MA30583B1 - Procede de fabrication d'une feuille d'acier austenitique fer-carbone-manganese dotee d'une excellente resistance a la fissuration differee, et feulle ainsi produite - Google Patents

Procede de fabrication d'une feuille d'acier austenitique fer-carbone-manganese dotee d'une excellente resistance a la fissuration differee, et feulle ainsi produite

Info

Publication number
MA30583B1
MA30583B1 MA31559A MA31559A MA30583B1 MA 30583 B1 MA30583 B1 MA 30583B1 MA 31559 A MA31559 A MA 31559A MA 31559 A MA31559 A MA 31559A MA 30583 B1 MA30583 B1 MA 30583B1
Authority
MA
Morocco
Prior art keywords
austenitic steel
manganized
fer
feel
carbon
Prior art date
Application number
MA31559A
Other languages
English (en)
Inventor
Colin Scott
Philippe Cugy
Christian Allely
Original Assignee
Thyssenkrupp Steel Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Thyssenkrupp Steel Ag filed Critical Thyssenkrupp Steel Ag
Publication of MA30583B1 publication Critical patent/MA30583B1/fr

Abstract

L'INVENTION CONCERNE UNE FEUILLE D'ACIER AUSTÉNITIQUE EXCELLENTE EN TERME DE RÉSISTANCE À LA FISSURATION DIFFÉRÉE, LA COMPOSITION DE LADITE FEUILLE COMPRENANT, EN POIDS : 0,35 % < C < 1,05 %, 15 %< MN < 26 %, SI < 3 %, AL < 0,050 %, S < 0,030 %, P < 0,080 %, N < 0,1 %, AU MOINS UN ÉLÉMENT MÉTALLIQUE X CHOISI PARMI LE VANADIUM, LE TITANE, LE NIOBIUM, LE MOLYBDÈNE, LE CHROME : 0,050 % < V < 0,50 %, 0,040 % = TI < 0,50 %, 0,070 % < NB < 0,50 %, 0,14 %< MO < 2 %, 0,070 % < CR < 2 % ET ÉVENTUELLEMENT, UN OU PLUSIEURS ÉLÉMENTS CHOISIS PARMI 0,0005 % < B < 0,010 %, NI < 2 %, CU < 5 %, LE RESTE ÉTANT DU FER ET DES IMPURETÉS INÉVITABLES INHÉRENTES À LA FABRICATION, INCLUANT DE L'HYDROGÈNE, LA QUANTITÉ XP DUDIT AU MOINS UN ÉLÉMENT MÉTALLIQUE SOUS LA FORME DE CARBURES, NITRURES OU CARBONITRURES REPRÉSENTANT, EN POIDS : 0,030 % < VP < 0,40 %, 0,030 %< TIP < 0,50 %, 0,040 % < NBP < 0,40 %, 0,14 %< MOP < 0,44 %, 0,070 % < CRP < 0,6 %, LA TENEUR EN HYDROGÈNE HMAX DÉSIGNANT LA TENEUR MAXIMALE EN HYDROGÈNE QUI PEUT ÊTRE MESURÉE À PARTIR D'UNE SÉRIE D'AU MOINS CINQ ÉCHANTILLONS, ET LA QUANTITÉ XP, EN POIDS, ÉTANT TELLE QUE (I) < 3,3.
MA31559A 2006-07-11 2009-01-09 Procede de fabrication d'une feuille d'acier austenitique fer-carbone-manganese dotee d'une excellente resistance a la fissuration differee, et feulle ainsi produite MA30583B1 (fr)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
EP06291136A EP1878811A1 (fr) 2006-07-11 2006-07-11 Procede de fabrication d'une tole d'acier austenitique fer-carbone-manganese ayant une excellente resistance a la fissuration differee, et tole ainsi produit

Publications (1)

Publication Number Publication Date
MA30583B1 true MA30583B1 (fr) 2009-07-01

Family

ID=37022992

Family Applications (1)

Application Number Title Priority Date Filing Date
MA31559A MA30583B1 (fr) 2006-07-11 2009-01-09 Procede de fabrication d'une feuille d'acier austenitique fer-carbone-manganese dotee d'une excellente resistance a la fissuration differee, et feulle ainsi produite

Country Status (17)

Country Link
US (3) US9200355B2 (fr)
EP (3) EP1878811A1 (fr)
JP (1) JP5697125B2 (fr)
KR (1) KR101105178B1 (fr)
CN (1) CN101506402B (fr)
AU (1) AU2007273982B2 (fr)
BR (2) BRPI0715458B1 (fr)
CA (2) CA2787998C (fr)
ES (1) ES2757815T3 (fr)
HU (1) HUE046647T2 (fr)
MA (1) MA30583B1 (fr)
MX (1) MX2009000356A (fr)
PL (1) PL2041330T3 (fr)
RU (1) RU2417265C2 (fr)
UA (1) UA95642C2 (fr)
WO (1) WO2008007192A2 (fr)
ZA (1) ZA200900177B (fr)

Families Citing this family (57)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1878811A1 (fr) 2006-07-11 2008-01-16 ARCELOR France Procede de fabrication d'une tole d'acier austenitique fer-carbone-manganese ayant une excellente resistance a la fissuration differee, et tole ainsi produit
US9067260B2 (en) 2006-09-06 2015-06-30 Arcelormittal France Steel plate for producing light structures and method for producing said plate
WO2009090443A1 (fr) * 2008-01-15 2009-07-23 Arcelormittal France Procédé pour fabriquer des produits estampés, et produits estampés préparés à l'aide de celui-ci
DE102008056844A1 (de) 2008-11-12 2010-06-02 Voestalpine Stahl Gmbh Manganstahlband und Verfahren zur Herstellung desselben
RU2482467C2 (ru) * 2008-11-14 2013-05-20 Сименс Фаи Металз Текнолоджиз Сас Способ и устройство измерения химического состава жидкого металла, предназначенного для покрытия стальной полосы
EP2208803A1 (fr) 2009-01-06 2010-07-21 ThyssenKrupp Steel Europe AG Acier à résistance élevée, formable à froid, produit plat en acier, procédé de fabrication d'un produit plat en acier et utilisation du produit plat en acier
DE102010034161B4 (de) * 2010-03-16 2014-01-02 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung von Werkstücken aus Leichtbaustahl mit über die Wanddicke einstellbaren Werkstoffeigenschaften
WO2012052626A1 (fr) 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
IT1403129B1 (it) * 2010-12-07 2013-10-04 Ct Sviluppo Materiali Spa Procedimento per la produzione di acciaio ad alto manganese con resistenza meccanica e formabilità elevate, ed acciaio così ottenibile.
CN102330019A (zh) * 2011-10-28 2012-01-25 上海大学 含钒低碳高强度高塑性的孪晶诱发塑性钢的制备方法
KR101353649B1 (ko) * 2011-12-23 2014-01-20 주식회사 포스코 내부식성이 우수한 스프링용 선재 및 강선, 스프링용 강선 및 스프링의 제조방법
CN104136647A (zh) * 2011-12-28 2014-11-05 Posco公司 在焊接热影响区具有优异机械加工性及韧性的耐磨奥氏体钢及其生产方法
KR101382950B1 (ko) * 2011-12-28 2014-04-09 주식회사 포스코 용접 열영향부 인성이 우수한 오스테나이트계 내마모 강재
DE102012100509B4 (de) * 2012-01-23 2015-10-08 Thyssenkrupp Rasselstein Gmbh Verfahren zum Veredeln einer metallischen Beschichtung auf einem Stahlband
EP2848715B1 (fr) * 2013-09-13 2018-10-31 ThyssenKrupp Steel Europe AG Procédé de fabrication d'un composant en acier revêtu d'une coiffe métallique protégeant de la corrosion
JP5608280B1 (ja) * 2013-10-21 2014-10-15 大同工業株式会社 チェーン用軸受部、その製造方法、及びそれを用いたチェーン
FR3014449B1 (fr) 2013-12-06 2020-12-04 Fives Celes Section de recuit apres galvanisation comportant un appareil de chauffage a inducteur a flux transverse
KR101568526B1 (ko) 2013-12-24 2015-11-11 주식회사 포스코 용접 열영향부 인성이 우수한 오스테나이트 강재
KR101585741B1 (ko) 2013-12-25 2016-01-14 주식회사 포스코 강성, 내덴트성 및 내부식성이 우수한 고강도 경량 클래드 강판 및 그 제조방법
WO2015114405A1 (fr) 2014-01-30 2015-08-06 Arcelormittal Procédé de réalisation de pièces à faible ondulation à partir d'une tôle électrozinguée, pièce et véhicule correspondants
CN103805864B (zh) * 2014-03-13 2016-08-24 国家电网公司 一种螺栓钢及其制备方法
AR101904A1 (es) * 2014-09-29 2017-01-18 Nippon Steel & Sumitomo Metal Corp Material de acero y tuberías expansibles para la industria del petróleo
DE102015111680A1 (de) * 2015-07-17 2017-01-19 Benteler Steel/Tube Gmbh Gasgenerator
KR101889187B1 (ko) * 2015-12-23 2018-08-16 주식회사 포스코 열간 가공성이 우수한 비자성 강재 및 그 제조방법
KR101758525B1 (ko) * 2015-12-23 2017-07-27 주식회사 포스코 고강도 고연신율 고Mn강의 열처리 방법
WO2017203314A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Tôle d'acier twip ayant une matrice austénitique
WO2017203341A1 (fr) 2016-05-24 2017-11-30 Arcelormittal Procédé de fabrication d'une tôle d'acier twip ayant une matrice austénitique
WO2017203315A1 (fr) 2016-05-24 2017-11-30 Arcelormittal Tôle mince en acier laminée à froid et recuite, son procédé de production et utilisation d'un tel acier pour produire des pièces de véhicule
WO2017203309A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Tôle d'acier twip ayant une matrice austénitique
WO2017203310A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Procédé de fabrication d'une tôle d'acier twip à microstructure austénitique
WO2017203313A1 (fr) * 2016-05-24 2017-11-30 Arcelormittal Procédé de fabrication d'une tôle d'acier de remploi à matrice austénitique
RU2652934C1 (ru) * 2016-11-28 2018-05-03 Федеральное государственное автономное образовательное учреждение высшего образования "Национальный исследовательский технологический университет "МИСиС" Конструкционная деформируемая аустенитная немагнитная теплостойкая криогенная сталь с высокой удельной прочностью и способ ее обработки
KR101917473B1 (ko) * 2016-12-23 2018-11-09 주식회사 포스코 내마모성과 인성이 우수한 오스테나이트계 강재 및 그 제조방법
RU2644709C1 (ru) * 2017-06-01 2018-02-13 Юлия Алексеевна Щепочкина Износостойкий сплав на основе железа
US11033963B1 (en) * 2017-10-31 2021-06-15 United States Of America As Represented By The Administrator Of National Aeronautics And Space Administration Method for making small diameter nickel-titanium metal alloy balls
KR102020386B1 (ko) 2017-12-24 2019-09-10 주식회사 포스코 고 강도 오스테나이트계 고 망간 강재 및 그 제조방법
WO2019171157A1 (fr) 2018-03-09 2019-09-12 Arcelormittal Procédé de fabrication de pièces durcies à la presse à productivité élevée
US10481052B2 (en) 2018-03-28 2019-11-19 Ford Global Technologies, Llc Quality control process to assess the aluminized coating characteristics of hot stamped parts
WO2019222950A1 (fr) 2018-05-24 2019-11-28 GM Global Technology Operations LLC Procédé pour améliorer à la fois la résistance et la ductilité d'un acier trempé sur presse
US11612926B2 (en) 2018-06-19 2023-03-28 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
WO2020070545A1 (fr) 2018-10-04 2020-04-09 Arcelormittal Procédé d'emboutissage à chaud
KR102245226B1 (ko) * 2018-10-25 2021-04-28 주식회사 포스코 산소 절단성이 우수한 고망간 강재 및 그 제조방법
KR20200046831A (ko) * 2018-10-25 2020-05-07 주식회사 포스코 표면품질 및 응력부식균열 저항성이 우수한 극저온용 오스테나이트계 고 망간 강재 및 그 제조방법
WO2020085855A1 (fr) * 2018-10-25 2020-04-30 주식회사 포스코 Acier à haute teneur en manganèse ayant d'excellentes propriétés de coupe à l'oxygène et procédé de fabrication s'y rapportant
CN109487178B (zh) * 2018-12-29 2020-06-16 广西长城机械股份有限公司 高纯净超高锰钢及其制备工艺
KR102145761B1 (ko) 2019-01-03 2020-08-19 (주)영신특수강 파쇄기용 고망간 주조합금강 및 그 제조방법
US11819909B2 (en) * 2019-01-25 2023-11-21 Jfe Steel Corporation Method for manufacturing high-manganese steel cast slab and method for manufacturing high-manganese steel slab or steel sheet
EP3726206B1 (fr) 2019-03-26 2022-11-02 FEI Company Procédés et systèmes d'analyse d'inclusion
CN110093573A (zh) * 2019-06-06 2019-08-06 阿克索健康科技(北京)有限公司 量子能量信息片的制备方法及量子能量信息片、穿戴装置
US11530469B2 (en) * 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
WO2021084303A1 (fr) * 2019-10-30 2021-05-06 Arcelormittal Procédé d'emboutissage à chaud
CN114787407B (zh) * 2019-11-07 2023-10-17 伟尔矿物澳大利亚私人有限公司 用于高应力凿削磨蚀的合金
CN111334796B (zh) * 2020-03-23 2022-05-20 首钢集团有限公司 热冲压用钢制造方法、热冲压用钢及热冲压部件制造方法
CN113061798A (zh) * 2021-03-22 2021-07-02 中铁宝桥集团有限公司 一种合金化高锰钢的冶炼工艺
US20220354488A1 (en) 2021-05-10 2022-11-10 Cilag Gmbh International Absorbable surgical staples comprising sufficient structural properties during a tissue healing window
CN115449697B (zh) * 2022-09-29 2023-04-25 南通高欣耐磨科技股份有限公司 一种陶瓷颗粒增强高锰钢基复合材料锤头及其制备方法
CN118147541B (zh) * 2024-02-01 2024-10-11 大湾区大学(筹) 一种超高强度、高韧性的钢及其制备方法和应用

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3963531A (en) * 1975-02-28 1976-06-15 Armco Steel Corporation Cold rolled, ductile, high strength steel strip and sheet and method therefor
JPS63266042A (ja) 1986-12-24 1988-11-02 Kawasaki Steel Corp Ｃｖｄ処理に適した非磁性金型用鋼
CA2006292C (fr) * 1988-12-22 1997-09-09 Yoshiyuki Ushigami Ruban d'acier tres mince a faible perte dans le fer et a induction magnetique elevee et sa methode de fabrication
US5431753A (en) 1991-12-30 1995-07-11 Pohang Iron & Steel Co. Ltd. Manufacturing process for austenitic high manganese steel having superior formability, strengths and weldability
JPH06346192A (ja) * 1993-06-11 1994-12-20 Kawasaki Steel Corp 耐衝撃性に優れた薄鋼板
JPH07113117A (ja) 1993-10-14 1995-05-02 Kobe Steel Ltd 高Ｍｎ非磁性鋼の鋼片加熱時における脱炭防止方法
JP3403263B2 (ja) * 1994-11-14 2003-05-06 臼井国際産業株式会社 加工性・耐食性の均一性に優れた耐熱・耐食性めっき鋼材
JPH11102777A (ja) * 1997-07-28 1999-04-13 Nkk Corp 連続誘導加熱装置
US6261388B1 (en) 1998-05-20 2001-07-17 Nippon Steel Corporation Cold forging steel having improved resistance to grain coarsening and delayed fracture and process for producing same
IT1302329B1 (it) 1998-09-15 2000-09-05 Acciai Speciali Terni Spa Procedimento per il trattamento termico di nastri di acciaio.
FR2796083B1 (fr) * 1999-07-07 2001-08-31 Usinor Procede de fabrication de bandes en alliage fer-carbone-manganese, et bandes ainsi produites
US6572713B2 (en) * 2000-10-19 2003-06-03 The Frog Switch And Manufacturing Company Grain-refined austenitic manganese steel casting having microadditions of vanadium and titanium and method of manufacturing
FR2829775B1 (fr) * 2001-09-20 2003-12-26 Usinor Procede de fabrication de tubes roules et soudes comportant une etape finale d'etirage ou d'hydroformage et tube soude ainsi obtenu
US6586117B2 (en) * 2001-10-19 2003-07-01 Sumitomo Metal Industries, Ltd. Steel sheet having excellent workability and shape accuracy and a method for its manufacture
FR2857980B1 (fr) * 2003-07-22 2006-01-13 Usinor Procede de fabrication de toles d'acier austenitique fer-carbone-manganese, a haute resistance, excellente tenacite et aptitude a la mise en forme a froid, et toles ainsi produites
EP1666865A4 (fr) 2003-08-18 2007-09-26 Nikon Corp Procede d'evaluation de la repartition d'une source de lumiere, procede de fabrication d'un element optique, dispositif optique d'eclairement, procede et appareil d'exposition
FR2859064B1 (fr) 2003-08-18 2005-12-30 Satimo Sa Dispositif de controle du debit d'absorption specifique d'objets rayonnants fabriques en serie et notamment de telephones portables
JP2006063358A (ja) * 2004-08-24 2006-03-09 Tanaka Galvanizing Co Ltd 鋼材に高耐候性を付与する表面処理方法
FR2876711B1 (fr) * 2004-10-20 2006-12-08 Usinor Sa Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese
FR2878257B1 (fr) * 2004-11-24 2007-01-12 Usinor Sa Procede de fabrication de toles d'acier austenitique, fer-carbone-manganese a tres hautes caracteristiques de resistance et d'allongement, et excellente homogeneite
FR2881144B1 (fr) * 2005-01-21 2007-04-06 Usinor Sa Procede de fabrication de toles d'acier austenitique fer-carbone-manganese a haute resistance a la fissuration differee, et toles ainsi produites
EP1878811A1 (fr) 2006-07-11 2008-01-16 ARCELOR France Procede de fabrication d'une tole d'acier austenitique fer-carbone-manganese ayant une excellente resistance a la fissuration differee, et tole ainsi produit

Also Published As

Publication number Publication date
PL2041330T3 (pl) 2020-04-30
ES2757815T3 (es) 2020-04-30
HUE046647T2 (hu) 2020-03-30
EP3587611A1 (fr) 2020-01-01
KR101105178B1 (ko) 2012-01-12
UA95642C2 (ru) 2011-08-25
ZA200900177B (en) 2009-11-25
CA2787998A1 (fr) 2008-01-17
US20160010173A1 (en) 2016-01-14
BRPI0715458A2 (pt) 2013-03-05
BR122013030320B8 (pt) 2018-07-10
CN101506402B (zh) 2013-06-19
US10131964B2 (en) 2018-11-20
CA2787998C (fr) 2016-01-19
KR20090043508A (ko) 2009-05-06
US9200355B2 (en) 2015-12-01
CA2657508A1 (fr) 2008-01-17
EP2041330B1 (fr) 2019-09-11
WO2008007192A2 (fr) 2008-01-17
EP2041330A2 (fr) 2009-04-01
JP2009542920A (ja) 2009-12-03
MX2009000356A (es) 2009-01-29
AU2007273982B2 (en) 2012-03-29
US20160010187A1 (en) 2016-01-14
WO2008007192A3 (fr) 2008-03-20
RU2417265C2 (ru) 2011-04-27
JP5697125B2 (ja) 2015-04-08
BRPI0715458B1 (pt) 2014-11-25
AU2007273982A1 (en) 2008-01-17
US10006099B2 (en) 2018-06-26
US20090308499A1 (en) 2009-12-17
RU2009104474A (ru) 2010-08-20
BR122013030320B1 (pt) 2018-05-15
CA2657508C (fr) 2012-11-13
CN101506402A (zh) 2009-08-12
EP1878811A1 (fr) 2008-01-16

Similar Documents

Publication Publication Date Title
MA30583B1 (fr) Procede de fabrication d&#39;une feuille d&#39;acier austenitique fer-carbone-manganese dotee d&#39;une excellente resistance a la fissuration differee, et feulle ainsi produite
FR2881144B1 (fr) Procede de fabrication de toles d&#39;acier austenitique fer-carbone-manganese a haute resistance a la fissuration differee, et toles ainsi produites
ATE522635T1 (de) Nickelarmer austenitischer nichtrostender stahl mit stabilisierenden elementen
MA29691B1 (fr) Procede de fabrication de toles d&#39;acier presentant une haute resistance et une excellente ductilite, et toles ainsi produites
TW200632113A (en) A steel with sulfuric acid dew-point corrosion resistance
EP2264202A4 (fr) Acier inoxydable ferritique ayant d&#39;excellentes résistance à la chaleur et ténacité
ATE535622T1 (de) Kostengünstigerer, ultra-hochfester, hochzäher stahl
DK1900835T3 (da) Cobalt-chrom-jern-nikkel-legeringer egnede til nitridforstærkning
BRPI0802627A2 (pt) produtos tubulares para paìses produtores de petróleo em aço sem costura, aço de baixa liga e método de produção de tubulação em aço sem costura
BRPI0604291E2 (pt) liga austenÍtica homogÊnea À base de ferro com boa resistÊncia À corrosço e ao desgaste
WO2009025314A1 (fr) Acier faiblement allié à haute résistance présentant une excellente résistance à la fragilisation dans un environnement d&#39;hydrogène haute pression et procédé de fabrication de l&#39;acier
CA2615682A1 (fr) Acier inoxydable martensitique a haute resistance, usinable, faconnable a froid, resistant a la corrosion
WO2009044758A1 (fr) PRODUIT D&#39;ALLIAGE DE Cr-Ni HAUTE RÉSISTANCE ET TUYAUX DE PUITS DE PÉTROLE SANS SOUDURE UTILISANT CELUI-CI
DK1423548T3 (da) Duplexstållegering
SE0300574L (sv) Duplex rostfri stållegering och dess användning
EP1571227A4 (fr) Feuille d&#39;acier resistante a la chaleur contenant du chrome et presentant une excellente aptitude au fa onnage et son procede de production
EP2159295A3 (fr) Acier inoxydable martensitique et palier à roulement l&#39;utilisant
CN106222539A (zh) 一种高强高塑性不锈钢复合板及其制造方法
MXPA05009319A (es) Aleacion de acero inoxidable doble y usos de la misma.
JP2005120458A5 (fr)
WO2009103259A3 (fr) Alliage d&#39;acier pour acier faiblement allié destiné à la fabrication de tubes d&#39;acier sans soudure à haute résistance
SE0502016L (sv) Pulvermetallurgiskt tillverkat snabbstål
DK1882756T3 (da) Ferritisk kromstål
SE0501838L (sv) Kompositmaterial innefattande en lastbärande del och en korrosionsbeständig del
CO6210750A2 (es) Aleacion refractaria placa formadora de fibras y metodo para producir lana mineral