BR112018071668A2 - chapa de aço galvanizada por imersão a quente - Google Patents
chapa de aço galvanizada por imersão a quenteInfo
- Publication number
- BR112018071668A2 BR112018071668A2 BR112018071668-5A BR112018071668A BR112018071668A2 BR 112018071668 A2 BR112018071668 A2 BR 112018071668A2 BR 112018071668 A BR112018071668 A BR 112018071668A BR 112018071668 A2 BR112018071668 A2 BR 112018071668A2
- Authority
- BR
- Brazil
- Prior art keywords
- amount
- steel sheet
- galvanized steel
- dip galvanized
- less
- Prior art date
Abstract
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/JP2016/070982 WO2018011978A1 (ja) | 2016-07-15 | 2016-07-15 | 溶融亜鉛めっき鋼板 |
Publications (1)
Publication Number | Publication Date |
---|---|
BR112018071668A2 true BR112018071668A2 (pt) | 2019-02-19 |
Family
ID=60952371
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112018071668-5A BR112018071668A2 (pt) | 2016-07-15 | 2016-07-15 | chapa de aço galvanizada por imersão a quente |
Country Status (8)
Country | Link |
---|---|
US (1) | US10718044B2 (pt) |
EP (1) | EP3438307A4 (pt) |
JP (1) | JP6852736B2 (pt) |
KR (1) | KR102193424B1 (pt) |
CN (1) | CN109154044B (pt) |
BR (1) | BR112018071668A2 (pt) |
MX (1) | MX2018012680A (pt) |
WO (1) | WO2018011978A1 (pt) |
Families Citing this family (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6108046B1 (ja) * | 2015-06-30 | 2017-04-05 | 新日鐵住金株式会社 | 高強度冷延鋼板、高強度溶融亜鉛めっき鋼板、および高強度合金化溶融亜鉛めっき鋼板 |
CN110168126B (zh) * | 2017-02-16 | 2021-07-13 | 日本制铁株式会社 | 热轧钢板及其制造方法 |
JP6628018B1 (ja) | 2018-04-17 | 2020-01-08 | 日本製鉄株式会社 | 熱延鋼板 |
KR102164086B1 (ko) * | 2018-12-19 | 2020-10-13 | 주식회사 포스코 | 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법 |
KR102164092B1 (ko) * | 2018-12-19 | 2020-10-13 | 주식회사 포스코 | 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판 |
KR102209612B1 (ko) * | 2018-12-19 | 2021-01-29 | 주식회사 포스코 | 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법 |
KR102164088B1 (ko) * | 2018-12-19 | 2020-10-13 | 주식회사 포스코 | 버링성이 우수한 고강도 냉연강판 및 그 제조방법 |
US11905570B2 (en) | 2019-02-06 | 2024-02-20 | Nippon Steel Corporation | Hot dip galvanized steel sheet and method for producing same |
MX2021010376A (es) * | 2019-03-29 | 2021-10-01 | Nippon Steel Corp | Lamina de acero. |
KR20220095232A (ko) | 2019-12-19 | 2022-07-06 | 닛폰세이테츠 가부시키가이샤 | 강판 및 그 제조 방법 |
JP7364942B2 (ja) * | 2020-01-22 | 2023-10-19 | 日本製鉄株式会社 | 鋼板およびその製造方法 |
WO2022004819A1 (ja) * | 2020-06-30 | 2022-01-06 | Jfeスチール株式会社 | 亜鉛めっき鋼板、部材及びそれらの製造方法 |
CN115715332B (zh) * | 2020-06-30 | 2024-04-12 | 杰富意钢铁株式会社 | 镀锌钢板、构件和它们的制造方法 |
MX2022016037A (es) * | 2020-07-20 | 2023-02-02 | Nippon Steel Corp | Lamina de acero y metodo de fabricacion de la misma. |
WO2022270100A1 (ja) * | 2021-06-24 | 2022-12-29 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法、ならびに、部材 |
Family Cites Families (37)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3247907B2 (ja) | 1992-11-05 | 2002-01-21 | 川崎製鉄株式会社 | 延性と耐遅れ破壊特性に優れた高強度冷延鋼板およびその製造方法 |
JP3247909B2 (ja) | 1992-11-05 | 2002-01-21 | 川崎製鉄株式会社 | 延性と耐遅れ破壊特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP3514276B2 (ja) | 1995-10-19 | 2004-03-31 | Jfeスチール株式会社 | 耐遅れ破壊特性に優れた超高強度鋼板及びその製造方法 |
JPH101740A (ja) | 1996-06-12 | 1998-01-06 | Kobe Steel Ltd | 耐遅れ破壊特性にすぐれる超高強度鋼板及びその製造方法 |
JP3587115B2 (ja) * | 2000-01-24 | 2004-11-10 | Jfeスチール株式会社 | 成形性に優れた高張力溶融亜鉛めっき鋼板の製造方法 |
JP4320913B2 (ja) * | 2000-04-20 | 2009-08-26 | 住友金属工業株式会社 | 成形性に優れた高張力溶融亜鉛系めっき鋼板およびその製造方法 |
JP2004032951A (ja) | 2002-06-28 | 2004-01-29 | Fujitsu General Ltd | 誘導電動機 |
JP4165272B2 (ja) * | 2003-03-27 | 2008-10-15 | Jfeスチール株式会社 | 疲労特性および穴拡げ性に優れる高張力溶融亜鉛めっき鋼板およびその製造方法 |
JP4317384B2 (ja) | 2003-04-28 | 2009-08-19 | 新日本製鐵株式会社 | 耐水素脆化、溶接性および穴拡げ性に優れた高強度亜鉛めっき鋼板とその製造方法 |
TWI302572B (en) * | 2003-09-30 | 2008-11-01 | Nippon Steel Corp | High yield ratio, high strength steel sheet, high yield ratio, high strength hot dip galvanized steel sheet and high yield ratio, high strength alloyed hot dip galvanized steel sheet and process for producing same |
JP3889767B2 (ja) * | 2005-03-31 | 2007-03-07 | 株式会社神戸製鋼所 | 溶融亜鉛めっき用高強度鋼板 |
US7887648B2 (en) | 2005-12-28 | 2011-02-15 | Kobe Steel, Ltd. | Ultrahigh-strength thin steel sheet |
JP4174592B2 (ja) | 2005-12-28 | 2008-11-05 | 株式会社神戸製鋼所 | 超高強度薄鋼板 |
JP5365216B2 (ja) | 2008-01-31 | 2013-12-11 | Jfeスチール株式会社 | 高強度鋼板とその製造方法 |
JP4894863B2 (ja) * | 2008-02-08 | 2012-03-14 | Jfeスチール株式会社 | 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
US20090283145A1 (en) | 2008-05-13 | 2009-11-19 | Kim Yun-Gi | Semiconductor Solar Cells Having Front Surface Electrodes |
JP5326362B2 (ja) * | 2008-05-30 | 2013-10-30 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5394709B2 (ja) | 2008-11-28 | 2014-01-22 | 株式会社神戸製鋼所 | 耐水素脆化特性および加工性に優れた超高強度鋼板 |
JP5609383B2 (ja) | 2009-08-06 | 2014-10-22 | Jfeスチール株式会社 | 低温靭性に優れた高強度熱延鋼板およびその製造方法 |
JP5370104B2 (ja) * | 2009-11-30 | 2013-12-18 | 新日鐵住金株式会社 | 耐水素脆化特性に優れた引張最大強度900MPa以上の高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法 |
WO2011065591A1 (ja) | 2009-11-30 | 2011-06-03 | 新日本製鐵株式会社 | 耐水素脆化特性に優れた引張最大強度900MPa以上の高強度鋼板及びその製造方法 |
JP4977879B2 (ja) | 2010-02-26 | 2012-07-18 | Jfeスチール株式会社 | 曲げ性に優れた超高強度冷延鋼板 |
JP5136609B2 (ja) | 2010-07-29 | 2013-02-06 | Jfeスチール株式会社 | 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
EP2730666B1 (en) | 2011-07-06 | 2018-06-13 | Nippon Steel & Sumitomo Metal Corporation | Method for producing a cold-rolled steel sheet |
CN103827341B (zh) * | 2011-09-30 | 2016-08-31 | 新日铁住金株式会社 | 热浸镀锌钢板及其制造方法 |
JP5413539B2 (ja) | 2011-09-30 | 2014-02-12 | 新日鐵住金株式会社 | 焼付硬化性に優れた高強度溶融亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法 |
JP5327410B1 (ja) | 2011-09-30 | 2013-10-30 | 新日鐵住金株式会社 | 耐衝撃特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法、並びに、高強度合金化溶融亜鉛めっき鋼板およびその製造方法 |
JP5741456B2 (ja) | 2012-01-13 | 2015-07-01 | 新日鐵住金株式会社 | 合金化溶融亜鉛めっき鋼板およびその製造方法 |
JP6001883B2 (ja) | 2012-03-09 | 2016-10-05 | 株式会社神戸製鋼所 | プレス成形品の製造方法およびプレス成形品 |
US20150203947A1 (en) * | 2012-07-31 | 2015-07-23 | Jfe Steel Corporation | High-strength galvanized steel sheet with excellent formability and shape fixability and method for manufacturing the same |
JP6040753B2 (ja) * | 2012-12-18 | 2016-12-07 | 新日鐵住金株式会社 | 強度と耐水素脆性に優れたホットスタンプ成形体及びその製造方法 |
JP6008039B2 (ja) * | 2013-02-26 | 2016-10-19 | 新日鐵住金株式会社 | 焼き付け硬化性と低温靭性に優れた引張最大強度980MPa以上の高強度熱延鋼板 |
BR112015024854B1 (pt) | 2013-05-14 | 2020-03-10 | Nippon Steel Corporation | Chapa de aço laminada a quente e método para sua produção |
CN105143488B (zh) | 2013-05-21 | 2017-05-17 | 新日铁住金株式会社 | 热轧钢板及其制造方法 |
JP6237364B2 (ja) | 2014-03-17 | 2017-11-29 | 新日鐵住金株式会社 | 衝突特性に優れた高強度鋼板及びその製造方法 |
CN106661698B (zh) | 2014-08-28 | 2018-09-04 | 杰富意钢铁株式会社 | 延伸凸缘性、延伸凸缘性的面内稳定性及弯曲性优异的高强度熔融镀锌钢板以及其制造方法 |
CN107208236B (zh) * | 2015-02-13 | 2019-01-25 | 杰富意钢铁株式会社 | 高强度熔融镀锌钢板及其制造方法 |
-
2016
- 2016-07-15 US US16/092,947 patent/US10718044B2/en active Active
- 2016-07-15 MX MX2018012680A patent/MX2018012680A/es unknown
- 2016-07-15 EP EP16908879.6A patent/EP3438307A4/en not_active Withdrawn
- 2016-07-15 CN CN201680086094.6A patent/CN109154044B/zh active Active
- 2016-07-15 BR BR112018071668-5A patent/BR112018071668A2/pt not_active IP Right Cessation
- 2016-07-15 WO PCT/JP2016/070982 patent/WO2018011978A1/ja active Application Filing
- 2016-07-15 KR KR1020187031102A patent/KR102193424B1/ko active IP Right Grant
- 2016-07-15 JP JP2018527357A patent/JP6852736B2/ja active Active
Also Published As
Publication number | Publication date |
---|---|
EP3438307A1 (en) | 2019-02-06 |
US10718044B2 (en) | 2020-07-21 |
EP3438307A4 (en) | 2019-08-28 |
WO2018011978A1 (ja) | 2018-01-18 |
CN109154044B (zh) | 2020-09-04 |
MX2018012680A (es) | 2019-01-30 |
US20190169729A1 (en) | 2019-06-06 |
KR20180126564A (ko) | 2018-11-27 |
KR102193424B1 (ko) | 2020-12-23 |
CN109154044A (zh) | 2019-01-04 |
JP6852736B2 (ja) | 2021-03-31 |
JPWO2018011978A1 (ja) | 2019-02-14 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112018071668A2 (pt) | chapa de aço galvanizada por imersão a quente | |
MX2019007165A (es) | Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma. | |
MX2017005568A (es) | Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para la fabricacion de las mismas. | |
MX2017009200A (es) | Lamina de acero galvanizada de alta resistencia y metodo para producir la misma. | |
MX2019007169A (es) | Hoja de acero revestida y templada con excelente capacidad de formacion y un metodo para fabricar la misma. | |
MX2018016000A (es) | Lamina de acero. | |
UA118036C2 (uk) | Високоміцна сталь та спосіб виготовлення | |
MX2018008561A (es) | Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma. | |
IN2014KN01673A (pt) | ||
MX2017005567A (es) | Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas. | |
MX2017001720A (es) | Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia. | |
MX2018007641A (es) | Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida. | |
MX2016008809A (es) | Miembro formado en caliente y proceso para manufacturar el mismo. | |
TW201612331A (en) | Hot-rolled steel sheet | |
MX2020006507A (es) | Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma. | |
MX354006B (es) | Lamina de acero laminada en caliente y proceso para producir la misma. | |
MX2016012708A (es) | Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en inmersion en caliente de alta resistencia y chapa de acero galvanfusionado en inmersion en caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad. | |
IN2014DN08590A (pt) | ||
MX2016003781A (es) | Lamina de acero de alta resistencia que tiene excelente capacidad de conformacion y dureza a baja temperatura,y metodo para la produccion de la misma. | |
MX2017010598A (es) | Hoja de acero laminada en caliente. | |
MX2016013771A (es) | Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia. | |
MY174534A (en) | Steel sheet hot-dip coated with zn-al-mg-based system having excellent workability and method for manufacturing same | |
MX2016012797A (es) | Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en baño caliente de alta resistencia y chapa de acero galvanofusionado en baño caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad. | |
MX2018001140A (es) | Lamina de acero laminada en caliente de alta resistencia. | |
MX2018001280A (es) | Lamina de acero de estructura tipo mixta de transformacion inducida por tension y metodo para fabricar la misma. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL CORPORATION (JP) |
|
B06U | Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette] | ||
B08F | Application dismissed because of non-payment of annual fees [chapter 8.6 patent gazette] |
Free format text: ARQUIVADO O PEDIDO DE PATENTE, NOS TERMOS DO ARTIGO 86, DA LPI, E ARTIGO 10 DA RESOLUCAO 113/2013, REFERENTE AO NAO RECOLHIMENTO DA 5A RETRIBUICAO ANUAL, PARA FINS DE RESTAURACAO CONFORME ARTIGO 87 DA LPI 9.279, SOB PENA DA MANUTENCAO DO ARQUIVAMENTO CASO NAO SEJA RESTAURADO DENTRO DO PRAZO LEGAL, CONFORME O DISPOSTO NO ARTIGO 12 DA RESOLUCAO 113/2013. |
|
B08K | Patent lapsed as no evidence of payment of the annual fee has been furnished to inpi [chapter 8.11 patent gazette] |
Free format text: EM VIRTUDE DO ARQUIVAMENTO PUBLICADO NA RPI 2627 DE 11-05-2021 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDO O ARQUIVAMENTO DO PEDIDO DE PATENTE, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013. |
|
B350 | Update of information on the portal [chapter 15.35 patent gazette] |