步骤：
(1).抗菌降解聚烯烃母料的制备
A.原料混合：首先将生物降解料20～80重量份、抗菌剂0.3～8重量份进行混合，并进行细化处理，使其粒度达到10μ以下，然后将该混合物加入另一高速混合机中，同时加入分散剂3～5重量份，偶联剂3～5重量份、交联剂0.5～3重量份进行高速混合，混合时间为15～20分钟，将该混合物冷却至常温，再加入聚烯烃5～20重量份进行混合，混合时间为10～15分钟，得到备料供造粒用；
B.挤出造粒：将上述备料用双螺杆挤出机或往复式螺杆挤出机挤出造粒，螺杆温度控制在130～210℃，得到抗菌降解聚烯烃母料；
(2).香味抗菌降解聚烯烃组合物的制备
将聚烯烃15～60重量份、香味剂1～9重量份加入上述抗菌降解聚烯烃母料中进行混合，混合温度为130～210℃，混合时间为10～20分钟，得到香味抗菌降解聚烯烃组合物。
6.根据权利要求5所述的香味抗菌降解聚烯烃组合物的制造方法，其特征在于，所述的步骤(1)A中还可加入包括促降剂0.5～1.5重量份、助熔剂1～3重量份、增塑剂0.5～3重量份中的一种或几种。
7.根据权利要求5所述的香味抗菌降解聚烯烃组合物的制造方法，其特征在于，所述的步骤(2)中的香味剂1～9重量份也可以提前在步骤(1)A中加入，该步骤(2)为单纯的聚烯烃15～60重量份与母料混合。
8.一种权利要求1所述的香味抗菌降解聚烯烃组合物的用途，其特征在于，该组合物用于制作膜制品，包括保鲜膜、保鲜袋、食品包装袋、透气膜。
9.一种权利要求1所述的香味抗菌降解聚烯烃组合物的用途，其特征在于，该组合物用于制作餐具制品，包括餐盒、杯、刀、叉、食品托盘。
10.一种权利要求1所述的香味抗菌降解聚烯烃组合物的用途，其特征在于，该组合物用于制作无纺布制品，包括妇女用卫生巾、婴儿用尿布以及台布、围裙、内衣、内裤。