CA2680623C - Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree - Google Patents

Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree Download PDF

Info

Publication number
CA2680623C
CA2680623C CA2680623A CA2680623A CA2680623C CA 2680623 C CA2680623 C CA 2680623C CA 2680623 A CA2680623 A CA 2680623A CA 2680623 A CA2680623 A CA 2680623A CA 2680623 C CA2680623 C CA 2680623C
Authority
CA
Canada
Prior art keywords
steel
blank
equal
coating
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CA2680623A
Other languages
English (en)
French (fr)
Other versions
CA2680623A1 (fr
Inventor
Jean-Pierre Laurent
Thierry Malot
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal France SA
Original Assignee
ArcelorMittal France SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ArcelorMittal France SA filed Critical ArcelorMittal France SA
Publication of CA2680623A1 publication Critical patent/CA2680623A1/fr
Application granted granted Critical
Publication of CA2680623C publication Critical patent/CA2680623C/fr
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0478—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/68—Temporary coatings or embedding materials applied before or during heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y10T428/12757—Fe
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
CA2680623A 2007-03-14 2008-03-03 Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree Active CA2680623C (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
PCT/FR2007/000441 WO2008110670A1 (fr) 2007-03-14 2007-03-14 Acier pour formage a chaud ou trempe sous outil a ductilite amelioree
FRPCT/FR2007/000441 2007-03-14
PCT/FR2008/000278 WO2008132303A1 (fr) 2007-03-14 2008-03-03 Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree

Publications (2)

Publication Number Publication Date
CA2680623A1 CA2680623A1 (fr) 2008-11-06
CA2680623C true CA2680623C (fr) 2013-02-05

Family

ID=38799374

Family Applications (1)

Application Number Title Priority Date Filing Date
CA2680623A Active CA2680623C (fr) 2007-03-14 2008-03-03 Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree

Country Status (17)

Country Link
US (2) US8722203B2 (https=)
EP (1) EP2137327B1 (https=)
JP (1) JP5726419B2 (https=)
KR (5) KR101952525B1 (https=)
CN (1) CN101631880B (https=)
AR (1) AR065764A1 (https=)
AT (1) ATE556152T1 (https=)
BR (1) BRPI0809006B1 (https=)
CA (1) CA2680623C (https=)
ES (1) ES2387229T3 (https=)
MA (1) MA31235B1 (https=)
MX (1) MX2009009769A (https=)
PL (1) PL2137327T3 (https=)
RU (1) RU2423532C1 (https=)
UA (1) UA99127C2 (https=)
WO (2) WO2008110670A1 (https=)
ZA (1) ZA200905998B (https=)

Families Citing this family (57)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1767659A1 (fr) * 2005-09-21 2007-03-28 ARCELOR France Procédé de fabrication d'une pièce en acier de microstructure multi-phasée
DE102010004081C5 (de) * 2010-01-06 2016-11-03 Benteler Automobiltechnik Gmbh Verfahren zum Warmformen und Härten einer Platine
CN102251177A (zh) * 2011-07-12 2011-11-23 内蒙古包钢钢联股份有限公司 一种含稀土高强度钢板及其轧制方法
CN102230129A (zh) * 2011-07-12 2011-11-02 内蒙古包钢钢联股份有限公司 一种含稀土高强度钢板及其热处理工艺
WO2013014481A1 (fr) 2011-07-26 2013-01-31 Arcelormittal Investigación Y Desarrollo Sl Pièce d'acier soudée préalablement mise en forme à chaud à très haute résistance mécanique et procédé de fabrication
RU2562582C1 (ru) * 2011-08-09 2015-09-10 Ниппон Стил Энд Сумитомо Метал Корпорейшн Горячекатаный стальной лист с высоким отношением предела текучести к пределу прочности, который имеет превосходные характеристики поглощения энергии удара при низкой температуре и устойчивость к размягчению зоны термического влияния (haz), и способ его получения
UA109963C2 (uk) * 2011-09-06 2015-10-26 Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
CN102367554A (zh) * 2011-10-28 2012-03-07 内蒙古包钢钢联股份有限公司 一种工程机械用高性能调质钢板及其生产工艺
EP2803748B1 (en) 2012-01-13 2018-03-14 Nippon Steel & Sumitomo Metal Corporation Hot stamp molded article, and method for producing hot stamp molded article
ES2727684T3 (es) * 2012-01-13 2019-10-17 Nippon Steel Corp Chapa de acero laminada en frío y método para producir chapa de acero laminada en frío
BR112014023783B1 (pt) 2012-03-28 2019-09-10 Nippon Steel & Sumitomo Metal Corp chapa feita sob medida para estampagem a quente, seu método de produção e membro estampado a quente
DE102012006941B4 (de) * 2012-03-30 2013-10-17 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Bauteils aus Stahl durch Warmumformen
EP2664682A1 (de) 2012-05-16 2013-11-20 ThyssenKrupp Steel Europe AG Stahl für die Herstellung eines Stahlbauteils, daraus bestehendes Stahlflachprodukt, daraus hergestelltes Bauteil und Verfahren zu dessen Herstellung
CN102747295B (zh) * 2012-07-27 2014-06-18 武汉钢铁(集团)公司 一种利用控轧控冷方法生产的贝氏体薄钢板及其制备方法
KR101448473B1 (ko) 2012-12-03 2014-10-10 현대하이스코 주식회사 테일러 웰디드 블랭크, 그 제조방법 및 이를 이용한 핫스탬핑 부품
CN103114292B (zh) * 2013-02-18 2015-01-07 梅河口市弘业无缝钢管有限公司 激光熔敷多元共渗复合处理的油井管、生产工艺及装置
EP2982772B1 (en) 2013-04-02 2018-10-10 Nippon Steel & Sumitomo Metal Corporation Hot-stamp-molded article, cold-rolled steel sheet, and method for manufacturing hot-stamp-molded article
CZ305175B6 (cs) * 2013-04-22 2015-05-27 Západočeská Univerzita V Plzni Způsob výroby ocelových dílů
DE202013011800U1 (de) * 2013-07-24 2014-10-27 GM Global Technology Operations LLC (n. d. Gesetzen des Staates Delaware) Linienverstärktes Kraftfahrzeugblech, insbesondere Karosserieblech
US20170029914A1 (en) * 2013-11-29 2017-02-02 Nippon Steel & Sumitomo Metal Corporation Hot formed steel sheet component and method for producing the same as well as steel sheet for hot forming
US10344351B2 (en) * 2013-12-20 2019-07-09 Nippon Steel & Sumitomo Metal Corporation Hot-pressed steel sheet member, method of manufacturing the same, and steel sheet for hot pressing
US20160326608A1 (en) 2014-01-06 2016-11-10 Nippon Steel & Sumitomo Metal Corporation Hot-formed member and method of manufacturing same
DE102014010661A1 (de) * 2014-07-18 2016-01-21 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Blech und Verfahren zu dessen Behandlung
WO2016016676A1 (fr) 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
KR20160078807A (ko) 2014-12-24 2016-07-05 주식회사 포스코 연신율 및 충격 인성이 우수한 열간 프레스 부재 및 그 제조방법
WO2016132165A1 (fr) * 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
EP3278895B1 (en) * 2015-03-31 2020-03-11 Nippon Steel Corporation Steel sheet for hot stamping, method for manufacturing same, and hot stamp molded article
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
WO2017017485A1 (en) 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
WO2017017484A1 (en) * 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
DE102015014490A1 (de) 2015-11-10 2017-05-11 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Verfahren zur Verarbeitung eines Blechwerkstücks
WO2017187215A1 (en) * 2016-04-29 2017-11-02 Arcelormittal Carbon steel sheet coated with a barrier coating
KR101726139B1 (ko) 2016-09-21 2017-04-12 주식회사 포스코 연신율 및 충격 인성이 우수한 열간 프레스 부재 및 그 제조방법
JP6424195B2 (ja) * 2016-11-14 2018-11-14 株式会社豊田中央研究所 熱間プレス成形方法
WO2018096387A1 (en) 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
CN107190203B (zh) * 2017-05-31 2019-07-23 武汉钢铁有限公司 用薄板坯直接轧制的屈服强度≥800MPa热轧薄板及生产方法
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
MX2020003896A (es) 2017-10-02 2020-08-20 Nippon Steel Corp Producto estampado en caliente, lamina de acero para estampado en caliente y metodo de fabricacion de los mismos.
CA3076934C (en) * 2017-11-02 2023-03-21 Ak Steel Properties, Inc. Press hardened steel with tailored properties after novel thermal treatment
WO2019102255A1 (en) 2017-11-24 2019-05-31 Arcelormittal Method of producing a welded steel blank with the provision of a filler wire having a defined carbon content, associated welded blank, method of producing a welded part with hot press-formed and cooled steel part and associated part
DE102017131247A1 (de) 2017-12-22 2019-06-27 Voestalpine Stahl Gmbh Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften
DE102017131253A1 (de) 2017-12-22 2019-06-27 Voestalpine Stahl Gmbh Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften
WO2019166852A1 (en) 2018-02-27 2019-09-06 Arcelormittal Method for producing a press-hardened laser welded steel part and press-hardened laser welded steel part
DE102018133143A1 (de) * 2018-11-06 2020-05-07 Salzgitter Flachstahl Gmbh Innenhochdruck umgeformtes Bauteil aus Stahl und Verwendung eines Stahls für Vorprodukte zur Herstellung eines innenhochdruckumgeformten Bauteiles sowie Vorprodukt hierfür
CN109821951B (zh) * 2018-12-06 2020-07-21 苏州普热斯勒先进成型技术有限公司 一种耐腐蚀热冲压零件的制备方法及装置
KR102633542B1 (ko) 2019-04-01 2024-02-06 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형품 및 그 제조 방법
WO2020204037A1 (ja) 2019-04-01 2020-10-08 日本製鉄株式会社 ホットスタンプ成形品およびホットスタンプ用鋼板、並びにそれらの製造方法
KR102213974B1 (ko) * 2019-04-30 2021-02-08 현대제철 주식회사 핫 스탬핑 부품 및 그 제조방법
JP7235621B2 (ja) 2019-08-27 2023-03-08 株式会社神戸製鋼所 低強度ホットスタンプ用鋼板、ホットスタンプ部品およびホットスタンプ部品の製造方法
CN113924373B (zh) 2019-12-20 2023-09-01 现代制铁株式会社 热冲压部件及其制造方法
MX2022007980A (es) 2020-01-16 2022-07-05 Nippon Steel Corp Carroceria estampada en caliente.
KR102747960B1 (ko) 2020-01-16 2024-12-31 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형체
CN112301276B (zh) * 2020-10-12 2021-10-22 马鞍山钢铁股份有限公司 一种高强、高耐候冷轧双相耐候钢的制作方法
CN112962021B (zh) * 2021-01-25 2022-06-10 唐山钢铁集团有限责任公司 激光拼焊后用于整体热冲压成形的强塑钢板及生产方法
WO2024023553A1 (en) * 2022-07-28 2024-02-01 Arcelormittal Method for manufacturing a coated press hardened steel part having an improved appearance and corresponding steel part
CN117327977B (zh) * 2023-09-25 2026-04-03 马鞍山钢铁有限公司 抗拉强度500MPa级铝合金涂层热成形钢板及生产方法、热成形钢构件和应用

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2082767C1 (ru) * 1993-02-10 1997-06-27 Акционерное общество "Верх-Исетский металлургический завод" Способ отжига оцинкованной тонкой стальной полосы
RU2055916C1 (ru) * 1993-09-10 1996-03-10 Научно-производственное предприятие "Эста" Способ производства оцинкованных металлических полос
RU2135622C1 (ru) * 1996-12-16 1999-08-27 Ниппон Стил Корпорейшн Сталь, имеющая высокую ударную вязкость в зоне термического воздействия при сварке
FR2780984B1 (fr) * 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
FR2787735B1 (fr) * 1998-12-24 2001-02-02 Lorraine Laminage Procede de realisation d'une piece a partir d'une bande de tole d'acier laminee et notamment laminee a chaud
JP3698046B2 (ja) * 1999-10-22 2005-09-21 Ｊｆｅスチール株式会社 加工性およびめっき性に優れた高強度溶融亜鉛めっき鋼板ならびにその製造方法
WO2001031077A1 (fr) * 1999-10-22 2001-05-03 Kawasaki Steel Corporation Tole d'acier galvanisee par immersion a chaud presentant de bonnes qualites de resistance, de formabilite et de galvanisation
CN1145709C (zh) * 2000-02-29 2004-04-14 川崎制铁株式会社 应变时效硬化特性优良的高强度冷轧钢板及其制造方法
FR2807447B1 (fr) * 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
AU780588B2 (en) * 2000-04-07 2005-04-07 Jfe Steel Corporation Hot rolled steel plate, cold rolled steel plate and hot dip galvanized steel plate being excellent in strain aging hardening characteristics, and method for their production
JP4333940B2 (ja) * 2001-08-31 2009-09-16 新日本製鐵株式会社 アルミ系めっき鋼板を用いた高強度自動車部材の熱間プレス方法
CN100434564C (zh) * 2001-10-23 2008-11-19 住友金属工业株式会社 热压成型方法,其电镀钢材及其制备方法
KR100467487B1 (ko) * 2001-10-26 2005-01-24 현대자동차주식회사 자동차용 강판의 강성강화 방법 및 그 성형품
FR2833504A1 (fr) * 2001-12-14 2003-06-20 Usinor Procede de mise en forme a chaud et notamment l'obtention de tout ou partie d'une roue de vehicule automobile
JP4400079B2 (ja) * 2002-03-29 2010-01-20 Ｊｆｅスチール株式会社 超微細粒組織を有する冷延鋼板の製造方法
JP4168750B2 (ja) * 2002-12-27 2008-10-22 Ｊｆｅスチール株式会社 超微細粒組織を有し疲労特性に優れる溶融亜鉛めっき冷延鋼板の製造方法
JP4506434B2 (ja) * 2004-11-29 2010-07-21 Ｊｆｅスチール株式会社 剛性に優れた高強度鋼板およびその製造方法
FR2883007B1 (fr) * 2005-03-11 2007-04-20 Usinor Sa Procede de fabrication d'une piece d'acier revetu presentant une tres haute resistance apres traitement thermique
KR100676935B1 (ko) * 2005-06-25 2007-02-02 신닛뽄세이테쯔 카부시키카이샤 가공성이 우수한 고강도 합금화 용융 아연 도금 강판 및 그제조 방법
RU2292404C1 (ru) * 2005-07-15 2007-01-27 Открытое акционерное общество "Северсталь" Способ производства полос для изготовления труб
JP5029361B2 (ja) * 2005-08-03 2012-09-19 住友金属工業株式会社 熱延鋼板及び冷延鋼板並びにそれらの製造方法

Also Published As

Publication number Publication date
CA2680623A1 (fr) 2008-11-06
BRPI0809006B1 (pt) 2017-11-21
KR20090128414A (ko) 2009-12-15
AR065764A1 (es) 2009-07-01
EP2137327B1 (fr) 2012-05-02
KR101952525B1 (ko) 2019-02-26
KR20190091571A (ko) 2019-08-06
KR102008641B1 (ko) 2019-08-07
RU2009137930A (ru) 2011-04-20
KR20180122489A (ko) 2018-11-12
ES2387229T3 (es) 2012-09-18
EP2137327A1 (fr) 2009-12-30
CN101631880B (zh) 2012-07-04
US20100221572A1 (en) 2010-09-02
JP5726419B2 (ja) 2015-06-03
KR20150048913A (ko) 2015-05-07
MA31235B1 (fr) 2010-03-01
US8722203B2 (en) 2014-05-13
WO2008132303A1 (fr) 2008-11-06
RU2423532C1 (ru) 2011-07-10
ZA200905998B (en) 2010-04-28
MX2009009769A (es) 2009-10-07
PL2137327T3 (pl) 2012-10-31
BRPI0809006A2 (pt) 2014-09-16
CN101631880A (zh) 2010-01-20
US20140216612A1 (en) 2014-08-07
JP2010521584A (ja) 2010-06-24
WO2008110670A1 (fr) 2008-09-18
ATE556152T1 (de) 2012-05-15
US9611517B2 (en) 2017-04-04
KR20170038119A (ko) 2017-04-05
UA99127C2 (ru) 2012-07-25

Similar Documents

Publication Publication Date Title
CA2680623C (fr) Acier pour formage a chaud ou trempe sous outil, a ductilite amelioree
EP3783116B1 (fr) Tôles prerevêtues permettant la fabrication de pieces d'acier revêtues et durcies a la presse
EP2171112B1 (fr) Procede de fabrication de tôles d'acier a hautes caracteristiques de resistance et de ductilite, et tôles ainsi produites
EP1929053B1 (fr) Procede de fabrication d une piece en acier de microstructure multi-phasee
EP3126459B1 (fr) Procédé de fabrication à haute productivité de pièces d'acier revêtues et durcies à la presse
EP2007545B1 (fr) Procede de fabrication d'une piece soudee a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
CA3065036C (fr) Procede de fabrication de pieces d'acier a haute resistance mecanique et ductilite amelioree, et pieces obtenues par ce procede
EP1943368B1 (fr) Procede de fabrication d'une piece a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
WO2016016676A1 (fr) Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
WO2012168567A1 (fr) Tôle d'acier laminée à froid et revêtue de zinc ou d'alliage de zinc, procede de fabrication et utilisation d'une telle tôle
WO2012153008A1 (fr) Procede de fabrication d'acier martensitique a tres haute resistance et tole ou piece ainsi obtenue
WO2012153009A1 (fr) Procede de fabrication d'acier martensitique a tres haute resistance et tole ainsi obtenue
WO2011104443A1 (fr) Procédé de fabrication d'une pièce a partir d'une tôle revêtue d'aluminium ou d'alliage d'aluminium
FR2827874A1 (fr) Procede de fabrication de pieces d'acier a tres haute resistance mecanique et excellente planeite

Legal Events

Date Code Title Description
EEER Examination request
MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 17TH ANNIV.) - STANDARD

Year of fee payment: 17

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20250220

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT PAID IN FULL

Effective date: 20250819

MPN Maintenance fee for patent paid

Free format text: FEE DESCRIPTION TEXT: MF (PATENT, 18TH ANNIV.) - STANDARD

Year of fee payment: 18

U00 Fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U00-U101 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE REQUEST RECEIVED

Effective date: 20260219

U11 Full renewal or maintenance fee paid

Free format text: ST27 STATUS EVENT CODE: A-4-4-U10-U11-U102 (AS PROVIDED BY THE NATIONAL OFFICE); EVENT TEXT: MAINTENANCE FEE PAYMENT PAID IN FULL

Effective date: 20260219