BR112018006379A2 - chapa de aço galvanizada, e, método para fabricar um produto formado por prensagem a quente. - Google Patents

chapa de aço galvanizada, e, método para fabricar um produto formado por prensagem a quente.

Info

Publication number
BR112018006379A2
BR112018006379A2 BR112018006379-7A BR112018006379A BR112018006379A2 BR 112018006379 A2 BR112018006379 A2 BR 112018006379A2 BR 112018006379 A BR112018006379 A BR 112018006379A BR 112018006379 A2 BR112018006379 A2 BR 112018006379A2
Authority
BR
Brazil
Prior art keywords
steel sheet
galvanized steel
press
heat
hot pressing
Prior art date
Application number
BR112018006379-7A
Other languages
English (en)
Japanese (ja)
Other versions
BR112018006379B1 (pt
Inventor
OTOMO Ryosuke
Takeda Mikako
Original Assignee
Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) filed Critical Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.)
Publication of BR112018006379A2 publication Critical patent/BR112018006379A2/pt
Publication of BR112018006379B1 publication Critical patent/BR112018006379B1/pt

Abstract

a presente invenção refere-se a uma chapa de aço galvanizada pela qual, em um processo de prensagem a quente, o aquecimento para suprimir a geração de rachaduras lme pode ser realizado em um curto espaço de tempo; e uma chapa de aço galvanizada para prensagem a quente, que é obtida submetendo-se a chapa de aço galvanizada à prensagem a quente. essa chapa de aço galvanizada para prensagem a quente é uma chapa de aço galvanizada que é usada para prensagem a quente, e é caracterizada pelo fato de que os óxidos internos estão presentes no lado da chapa de aço de base de uma interface entre uma camada de galvanização e a chapa de aço de base e pelo fato de que a chapa de aço de base contém quantidades estipuladas de c, si, mn e cr, com o restante sendo constituído por ferro e impurezas inevitáveis, e satisfaz a fórmula (1). fórmula (1): (2×[si]/28,1+[mn]/54,9+1,5×[cr]/52,0) = 0,05. na fórmula (1), [si] denota o conteúdo em termos de % em massa na chapa de aço de base, [mn] denota o conteúdo em termos de % em massa de mn na chapa de aço de base e [cr] denota o conteúdo em termos de % em massa de cr na chapa de aço de base.
BR112018006379-7A 2015-10-02 2016-09-29 Chapa de aço galvanizada, e, método para fabricar um produto formado por prensagem a quente. BR112018006379B1 (pt)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2015-197226 2015-10-02
JP2015197226A JP2017066508A (ja) 2015-10-02 2015-10-02 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
PCT/JP2016/078814 WO2017057570A1 (ja) 2015-10-02 2016-09-29 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法

Publications (2)

Publication Number Publication Date
BR112018006379A2 true BR112018006379A2 (pt) 2018-10-09
BR112018006379B1 BR112018006379B1 (pt) 2021-09-14

Family

ID=58427597

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112018006379-7A BR112018006379B1 (pt) 2015-10-02 2016-09-29 Chapa de aço galvanizada, e, método para fabricar um produto formado por prensagem a quente.

Country Status (11)

Country Link
US (1) US20180281348A1 (pt)
EP (1) EP3358032B1 (pt)
JP (1) JP2017066508A (pt)
KR (1) KR102051284B1 (pt)
CN (1) CN108138282B (pt)
BR (1) BR112018006379B1 (pt)
CA (1) CA2999835C (pt)
ES (1) ES2883267T3 (pt)
MX (1) MX2018003455A (pt)
RU (1) RU2693226C1 (pt)
WO (1) WO2017057570A1 (pt)

Families Citing this family (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018115948A1 (en) * 2016-12-21 2018-06-28 Arcelormittal A method for the manufacture of a coated steel sheet
EP3725904B1 (en) * 2017-12-15 2024-03-06 Nippon Steel Corporation Steel sheet, hot-dip zinc-coated steel sheet, and alloyed hot-dip zinc-coated steel sheet
CN115404409A (zh) * 2018-03-27 2022-11-29 株式会社神户制钢所 热冲压用钢板
CN108950160A (zh) * 2018-08-25 2018-12-07 马鞍山钢铁股份有限公司 一种基于csp流程的锌基镀层热成形钢及其制备方法
CN109365606A (zh) * 2018-11-30 2019-02-22 宝山钢铁股份有限公司 一种耐腐蚀性优良的锌系镀层钢板或钢带的成形方法
KR102200175B1 (ko) * 2018-12-19 2021-01-08 주식회사 포스코 점 용접성이 우수한 아연도금강판 및 그 제조방법
US20220213572A1 (en) * 2019-07-02 2022-07-07 Nippon Steel Corporation Hot-stamping formed body
JP6839732B2 (ja) * 2019-07-08 2021-03-10 日本発條株式会社 スタビライザ、およびスタビライザの製造方法
EP4130326A4 (en) * 2020-03-31 2023-08-30 JFE Steel Corporation STEEL SHEET, ELEMENT, AND METHODS OF MAKING THE SAME
US20230129828A1 (en) * 2020-03-31 2023-04-27 Jfe Steel Corporation Steel sheet, member, and method for producing them
CN111545670A (zh) * 2020-06-16 2020-08-18 汉腾汽车有限公司 一种热冲压成型b柱及其成型工艺
JP7481651B2 (ja) 2020-09-30 2024-05-13 日本製鉄株式会社 鋼板
KR20220084651A (ko) * 2020-12-14 2022-06-21 주식회사 포스코 굽힘성 및 성형성이 우수한 고강도 강판 및 이의 제조방법
MX2023010438A (es) * 2021-03-08 2023-09-12 Kobe Steel Ltd Metodo para la fabricacion de chapa de acero galvanizada en ba?o de zinc caliente y metodo para la fabricacion de chapa de acero galvanizada en ba?o de zinc caliente aleado.
KR20230166779A (ko) * 2022-05-31 2023-12-07 현대제철 주식회사 핫 스탬핑 부품 및 이의 제조 방법
KR20230166780A (ko) * 2022-05-31 2023-12-07 현대제철 주식회사 핫 스탬핑 부품 및 이의 제조 방법

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006307261A (ja) * 2005-04-27 2006-11-09 Toyo Kohan Co Ltd プラズマディスプレイ固定板用鋼板、プラズマディスプレイ固定用鋼板の製造方法及びプラズマディスプレイ固定板。
CN101627142B (zh) * 2007-02-23 2012-10-03 塔塔钢铁艾默伊登有限责任公司 冷轧且连续退火的高强度钢带材及生产所述钢的方法
CN101680048B (zh) * 2007-06-15 2013-12-25 新日铁住金株式会社 成形品的制造方法
DE102007061489A1 (de) 2007-12-20 2009-06-25 Voestalpine Stahl Gmbh Verfahren zum Herstellen von gehärteten Bauteilen aus härtbarem Stahl und härtbares Stahlband hierfür
EP2379756A1 (en) 2008-12-19 2011-10-26 Tata Steel IJmuiden B.V. Method for manufacturing a coated part using hot forming techniques
ES2876258T3 (es) * 2009-12-29 2021-11-12 Posco Partes prensadas en caliente con chapadas con zinc y procedimiento de producción de las mismas
DE102011001140A1 (de) 2011-03-08 2012-09-13 Thyssenkrupp Steel Europe Ag Stahlflachprodukt, Verfahren zum Herstellen eines Stahlflachprodukts und Verfahren zum Herstellen eines Bauteils
JP5569647B2 (ja) * 2011-09-30 2014-08-13 新日鐵住金株式会社 溶融亜鉛めっき鋼板及びその製造方法
MX2014012798A (es) * 2012-04-23 2015-04-14 Kobe Steel Ltd Metodo de fabricacion de hoja de acero galvanizado para estampacion en caliente, hoja de acero galvanizado y recocido por inmersion en caliente para estampacion en caliente y metodo de fabricacion de las mismas, y componente estampado en caliente.
CN104411857B (zh) * 2012-06-25 2018-06-12 杰富意钢铁株式会社 抗粉化性优良的合金化热镀锌钢板
WO2014037627A1 (fr) * 2012-09-06 2014-03-13 Arcelormittal Investigación Y Desarrollo Sl Procede de fabrication de pieces d'acier revêtues et durcies a la presse, et tôles prerevêtues permettant la fabrication de ces pieces
KR101482357B1 (ko) * 2012-12-27 2015-01-13 주식회사 포스코 가공성이 우수한 열간 프레스 성형용 강판 및 그 제조방법
JP5852690B2 (ja) * 2013-04-26 2016-02-03 株式会社神戸製鋼所 ホットスタンプ用合金化溶融亜鉛めっき鋼板
CA2914464C (en) * 2013-06-11 2017-07-18 Nippon Steel & Sumitomo Metal Corporation Hot stamp molded body, and method for producing hot stamp molded body
JP2015034334A (ja) * 2013-07-12 2015-02-19 株式会社神戸製鋼所 めっき性、加工性、および耐遅れ破壊特性に優れた高強度めっき鋼板、並びにその製造方法
FI20135775L (fi) * 2013-07-16 2014-09-03 Rautaruukki Oyj Menetelmä valmistaa galvannealed-käsitelty teräsnauhatuote kuumapuristusmuovaukseen, menetelmä valmistaa kuumapuristettu teräskomponentti, ja galvannealed-käsitelty teräsnauhatuote
KR101833655B1 (ko) * 2013-12-27 2018-02-28 신닛테츠스미킨 카부시키카이샤 열간 프레스 강판 부재, 그 제조 방법 및 열간 프레스용 강판
WO2015144692A1 (en) * 2014-03-24 2015-10-01 Institut National De La Recherche Agronomique Expression decrease of the gene coding for the ephrin receptor in aphids inhibits the transmission of the turnip yellow virus
JP2015193907A (ja) * 2014-03-28 2015-11-05 株式会社神戸製鋼所 加工性、および耐遅れ破壊特性に優れた高強度合金化溶融亜鉛めっき鋼板、並びにその製造方法
WO2015197882A1 (es) * 2014-06-26 2015-12-30 Aislamientos Térmicos Y Frigoríficos, S.A. (Atefrisa) Recipiente

Also Published As

Publication number Publication date
MX2018003455A (es) 2018-05-23
CN108138282B (zh) 2020-09-08
US20180281348A1 (en) 2018-10-04
KR20180043331A (ko) 2018-04-27
WO2017057570A1 (ja) 2017-04-06
JP2017066508A (ja) 2017-04-06
CA2999835A1 (en) 2017-04-06
CA2999835C (en) 2020-05-12
CN108138282A (zh) 2018-06-08
ES2883267T3 (es) 2021-12-07
EP3358032A1 (en) 2018-08-08
EP3358032B1 (en) 2021-08-04
EP3358032A4 (en) 2019-04-10
BR112018006379B1 (pt) 2021-09-14
RU2693226C1 (ru) 2019-07-01
KR102051284B1 (ko) 2019-12-03

Similar Documents

Publication Publication Date Title
BR112018006379A2 (pt) chapa de aço galvanizada, e, método para fabricar um produto formado por prensagem a quente.
ATE522628T1 (de) Verfahren zum formen eines rohlings aus einem härtenden material mit differentieller kühlung
BR112018000234A2 (pt) chapa de aço elétrico de grão orientado e método para produção da mesma
BR112013022359A2 (pt) método para dobrar chapa metálica e produto da chapa metálica
BR112017004225A2 (pt) produto de aço plano para uma moldagem a quente, componente de aço, processo para produzir um produto de aço plano, e, processo para produzir um componente de aço
MX360028B (es) Tubo de acero sin costuras para inyeccion de vapor y metodo para fabricar el mismo.
BRPI0610872A2 (pt) processo para a produção de um componente com segmentos adjacentes de diferentes propriedades de material, por meio de têmpera com prensa
BR112015016863A2 (pt) método de fabricação de elemento de aço formado em prensa a quente
MX2016013666A (es) Metodo para fabricar una parte de formacion por prensado en caliente y una parte de formacion por prensado en caliente.
MX2013010249A (es) Productos de acero plano y metodo para la produccion de un producto de acero plano.
MX360240B (es) Lámina de acero para miembro estampado en caliente y método para producirla.
MX2019007946A (es) Parte estampada en caliente y metodo de fabricacion de la misma.
MX341647B (es) Metodo y herramienta de formacion para formar en caliente y endurecer con prensa piezas de trabajo de acero laminado, en particular piezas de trabajo galvanizadas de acero laminado.
BR112015000178A2 (pt) processo para produção de tira de aço laminada a quente e uma tira de aço produzida com o mesmo
MX354874B (es) Método para fabricar un miembro de acero formado en una prensa caliente y el miembro de acero formado en la prensa caliente.
BR112012022221A2 (pt) processo para a fabricação e aparelho para a fabricação de folha de aço laminado a quente
MX2018006621A (es) Metodo para producir lamina de acero electrico de grano orientado.
RU2013140668A (ru) Инструмент для горячей формовки или штамповки металлических листов с покрытием из cr-si-n
BR112015025477A2 (pt) processo de transformação de chapas em liga al-cu-li, melhorando a formabilidade e a resistência à corrosão
BR112012015515B8 (pt) Processo de tratamento termomecânico para a produção de chapa grossa e chapa grossa obtida
BR112018009722A2 (pt) método para produção de uma chapa de aço elétrica não orientada
BR112014000185A2 (pt) método para produzir um produto plano de aço para fins elétricos de grãos orientados destinado a aplicações eletroquímicas
BR112019008260A2 (pt) método para produzir lâmina de aço elétrico de grão orientado
BR112016022605B8 (pt) Substrato dotado de uma pluralidade de camadas e método para a fabricação de um substrato
BR112017008044A2 (pt) método para a produção de um aço nitretado para embalagem

Legal Events

Date Code Title Description
B06U Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 29/09/2016, OBSERVADAS AS CONDICOES LEGAIS.

B21F Lapse acc. art. 78, item iv - on non-payment of the annual fees in time

Free format text: REFERENTE A 7A ANUIDADE.

B24J Lapse because of non-payment of annual fees (definitively: art 78 iv lpi, resolution 113/2013 art. 12)

Free format text: EM VIRTUDE DA EXTINCAO PUBLICADA NA RPI 2742 DE 25-07-2023 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDA A EXTINCAO DA PATENTE E SEUS CERTIFICADOS, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013.