WO2024057824A1 - ビスマス系ガラス粉末及びこれを用いた複合粉末 - Google Patents

ビスマス系ガラス粉末及びこれを用いた複合粉末 Download PDF

Info

Publication number
WO2024057824A1
WO2024057824A1 PCT/JP2023/029851 JP2023029851W WO2024057824A1 WO 2024057824 A1 WO2024057824 A1 WO 2024057824A1 JP 2023029851 W JP2023029851 W JP 2023029851W WO 2024057824 A1 WO2024057824 A1 WO 2024057824A1
Authority
WO
WIPO (PCT)
Prior art keywords
bismuth
based glass
content
powder
glass powder
Prior art date
Application number
PCT/JP2023/029851
Other languages
English (en)
French (fr)
Inventor
嘉朗 北村
Original Assignee
日本電気硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本電気硝子株式会社 filed Critical 日本電気硝子株式会社
Publication of WO2024057824A1 publication Critical patent/WO2024057824A1/ja

Abstract

低融点特性を維持しつつ、熱的安定性の高いビスマス系ガラス粉末を提供する。　本発明のビスマス系ガラス粉末は、ガラス組成として、モル％で、Ｂｉ２Ｏ３　３０～６０％、ＳｎＯ２　０．１～２０％、Ｌａ２Ｏ３＋Ｎｄ２Ｏ３　０．１～２０％を含有することを特徴とする。

Description

ビスマス系ガラス粉末及びこれを用いた複合粉末
　本発明は、ビスマス系ガラス粉末及びこれを用いた複合粉末に関し、特に低膨張部材の低温封着に好適なビスマス系ガラス粉末及びこれを用いた複合粉末に関する。
　低膨張部材（例えば、ＡｌＮ、シリコン、無アルカリガラス等）の封着には低融点ガラスからなるガラス粉末が使用されている。そして、低融点ガラスは、用途に応じて、化学耐久性、機械的強度、電気絶縁性等の特性が要求される。
　これらの要求特性を満たす低融点ガラスとして、ＰｂＯを多量に含む鉛系ガラスが広く用いられてきた（特許文献１参照）。
　しかし、ＰｂＯは、環境負荷が大きいという問題がある。このため、鉛系ガラスから無鉛ガラスへの置き換えが望まれており、種々の無鉛ガラスが開発されるに至っている。特に、特許文献２等に記載のビスマス系ガラスは、低融点であるため、鉛系ガラスの代替候補として有力である。
特開昭６３－３１５５３６号公報 特開２０００－１２８５７４号公報
　しかし、上記ビスマス系ガラスは、熱的安定性が低く、封着時にビスマス系の結晶が析出する等の問題があった。
　熱的安定性を向上させるためには、ビスマス系ガラス中の低融点成分の含有割合を低下させることが効果的であるが、この場合、低融点特性が維持できず、封着温度が例えば５００℃超に上昇して、低膨張部材の熱劣化を招いてしまう。
　そこで、本発明は、上記事情に鑑み成されたものであり、低融点特性を維持しつつ、熱的安定性の高いビスマス系ガラス粉末を提供することを目的とする。
　本発明者が種々の実験を行った結果、特定の組成を有するビスマス系ガラス粉末により上記課題を解決できることを見出した。以下、上記課題を解決するビスマス系ガラス粉末、複合粉末の各態様について説明する。
　態様１のビスマス系ガラス粉末は、ガラス組成として、モル％で、Ｂｉ２Ｏ３　３０～６０％、ＳｎＯ２　０．１～２０％、Ｌａ２Ｏ３＋Ｎｄ２Ｏ３　０．１～２０％を含有することを特徴とする。本発明において、「Ａ＋Ｂ」とは、成分Ａ及び成分Ｂの合量を指す。例えば、「Ｌａ２Ｏ３＋Ｎｄ２Ｏ３」は、Ｌａ２Ｏ３及びＮｄ２Ｏ３の合量を指す。
　態様２のビスマス系ガラス粉末は、態様１において、さらに、ガラス組成として、モル％で、Ｂ２Ｏ３　１０～４０％、ＺｎＯ　１０～４０％、ＢａＯ　０．１～２０％、Ａｌ２Ｏ３　０．１～２０％を含有することが好ましい。
　態様３のビスマス系ガラス粉末は、態様１又は２において、軟化点が４４０℃以下であることが好ましい。ここで、「軟化点」は、マクロ型示差熱分析（ＤＴＡ）装置で測定した値である。ＤＴＡは、大気中において、昇温速度１０℃／分で行い、室温から測定を開始するものとする。
　態様４の複合粉末は、態様１～３のいずれか一つの態様のビスマス系ガラス粉末と耐火性フィラーを含むことが好ましい。
　態様５の複合粉末は、態様４において、耐火性フィラーの含有量が１～３０質量％であることが好ましい。
　態様６の複合粉末は、態様４又は５において、線熱膨張係数が４０×１０－７／℃以上、且つ８０×１０－７／℃以下であることが好ましい。ここで、「複合粉末の線熱膨張係数」は、緻密な焼結体を測定試料とし、３０～３００℃の温度範囲において、押し棒式線熱膨張係数測定（ＴＭＡ）装置で測定した値である。
　態様７の複合粉末は、態様４～６のいずれか一つの態様において、封着に用いることが好ましい。
　本発明によれば、低融点特性を維持しつつ、熱的安定性の高いビスマス系ガラス粉末を提供することができる。
　本発明のビスマス系ガラス粉末は、ガラス組成として、モル％で、Ｂｉ２Ｏ３　３０～６０％、ＳｎＯ２　０．１～２０％、Ｌａ２Ｏ３＋Ｎｄ２Ｏ３　０．１～２０％を含有することを特徴とする。上記のようにガラス組成を限定した理由は以下の通りである。なお、以下の含有範囲の説明において、％表示は、モル％を指す。
　Ｂｉ２Ｏ３は、軟化点を低下させる主要成分であり、また耐水性、耐候性を高める成分である。Ｂｉ２Ｏ３の含有量は３０～６０％であり、好ましくは３５～５５％、より好ましくは３８～５０％である。Ｂｉ２Ｏ３の含有量が少なくなると、軟化点が高くなり過ぎて、５００℃以下の温度域で軟化流動し難くなり、封着不良等が発生し易くなる。一方、Ｂｉ２Ｏ３の含有量が多くなると、線熱膨張係数が上昇して、低膨張部材（例えば、ＡｌＮ、シリコン、無アルカリガラス等）の封着後に、残留応力が過大になり易い。また熱的安定性（耐失透性）が低下し易くなり、ビスマイト等の結晶が析出し易くなる。
　ＳｎＯ２は、熱的安定性を高め、Ｂｉ２Ｏ３の還元を抑制する成分である。ＳｎＯ２の含有量は０．１～２０％であり、好ましくは０．５～１５％、より好ましくは１～１０％である。ＳｎＯ２の含有量が少なくなると、熱的安定性が低下し、封着時にビスマイト等の結晶が析出し易くなる。一方、ＳｎＯ２の含有量が多くなると、ガラスが失透し易くなる。
　Ｌａ２Ｏ３、Ｎｄ２Ｏ３は、熱的安定性を高め、ＳｎＯ２と併用することで、Ｂｉ２Ｏ３の還元をさらに抑制する成分である。Ｌａ２Ｏ３＋Ｎｄ２Ｏ３の含有量は０．１～２０％であり、好ましくは０．３～１５％、より好ましくは０．５～１０％である。Ｌａ２Ｏ３＋Ｎｄ２Ｏ３の含有量が少なくなると、熱的安定性が低下し、封着時にビスマイト等の結晶が析出し易くなる。一方、Ｌａ２Ｏ３＋Ｎｄ２Ｏ３の含有量が多くなると、ガラスが失透し易くなる。
　Ｌａ２Ｏ３の含有量は、好ましくは０～２０％、より好ましくは０．３～１５％、更に好ましくは０．５～１０％である。
　Ｎｄ２Ｏ３の含有量は、好ましくは０～２０％、より好ましくは０．３～１５％、更に好ましくは０．５～１０％である。
　上記の成分以外にも、例えば、以下の成分を添加することができる。
　Ｂ２Ｏ３は、ビスマス系ガラスのガラスネットワークを形成する成分である。Ｂ２Ｏ３の含有量は、好ましくは１０～４０％、より好ましくは１５～３５％、更に好ましくは１８～３０％である。Ｂ２Ｏ３の含有量が少なくなると、熱的安定性が低下し易くなる。一方、Ｂ２Ｏ３の含有量が多くなると、軟化点が高くなり過ぎて、５００℃以下の温度域で軟化流動し難くなり、封着不良等が発生し易くなる。
　ＺｎＯは、線熱膨張係数を低下させる成分である。ＺｎＯの含有量は、好ましくは１０～４０％、より好ましくは１５～３５％、更に好ましくは１８～３２％である。ＺｎＯの含有量が少なくなると、線熱膨張係数が上昇して、低膨張部材の封着後に、残留応力が過大になり易い。一方、ＺｎＯの含有量が多くなると、熱的安定性が低下し易くなる。
　ＢａＯは、熱的安定性を高める成分である。ＢａＯの含有量は、好ましくは０．１～２０％、より好ましくは１～１５％、更に好ましくは２～１０％である。ＢａＯの含有量が少なくなると、熱的安定性が低下し易くなる。一方、ＢａＯの含有量が多くなると、軟化点が高くなり過ぎて、５００℃以下の温度域で軟化流動し難くなり、封着不良等が発生し易くなる。
　Ａｌ２Ｏ３は、ガラス成形時における失透を抑制し、熱的安定性を高める成分である。Ａｌ２Ｏ３の含有量は、好ましくは０．１～２０％、より好ましくは０．５～１５％、更に好ましくは１～１０％である。Ａｌ２Ｏ３の含有量が少なくなると、熱的安定性が低下し易くなる。一方、Ａｌ２Ｏ３の含有量が多くなると、軟化点が高くなり過ぎて、５００℃以下の温度域で軟化流動し難くなり、封着不良等が発生し易くなる。
　ＳｉＯ２は、耐水性や耐候性を高める成分であるが、軟化点を著しく高める成分である。よって、ＳｉＯ２の含有量は好ましくは１％未満、より好ましくは０．５％未満、更に好ましくは０．１％未満である。
　Ｌｉ２Ｏ、Ｎａ２Ｏ及びＫ２Ｏは、軟化点を低下させる成分であるが、失透を促進する作用を有する成分である。よって、Ｌｉ２Ｏ、Ｎａ２Ｏ及びＫ２Ｏの合量及び個別含有量は、好ましくは２％以下、より好ましくは０．５％未満、更に好ましくは０．１％未満である。
　Ｐ２Ｏ５は、熱的安定性を高める成分であるが、その含有量が多くなると、ガラスの分相を助長する傾向がある。よって、Ｐ２Ｏ５の含有量は、好ましくは２％以下、より好ましくは０．５％未満、更に好ましくは０．１％未満である。
　ＭｏＯ３、Ｙ２Ｏ５及びＣｅＯ２は、熱的安定性を高める成分であるが、これらの含有量が多くなると、軟化点が高くなり過ぎて、５００℃以下の温度域で軟化流動し難くなり、封着不良等が発生し易くなる。よって、ＭｏＯ３、Ｙ２Ｏ５及びＣｅＯ２の合量及び個別含有量は、好ましくは２％以下、より好ましくは０．５％未満、更に好ましくは０．１％未満である。
　ＣｕＯとＦｅ２Ｏ３は、熱的安定性を高め、Ｂｉ２Ｏ３の還元を抑制する成分である。しかし、ＣｕＯとＦｅ２Ｏ３の含有量が多くなると、ガラスが失透し易くなる。ＣｕＯとＦｅ２Ｏ３の合量は０～１％未満であり、好ましくは０～０．５％未満、より好ましくは０～０．１％未満である。なお、ＣｕＯの含有量は、好ましくは０～１％未満、より好ましくは０～０．５％未満、更に好ましくは０～０．１％未満である。Ｆｅ２Ｏ３の含有量は、好ましくは０～０．５％未満、より好ましくは０～０．１％未満、更に好ましくは０～０．０５％未満である。
　環境上の理由から、実質的にＰｂＯを含有しないこと、つまりＰｂＯの含有量が０．１％未満であることが好ましい。また、ガラス組成中にＰｂＯを添加すると、絶縁体として使用する場合、ガラス中にＰｂ２＋が拡散して、電気絶縁性が低下する場合がある。
　上記成分以外にも、他の成分（ＭｇＯ、ＣａＯ、ＳｒＯ等）を５％まで添加してもよい。
　本発明のビスマス系ガラス粉末は、以下の特性を有することが好ましい。
　ビスマス系ガラス粉末の線熱膨張係数は、好ましくは８０×１０－７／℃以上、且つ１３０×１０－７／℃以下、より好ましくは９０×１０－７／℃以上、且つ１２０×１０－７／℃以下である。ビスマス系ガラス粉末の線熱膨張係数が上記範囲外になると、耐火性フィラーを添加しても、複合粉末の線熱膨張係数を低下させ難くなる。ここで、「ビスマス系ガラス粉末の線熱膨張係数」は、バルク試料を測定試料とし、３０～３００℃の温度範囲において、ＴＭＡ装置で測定した値である。
　ビスマス系ガラス粉末の軟化点は、好ましくは３９０～４４０℃、より好ましくは３９５～４３０℃である。ビスマス系ガラス粉末の軟化点が低過ぎると、ガラス組成中のＢｉ２Ｏ３の含有量が多くなる傾向があり、この場合、熱的安定性が低下し易くなる。一方、ビスマス系ガラス粉末の軟化点が高過ぎると、封着温度が不当に上昇し易くなる。
　ビスマス系ガラス粉末の平均粒子径Ｄ５０は、好ましくは５μｍ未満、０．５～４μｍ、特に１～３μｍである。ビスマス系ガラス粉末の平均粒子径Ｄ５０が大きいと、ビスマス系ガラス粉末の軟化点が低下し難くなる。一方、ビスマス系ガラス粉末の平均粒子径Ｄ５０が小さいと、取り扱い難くなる。ここで、「平均粒子径Ｄ５０」は、レーザー回折法により体積基準で測定した値を指す。
　本発明の複合粉末は、上記のビスマス系ガラス粉末と耐火性フィラーを含むことが好ましい。ビスマス系ガラス粉末は、封着の際に軟化変形して、低膨張部材等を気密一体化する成分である。耐火性フィラーは、骨材として作用し、複合粉末の熱膨張係数を低下させつつ、機械的強度を高める成分である。なお、複合粉末には、ビスマス系ガラス粉末と耐火性フィラー以外にも、視認性を高めるために、顔料等を含んでいてもよい。
　耐火性フィラーの含有量は、好ましくは１～３０質量％、より好ましくは１０～２５質量％、更に好ましくは１３～２０質量％である。耐火性フィラーが少なくなると、耐火性フィラーの添加効果が乏しくなり、耐火性フィラーが多くなると、複合粉末の軟化流動性が低下し易くなり、また封着の際に耐火性フィラーの一部がガラス中に溶け出し、その影響でガラスが失透し易くなる。
　耐火性フィラーとして、ウイレマイト系セラミック、β－ユークリプタイト、コーディエライト、ジルコン系セラミック、酸化錫系セラミック、リン酸ジルコニウム系セラミック、ムライト、石英ガラス、アルミナ等の粉末を単独、或いは組み合わせて使用することができる。その中でも、コーディエライトは、ビスマス系ガラスとの適合性が良好であり、線熱膨張係数を低下させる効果が高いため、好適である。
　複合粉末の線熱膨張係数は、好ましくは４０×１０－７／℃以上、且つ８０×１０－７／℃以下、より好ましくは４５×１０－７／℃以上、且つ７０×１０－７／℃以下である。複合粉末の線熱膨張係数が上記範囲外になると、低膨張部材（例えば、ＡｌＮ、シリコン、無アルカリガラス等）の封着後に、残留応力が過大になり易い。
　大気中での封着温度は、好ましくは５００℃以下、より好ましくは４９０℃以下である。封着温度が高過ぎると、低膨張部材及びその周辺部材の熱劣化を招く虞が生じる。ここで、「封着温度」は、フローボタン試験により評価する。詳述すると、比重に相当する質量の粉末を金型により外径２０ｍｍのボタン状に乾式プレスし、次に無アルカリガラス基板上にこのボタンを載置した上で、各種焼成温度で焼成した後、焼成後のボタン（フローボタン）の直径を測定し、その直径が２０ｍｍを超えた最小温度を封着温度とする。なお、焼成は、室温から焼成温度まで１０℃／分で昇温し、焼成温度で１０分間保持した後、焼成温度から室温まで１０℃／分で降温することで行う。
　本発明の複合粉末は、ビークルを添加し、ペースト化することにより、塗布作業性等を飛躍的に高めることができる。
　ビークルは、主に溶媒と樹脂バインダーとからなり、樹脂バインダーはペーストの粘性を調整する目的で添加される。また、必要に応じて、界面活性剤、増粘剤等を添加することもできる。作製されたペーストは、通常、ディスペンサーやスクリーン印刷機等の塗布機を用いて基板等に塗布された後、脱バインダー工程に供される。
　樹脂バインダーとしては、アクリル酸エステル（アクリル樹脂）、エチルセルロース、ポリエチレングリコール誘導体、ニトロセルロース、ポリメチルスチレン、ポリエチレンカーボネート、メタクリル酸エステル等が使用可能である。
　溶媒としては、Ｎ、Ｎ’－ジメチルホルムアミド（ＤＭＦ）、α－ターピネオール、高級アルコール、γ－ブチルラクトン（γ－ＢＬ）、テトラリン、ブチルカルビトールアセテート、酢酸エチル、酢酸イソアミル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ベンジルアルコール、トルエン、３－メトキシ－３－メチルブタノール、トリエチレングリコールモノメチルエーテル、トリエチレングリコールジメチルエーテル、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノブチルエーテル、トリプロピレングリコールモノメチルエーテル、トリプロピレングリコールモノブチルエーテル、プロピレンカーボネート、ジメチルスルホキシド（ＤＭＳＯ）、Ｎ－メチル－２－ピロリドン等が使用可能である。特に、α－ターピネオールは、高粘性であり、樹脂バインダー等の溶解性も良好であるため、好ましい。
　本発明の複合粉末は、所定形状の焼結させた焼結体に加工しても構わない。このようにすれば、封着すべき部分に安定して、配置することができる。
　焼結体は、複合粉末にビークルを添加して、スプレードライヤー等より顆粒化した後、得られた顆粒を金型に投入、プレス成型して、プレス体を作製し、更にそのプレス体を焼結することで作製することができる。
　本発明の複合粉末は、線熱膨張係数が低く、軟化流動性に優れるため、低膨張部材（例えば、ＡｌＮ、シリコン、無アルカリガラス等）の封着に用いることが好ましい。なお、本発明の複合粉末は、封着用途以外にも、低膨張部材の絶縁被覆に用いることも好ましい。
　以下、実施例に基づいて、本発明を詳細に説明する。
　表１は、本発明の実施例（試料Ｎｏ．１～４）および比較例（試料Ｎｏ．５～７）を示している。
Figure JPOXMLDOC01-appb-T000001
　次のようにして表１の各試料を調製した。まず、表中に示すガラス組成となるように、各種酸化物、炭酸塩等の原料を調合したガラスバッチを準備し、これを白金坩堝に入れて１０００℃で２時間溶融した。次に、溶融ガラスの一部を線熱膨張係数の測定試料としてステンレス製の金型に流し出し、その他の溶融ガラスを水冷ローラーによりフィルム状に成形した。最後に、フィルム状のガラスをボールミルまたはライカイ機にて粉砕した後、空気分級して、平均粒子径Ｄ５０約３．０μｍのビスマス系ガラス粉末を得た。
　以上の試料を用いて、軟化点、線熱膨張係数を評価した。その結果を表１に示す。
　ビスマス系ガラス粉末の線熱膨張係数は、緻密な焼結体を測定試料とし、３０～３００℃の温度範囲において、ＴＭＡ装置で測定したものである。
　ビスマス系ガラス粉末の軟化点は、マクロ型ＤＴＡ装置で測定したものである。測定は、大気中において、昇温速度１０℃／分で行い、室温から測定を開始した。
　続いて、ビスマス系ガラス粉末とコーディエライト粉末（表中ではＣＤＲと表記）を表中の質量割合で混合して、複合粉末を作製した。なお、コーディエライト粉末の平均粒子径Ｄ５０を２．０μｍ、９９％粒径Ｄ９９を８．０μｍとした。
　複合粉末の線熱膨張係数は、緻密な焼結体を測定試料とし、３０～３００℃の温度範囲において、ＴＭＡ装置で測定したものである。
　封着温度は、フローボタン試験により評価したものである。詳述すると、比重に相当する質量の複合粉末を金型により外径２０ｍｍのボタン状に乾式プレスし、次に無アルカリガラス基板（日本電気硝子社製ＯＡ－１０Ｇ）上にこのボタンを載置した上で、各種焼成温度で焼成した後、焼成後のボタン（フローボタン）の直径を測定し、その直径が２０ｍｍを超えた最小温度を封着温度とした。なお、封着温度の測定に際し、室温から焼成温度まで１０℃／分で昇温し、焼成温度で１０分間保持した後、焼成温度から室温まで１０℃／分で降温した。
　封着後の表面状態は、上記封着温度における焼成後のボタンを観察して、結晶の析出が観察されなかったものを「○」、結晶の析出が観察されたものを「×」として評価した。
　表から明らかなように、試料Ｎｏ．１～４は、ガラス組成が所定範囲に規制されているため、線熱膨張係数が６７×１０－７／℃以下であり、且つ封着温度が５００℃以下であった。更に封着後の表面状態の評価が良好であった。一方、試料Ｎｏ．５は、ビスマス系ガラス粉末中にＳｎＯ２、Ｌａ２Ｏ３及びＮｄ２Ｏ３を含有しないため、封着後の表面状態の評価が不良であった。試料Ｎｏ．６は、ビスマス系ガラス粉末中にＬａ２Ｏ３及びＮｄ２Ｏ３を含有しないため、封着後の表面状態の評価が不良であった。試料Ｎｏ．７は、ビスマス系ガラス粉末中にＳｎＯ２を含有しないため、封着後の表面状態の評価が不良であった。

Claims (7)

  1. 　ガラス組成として、モル％で、Ｂｉ２Ｏ３　３０～６０％、ＳｎＯ２　０．１～２０％、Ｌａ２Ｏ３＋Ｎｄ２Ｏ３　０．１～２０％を含有することを特徴とするビスマス系ガラス粉末。
  2. 　さらに、ガラス組成として、モル％で、Ｂ２Ｏ３　１０～４０％、ＺｎＯ　１０～４０％、ＢａＯ　０．１～２０％、Ａｌ２Ｏ３　０．１～２０％を含有することを特徴とする請求項１に記載のビスマス系ガラス粉末。
  3. 　軟化点が４４０℃以下であることを特徴とする請求項１又は２に記載のビスマス系ガラス粉末。
  4. 　請求項１又は２に記載のビスマス系ガラス粉末と耐火性フィラーを含むことを特徴とする複合粉末。
  5. 　耐火性フィラーの含有量が１～３０質量％であることを特徴とする請求項４に記載の複合粉末。
  6. 　線熱膨張係数が４０×１０－７／℃以上、且つ８０×１０－７／℃以下であることを特徴とする請求項４に記載の複合粉末。
  7. 　封着に用いることを特徴とする請求項４に記載の複合粉末。
PCT/JP2023/029851 2022-09-14 2023-08-18 ビスマス系ガラス粉末及びこれを用いた複合粉末 WO2024057824A1 (ja)