ZA200900177B - Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced - Google Patents

Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced

Info

Publication number
ZA200900177B
ZA200900177B ZA200900177A ZA200900177A ZA200900177B ZA 200900177 B ZA200900177 B ZA 200900177B ZA 200900177 A ZA200900177 A ZA 200900177A ZA 200900177 A ZA200900177 A ZA 200900177A ZA 200900177 B ZA200900177 B ZA 200900177B
Authority
ZA
South Africa
Prior art keywords
sheet
carbon
produced
excellent resistance
austenitic steel
Prior art date
Application number
ZA200900177A
Other languages
English (en)
Inventor
Scott Colin
Cugy Philippe
Allely Christian
Original Assignee
Arcelormittal France
Thyssenkrupp Steel Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal France, Thyssenkrupp Steel Ag filed Critical Arcelormittal France
Publication of ZA200900177B publication Critical patent/ZA200900177B/xx

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/34—Methods of heating
    • C21D1/42—Induction heating
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/74—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material
    • C21D1/767—Methods of treatment in inert gas, controlled atmosphere, vacuum or pulverulent material with forced gas circulation; Reheating thereof
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
    • C23C28/025—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only with at least one zinc-based layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/028—Including graded layers in composition or in physical properties, e.g. density, porosity, grain size
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P10/00—Technologies related to metal processing
    • Y02P10/25—Process efficiency
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Steel (AREA)
ZA200900177A 2006-07-11 2009-01-08 Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced ZA200900177B (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
EP06291136A EP1878811A1 (fr) 2006-07-11 2006-07-11 Procede de fabrication d'une tole d'acier austenitique fer-carbone-manganese ayant une excellente resistance a la fissuration differee, et tole ainsi produit

Publications (1)

Publication Number Publication Date
ZA200900177B true ZA200900177B (en) 2009-11-25

Family

ID=37022992

Family Applications (1)

Application Number Title Priority Date Filing Date
ZA200900177A ZA200900177B (en) 2006-07-11 2009-01-08 Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced

Country Status (17)

Country Link
US (3) US9200355B2 (fr)
EP (3) EP1878811A1 (fr)
JP (1) JP5697125B2 (fr)
KR (1) KR101105178B1 (fr)
CN (1) CN101506402B (fr)
AU (1) AU2007273982B2 (fr)
BR (2) BR122013030320B8 (fr)
CA (2) CA2787998C (fr)
ES (1) ES2757815T3 (fr)
HU (1) HUE046647T2 (fr)
MA (1) MA30583B1 (fr)
MX (1) MX2009000356A (fr)
PL (1) PL2041330T3 (fr)
RU (1) RU2417265C2 (fr)
UA (1) UA95642C2 (fr)
WO (1) WO2008007192A2 (fr)
ZA (1) ZA200900177B (fr)

Families Citing this family (57)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1878811A1 (fr) 2006-07-11 2008-01-16 ARCELOR France Procede de fabrication d'une tole d'acier austenitique fer-carbone-manganese ayant une excellente resistance a la fissuration differee, et tole ainsi produit
US9067260B2 (en) 2006-09-06 2015-06-30 Arcelormittal France Steel plate for producing light structures and method for producing said plate
WO2009090443A1 (fr) 2008-01-15 2009-07-23 Arcelormittal France Procédé pour fabriquer des produits estampés, et produits estampés préparés à l'aide de celui-ci
DE102008056844A1 (de) 2008-11-12 2010-06-02 Voestalpine Stahl Gmbh Manganstahlband und Verfahren zur Herstellung desselben
AU2008364127B2 (en) * 2008-11-14 2014-09-18 Clecim SAS Method and device for measuring a chemical composition of a liquid metal suitable for coating a steel strip
EP2208803A1 (fr) 2009-01-06 2010-07-21 ThyssenKrupp Steel Europe AG Acier à résistance élevée, formable à froid, produit plat en acier, procédé de fabrication d'un produit plat en acier et utilisation du produit plat en acier
DE102010034161B4 (de) * 2010-03-16 2014-01-02 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung von Werkstücken aus Leichtbaustahl mit über die Wanddicke einstellbaren Werkstoffeigenschaften
WO2012052626A1 (fr) 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
IT1403129B1 (it) * 2010-12-07 2013-10-04 Ct Sviluppo Materiali Spa Procedimento per la produzione di acciaio ad alto manganese con resistenza meccanica e formabilità elevate, ed acciaio così ottenibile.
CN102330019A (zh) * 2011-10-28 2012-01-25 上海大学 含钒低碳高强度高塑性的孪晶诱发塑性钢的制备方法
KR101353649B1 (ko) * 2011-12-23 2014-01-20 주식회사 포스코 내부식성이 우수한 스프링용 선재 및 강선, 스프링용 강선 및 스프링의 제조방법
EP2799581B1 (fr) 2011-12-28 2019-11-27 Posco Acier austénitique résistant à l'usure et présentant une usinabilité et une résistance améliorées dans des zones affectées par la température de soudage, et procédé de production correspondant
KR101382950B1 (ko) * 2011-12-28 2014-04-09 주식회사 포스코 용접 열영향부 인성이 우수한 오스테나이트계 내마모 강재
DE102012100509B4 (de) * 2012-01-23 2015-10-08 Thyssenkrupp Rasselstein Gmbh Verfahren zum Veredeln einer metallischen Beschichtung auf einem Stahlband
EP2848715B1 (fr) * 2013-09-13 2018-10-31 ThyssenKrupp Steel Europe AG Procédé de fabrication d'un composant en acier revêtu d'une coiffe métallique protégeant de la corrosion
JP5608280B1 (ja) * 2013-10-21 2014-10-15 大同工業株式会社 チェーン用軸受部、その製造方法、及びそれを用いたチェーン
FR3014449B1 (fr) * 2013-12-06 2020-12-04 Fives Celes Section de recuit apres galvanisation comportant un appareil de chauffage a inducteur a flux transverse
KR101568526B1 (ko) 2013-12-24 2015-11-11 주식회사 포스코 용접 열영향부 인성이 우수한 오스테나이트 강재
KR101585741B1 (ko) 2013-12-25 2016-01-14 주식회사 포스코 강성, 내덴트성 및 내부식성이 우수한 고강도 경량 클래드 강판 및 그 제조방법
JP6675314B2 (ja) 2014-01-30 2020-04-01 アルセロールミタル 電気亜鉛めっき金属シートからうねりの少ない部品を製造するための方法、対応する部品および車両
CN103805864B (zh) * 2014-03-13 2016-08-24 国家电网公司 一种螺栓钢及其制备方法
AR101904A1 (es) * 2014-09-29 2017-01-18 Nippon Steel & Sumitomo Metal Corp Material de acero y tuberías expansibles para la industria del petróleo
DE102015111680A1 (de) * 2015-07-17 2017-01-19 Benteler Steel/Tube Gmbh Gasgenerator
KR101758525B1 (ko) * 2015-12-23 2017-07-27 주식회사 포스코 고강도 고연신율 고Mn강의 열처리 방법
KR101889187B1 (ko) * 2015-12-23 2018-08-16 주식회사 포스코 열간 가공성이 우수한 비자성 강재 및 그 제조방법
WO2017203315A1 (fr) 2016-05-24 2017-11-30 Arcelormittal Tôle mince en acier laminée à froid et recuite, son procédé de production et utilisation d'un tel acier pour produire des pièces de véhicule
WO2017203313A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Procédé de fabrication d'une tôle d'acier de remploi à matrice austénitique
WO2017203309A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Tôle d'acier twip ayant une matrice austénitique
MA45114A (fr) * 2016-05-24 2019-04-10 Arcelormittal Procédé de fabrication d'une tôle d'acier twip ayant une matrice austénitique
WO2017203314A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Tôle d'acier twip ayant une matrice austénitique
WO2017203310A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique
RU2652934C1 (ru) * 2016-11-28 2018-05-03 Федеральное государственное автономное образовательное учреждение высшего образования "Национальный исследовательский технологический университет "МИСиС" Конструкционная деформируемая аустенитная немагнитная теплостойкая криогенная сталь с высокой удельной прочностью и способ ее обработки
KR101917473B1 (ko) * 2016-12-23 2018-11-09 주식회사 포스코 내마모성과 인성이 우수한 오스테나이트계 강재 및 그 제조방법
RU2644709C1 (ru) * 2017-06-01 2018-02-13 Юлия Алексеевна Щепочкина Износостойкий сплав на основе железа
US11033963B1 (en) * 2017-10-31 2021-06-15 United States Of America As Represented By The Administrator Of National Aeronautics And Space Administration Method for making small diameter nickel-titanium metal alloy balls
KR102020386B1 (ko) 2017-12-24 2019-09-10 주식회사 포스코 고 강도 오스테나이트계 고 망간 강재 및 그 제조방법
WO2019171157A1 (fr) * 2018-03-09 2019-09-12 Arcelormittal Procédé de fabrication de pièces durcies à la presse à productivité élevée
US10481052B2 (en) 2018-03-28 2019-11-19 Ford Global Technologies, Llc Quality control process to assess the aluminized coating characteristics of hot stamped parts
CN112513310A (zh) 2018-05-24 2021-03-16 通用汽车环球科技运作有限责任公司 改善压制硬化钢的强度和延性的方法
CN112534078A (zh) 2018-06-19 2021-03-19 通用汽车环球科技运作有限责任公司 具有增强的机械性质的低密度压制硬化钢
WO2020070545A1 (fr) 2018-10-04 2020-04-09 Arcelormittal Procédé d'emboutissage à chaud
KR20200046831A (ko) * 2018-10-25 2020-05-07 주식회사 포스코 표면품질 및 응력부식균열 저항성이 우수한 극저온용 오스테나이트계 고 망간 강재 및 그 제조방법
KR102245226B1 (ko) * 2018-10-25 2021-04-28 주식회사 포스코 산소 절단성이 우수한 고망간 강재 및 그 제조방법
WO2020085855A1 (fr) * 2018-10-25 2020-04-30 주식회사 포스코 Acier à haute teneur en manganèse ayant d'excellentes propriétés de coupe à l'oxygène et procédé de fabrication s'y rapportant
CN109487178B (zh) * 2018-12-29 2020-06-16 广西长城机械股份有限公司 高纯净超高锰钢及其制备工艺
KR102145761B1 (ko) 2019-01-03 2020-08-19 (주)영신특수강 파쇄기용 고망간 주조합금강 및 그 제조방법
WO2020153407A1 (fr) * 2019-01-25 2020-07-30 Ｊｆｅスチール株式会社 Procédé de production de brame coulée d'acier à haute teneur en manganèse et procédé de production de billette ou de tôle d'acier à haute teneur en manganèse
EP3726206B1 (fr) 2019-03-26 2022-11-02 FEI Company Procédés et systèmes d'analyse d'inclusion
CN110093573A (zh) * 2019-06-06 2019-08-06 阿克索健康科技(北京)有限公司 量子能量信息片的制备方法及量子能量信息片、穿戴装置
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
WO2021084303A1 (fr) * 2019-10-30 2021-05-06 Arcelormittal Procédé d'emboutissage à chaud
MX2022005543A (es) * 2019-11-07 2022-06-08 Weir Minerals Australia Ltd Aleacion para abrasion por ranurado de alta tension.
CN111334796B (zh) * 2020-03-23 2022-05-20 首钢集团有限公司 热冲压用钢制造方法、热冲压用钢及热冲压部件制造方法
CN113061798A (zh) * 2021-03-22 2021-07-02 中铁宝桥集团有限公司 一种合金化高锰钢的冶炼工艺
US11998192B2 (en) 2021-05-10 2024-06-04 Cilag Gmbh International Adaptive control of surgical stapling instrument based on staple cartridge type
CN115449697B (zh) * 2022-09-29 2023-04-25 南通高欣耐磨科技股份有限公司 一种陶瓷颗粒增强高锰钢基复合材料锤头及其制备方法
CN118147541B (zh) * 2024-02-01 2024-10-11 大湾区大学(筹) 一种超高强度、高韧性的钢及其制备方法和应用

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3963531A (en) * 1975-02-28 1976-06-15 Armco Steel Corporation Cold rolled, ductile, high strength steel strip and sheet and method therefor
JPS63266042A (ja) 1986-12-24 1988-11-02 Kawasaki Steel Corp Ｃｖｄ処理に適した非磁性金型用鋼
CA2006292C (fr) * 1988-12-22 1997-09-09 Yoshiyuki Ushigami Ruban d'acier tres mince a faible perte dans le fer et a induction magnetique elevee et sa methode de fabrication
CA2100656C (fr) 1991-12-30 2000-02-22 Tai Woung Kim Acier austenitique a forte teneur en manganese offrant des caracteristiques superieures de formalite, resistance et sondabilite, et procede d'elaboration
JPH06346192A (ja) * 1993-06-11 1994-12-20 Kawasaki Steel Corp 耐衝撃性に優れた薄鋼板
JPH07113117A (ja) 1993-10-14 1995-05-02 Kobe Steel Ltd 高Ｍｎ非磁性鋼の鋼片加熱時における脱炭防止方法
JP3403263B2 (ja) * 1994-11-14 2003-05-06 臼井国際産業株式会社 加工性・耐食性の均一性に優れた耐熱・耐食性めっき鋼材
JPH11102777A (ja) * 1997-07-28 1999-04-13 Nkk Corp 連続誘導加熱装置
US6261388B1 (en) 1998-05-20 2001-07-17 Nippon Steel Corporation Cold forging steel having improved resistance to grain coarsening and delayed fracture and process for producing same
IT1302329B1 (it) 1998-09-15 2000-09-05 Acciai Speciali Terni Spa Procedimento per il trattamento termico di nastri di acciaio.
FR2796083B1 (fr) * 1999-07-07 2001-08-31 Usinor Procede de fabrication de bandes en alliage fer-carbone-manganese, et bandes ainsi produites
US6572713B2 (en) * 2000-10-19 2003-06-03 The Frog Switch And Manufacturing Company Grain-refined austenitic manganese steel casting having microadditions of vanadium and titanium and method of manufacturing
FR2829775B1 (fr) * 2001-09-20 2003-12-26 Usinor Procede de fabrication de tubes roules et soudes comportant une etape finale d'etirage ou d'hydroformage et tube soude ainsi obtenu
CN1169991C (zh) * 2001-10-19 2004-10-06 住友金属工业株式会社 具有优异的可加工性和成型精度的薄钢板及其制造方法
FR2857980B1 (fr) * 2003-07-22 2006-01-13 Usinor Procede de fabrication de toles d'acier austenitique fer-carbone-manganese, a haute resistance, excellente tenacite et aptitude a la mise en forme a froid, et toles ainsi produites
FR2859064B1 (fr) 2003-08-18 2005-12-30 Satimo Sa Dispositif de controle du debit d'absorption specifique d'objets rayonnants fabriques en serie et notamment de telephones portables
JP4599632B2 (ja) 2003-08-18 2010-12-15 株式会社ニコン 照度分布の評価方法、光学部材の製造方法、照度測定装置、露光装置および露光方法
JP2006063358A (ja) * 2004-08-24 2006-03-09 Tanaka Galvanizing Co Ltd 鋼材に高耐候性を付与する表面処理方法
FR2876711B1 (fr) * 2004-10-20 2006-12-08 Usinor Sa Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese
FR2878257B1 (fr) 2004-11-24 2007-01-12 Usinor Sa Procede de fabrication de toles d'acier austenitique, fer-carbone-manganese a tres hautes caracteristiques de resistance et d'allongement, et excellente homogeneite
FR2881144B1 (fr) * 2005-01-21 2007-04-06 Usinor Sa Procede de fabrication de toles d'acier austenitique fer-carbone-manganese a haute resistance a la fissuration differee, et toles ainsi produites
EP1878811A1 (fr) 2006-07-11 2008-01-16 ARCELOR France Procede de fabrication d'une tole d'acier austenitique fer-carbone-manganese ayant une excellente resistance a la fissuration differee, et tole ainsi produit

Also Published As

Publication number Publication date
BR122013030320B8 (pt) 2018-07-10
EP3587611A1 (fr) 2020-01-01
BR122013030320B1 (pt) 2018-05-15
US10131964B2 (en) 2018-11-20
JP5697125B2 (ja) 2015-04-08
AU2007273982B2 (en) 2012-03-29
RU2009104474A (ru) 2010-08-20
CA2787998C (fr) 2016-01-19
CA2657508A1 (fr) 2008-01-17
WO2008007192A2 (fr) 2008-01-17
US20160010187A1 (en) 2016-01-14
KR101105178B1 (ko) 2012-01-12
BRPI0715458A2 (pt) 2013-03-05
US20160010173A1 (en) 2016-01-14
CA2657508C (fr) 2012-11-13
RU2417265C2 (ru) 2011-04-27
CN101506402B (zh) 2013-06-19
UA95642C2 (ru) 2011-08-25
EP1878811A1 (fr) 2008-01-16
US20090308499A1 (en) 2009-12-17
CN101506402A (zh) 2009-08-12
AU2007273982A1 (en) 2008-01-17
KR20090043508A (ko) 2009-05-06
ES2757815T3 (es) 2020-04-30
MX2009000356A (es) 2009-01-29
US9200355B2 (en) 2015-12-01
JP2009542920A (ja) 2009-12-03
HUE046647T2 (hu) 2020-03-30
EP2041330B1 (fr) 2019-09-11
PL2041330T3 (pl) 2020-04-30
WO2008007192A3 (fr) 2008-03-20
EP2041330A2 (fr) 2009-04-01
US10006099B2 (en) 2018-06-26
BRPI0715458B1 (pt) 2014-11-25
CA2787998A1 (fr) 2008-01-17
MA30583B1 (fr) 2009-07-01

Similar Documents

Publication Publication Date Title
ZA200900177B (en) Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced
EP2377965A4 (fr) Tôle d'acier plaquée d'aluminium ayant une meilleure résistance à la corrosion, produit formé par pressage à chaud utilisant cette tôle et procédé de fabrication de cette tôle
PL2171112T3 (pl) Sposób wytwarzania blach stalowych o dobrych własnościach wytrzymałościowych i plastycznych oraz blachy tak wytworzone
EP2240618A4 (fr) Tôle d'acier à haute résistance avec une excellente ténacité à basse température et procédé de fabrication de celle-ci
ZA200907430B (en) Process for manufacturing cold-rolled and annealed steel sheet with a very high strength, and sheet thus produced
EP2357259A4 (fr) Acier ferritique inoxydable de grande pureté présentant une excellente résistance à la corrosion, et procédé de production de celui-ci
EP2154262A4 (fr) Tôle d'acier résistante à l'abrasion extrêmement facile à mettre en uvre et son procédé de production
EP2309014A4 (fr) Tôles d'acier épaisses laminées à chaud présentant une résistance élevée à la traction et une excellente résistance à basse température, et procédé de production de celles-ci
EP2097548A4 (fr) Tôle d'acier à haute résistance et à remarquable résistance à l'impact, et son procédé de fabrication
EP2009130A4 (fr) Processus de fabrication de toles d'acier enduites de zinc par immersion a chaud faciles à traiter, ne farinant pas, avec propriété de glissement
ZA200807786B (en) Steel tube with excellent steam oxidation resistance and method for producing the steel tube
EP2128295A4 (fr) Tôle d'acier galvanisé à chaud, haute résistance, possédant une excellente aptitude au moulage, et son procédé de production
ZA200902032B (en) Articles having improved resistance to thermal cracking
EP2143822A4 (fr) Feuille d'acier plaqué pour boîte-boisson et procédé de production de cette feuille
EP2143815A4 (fr) Acier inoxydable austénitique possédant d'excellentes propriétés de résistance à la corrosion intergranulaire et de résistance à la fissuration par corrosion sous contraintes, et procédé de production d'acier inoxydable austénitique
EP2138596A4 (fr) Feuille d'acier pour une utilisation dans une boîte métallique, et son procédé de fabrication
EP2458038A4 (fr) Acier inoxydable pour pile à combustible présentant une excellente résistance à la corrosion et son procédé de production
PL2137327T3 (pl) Stal do obróbki na gorąco lub hartowania w tłoczniku, o ulepszonej ciągliwości
EP1992708A4 (fr) Procede de production d'une tole d'acier magnetique a grains orientes presentant d'excellentes proprietes magnetiques
EP2208799A4 (fr) Acier destiné à des tuyaux en acier qui présentent une excellente résistance à l'acidité, et procédé de fabrication de celui-ci
EP1918399A4 (fr) Feuille d acier inoxydable ferritique présentant une excellente résistance à la corrosion et son procédé de production
EP2520683A4 (fr) Tôle d'acier à haute résistance présentant une excellente résistance aux fissures fragiles et procédé de fabrication de celle-ci
EP2617857A4 (fr) Tuyau d'acier soudé épais présentant une excellente ténacité à faible température, procédé de production d'un tuyau d'acier soudé épais présentant une excellente ténacité à faible température, et tôle d'acier destinée à produire un tuyau d'acier soudé épais
EP2692889A4 (fr) Feuille d'acier inoxydable ferritique présentant d'excellentes résistance à la chaleur et aptitude au traitement, et son procédé de production
EP2290116A4 (fr) Tôle d'acier épaisse présentant une résistance élevée et son procédé de fabrication