CN102251177A - 一种含稀土高强度钢板及其轧制方法 - Google Patents
一种含稀土高强度钢板及其轧制方法 Download PDFInfo
- Publication number
- CN102251177A CN102251177A CN2011101930926A CN201110193092A CN102251177A CN 102251177 A CN102251177 A CN 102251177A CN 2011101930926 A CN2011101930926 A CN 2011101930926A CN 201110193092 A CN201110193092 A CN 201110193092A CN 102251177 A CN102251177 A CN 102251177A
- Authority
- CN
- China
- Prior art keywords
- percent
- steel plate
- rolling
- rare earth
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种含稀土高强度钢板及其轧制方法，属于冶金技术领域，涉及成型工艺技术，其特征在于板坯的(重量百分比)化学成分为：C 0.15％-0.25％，Mn 1.5％-1.85％，Si 0.7％-1.0％，P≤0.015％，S≤0.003％，Ti 0.01％-0.06％，B 0.0005％-0.0035％，RE 0.001％-0.09％，余量为Fe和不可避免的杂质。轧制工艺为：加热温度1220-1250℃，保温时间1-3小时，粗轧温度1000-1100℃，精轧温度920-960℃，终轧温度850-900℃，两段轧制总压下量≥75％。钢板力学性能优良，抗拉强度达600-850MPa，延伸率25-35％，屈强比≤0.8，且生产成本低，可工业化生产5-25mm厚度钢板。
Description
一、技术领域
本发明属于成型技术领域，涉及钢板轧制，特别是热轧工艺。
二、背景技术
目前，C-Mn高强度热轧钢板大多是通过在奥氏体可发生再结晶区进行轧制后，再控制冷却温度和冷却速度来获得高强度热轧钢板。如“一种抗拉强度1000MPa级复相钢板及制造方法”，通过控制冷却方式获得抗拉强度在1000-1100MPa之间，屈服强度在615-810MPa之间，延伸率11％左右的优良性能，广泛应用于汽车等制造行业。对于高强度热轧钢板，国内外已经形成多项专利技术，如“屈服强度1100MPa以上超高强度钢板及其制造方法”，通过添加昂贵的合金元素B、Ni、Cr、Cu、Mo中的一种或几种，Ti、V、Nb中的一种或几种以获得高强度高塑性热轧钢板。这种方法的缺点是合金成分多，冶炼工艺复杂，生产成本高，产品竞争力相对较低，与资源节约型、环境友好型的经济发展国策不符。
三、发明内容
本发明的目的是公开一种含稀土高强度钢板及其轧制方法，其板坯的(重量百分比)化学成分含量应符合：C 0.15％-0.25％，Mn 1.5％-1.85％，Si 0.7％-1.0％，P≤0.015％，S≤0.003％，Ti 0.01％-0.06％，B 0.0005％-0.0035％，RE 0.001％-0.09％，余量为Fe和不可避免的杂质。
板坯的加热温度为1220-1250℃，保温时间1-3小时，粗轧温度1000-1100℃，精轧温度920-960℃，终轧温度850-900℃，两段轧制总压下量≥75％。
成品板厚度为5-25mm。由此工艺生产的产品具有优良的力学性能，抗拉强度达到600-850MPa，延伸率25-35％，屈强比≤0.8。
本发明突出优点是热轧钢板不仅具有高强度高塑性，而且还可以通过稀土来替代和减少合金元素的加入量，节约成本。实现材料领域的环境友好型、资源节约型生产发展模式。
四、附图说明
图1为实施例1对应典型金相组织照片；
图2为实施例2对应典型金相组织照片。
五、具体实施方式
以下结合实施例对本发明作进一步详细的说明。
实施例1：
将拟轧制的板坯放入加热炉，板坯的(重量百分比)化学成分为：C 0.24％，Mn 1.72％，Si 0.73％，P 0.0115％，S 0.002％，Ti 0.03％，B 0.0007％，Ce 0.008％，余量为Fe和不可避免的杂质。
板坯厚度为95mm，加热温度1220℃，保温时间1.5小时。将加热好的板坯送入粗轧机进行轧制，粗轧温度1020℃。然后，将粗轧后的板坯送入精轧机工位进行轧制，精轧温度950℃，终轧温度890℃。两段轧制总压下量91.5％。精轧后钢板的厚度为8mm，平均晶粒度评定为10.5级，其力学性能检测值见表1：
表1力学性能检测值
精轧钢板的金相组织如图1所示。
实施例2：
将拟轧制的板坯放入加热炉，板坯的(重量百分比)化学成分为：C 0.24％，Mn 1.74％，Si 0.71％，P 0.0114％，S 0.002％，Ti 0.034％，B 0.0011％，Ce 0.08％，余量为Fe和不可避免的杂质。
板坯厚度为95mm，加热温度1220℃，保温时间1.5小时。将加热好的板坯送入粗轧机进行轧制，粗轧温度1030℃。然后，将完成粗轧的板坯送入精轧机工位进行轧制，精轧温度950℃，终轧温度850℃。两段轧制总压下量91.5％。精轧后的钢板厚度为8mm，平均晶粒度评定为11.5级，其力学性能检测值见表2：
表2力学性能检测值
精轧钢板的金相组织如图2所示。
Claims (3)
1.一种含稀土高强度钢板，其特征在于以重量百分比计化学成分：C0.15％-0.25％，Mn 1.5％-1.85％，Si 0.7％-1.0％，P≤0.015％，S≤0.003％，Ti0.01％-0.06％，B 0.0005％-0.0035％，RE 0.001％-0.09％，余量为Fe和不可避免的杂质，其厚度为5-25mm。
2.如权利要求1所述的一种含稀土高强度钢板，其特征在于其力学性能检测值为：抗拉强度达到600-850MPa，延伸率25-35％，屈强比≤0.8。
3.一种含稀土高强度钢板的轧制方法，其特征在于所述钢板具有权利要求1中钢的化学成分，轧制工艺如下：加热温度为1220-1250℃，保温时间1-3小时，粗轧温度1000-1100℃，精轧温度920-960℃，终轧温度850-900℃，两段轧制总压下量≥75％。