CA2972470C - Acier a deux phases a proprietes ameliorees - Google Patents

Acier a deux phases a proprietes ameliorees Download PDF

Info

Publication number
CA2972470C
CA2972470C CA2972470A CA2972470A CA2972470C CA 2972470 C CA2972470 C CA 2972470C CA 2972470 A CA2972470 A CA 2972470A CA 2972470 A CA2972470 A CA 2972470A CA 2972470 C CA2972470 C CA 2972470C
Authority
CA
Canada
Prior art keywords
steel sheet
temperature
tempera
molybdenum
carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CA2972470A
Other languages
English (en)
Other versions
CA2972470A1 (fr
Inventor
Grant Aaron Thomas
Jose Mauro Barros Losz
Luis Gonzalo Garza-Martinez
Eddie Ray Case
Eric Petersen
Prabhat Rastogi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cleveland Cliffs Steel Properties Inc
Original Assignee
AK Steel Properties Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AK Steel Properties Inc filed Critical AK Steel Properties Inc
Publication of CA2972470A1 publication Critical patent/CA2972470A1/fr
Application granted granted Critical
Publication of CA2972470C publication Critical patent/CA2972470C/fr
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Cette invention concerne un procédé de traitement d'une tôle d'acier à deux phases. Ledit procédé consiste à chauffer la tôle d'acier à une première température (Tl), refroidir la tôle d'acier à une seconde température (T2), faire passer la tôle d'acier à une troisième température (T3), et refroidir la tôle d'acier à la température ambiante. La température Tl est au moins supérieure à la température de transformation austénitique et ferritique de la tôle d'acier. La température T2 est supérieure à la température de début de transformation martensitique (Ms) La vitesse de refroidissement à la température T2 est suffisamment rapide pour transformer au moins une partie de l'austénite en martensite.
CA2972470A 2015-01-14 2016-01-14 Acier a deux phases a proprietes ameliorees Active CA2972470C (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201562103286P 2015-01-14 2015-01-14
US62/103,286 2015-01-14
PCT/US2016/013338 WO2016115303A2 (fr) 2015-01-14 2016-01-14 Acier à deux phases à propriétés améliorées

Publications (2)

Publication Number Publication Date
CA2972470A1 CA2972470A1 (fr) 2016-07-21
CA2972470C true CA2972470C (fr) 2019-10-22

Family

ID=55410188

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2972470A Active CA2972470C (fr) 2015-01-14 2016-01-14 Acier a deux phases a proprietes ameliorees

Country Status (15)

Country Link
US (1) US20160201159A1 (fr)
EP (1) EP3245310A2 (fr)
JP (1) JP2018508653A (fr)
KR (2) KR20170095363A (fr)
CN (2) CN107109586A (fr)
AU (1) AU2016206736B2 (fr)
BR (1) BR112017014686A2 (fr)
CA (1) CA2972470C (fr)
CO (1) CO2017006995A2 (fr)
MX (1) MX2017009192A (fr)
PH (1) PH12017501293A1 (fr)
RU (1) RU2017123566A (fr)
TW (2) TWI653342B (fr)
UA (1) UA119189C2 (fr)
WO (1) WO2016115303A2 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI628310B (zh) * 2017-08-08 2018-07-01 中國鋼鐵股份有限公司 High-strength lubricating galvanized steel sheet and manufacturing method thereof

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS56146853A (en) * 1980-04-11 1981-11-14 Nippon Steel Corp Dual-phase steel plate for car with superior weldability and high corrosion resistance
JP2761096B2 (ja) * 1990-11-05 1998-06-04 株式会社神戸製鋼所 高延性高強度合金化溶融亜鉛めっき鋼板の製造方法
JPH0693340A (ja) * 1992-09-14 1994-04-05 Kobe Steel Ltd 伸びフランジ性の優れた高強度合金化溶融亜鉛めっき鋼板の製造方法及び製造設備
JP3126911B2 (ja) * 1995-12-27 2001-01-22 川崎製鉄株式会社 めっき密着性の良好な高強度溶融亜鉛めっき鋼板
CN100471982C (zh) * 2002-11-26 2009-03-25 Uec科技有限责任公司 制造双相钢板的方法
JP4681290B2 (ja) * 2004-12-03 2011-05-11 本田技研工業株式会社 高強度鋼板及びその製造方法
US11155902B2 (en) * 2006-09-27 2021-10-26 Nucor Corporation High strength, hot dip coated, dual phase, steel sheet and method of manufacturing same
ES2387040T3 (es) * 2007-08-15 2012-09-12 Thyssenkrupp Steel Europe Ag Acero de doble fase, producto plano de un acero de doble fase de este tipo y procedimiento para la fabricación de un producto plano
EP2031081B1 (fr) * 2007-08-15 2011-07-13 ThyssenKrupp Steel Europe AG Acier en phase double, produit plat à partir d'un tel acier en phase double et son procédé de fabrication
EP2123786A1 (fr) * 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
JP5304522B2 (ja) * 2009-08-03 2013-10-02 新日鐵住金株式会社 加工性に優れた高強度鋼板及びその製造方法
KR100958019B1 (ko) * 2009-08-31 2010-05-17 현대하이스코 주식회사 복합조직강판 및 이를 제조하는 방법
CN102021482B (zh) * 2009-09-18 2013-06-19 宝山钢铁股份有限公司 一种冷轧热镀锌双相钢及其制造方法
BR112015027901B1 (pt) * 2013-05-17 2020-04-22 Ak Steel Properties Inc método para o processamento de uma placa de aço

Also Published As

Publication number Publication date
TW201812053A (zh) 2018-04-01
AU2016206736A1 (en) 2017-07-13
MX2017009192A (es) 2018-04-30
PH12017501293A1 (en) 2018-01-29
CO2017006995A2 (es) 2017-09-20
KR20200003264A (ko) 2020-01-08
TW201641715A (zh) 2016-12-01
CN107109586A (zh) 2017-08-29
BR112017014686A2 (pt) 2018-01-09
US20160201159A1 (en) 2016-07-14
JP2018508653A (ja) 2018-03-29
WO2016115303A2 (fr) 2016-07-21
TWI653342B (zh) 2019-03-11
EP3245310A2 (fr) 2017-11-22
CN110218942A (zh) 2019-09-10
KR20170095363A (ko) 2017-08-22
UA119189C2 (uk) 2019-05-10
RU2017123566A3 (fr) 2019-02-14
AU2016206736B2 (en) 2019-02-14
TWI605137B (zh) 2017-11-11
RU2017123566A (ru) 2019-02-14
CA2972470A1 (fr) 2016-07-21
WO2016115303A3 (fr) 2016-09-09

Similar Documents

Publication Publication Date Title
US11492676B2 (en) Method for producing a high strength coated steel sheet having improved strength, ductility and formability
JP6564963B1 (ja) 超高強度被覆または非被覆鋼板を製造する方法および得られる鋼板
CA3007647C (fr) Procede de production d'une tole d'acier a haute resistance presentant une resistance et une aptitude au formage ameliorees et tole d'acier a haute resistance ainsi obtenue
JP7033625B2 (ja) 強度、延性および成形性が改善された被覆鋼板の製造方法
JP6310452B2 (ja) 鋼、平鋼材及び平鋼材の製造方法
CA2954140C (fr) Procede permettant de produire une tole d'acier revetue a haute resistance presentant une resistance et une ductilite ameliorees, et tole ainsi obtenue
CA2954135C (fr) Procede de fabrication d'une tole d'acier a haute resistance et tole obtenue par le procede
US11718888B2 (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet
US11512362B2 (en) Method for producing an ultra high strength galvannealed steel sheet and obtained galvannealed steel sheet
JPH0693340A (ja) 伸びフランジ性の優れた高強度合金化溶融亜鉛めっき鋼板の製造方法及び製造設備
CA2972470C (fr) Acier a deux phases a proprietes ameliorees
CN113981300A (zh) 屈服强度330MPa级的冷轧搪瓷钢生产方法
JPH05311244A (ja) 伸びフランジ性の優れた高強度熱延原板合金化溶融亜鉛めっき鋼板の製造方法
JP2000119831A (ja) 成形性と耐食性に優れた高強度溶融亜鉛メッキ熱延鋼板及びその製造方法

Legal Events

Date Code Title Description
EEER Examination request

Effective date: 20170627