WO2024004430A1 - Film de transfert, procédé de formation de motif et procédé de fabrication de câblage de circuit - Google Patents

Film de transfert, procédé de formation de motif et procédé de fabrication de câblage de circuit Download PDF

Info

Publication number
WO2024004430A1
WO2024004430A1 PCT/JP2023/018834 JP2023018834W WO2024004430A1 WO 2024004430 A1 WO2024004430 A1 WO 2024004430A1 JP 2023018834 W JP2023018834 W JP 2023018834W WO 2024004430 A1 WO2024004430 A1 WO 2024004430A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
temporary support
mass
transfer film
transfer
Prior art date
Application number
PCT/JP2023/018834
Other languages
English (en)
Japanese (ja)
Inventor
壮二 石坂
一真 両角
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Publication of WO2024004430A1 publication Critical patent/WO2024004430A1/fr

Abstract

L'invention concerne : un film de transfert comprenant un support temporaire et une couche de transfert disposée sur le support temporaire, le support temporaire ayant un taux de déformation thermique inférieur ou égal à 1,0 % ; et une utilisation pour ledit film de transfert.
PCT/JP2023/018834 2022-06-30 2023-05-19 Film de transfert, procédé de formation de motif et procédé de fabrication de câblage de circuit WO2024004430A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2022-106641 2022-06-30
JP2022106641 2022-06-30
JP2023000740 2023-01-05
JP2023-000740 2023-01-05

Publications (1)

Publication Number Publication Date
WO2024004430A1 true WO2024004430A1 (fr) 2024-01-04

Family

ID=89381989

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/018834 WO2024004430A1 (fr) 2022-06-30 2023-05-19 Film de transfert, procédé de formation de motif et procédé de fabrication de câblage de circuit

Country Status (2)

Country Link
TW (1) TW202402530A (fr)
WO (1) WO2024004430A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004207425A (ja) * 2002-12-25 2004-07-22 Panac Co Ltd 耐熱収縮性が優れたプリント配線用導電層転写シート
WO2019074112A1 (fr) * 2017-10-13 2019-04-18 富士フイルム株式会社 Procédé de fabrication de ligne de câblage de circuit, procédé de fabrication de panneau tactile et procédé de fabrication de substrat ayant un motif
KR102127757B1 (ko) * 2020-01-28 2020-06-29 와이엠티 주식회사 회로기판 제조용 적층 구조체 및 회로기판의 제조방법
WO2020194948A1 (fr) * 2019-03-28 2020-10-01 富士フイルム株式会社 Matériau de transfert conducteur, procédé de production d'un motif conducteur, corps multicouche, panneau tactile et dispositif d'affichage à cristaux liquides
WO2021065317A1 (fr) * 2019-09-30 2021-04-08 富士フイルム株式会社 Film de transfert, stratifié ainsi que procédé de fabrication de celui-ci, capteur d'écran tactile, et écran tactile
WO2022092160A1 (fr) * 2020-10-30 2022-05-05 富士フイルム株式会社 Procédé de fabrication de stratifié, procédé de fabrication de substrat de câblage de circuit, et film de transfert

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004207425A (ja) * 2002-12-25 2004-07-22 Panac Co Ltd 耐熱収縮性が優れたプリント配線用導電層転写シート
WO2019074112A1 (fr) * 2017-10-13 2019-04-18 富士フイルム株式会社 Procédé de fabrication de ligne de câblage de circuit, procédé de fabrication de panneau tactile et procédé de fabrication de substrat ayant un motif
WO2020194948A1 (fr) * 2019-03-28 2020-10-01 富士フイルム株式会社 Matériau de transfert conducteur, procédé de production d'un motif conducteur, corps multicouche, panneau tactile et dispositif d'affichage à cristaux liquides
WO2021065317A1 (fr) * 2019-09-30 2021-04-08 富士フイルム株式会社 Film de transfert, stratifié ainsi que procédé de fabrication de celui-ci, capteur d'écran tactile, et écran tactile
KR102127757B1 (ko) * 2020-01-28 2020-06-29 와이엠티 주식회사 회로기판 제조용 적층 구조체 및 회로기판의 제조방법
WO2022092160A1 (fr) * 2020-10-30 2022-05-05 富士フイルム株式会社 Procédé de fabrication de stratifié, procédé de fabrication de substrat de câblage de circuit, et film de transfert

Also Published As

Publication number Publication date
TW202402530A (zh) 2024-01-16

Similar Documents

Publication Publication Date Title
JP7342246B2 (ja) 感光性転写材料、樹脂パターンの製造方法、回路配線の製造方法及びタッチパネルの製造方法
WO2021199542A1 (fr) Matériau de transfert sensible à la lumière, procédé de fabrication de motif de résine et procédé de fabrication de câblage de circuit
WO2024004430A1 (fr) Film de transfert, procédé de formation de motif et procédé de fabrication de câblage de circuit
WO2023182092A1 (fr) Film de transfert, stratifié, procédé de production de stratifié à motif de réserve, et procédé de production de stratifié à motif conducteur
WO2022181485A1 (fr) Procédé de fabrication de stratifié et procédé de fabrication de câblage de circuit
WO2022138154A1 (fr) Procédé de fabrication de stratifié, procédé de fabrication de câblage de circuit, et film de transfert
WO2021220980A1 (fr) Matériau de transfert photosensible, procédé de production de motif de résine, procédé de production de câblage de circuit et procédé de production de panneau tactile
WO2022138493A1 (fr) Procédé de fabrication de stratifié, procédé de fabrication de câblage de circuit, et film de transfert
JP7321388B2 (ja) 情報付与方法、樹脂パターンの製造方法、回路配線の製造方法及びタッチパネルの製造方法
WO2022181611A1 (fr) Procédé de production d'un stratifié doté d'un motif conducteur
WO2022181455A1 (fr) Film de transfert et procédé de fabrication d'un motif conducteur
WO2023145156A1 (fr) Film de transfert et procédé de formation de parcours conducteur
WO2022181456A1 (fr) Film de transfert et procédé de fabrication d'un motif conducteur
WO2023100553A1 (fr) Film de transfert, stratifié à motif conducteur, procédé de production de stratifié à motif conducteur, et procédé de production de film de transfert
WO2022138468A1 (fr) Matériau de transfert, et procédé de fabrication de stratifié
WO2023119998A1 (fr) Procédé de production d'un stratifié ayant un motif conducteur, composition photosensible et film de transfert
WO2022181539A1 (fr) Procédé de fabrication d'un stratifié présentant un motif conducteur
WO2022138576A1 (fr) Matériau de transfert photosensible, procédé de production de motif de résine, procédé de production de ligne de câblage de circuit, procédé de production de dispositif électronique et procédé de production de corps multicouche
JP2024095515A (ja) 積層体の製造方法、及び、半導体パッケージ
TW202311871A (zh) 具有導體圖案之積層體之製造方法及轉印膜
TW202311049A (zh) 轉印膜、具有導體圖案之積層體之製造方法
TW202311872A (zh) 具有導體圖案之積層體之製造方法、轉印膜
TW202307026A (zh) 轉印膜及具有導體圖案之積層體之製造方法
JP2023035807A (ja) 導体パターンを有する積層体の製造方法及び転写フィルム
JP2023020993A (ja) 透明導電パターンを含む積層体の製造方法、および、タッチパネルの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23830882

Country of ref document: EP

Kind code of ref document: A1