WO2023224004A1 - インセル型液晶パネル - Google Patents

インセル型液晶パネル Download PDF

Info

Publication number
WO2023224004A1
WO2023224004A1 PCT/JP2023/018121 JP2023018121W WO2023224004A1 WO 2023224004 A1 WO2023224004 A1 WO 2023224004A1 JP 2023018121 W JP2023018121 W JP 2023018121W WO 2023224004 A1 WO2023224004 A1 WO 2023224004A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
mass
meth
adhesive layer
cell
Prior art date
Application number
PCT/JP2023/018121
Other languages
English (en)
French (fr)
Inventor
雄太 紺野
Original Assignee
綜研化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 綜研化学株式会社 filed Critical 綜研化学株式会社
Publication of WO2023224004A1 publication Critical patent/WO2023224004A1/ja

Abstract

【課題】　本発明は、高い耐久性を有する粘着剤組成物を提供する。 【解決手段】　本発明は、第１の偏光フィルム（３０ａ）、第１の透明基板（１０ａ）、及びそれらの間に設置される粘着剤層（２０ａ）を含むインセル型液晶パネル（１）であって、前記粘着剤層（２０ａ）が、（メタ）アクリル重合体、架橋剤、及び帯電防止剤を含有する粘着剤組成物より形成され、前記（メタ）アクリル重合体が、５０質量％超のアルコキシアルキル（メタ）アクリレートと、０．１～１５質量％の官能基含有モノマーとを含むモノマー組成物の重合体である、インセル型液晶パネル（１）に関する。

Description

インセル型液晶パネル
　本発明は、インセル型液晶パネルに関する。特に、本発明は、高い耐久性を有するインセル型液晶パネルに関する。
　液晶パネルは、通常、液晶セルアレイを２枚の透明基板で挟み、さらにその外側に偏光フィルムを取り付けた構造を有している。ここで、透明基板は、通常は、１枚はカラーフィルター及び電極付きのガラス基板であり、もう１枚は薄膜トランジスタ回路付きのガラス基板である。
　タッチパネル式の液晶パネルとしては、外付け型液晶パネルと内蔵型液晶パネルとに分けることができ、内蔵型液晶パネルとしては、オンセル型液晶パネル及びインセル型液晶パネルが知られている。外付け型液晶パネルは、タッチパネルを液晶に外付けする方式であり、液晶とタッチパネルの間に物理的な空間が必要なため厚みが大きくなる。
　内蔵型のオンセル型液晶パネル及びインセル型液晶パネルは、タッチパネル機能を有する部材が異なっている。オンセル型液晶パネルは、視認側（表側）のガラス基板と偏光フィルムとの間に、タッチセンサーを挿入した方式であり、インセル型液晶パネルは、２枚のガラス基板と液晶セルアレイにタッチセンサーを組み込んだ方式である。
　図１は、インセル型液晶パネルの層構成を例示している。このインセル型液晶パネル１は、第１の偏光フィルム３０ａ、第１の粘着剤層２０ａ、第１の透明基板１０ａ、液晶層４、タッチセンシング機能部５、第２の透明基板１０ｂ、第２の粘着剤層２０ｂ、及び第２の偏光フィルム３０ｂを有している。第１の粘着剤層２０ａ及び第２の粘着剤層２０ｂは、偏光フィルムと透明基板との接着性を有しているだけではなく、表面抵抗が低い必要があるため、帯電防止剤を含有している。インセル型液晶パネルは、液晶セルの透明基板上にセンサー電極を有するオンセル型液晶セルに比べて帯電しやすいため、さらに低い表面抵抗が必要である。
　特許文献１は、そのような粘着剤層を含むインセル型液晶パネルを開示している。
国際公開第２０１８／１８１４９０号
　本発明は、高い耐久性を有するインセル型液晶パネルを提供する。
　本発明者らは、以下の態様を有する本発明により、上記課題を解決できることを見出した。
　＜態様１＞
　第１の偏光フィルム、第１の透明基板、及び前記第１の偏光フィルムと前記第１の透明基板との間に設置される粘着剤層を含むインセル型液晶パネルであって、
　前記粘着剤層が、（メタ）アクリル重合体、架橋剤、及び帯電防止剤を含有する粘着剤組成物より形成され、
　前記（メタ）アクリル重合体が、５０質量％超のアルコキシアルキル（メタ）アクリレートと、０．１～１５質量％の官能基含有モノマーとを含むモノマー組成物の重合体である、インセル型液晶パネル。
　＜態様２＞
　前記モノマー組成物が、８０質量％以上でアルコキシアルキル（メタ）アクリレートを含む、態様１に記載のインセル型液晶パネル。
　＜態様３＞
　前記（メタ）アクリル重合体の重量平均分子量が１２０万以上である、態様１に記載のインセル型液晶パネル。
　＜態様４＞
　前記粘着剤層の耐久試験前後の表面抵抗率の変動比（ｂ／ａ）が、５．０以下であり、ここでａは、前記粘着剤層に離型フィルムが設けられた状態の粘着剤層付きの偏光フィルムを作製し、前記離型フィルムを剥離した直後の前記粘着剤層の表面抵抗率であり、ｂは、離型フィルムを付けたままの粘着剤層付偏光フィルムを８５℃×８５％ＲＨの加湿環境下に２４時間投入し、さらに４０℃で１時間乾燥させた後に、前記離型フィルムを剥離した直後の粘着剤層の表面抵抗率をいう、態様１に記載のインセル型液晶パネル。
　＜態様５＞
　耐久試験後の偏光度が９９．０％以上であり、前記耐久試験後の偏光度とは、粘着剤層付きの偏光フィルムを、インセル型液晶セルに貼り合わせ、５０℃／５気圧に調整されたオートクレーブ中に２０分間保持した後、８５℃８５％ＲＨの加湿環境下に２４時間投入した後に測定した偏光度である、態様１に記載のインセル型液晶パネル。
　＜態様６＞
　液晶層、前記液晶層を両面で挟持する第１の透明基板及び第２の透明基板、並びに前記第１の透明基板と第２の透明基板との間にタッチセンシング機能部を有するインセル型液晶セルと、
　前記インセル型液晶セルの視認側に配置された第１の偏光フィルムと視認側の反対側に配置された第２の偏光フィルム、及び前記第１の偏光フィルムと前記インセル型液晶セルの第１の透明基板との間に配置された前記粘着剤層を有する、態様１～５のいずれか一項に記載のインセル型液晶パネル。
図１は、インセル型液晶パネルの層構成を例示している。 図２は、積層体の１つの例を模式的に示す断面図である。 図３は、積層体の他の１つの例を模式的に示す断面図である。
　＜インセル型液晶パネル＞
　１つの実施形態において、本発明は、インセル型液晶パネルに関する。このインセル型液晶パネルは、第１の偏光フィルム、第１の透明基板、及び前記第１の偏光フィルムと前記第１の透明基板との間に設置される粘着剤層を含み、粘着剤層が、（メタ）アクリル重合体、架橋剤、及び帯電防止剤を含有する粘着剤組成物から形成される。ここで、（メタ）アクリル重合体は、５０質量％超のアルコキシアルキル（メタ）アクリレートと、０．１～１５質量％の官能基含有モノマーとを含むモノマー組成物の重合体である。
　本発明者らは、このような粘着剤組成物から形成された粘着剤層によれば、従来技術と比較して、帯電防止剤の配合量を少なくしても十分に表面抵抗率を下げられることを見出した。また、帯電防止剤の配合量を多くした場合であっても、前記（メタ）アクリル重合体と帯電防止剤との相溶性がよいことから、本発明のインセル型液晶パネルは、特に高温高湿条件下に長期間置かれても、帯電防止剤のブリードを抑制でき、それにより高い耐久性を有することができた。
　このインセル型液晶パネルは、粘着剤層以外の構成については、周知のインセル型液晶パネルと同様であってもよい。例えば、このインセル型液晶パネルは、液晶層、前記液晶層を両面で挟持する第１の透明基板及び第２の透明基板、並びに前記第１の透明基板と第２の透明基板との間にタッチセンシング機能部を有するインセル型液晶セルと、前記インセル型液晶セルの視認側に配置された第１の偏光フィルムと視認側の反対側に配置された第２の偏光フィルム、及び前記第１の偏光フィルムと前記インセル型液晶セルの第１の透明基板との間に配置された前記粘着剤層を有する。ここで、タッチセンシング機能部は、タッチセンサー及びタッチ駆動の機能に係るタッチセンシング電極部から構成することができる。これらの各構成も周知であり、例えば特許文献１と同様の構成を採用することができる。
　図１に示すように、このインセル型液晶パネル１は、第１の偏光フィルム３０ａ、第１の粘着剤層２０ａ、第１の透明基板１０ａ、液晶層４、タッチセンシング機能部５、第２の透明基板１０ｂ、第２の粘着剤層２０ｂ、及び第２の偏光フィルム３０ｂをこの順に有していてもよいが、タッチセンシング機能部５は、特許文献１に開示されているように液晶層４との関係で、様々な位置に構成することができる。
　第１及び第２の偏光フィルムは、それぞれ第１及び第２の粘着剤層と接着し、偏光子の片面又は両面に透明保護フィルムを有するものが一般に用いられる。偏光子は、特に限定されないが、ポリビニルアルコール系フィルムとヨウ素等の二色性物質からなる偏光子が好適に用いられる。透明保護フィルムを構成する材料としては、例えば透明性、機械的強度、熱安定性、水分遮断性、等方性等に優れる熱可塑性樹脂が用いられ、例えばトリアセチルセルロース等のセルロース樹脂、環状オレフィン樹脂等を挙げることができる。偏光子と透明保護フィルムとは、周知の接着剤によって接着される。
　偏光フィルムと粘着剤層との間に、特許文献１に記載のようなアンカー層が存在していてもよい。アンカー層は、導電性ポリマー及びバインダーを含む組成物から形成することができる。導電性ポリマーとしては、ポリアニリン、ポリチオフェン等を用いることができ、バインダーとしては、特にポリウレタン系樹脂、ポリエステル系樹脂、アクリル系樹脂等を挙げることができる。
　第１及び第２の透明基板は、それぞれ第１及び第２の粘着剤層と接着し、ガラス又はポリマーフィルムが挙げられる。ポリマーフィルムとしては、例えば、ポリエチレンテレフタレート、環状オレフィン樹脂、ポリカーボネート等を含むフィルムが挙げられる。前記透明基板がガラスにより形成される場合、その厚みは、例えば０．１ｍｍ～１ｍｍ程度とすることができ。透明基板がポリマーフィルムにより形成される場合、その厚みは、例えば１０μｍ～２００μｍ程度とすることができる。透明基板は、その表面に易接着層やハードコート層を有することができる。
　第１及び第２の粘着剤層は、以下に記載の粘着剤組成物を含み、粘着剤層は、例えば以下の粘着剤組成物を塗工、乾燥及び／又は養生させて得ることができる。
　粘着剤層は、被着体である偏光フィルム及び／又は透明基板に、又は、離型フィルム（セパレーター）の表面に粘着剤組成物を塗布し、例えば溶媒の種類に応じて５０℃～１５０℃で乾燥させた後、粘着剤層の他の層と接していない面に離型フィルムを貼付した後に、例えば３～１０日間、２３℃～５０℃環境下等で養生させて形成することができる。
　粘着剤組成物の塗布方法としては、公知の方法、例えばスピンコート法、ナイフコート法、ロールコート法、バーコート法、ブレードコート法、ダイコート法、グラビアコート法等を挙げることができ、特にブレードコート法を挙げることができる。
　粘着剤層の厚みは、５μｍ以上、７μｍ以上、１０μｍ以上、又は１５μｍ以上であってもよく、５０μｍ以下、３０μｍ以下、２０μｍ以下、又は１５μｍ以下であってもよい。例えば、粘着剤層の厚みは、５μｍ以上５０μｍ以下、又は１０μｍ以上３０μｍ以下であってもよい。
　粘着剤層の表面抵抗率は、実施例に記載の方法で測定した場合に、１．０×１０１０Ω／□以下、５．０×１０９Ω／□以下、２．０×１０９Ω／□以下、１．０×１０９Ω／□以下、５．０×１０８Ω／□以下、又は３．０×１０８Ω／□以下であってもよく、１．０×１０７Ω／□以上、５．０×１０７Ω／□以上、１．０×１０８Ω／□以上、又は５．０×１０８Ω／□以上であってもよい。
　耐久試験前後の表面抵抗率の変動比（ｂ／ａ）は、１０．０以下、５．０以下、３．０以下、２．０以下、又は１．５以下であることが好ましい。すなわち、耐久試験前後で、粘着剤層の表面抵抗率は変化しないことが好ましい。ここで、ａは、粘着剤層に離型フィルムが設けられた状態の粘着剤層付きの偏光フィルムを作製し、離型フィルムを剥離した直後の粘着剤層の表面抵抗率をいう。また、ｂは、離型フィルムを付けたままの粘着剤層付偏光フィルムを８５℃×８５％ＲＨの加湿環境下に２４時間投入し、さらに４０℃で１時間乾燥させた後に、離型フィルムを剥離した直後の粘着剤層側の表面抵抗率をいう。
　粘着剤層の耐久試験後の偏光度は、９９．００％以上、９９．５０％以上、９９．８０％以上、９９．９０％以上、又は９９．９５％以上であることが好ましい。ここで、耐久試験後の偏光度とは、粘着剤層付きの偏光フィルムを、インセル型液晶セルに貼り合わせ、５０℃／５気圧に調整されたオートクレーブ中に２０分間保持した後、８５℃８５％ＲＨの加湿環境下に２４時間投入した後に測定した偏光度をいう。偏光度は、実施例に記載の方法で測定される。
　＜粘着剤組成物＞
　１つの実施形態において、本発明は、粘着剤組成物に関する。この粘着剤組成物は、特に液晶パネルの偏光フィルム及び透明基板を接着するために好適である。
　＜（メタ）アクリル重合体＞
　粘着剤層を形成する粘着剤組成物は、（メタ）アクリル重合体を含有し、ここで（メタ）アクリル重合体は、５０質量％超のアルコキシアルキル（メタ）アクリレートと、０．１～１５質量％の官能基含有モノマーとを含むモノマー組成物の重合体である。
　（メタ）アクリル重合体は、好ましくは重量平均分子量（Ｍｗ）が６０万以上である。その重量平均分子量は、８０万以上、１００万以上、１２０万以上、１３０万以上、１５０万以上、１６５万以上、１８０万以上、又は１９０万以上であってもよく、３００万以下、２８０万以下、２５０万以下、２２０万以下、２００万以下、１８０万以下、又は１６５万以下であってもよい。例えば、その重量平均分子量は、１２０万以上３００万以下、又は１３０万以上２００万以下であってもよい。このような範囲であると、粘着剤組成物に塗布性の課題を与えることなく、得られる粘着剤層に極めて高い耐熱性を与えることができる。
　（メタ）アクリル重合体の数平均分子量（Ｍｎ）に対する重量平均分子量（Ｍｗ）の比で表される多分散度（Ｍｗ／Ｍｎ）は、１５．０以下、１０．０以下、８．０以下、６．０以下、又は５．０以下とすることができ、１．５以上、２．０以上、３．０以上、又は４．０以上であってもよい。例えば、（メタ）アクリル重合体の多分散度は、１．５以上１５．０以下、又は２．０以上８．０以下であってもよい。
　重量平均分子量及び数平均分子量は、ＧＰＣ（ゲルパーミエーションクロマトグラフィー）を用い、下記の条件で標準ポリスチレン換算により求められる。
　＜ＧＰＣ測定条件＞
　測定装置：ＨＬＣ－８１２０ＧＰＣ（東ソー製）
　ＧＰＣカラム構成：以下の５連カラム（すべて東ソー製）
　（１）ＴＳＫ－ＧＥＬ　ＨＸＬ－Ｈ（ガードカラム）
　（２）ＴＳＫ－ＧＥＬ　Ｇ７０００ＨＸＬ
　（３）ＴＳＫ－ＧＥＬ　ＧＭＨＸＬ
　（４）ＴＳＫ－ＧＥＬ　ＧＭＨＸＬ
　（５）ＴＳＫ－ＧＥＬ　Ｇ２５００ＨＸＬ
　サンプル濃度：１．０ｍｇ／ｃｍ３となるように、テトラヒドロフランで希釈
　移動相溶媒：テトラヒドロフラン
　流量：１．０ｃｍ３／分
　カラム温度：４０℃
　＜（メタ）アクリル重合体－アルコキシアルキル（メタ）アクリレート＞
　（メタ）アクリル重合体を得るためのモノマー組成物は、アルコキシアルキル（メタ）アクリレートを含む。アルコキシアルキル（メタ）アクリレートは、アルキル（メタ）アクリレートのアルキル基の水素原子の少なくとも一つが、アルコキシ基又はアルコキシ基を有する化合物に置換されたモノマーである。アルキル（メタ）アクリレートのアルキル基の水素原子の少なくとも一つが、アルコキシ基を有する化合物に置換された化合物としては、例えばポリアルキレングリコール（メタ）アクリレートを挙げることができる。
　例えば、このモノマーは、ＣＨ２＝ＣＲ１－ＣＯＯ－Ｒ２で表され、ここで、Ｒ１は、水素原子又はメチル基であり、Ｒ２は、炭素数１４以下の直鎖又は分岐鎖のアルキル基又はアラルキル基を表すが、それらの基を構成する水素原子の少なくとも一つが、基－Ｏ－(ＣｎＨ２ｎＯ)ｍ－Ｒ３で置換され、ｎは１～４の整数を表し、ｍは０又は１～１０の整数を表し、Ｒ３は炭素数１４以下の直鎖又は分岐鎖のアルキル基を構成する。
　具体的には、アルコキシアルキル（メタ）アクリレートとしては、メトキシメチル（メタ）アクリレート、２－メトキシエチル（メタ）アクリレート、２－エトキシエチル（メタ）アクリレート、３－メトキシプロピル（メタ）アクリレート、３－エトキシプロピル（メタ）アクリレート、４－メトキシブチル（メタ）アクリレート、４－エトキシブチル（メタ）アクリレート、エチルカルビトールアクリレート、 ２-エチルヘキシル-ジグルコールアクリレート、メトキシ－ポリエチレングリコールアクリレート、エトキシ－ジエチレングリコールアクリレート等を挙げることができ、この中でも特に、２－メトキシエチル（メタ）アクリレートを挙げることができる。
　アルコキシアルキル（メタ）アクリレートは、モノマー組成物中に、５０質量％超で含有される。例えば、アルコキシアルキル（メタ）アクリレートは、モノマー組成物中に、５１質量％以上、６０質量％以上、７０質量％以上、８０質量％以上、８５質量％以上、９０質量％以上、９５質量％以上、又は９８質量％以上含有されていてもよく、９９．９質量％以下、９９．５質量％以下、９９．０質量％以下、９８質量％以下、９５質量％以下、９０質量％以下、又は８０質量％以下で含有されていてもよい。例えば、アルコキシアルキル（メタ）アクリレートは、モノマー組成物中に、７０質量％以上９９．９質量％以下、又は８５質量％以上９９．９質量％以下で含まれていてもよい。
　本分野で用いられる他のモノマーと比較して、（メタ）アクリル重合体中のアルコキシアルキル（メタ）アクリレートの含有量が上記のように高い範囲である場合には、粘着剤層の電気抵抗を低くできる。通常、粘着剤層は、イオン性化合物等の帯電防止剤を用いることで電気抵抗を下げているが、（メタ）アクリル重合体の組成を変更することで電気抵抗をさらに低くできる。また、前記（メタ）アクリル重合体は、本分野でよく使用される帯電防止剤との相溶性が高く、帯電防止剤のブリードを抑制し、インセル型液晶パネルに高い耐久性を提供することができる。
　＜（メタ）アクリル重合体－官能基含有モノマー＞
　（メタ）アクリル重合体を得るためのモノマー組成物は、官能基含有モノマーを含む。官能基含有モノマーの官能基は、粘着剤組成物が含む架橋剤と反応する架橋点となることができ、得られる粘着剤層のゲル分率を適切な範囲に調整できる。
　官能基含有モノマーとしては、水酸基含有モノマー酸基含有モノマー等が挙げられる。
　水酸基含有モノマーは、水酸基及び重合性基を有するモノマーであれば、特に限定されないが、例えば、重合性基としては、ビニル基、（メタ）アクリロイル基等の重合性二重結合を有する基を挙げることができる。
　水酸基含有モノマーとしては、例えば、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、４－ヒドロシキブチル（メタ）アクリレート、６－ヒドロキシヘキシル（メタ）アクリレート、８－ヒドロキシオクチル（メタ）アクリレート、２－ヒドロキシ－３－フェノキシプロピル（メタ）アクリレート等を挙げることができる。
　酸性基含有モノマーとしては、カルボキシル基含有モノマーを含むことができ、例えば、（メタ）アクリル酸、β－カルボキシエチル（メタ）アクリレート、５－カルボキシペンチル（メタ）アクリレート、イタコン酸、マレイン酸、フマル酸、クロトン酸、イソクロトン酸などのカルボキシル基含有単量体又はその無水物（無水マレイン酸など）が挙げられことができる。
　官能基含有モノマーは、モノマー組成物中に、０．１質量％以上１５質量％以下で含有される。例えば、官能基含有モノマーは、モノマー組成物中に、０．３質量％以上、０．５質量％以上、０．８質量％以上、又は１．０質量％以上含有されていてもよく、１０質量％以下、８．０質量％以下、５．０質量％以下、３．０質量％以下、２．０質量％以下、又は１．５質量％以下で含有されていてもよい。例えば、官能基含有モノマーは、モノマー組成物中に、０．３質量％以上５．０質量％以下、又は０．５質量％以上２．０質量％以下で含まれていてもよい。
　＜（メタ）アクリル重合体－他のモノマー成分＞
　（メタ）アクリル重合体を得るためのモノマー組成物は、本発明の有利な効果が得られる範囲で、アルコキシアルキル（メタ）アクリレート及び官能基含有モノマー以外のその他モノマーも含有することができる。
　その他モノマーとしては、例えば、アルキル基の炭素数が１～２０であるアルキル（メタ）アクリレートを挙げることができる。アルキル（メタ）アクリレートが有するアルキルは直鎖又は分岐鎖であり、アルキル基の炭素数は、１以上２０以下、１以上１０以下、又は２以上８以下の範囲とすることができる。
　アルキル（メタ）アクリレートとしては、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ－プロピル（メタ）アクリレート、イソプロピル（メタ）アクリレート、ｎ－ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｔｅｒｔ－ブチル（メタ）アクリレート、ｎ－ペンチル（メタ）アクリレート、ｎ－ヘキシル（メタ）アクリレート、ｎ－ヘプチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ｎ－オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ｎ－ノニル（メタ）アクリレート、イソノニル（メタ）アクリレート、デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ウンデカ（メタ）アクリレート、ラウリル（メタ）アクリレート、オレイル（メタ）アクリレート、ｎ－ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレート等を挙げることができる。
　また、その他モノマーとして、例えば、（メタ）アクリルアミド、Ｎ－（メタ）アクリロイルピペリジン、Ｎ－ビニルピロリドン、Ｎ，Ｎ－ジメチルアミノエチルアクリレート、Ｎ，Ｎ－ジメチルアミノエチルメタクリレート、Ｎ，Ｎ－ジエチルアミノエチルメタクリレート等の窒素含有モノマー；ベンジル（メタ）アクリレート、２－ナフチルアクリレート、フェノキシエチルアクリレート等の芳香環基を有する（メタ）アクリル酸エステル、スチレン、α－メチルスチレン、ｏ－メチルスチレン、ｐ－メチルスチレン等のスチレン系モノマー；酢酸ビニル等のカルボン酸ビニルエステル；ビニル（メタ）アクリロイル基含有マクロモノマー等を挙げることもできる。
　その他モノマーは、モノマー組成物中に、０質量％以上、５質量％以上、１０質量％以上、又は１５質量％以上含有されていてもよく、４９質量％未満、４８質量％以下、４０質量％以下、３０質量％以下、２０質量％以下、１０質量％以下、５．０質量％以下、３．０質量％以下、又は１．０質量％未満で含有されていてもよい。例えば、その他モノマーは、モノマー組成物中に、０質量％以上４８質量％以下、又は０質量％以上１０質量％以下で含まれていてもよい。本発明者らの検討によれば、その他モノマーの含有量が多い場合、得られる粘着剤層の諸物性値に悪影響を及ぼす場合もあることが分かった。したがって、その他モノマーは、モノマー組成物中に実質的に含まれていなくてもよい。
　本明細書において「実質的に含まない」とは、本発明の有利な効果を損なわない範囲であれば、その成分を含有してもいてもよいことを意味する。例えば、その成分を組成物中に実質的に含まないとは、その成分がその組成物中に０．５０質量％未満、０．３０質量％未満、０．２０質量％未満、０．１０質量％未満、又は０．０５質量％未満であることを意味する場合がある。
　＜（メタ）アクリル重合体－重合開始剤＞
　（メタ）アクリル重合体を公知の重合開始剤により重合することができる。重合開始剤としては、通常ラジカル重合で使用できる有機過酸化物、アゾ化合物等を使用することが可能である。具体的には、重合開始剤として、ｔ－ブチルハイドロパーオキサイド、クメンハイドロオキサイド、ジクミルパーオキサイド、ベンゾイルパーオキシド等の有機過酸化物、２，２’－アゾビス－ｉｓｏ－ブチロニトリル、２，２’－アゾビス－２，４－ジメチルバレロニトリル、２，２’アゾビス－４－メトキシ－２，４－ジメチルバレロニトリル等のアゾ化合物を挙げることができる。
　重合開始剤は、モノマー成分合計１００質量部に対して０．０１質量部以上２．０質量部以下、又は０．１質量部以上１．０質量部以下で用いることができる。
　＜（メタ）アクリル重合体－溶媒＞
　モノマー組成物は、重合方法に応じて、溶媒を含んでいてもよい。例えば、溶液重合によって重合体を得る場合には、モノマー成分を溶解可能な有機溶媒を用いることができる。
　具体的には、有機溶媒としては、例えば、ベンゼン、トルエン、エチルベンゼン、ｔ－ブチルベンゼン、キシレン、芳香族ナフサ等の芳香族炭化水素；ｎ－ヘキサン、ｎ－ヘプタン、ジペンテン、石油スピリット、石油ナフサ、テレピン油等の脂肪族系又は脂環族系炭化水素；酢酸エチル、酢酸ｎ－ブチル、酢酸ｎ－アミル、安息香酸メチル等のエステル；アセトン、メチルエチルケトン、シクロヘキサノン等のケトン；エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル等のグリコールエーテル；メチルアルコール、エチルアルコール、ｔ－ブチルアルコール等のアルコール；を挙げることができ、これらの有機溶媒はそれぞれ単独で、又は２種以上混合して用いることができる。例えば、その中でも特に、重合反応中に連鎖移動を生じにくい有機溶媒、例えば、エステル、ケトンを使用することが好ましく、特に、モノマー成分の溶解性、重合反応の容易さなどの点から、酢酸エチル、メチルエチルケトン、アセトン等を使用することができる。
　＜（メタ）アクリル重合体－他の成分＞
　モノマー組成物は、本発明の有利な効果を損なわない範囲であれば、他の成分を含むことができる。例えば、モノマー成分は、連鎖移動剤を含むことができ、また重合方法に応じて、乳化剤、分散剤、分散媒等を含んでいてもよい。
　連鎖移動剤としては、例えば、シアノ酢酸、ブロモ酢酸、又はこれらの炭素数１～８のアルキルエステル；アントラセン、フェナントレン、フルオレン等の芳香族化合物；ｐ－ニトロアニリン、ニトロベンゼン、ｐ－ニトロ安息香酸等の芳香族ニトロ化合物；ベンゾキノン、２，３，５，６－テトラメチル－ｐ－ベンゾキノン等のベンゾキノン誘導体；トリブチルボラン等のボラン誘導体；四臭化炭素、四塩化炭素、１，１，２，２－テトラブロモエタン、３－クロロ－１－プロペン等のハロゲン化炭化水素；クロラール、フラルデヒド等のアルデヒド：炭素数１～１８のアルキルメルカプタン；チオフェノール、トルエンメルカプタン等の芳香族メルカプタン；メルカプト酢酸、メルカプト酢酸の炭素数１～１０のアルキルエステル；炭素数１～１２のヒドロキシアルキルメルカプタン；ピネン、ターピノレン等のテルペン；を挙げることができる。
　＜（メタ）アクリル重合体－重合方法＞
　（メタ）アクリル重合体の重合方法は、特に制限されるものではなく、溶液重合、乳化重合、懸濁重合、塊状重合等の公知の方法により重合できる。重合体を用いて粘着剤組成物を製造するにあたり、処理工程が比較的簡単でかつ短時間で行える観点からは、溶液重合で重合体を得ることが好ましい。
　＜架橋剤＞
　粘着剤組成物は、架橋剤を含むことができる。架橋剤を含有させることによって、得られる粘着剤層のゲル分率を適切な範囲にすることができる。架橋剤としては、本分野で知られたイソシアネート系架橋剤を用いることができ、例えば２つ以上のイソシアネート基又はイソシアヌレート基及び随意に酸素原子を含む炭素数１～２０の範囲の炭化水素基を有する架橋剤を用いることができる。
　具体的には、イソシアネート系架橋剤としては、常温又は加熱下で官能基含有モノマーと架橋できる架橋剤であれば特に限定されないが、例えば、キシリレンジイソシアネート、トリレンジイソシアネート、クロルフェニレンジイソシアネート、ヘキサメチレンジイソシアネート等のイソシアネートモノマー、それらをトリメチロールプロパン等の２価以上のアルコール化合物等に付加反応させたイソシアネート化合物、イソシアヌレート化物等を挙げることができる。また、イソシアネート系架橋剤としては、公知のポリエーテルポリオール、ポリエステルポリオール、アクリルポリオール、ポリブタジエンポリオール、ポリイソプレンポリオール等にイソシアネート化合物を付加反応させたウレタンプレポリマー型のイソシアネート等も挙げることができる。
　また、架橋剤として、エポキシ系架橋剤を用いることができる。エポキシ系架橋剤としては、１分子中にエポキシ基を２つ以上有するエポキシ化合物を用いることができ、具体的には、エチレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、グリセリンジグリシジルエーテル、グリセリントリグリシジルエーテル、１，３－ビス（Ｎ，Ｎ－ジグリシジルアミノメチル）シクロヘキサン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジル－ｍ－キシリレンジアミン、Ｎ，Ｎ，Ｎ’ ，Ｎ’－テトラグリシジルアミノフェニルメタン、トリグリシジルイソシアヌレート、ｍ－Ｎ，Ｎ－ジグリシジルアミノフェニルグリシジルエーテル、Ｎ，Ｎ－ジグリシジルトルイジン、Ｎ，Ｎ－ジグリシジルアニリンを用いることができる。
　また、架橋剤として、金属キレート架橋剤を用いることができる。金属キレート架橋剤としては、アルミニウム、鉄、銅、亜鉛、スズ、チタン、ニッケル、アンチモン、マグネシウム、バナジウム、クロム、ジルコニウム等の多価金属に、アルコキシド、アセチルアセトン、アセト酢酸エチル等が配位した化合物を用いることができ、具体的には、アルミニウムイソプロピレート、アルミニウムセカンダリーブチレート、アルミニウムエチルアセトアセテート・ジイソプロピレート、アルミニウムトリスエチルアセトアセテート、アルミニウムトリスアセチルアセトネートを用いることができる。
　架橋剤は、粘着剤組成物中に、（メタ）アクリル重合体１００質量部に対して、０．０１質量部以上、０．１質量部以上、０．２質量部以上、０．３質量部以上、又は０．５質量部以上で含有されていてもよく、３．０質量部以下、１．０質量部以下、０．５質量部以下、又は０．２質量部以下で含有されていてもよい。例えば、架橋剤は、（メタ）アクリル重合体１００質量部に対して、０．０１質量部以上３．０質量部以下又は０．１質量部以上０．５質量部以下で含有されていてもよい。
　粘着剤組成物より形成される粘着剤層は、架橋剤が重合体を架橋した後の状態で、実施例に記載の方法で測定したゲル分率が、５０％以上、５５％以上、６０％以上、６２％以上、６４％以上、６６％以上、又は６８％以上であってもよく、９０％以下、８５％以下、８０％以下、７５％以下、又は７０％以下であってもよい。例えば、粘着剤層のゲル分率は、５０％以上９０％以下、又は６２％以上９０％以下であってもよい。
　＜帯電防止剤＞
　粘着剤組成物は、イオン性化合物からなる帯電防止剤を含むことができる。帯電防止剤を含む粘着剤組成物は、（メタ）アクリル重合体のアルコキシアルキル基の酸素原子が、帯電防止剤に含まれるイオン性基に配位することにより、高い帯電防止性能を実現することができると考えられる。
　帯電防止剤としては、例えば、イオン性化合物、界面活性剤等が挙げられる。前記イオン性化合物は、カチオンとアニオンとを含み、２５℃で固体状のものであっても、液体状のものであってもよい。
　イオン性化合物を構成するカチオンとしては、無機系カチオン、有機系カチオンを挙げることができる。無機系カチオンとしては、例えば、Ｌｉ＋、Ｎａ＋、Ｋ＋が挙げられる。有機系カチオンとしては、例えば、ピリジニウムカチオン、ピペリジニウムカチオン、ピロリジニウム系カチオン、ピロリンカチオン、ピロールカチオン、イミダゾリウムカチオン、テトラヒドロピリミジニウムカチオン、ジヒドロピリミジニウムカチオン、ピラゾリウムカチオン、ピラゾリニウムカチオン、テトラアルキルアンモニウムカチオン、トリアルキルスルホニウムカチオン、テトラアルキルホスホニウムカチオンおよびこれらの誘導体が挙げられる。
　イオン性化合物を構成するアニオンとしては、前記カチオンとイオン結合してイオン性化合物を形成し得るものであれば特に制限されないが、例えば、Ｆ－、Ｃｌ－、Ｂｒ－、Ｉ－、ＡｌＣｌ４ －、Ａｌ２Ｃｌ７ －、ＢＦ４ －、ＰＦ６ －、ＳＣＮ－、ＣｌＯ４ －、ＮＯ３ －、ＣＨ３ＣＯＯ－、ＣＦ３ＣＯＯ－、ＣＨ３ＳＯ３ －、ＣＦ３ＳＯ３ －、(ＣＦ３ＳＯ２) ２Ｎ－、(Ｆ２ＳＯ２) ２Ｎ－、(ＣＦ３ＳＯ２) ３Ｃ－、ＡｓＦ６ －、ＳｂＦ６ －、ＮｂＦ６ －、ＴａＦ６ －、Ｆ(ＨＦ)n－、(ＣＮ) ２Ｎ－、Ｃ４Ｆ９ＳＯ３ －、(Ｃ２Ｆ５ＳＯ２) ２Ｎ－、Ｃ３Ｆ7ＣＯＯ－および(ＣＦ３ＳＯ２)(ＣＦ３ＣＯ)Ｎ－が挙げられる。
　イオン性化合物としては、これらのカチオンとアニオンとから構成され具体的には、リチウムビス（トリフルオロメタンスルホニル）イミド、リチウムビス（ジフルオロスルホニル）イミド、リチウムトリス（トリフルオロメタンスルホニル）メタン、カリウムビス（トリフルオロメタンスルホニル）イミド、カリウムビス（ジフルオロスルホニル）イミド、１－エチルピリジニウムヘキサフルオロホスフェート、１－ブチル－４－ピリジニウムヘキサフルオロホスフェート、１－ヘキシル－４－メチルピリジニウムヘキサフルオロホスフェート、１－オクチル－４－メチルピリジニウムヘキサフルオロホスフェート、１－オクチル－４－メチルピリジニウムビス（フルオロスルホニル）イミド、１－オクチル－４－メチルピリジニウムビス（トリフルオロメタンスルホニル）イミド、（Ｎ，Ｎ－ジエチル－Ｎ－メチル－Ｎ－（２－メトキシエチル）アンモニウムテトラフルオロボレート、Ｎ，Ｎ－ジエチル－Ｎ－メチル－Ｎ－（２－メトキシエチル）アンモニウムビス（トリフルオロメタンスルホニル）イミド、ブチルトリメチルアンモニウムビス（トリフルオロメタンスルホニル）イミド、１－オクチルピリジニウムフルオロスホニウムイミド、１－オクチル－３－メチルピリジニウム、トリフルオロスルホニウムイミドを挙げることができる。
　上記界面活性剤としては、ノニオン系界面活性剤、カチオン系界面活性剤、アニオン系界面活性剤および両性界面活性剤の何れも使用することができる。また、その他に、帯電防止剤として、導電性ポリマー、導電性カーボン、塩化アンモニウム、塩化アルミニウム、塩化銅、塩化鉄、硫酸アンモニウム等を使用することができる。
　帯電防止剤は、粘着剤組成物中に、（メタ）アクリル重合体１００質量部に対して、０．１質量部以上、０．３質量部以上、０．５質量部以上、１．０質量部以上、又は２．０質量部以上で含有されていてもよく、１５質量部以下、１０質量部以下、５．０質量部以下、３．０質量部以下、又は２．０質量部以下で含有されていてもよい。例えば、帯電防止剤は、（メタ）アクリル重合体１００質量部に対して、０．１質量部以上１０質量部以下又は０．５質量部以上５．０質量部以下で含有されていてもよい。
　＜シランカップリング剤＞
　粘着剤組成物は、シランカップリング剤を含むことができる。シランカップリング剤を含む粘着剤組成物は、被着体と粘着剤層との接着を良好に保つことができる。
　シランカップリング剤としては、本分野で知られているシランカップリング剤を用いることができ、例えば、ビニルトリメトキシシラン等の重合性不飽和基含有ケイ素化合物；３－グリシドキシプロピルトリメトキシシラン等のエポキシ構造を有するケイ素化合物；３－アミノプロピルトリメトキシシラン等のアミノ基含有ケイ素化合物；３－クロロプロピルトリメトキシシラン；オリゴマー型シランカップリング剤が挙げられる。これらの中でも特に、（メタ）アクリル重合体又はそのモノマー成分に含まれる官能基と反応する官能基を有するシランカップリング剤が、高湿熱環境下での粘着剤層の被着体からのハガレを生じさせにくいという点で好ましい。
　シランカップリング剤は、粘着剤組成物中に、（メタ）アクリル重合体１００質量部に対して、０．０５質量部以上、０．１質量部以上、０．２質量部以上、０．３質量部以上、又は０．５質量部以上で含有されていてもよく、１．０質量部以下、０．５質量部以下、０．３質量部以下、又は０．２質量部以下で含有されていてもよい。例えば、シランカップリング剤は、（メタ）アクリル重合体１００質量部に対して、０．０５質量部以上１．０質量部以下又は０．１質量部以上０．５質量部以下で含有されていてもよい。
　＜溶媒＞
　粘着剤組成物は、塗布性を調整するために、溶媒を含むことができる。溶媒の種類としては、（メタ）アクリル重合体を重合するための上記の重合溶媒と同じものであってよい。
　粘着剤組成物は溶媒を含有することで、固形分濃度を調整することができる。粘着剤組成物の固形分濃度は、１０質量％以上、１２質量％以上、１４質量％以上、又は１６質量％以上であってもよく、４０質量％以下、３０質量％以下、２０質量％以下、又は１８質量％以下であってもよい。例えば、粘着剤組成物の固形分濃度は、１０質量％以上３０質量％以下又は１２質量％以上２０質量％以下であってもよい。
　粘着剤組成物は、上記成分のほか、本発明の効果を損なわない範囲で、紫外線吸収剤、酸化防止剤、粘着付与樹脂、可塑剤、消泡剤、充填剤、安定剤、軟化剤、および濡れ性調整剤から選択される成分が含有されてもよい。
　＜積層体＞
　１つの実施形態において、本発明は積層体である。この積層体は、第１の部材、第２の部材、及びこれらを接着する粘着剤層を含み、粘着剤層は、上記の粘着剤組成物から形成される。粘着剤層は、インセル型液晶パネルの粘着剤層と同じ粘着剤層であってよく、またその粘着剤層を形成するときと同様にして得ることができる。
　図２は、積層体の１つの例を模式的に示す断面図である。
　積層体１００は、図２に示されるように、第１の部材であるガラス基板１０、第２の部材である偏光フィルム３０、及びそれらを接着する粘着剤層２０を含む。偏光フィルム３０は、ポリシクロオレフィン系フィルム３２と、ポリシクロオレフィン系フィルム３２上のポリビニルアルコールフィルム３４と、ポリビニルアルコールフィルム３４上のＴＡＣフィルム３６とを有する。ガラス基板１０とポリシクロオレフィン系フィルム３２とが、粘着剤層２０で接着されている。
　図３は、積層体の他の１つの例を模式的に示す断面図である。
　積層体２００は、図３に示されるように、第１の部材であるガラス基板１０と、第２の部材であるポリシクロオレフィン系フィルム（位相差フィルム）３２と、第３の部材である偏光フィルム１３０とを含み、これらを接着する粘着剤層２０，２２を含む。より具体的には、ポリシクロオレフィン系フィルム３２と偏光フィルム１３０とは、粘着剤層２０で接着されている。また、ガラス基板１０とポリシクロオレフィン系フィルム３２とは、粘着剤層２２で接着されている。偏光フィルム１３０は、ポリシクロオレフィン系フィルム（第２のポリシクロオレフィン系フィルム）又はＴＡＣフィルムである層３８と、層３８上のポリビニルアルコールフィルム３４と、ポリビニルアルコールフィルム３４上のＴＡＣフィルム３６とを有する。ポリシクロオレフィン系フィルム（第１のポリシクロオレフィン系フィルム）３２と層（第２のポリシクロオレフィン系フィルム）３８とは、粘着剤層２０で接着されている。
　図２及び図３における粘着剤層２０，２２は、被着体の表面に形成されている。粘着剤組成物を被着体の表面に形成する方法としては、例えば、平滑性の良好な離型フィルム（セパレーター）の表面に粘着剤組成物を塗布し、塗膜を乾燥した後、当該塗膜を特定の樹脂フィルムの表面に転写する転写法が挙げられる。
　積層体は、例えば、画像表示装置、特に液晶表示装置に用いることができる。より具体的には、積層体は例えば、タッチパネル用の画像表示装置に用いることができる。この場合、積層体に含まれるガラス基板は、液晶表示装置用のガラス基板であってもよい。
　画像表示装置としては、例えば、液晶テレビ、コンピュータのモニター、携帯電話、タブレット等に用いられるＴＦＴ（薄膜トランジスタ）液晶表示装置であってもよい。
　本発明を以下の実施例でさらに具体的に説明をするが、本発明はこれによって限定されるものではない。
　＜製造例＞
　＜実施例１＞
　撹絆装置、窒素ガス導入管、温度計及び還流冷却管を備えたフラスコに、２－メトキシエチルアクリレート９８．８質量部、４－ヒドロキシブチルアクリレート１質量部、アクリル酸０．２質量部及び酢酸エチル１００質量部を投入した。その後、フラスコ内に窒素ガスを導入しながら、内容物を６５℃に加熱した。次いで、窒素ガスで十分に置換されたフラスコ内に、２，２’－アゾビス－ｉｓｏ－ブチロニトリル（ＡＩＢＮ）０．０５質量部を撹絆下で添加した。フラスコ内の内容物の温度を６５℃に維持しながら６時間反応させた。
　６時間経過後の反応混合物に酢酸エチル３００質量部をさらに添加して、（メタ）アクリル重合体を含む溶液を得た。得られた（メタ）アクリル重合体についてＧＰＣにより測定されたＭｗは１９０万であった。
　得られた（メタ）アクリル重合体を含む溶液の固形分１００質量部に対して、固形分で表１に記載の量で、架橋剤、帯電防止剤、及びシランカップリング剤を配合した後、よく混合し、粘着剤組成物を得た。ここで、固形分とは、粘着剤組成物から有機溶媒を除いた全成分をいう。
　＜実施例２～１８、比較例１～２＞
　使用した成分を表１のように変更したこと以外は実施例１と同様にして、実施例２～１８及び比較例１～２の粘着剤組成物を得た。なお、初期に投入する酢酸エチルの量として、実施例１２では１２０部に、実施例１３では１５０部に、実施例１４では８０部にそれぞれ変更して反応を行った。
　＜粘着シート＞
　剥離処理されたＰＥＴフィルム上に、液温２５℃で、ドクターブレードを用いて乾燥後の膜厚が２５μｍとなるように、実施例及び比較例で得られた粘着剤組成物を塗布した。その後、９０℃で３分間乾燥させ、剥離処理されたＰＥＴフィルムとは反対側の粘着剤層に更に剥離処理されたＰＥＴフィルムを貼り合わせた。そして、５０℃の条件でそれを３日間静置し、粘着シートを得た。
　＜粘着剤層付き偏光フィルム＞
　剥離処理されたＰＥＴフィルム上に、液温２５℃で、ドクターブレードを用いて乾燥後の膜厚が２５μｍとなるように、実施例及び比較例で得られた粘着剤組成物を塗布した。その後、９０℃で３分間乾燥させ、剥離処理されたＰＥＴフィルムとは反対側の粘着剤層と偏光フィルム（ＣＯＰフィルム４０μｍ／ＰＶＡフィルム２０μｍ／ＴＡＣフィルム４０μｍ）とを、粘着剤層と偏光フィルムのＣＯＰフィルム面とが接するように貼り合わせた。そして、５０℃の条件でそれを３日間静置し、粘着剤層付き偏光フィルムを得た。
　＜試験方法＞
　＜ゲル分率＞
　前記粘着シートから、粘着剤約０．１ｇをサンプリング瓶に採取した。そのサンプリング瓶に、酢酸エチル３０ｍＬを加えて４時間振盪した。このサンプル瓶の内容物を２００メッシュのステンレス製金網で濾過し、金網上の残留物を９０℃で２時間乾燥して乾燥重量を測定した。次式により、粘着剤のゲル分率を求めた。
　ゲル分率（％）＝（乾燥重量／粘着剤採取重量）×１００（％）
　＜湿熱熱耐久性＞
　前記粘着剤層付き偏光フィルムを１６０ｍｍ（ＭＤ方向）×９０ｍｍ（ＴＤ方向）の大きさに裁断して試験片を作製した。前記試験片から離型フィルム（剥離処理されたＰＥＴフィルム）を剥離し、インセル型液晶セルの視認側に、粘着剤層とインセル型液晶セルのガラス基板とが接するように貼着した。得られた積層体を、５０℃／５気圧に調整されたオートクレーブ中に２０分間保持して、試験板を作製した。前記試験板を、温度８５℃８５％ＲＨの条件下で２４時間放置し、試験板の粘着剤層からの発泡、試験板の亀裂、粘着剤層の剥がれ等の外観欠陥を以下の基準で目視観察して評価した。
　◎：不具合なし　〇：僅かな外観欠陥が確認されるが実使用上、問題なし
　△：外観欠陥が確認されるが、実使用可能　×：外観欠陥あり、実使用不可
　＜耐白化性＞
　前記粘着剤層付き偏光フィルムを１６０ｍｍ（ＭＤ方向）×９０ｍｍ（ＴＤ方向）の大きさに裁断して試験片を作製した。前記試験片を８５℃８５％ＲＨの条件下で２４時間放置し、粘着剤層の白化について以下の基準で目視観察して評価した。
　〇：白化なし　△：僅かに濁りが確認されるが、実使用可能　×：白化
　＜表面抵抗率＞
　前記粘着剤層付き偏光フィルムの粘着剤層から離型フィルム（剥離処理されたＰＥＴフィルム）を剥離し、抵抗率計（ハイレスタＵＸ　ＭＣＰ－ＨＴ８００、三菱化学アナリティック製）を用い、印加電圧１０００Ｖで、ＪＩＳ－Ｋ－６９１１に準じて、粘着層の表面抵抗率ａを測定した。
　また、別の粘着剤層付き偏光フィルムを８５℃８５％ＲＨの加湿環境下に２４時間投入し、さらに４０℃で１時間乾燥させた後、粘着剤層から離型フィルム（剥離処理されたＰＥＴフィルム）を剥離し、表面抵抗率ｂを測定した。表面抵抗率ａ及び表面抵抗率ｂより、表面抵抗率の変動比（ｂ／ａ）を算出した。
　＜偏光度＞
　前記粘着剤層付き偏光フィルムを２０ｍｍ（ＭＤ方向）×３０ｍｍ（ＴＤ方向）の大きさに裁断して試験片を２枚作製した。前記試験片から離型フィルム（剥離処理されたＰＥＴフィルム）を剥離し、積分球付き分光光度計Ｖ７１００（日本分光製）を用いて、ＪＩＳＺ８７２２（物体色の測定方法）に準拠し、Ｃ光源、２°視野の可視光領域の視感度補正を行い、当該サンプルについて、パラレルニコル状態での光の透過率Ｔ∥（％）、クロスニコル状態での光の透過率Ｔ⊥（％）を測定し、下記式により偏光度を求めた。
　偏光度＝｛（Ｔ∥－Ｔ⊥）／（Ｔ∥＋Ｔ⊥）｝１／２×１００
　湿熱後の偏光度については、試験片から離型フィルム（剥離処理されたＰＥＴフィルム）を剥離し、インセル型液晶セルの視認側に、粘着剤層とインセル型液晶セルの透明基板とが接するように貼着した後、得られた積層体を、５０℃／５気圧に調整されたオートクレーブ中に２０分間、その後、８５℃８５％ＲＨの加湿環境下に２４時間保持し、次いで、インセル型液晶セルから粘着剤層付き偏光フィルムを剥離した後、上記の方法で、湿熱後偏光度を求めた。
　＜結果＞
　結果を以下の表に示す。
　ＭＥＡ：２－メトキシエチルアクリレート
　ＥＣ－Ａ：エトキシ－ジエチレングリコールアクリレート
　ＢＡ：ブチルアクリレート
　４ＨＢＡ：４－ヒドロキシブチルアクリレート
　ＡＡ：アクリル酸
　ＴＤ－７５：イソシアネート架橋剤（綜研化学製）
　Ｐｙ－ＰＦ６：１－ブチル－４－メチルピリジニウムヘキサフルオロホスファート
　Ｌｉ－ＴＦＳＩ：リチウムビス（トリフルオロメタンスルホニル）イミド
　Ａｍ－ＴＦＳＩ：ブチルトリメチルアンモニウムビス（トリフルオロメタンスルホニル）イミド
　ＫＢＭ－４０３：３－グリシドキシプロピルトリメトキシシラン（信越化学製）
　実施例１～７を参照すると、帯電防止剤を多く含むほど表面抵抗は下がるが、湿熱耐久性は帯電防止剤が少ないほうが良好となることがわかる。
　実施例８～１１を参照すると、（メタ）アクリル重合体が、アルコキシアルキル（メタ）アクリレートを多く含むモノマーから製造されている場合には、湿熱耐久性、表面抵抗等の点で良好になることが分かった。比較例１をさらに含めて参照すると、アルコキシアルキル（メタ）アクリレートの有利な効果は特に理解できた。比較例２は、帯電防止剤が少ないために湿熱耐久性等については問題なかったものの、表面抵抗が非常に高い結果となった。
　１　インセル型液晶パネル
　１０ａ　第１の透明基板
　１０ｂ　第２の透明基板
　２０ａ　第１の粘着剤層
　２０ｂ　第２の粘着剤層
　３０ａ　第１の偏光フィルム
　３０ｂ　第２の偏光フィルム
　４　液晶層
　５　タッチセンシング機能部
　１０  ガラス基板
　２０，２２  粘着剤層
　３０，１３０  偏光フィルム
　３２  位相差フィルム（ポリシクロオレフィン系フィルム）
　３４  ポリビニルアルコール（ＰＶＡ）フィルム
　３６  ＴＡＣフィルム
　３８  ポリシクロオレフィン系フィルム又はＴＡＣフィルム
　１００，２００  積層体

Claims (6)

  1. 　第１の偏光フィルム、第１の透明基板、及び前記第１の偏光フィルムと前記第１の透明基板との間に設置される粘着剤層を含むインセル型液晶パネルであって、
    　前記粘着剤層が、（メタ）アクリル重合体、架橋剤、及び帯電防止剤を含有する粘着剤組成物より形成され、
    　前記（メタ）アクリル重合体が、５０質量％超のアルコキシアルキル（メタ）アクリレートと、０．１～１５質量％の官能基含有モノマーとを含むモノマー組成物の重合体である、インセル型液晶パネル。
  2. 　前記モノマー組成物が、８０質量％以上でアルコキシアルキル（メタ）アクリレートを含む、請求項１に記載のインセル型液晶パネル。
  3. 　前記（メタ）アクリル重合体の重量平均分子量が１２０万以上である、請求項１に記載のインセル型液晶パネル。
  4. 　前記粘着剤層の耐久試験前後の表面抵抗率の変動比（ｂ／ａ）が、５．０以下であり、ここでａは、前記粘着剤層に離型フィルムが設けられた状態の粘着剤層付きの偏光フィルムを作製し、前記離型フィルムを剥離した直後の前記粘着剤層の表面抵抗率であり、ｂは、離型フィルムを付けたままの粘着剤層付偏光フィルムを８５℃×８５％ＲＨの加湿環境下に２４時間投入し、さらに４０℃で１時間乾燥させた後に、前記離型フィルムを剥離した直後の粘着剤層の表面抵抗率をいう、請求項１に記載のインセル型液晶パネル。
  5. 　耐久試験後の偏光度が９９．０％以上であり、前記耐久試験後の偏光度とは、粘着剤層付きの偏光フィルムを、インセル型液晶セルに貼り合わせ、５０℃／５気圧に調整されたオートクレーブ中に２０分間保持した後、８５℃８５％ＲＨの加湿環境下に２４時間投入した後に測定した偏光度である、請求項１に記載のインセル型液晶パネル。
  6. 　液晶層、前記液晶層を両面で挟持する第１の透明基板及び第２の透明基板、並びに前記第１の透明基板と第２の透明基板との間にタッチセンシング機能部を有するインセル型液晶セルと、
    　前記インセル型液晶セルの視認側に配置された第１の偏光フィルムと視認側の反対側に配置された第２の偏光フィルム、及び前記第１の偏光フィルムと前記インセル型液晶セルの第１の透明基板との間に配置された前記粘着剤層を有する、請求項１～５のいずれか一項に記載のインセル型液晶パネル。
PCT/JP2023/018121 2022-05-20 2023-05-15 インセル型液晶パネル WO2023224004A1 (ja)