CN100350114C - 一种轻质墙板 - Google Patents
一种轻质墙板 Download PDFInfo
- Publication number
- CN100350114C CN100350114C CNB2006100096620A CN200610009662A CN100350114C CN 100350114 C CN100350114 C CN 100350114C CN B2006100096620 A CNB2006100096620 A CN B2006100096620A CN 200610009662 A CN200610009662 A CN 200610009662A CN 100350114 C CN100350114 C CN 100350114C
- Authority
- CN
- China
- Prior art keywords
- parts
- slurry
- portions
- magnesium chloride
- lime
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种轻质墙板,所用原料按重量配比,配料为:粉煤灰30~40份、氧化镁15~25份、氯化镁10~20份、石灰或水泥3~10份、石膏5~15份、草木粉5~15份、玻璃丝1~5份;外加剂为:硫酸亚铁0.5~1.5份、草酸0.5~1.5份、磷酸三钠0.1~1份、六偏磷酸钠0.1~1份、聚醋酸乙烯1~2份;将氧化镁加水搅拌均匀,配制成波美度为18~25的溶液后,加入外加剂搅拌均匀,再加入粉煤灰、氯化镁、石灰或水泥、石膏、草木粉搅拌均匀制成浆料,向模具中铺装浆料,浆料铺至一半厚度时环形抛撒玻璃丝,再铺装浆料,捣实成型,脱模、干燥后而成。它具有强度高、不易变形、不翘曲、耐水性好、不反卤和造价低的优点。
Description
技术领域
本发明涉及一种轻质墙板。
背景技术
现楼房建筑中广泛使用轻质墙板,但现有轻质墙板存在或强度低,或易翘曲,或耐水性差,或易反卤,或造价高的缺点。
发明内容
本发明的目的是提供一种强度高、不易变形、不翘曲、耐水性好、不反卤和造价低的轻质墙板。
本发明的技术解决方案是:本发明所用原料由配料和外加剂组成,按重量配比,配料为:粉煤灰30~40份、氧化镁15~25份、氯化镁10~20份、石灰或水泥3~10份、石膏5~15份、草木粉5~15份、玻璃丝1~5份;外加剂为:硫酸亚铁0.5~1.5份、草酸0.5~1.5份、磷酸三钠0.1~1份、六偏磷酸钠0.1~1份、聚醋酸乙烯1~2份;将氧化镁加水搅拌均匀,配制成波美度为18~25的溶液后,加入外加剂搅拌均匀,再加入粉煤灰、氯化镁、石灰或水泥、石膏、草木粉搅拌均匀制成浆料,向模具中铺装浆料,浆料铺至一半厚度时环形抛撒玻璃丝,再铺装浆料,捣实成型,脱模、干燥后后而成。
本发明的技术效果是:它具有强度高、不易变形、不翘曲、耐水性好、不反卤和造价低的优点。
具体实施方式
按重量配比,将氧化镁15份加水搅拌均匀,配制成波美度为18~25的溶液后,加入硫酸亚铁1份、草酸1份、磷酸三钠0.5份、六偏磷酸钠0.5份、聚醋酸乙烯1.5份、搅拌均匀,再加入粉煤灰35份、氯化镁20份、石灰或水泥5份、石膏10份、锯末子10份搅拌均匀制成浆料,向模具中铺装浆料,浆料铺至5厘米厚时抛撒玻璃丝,再铺装5厘米厚浆料,捣实成型,脱模、干燥后后而成。
Claims (2)
1、一种轻质墙板,所用原料由配料和外加剂组成,其特征在于,按重量配比,配料为:粉煤灰30~40份、氧化镁15~25份、氯化镁10~20份、石灰或水泥3~10份、石膏5~15份、草木粉5~15份、玻璃丝1~5份;外加剂为:硫酸亚铁0.5~1.5份、草酸0.5~1.5份、磷酸三钠0.1~1份、六偏磷酸钠0.1~1份、聚醋酸乙烯1~2份;将氧化镁加水搅拌均匀,配制成波美度为18~25的溶液后,加入外加剂搅拌均匀,再加入粉煤灰、氯化镁、石灰或水泥、石膏、草木粉搅拌均匀制成浆料,向模具中铺装浆料,浆料铺至一半厚度时环形抛撒玻璃丝,再铺装浆料,捣实成型,脱模、干燥后而成。
2、如权利要求1所述的一种轻质墙板,其特征是,按重量配比,将氧化镁15份加水搅拌均匀,配制成波美度为18~25的溶液后,加入硫酸亚铁1份、草酸1份、磷酸三钠0.5份、六偏磷酸钠0.5份、聚醋酸乙烯1.5份、搅拌均匀,再加入粉煤灰35份、氯化镁20份、石灰或水泥5份、石膏10份、锯末子10份搅拌均匀制成浆料,向模具中铺装浆料,浆料铺至5厘米厚时抛撒玻璃丝,再铺装5厘米厚浆料,捣实成型,脱模、干燥后而成。