WO2023205967A1 - 隔膜及包含其的装置 - Google Patents

隔膜及包含其的装置 Download PDF

Info

Publication number
WO2023205967A1
WO2023205967A1 PCT/CN2022/088840 CN2022088840W WO2023205967A1 WO 2023205967 A1 WO2023205967 A1 WO 2023205967A1 CN 2022088840 W CN2022088840 W CN 2022088840W WO 2023205967 A1 WO2023205967 A1 WO 2023205967A1
Authority
WO
WIPO (PCT)
Prior art keywords
binder
separator
separator according
porous coating
metal element
Prior art date
Application number
PCT/CN2022/088840
Other languages
English (en)
French (fr)
Inventor
熊长川
冯波
魏增斌
Original Assignee
宁德新能源科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 宁德新能源科技有限公司 filed Critical 宁德新能源科技有限公司
Priority to CN202280005580.6A priority Critical patent/CN116171506A/zh
Priority to PCT/CN2022/088840 priority patent/WO2023205967A1/zh
Publication of WO2023205967A1 publication Critical patent/WO2023205967A1/zh

Abstract

本申请涉及一种隔膜及包含其的装置。具体而言，本申请提供的隔膜包括：多孔基材和多孔涂层，多孔涂层设置在多孔基材的至少一个表面上，多孔涂层包括无机颗粒和粘结剂，所述粘结剂包括第一粘结剂，所述第一粘结剂包括金属元素。本申请隔膜具有优异的热安全稳定性和机械稳定性，这主要表现在：以直径为R且加热到500℃的圆针对隔膜进行热穿刺得到在隔膜上产生的破裂孔，对破裂孔边缘上的任意两点进行连线并计算两点之间的距离，取最大值为r，其中，400μm≤R≤1000μm且0.9≤r/R≤5。

Description

隔膜及包含其的装置 技术领域
本申请涉及储能技术领域，更具体地，涉及一种隔膜及包含其的装置。
背景技术
由于具有高能量密度和相对简单的反应机理、工作电压高、寿命长、绿色环保等优点，可再充电的二次电池被认为是最具吸引力的储能系统之一。如今，二次电池已经广泛地应用于可穿戴设备、智能手机、无人机、笔记本电脑等各个领域中。
随着二次电池在各个领域的广泛应用，人们对二次电池的需求越来越高。然而，当二次电池在一些极端环境(如撞击、穿钉以及热箱)下使用或者在其他情形下被非正常使用时，电池的安全性能难以保证，甚至会出现电池爆炸的情况。有鉴于此，亟需改进二次电池的安全性能。
发明内容
至少为了解决上述问题，本申请通过对电化学装置的隔膜进行改进以改善电化学装置的安全性能。具体的，本申请提供了一种具有高安全性能的隔膜，所述隔膜具有优异的耐热收缩性能、热穿刺性能以及热箱性能。
根据本申请的一个方面，本申请提供一种隔膜，其包括：多孔基材；和多孔涂层，所述多孔涂层设置在所述多孔基材的至少一个表面上，所述多孔涂层包括无机颗粒和粘结剂，所述粘结剂包括第一粘结剂，所述第一粘结剂包括金属元素；其中，以直径为R且加热到500℃的圆针对所述隔膜进行热穿刺得到在所述隔膜上产生的破裂孔，对所述破裂孔边缘上的任意两点进行连线并计算所述两点之间的距离，取最大值为r，以及其中，400μm≤R≤1000μm且0.9≤r/R≤5。
根据本申请的实施例，其中，400μm≤r≤1500μm。
根据本申请的实施例，其中，所述粘结剂的压缩强度为αMPa，0.5≤α≤10。
根据本申请的实施例，其中，所述粘结剂的玻璃化转变温度为Tg，150℃≤ Tg≤300℃。
根据本申请的实施例，其中，所述金属元素包括化合价为+1、+2或+3的金属元素中的至少一种。
根据本申请的实施例，其中，所述金属元素包括化合价为+1、+2或+3的所述金属元素中的至少两种。
根据本申请的实施例，其中，所述第一粘结剂满足以下条件(a)～(c)中的至少一者：(a)化合价为+1的所述金属元素包括Li或Na中的至少一种；(b)化合价为+2的所述金属元素包括Ca或Mg中的至少一种；(c)化合价为+3的所述金属元素包括Al。
根据本申请的实施例，其中，所述粘结剂满足以下条件(d)～(e)中的至少一者：(d)化合价为+1的所述金属元素与化合价为+2的所述金属元素的摩尔含量比为a，1≤a≤10；(e)化合价为+1的所述金属元素与化合价为+3的所述金属元素的摩尔含量比为b，1≤b≤50。
根据本申请的实施例，其中，所述第一粘结剂包括羧基或磺酸基中的至少一种，所述第一粘结剂pH值为pH 1，7≤pH 1≤11。
根据本申请的实施例，其中，所述第一粘结剂包括以下各者中的至少一种：聚甲基纤维素钠、聚甲基纤维素锂、聚羧甲基纤维素锂、聚羟丙基甲基纤维素锂、聚丙烯酸钙、聚丙烯酸锂或聚甲基丙烯酸钙。
根据本申请的实施例，其中，所述粘结剂还包括第二粘结剂，基于所述多孔涂层的总重量，所述第一粘结剂与所述第二粘结剂的重量比为β，0.2≤β≤4。
根据本申请的实施例，其中，所述第二粘结剂包括羧基或磺酸基中的至少一种，所述第二粘结剂pH值为pH 2，3≤pH 2≤7。
根据本申请的实施例，其中，所述第二粘结剂包括以下各者中的至少一种：聚丙烯酸丁酯、聚丙烯酸乙酯、聚甲基丙烯酸丁酯、聚甲基丙烯酸甲酯或丁苯橡胶。
根据本申请的实施例，其中，所述无机颗粒的比表面积为S BETm 2/g，2≤S BET≤10。
根据本申请的实施例，其中，所述无机颗粒的粒径Dv50和Dv99分别满足0.3μm≤Dv50≤3μm和Dv99≤4μm。
根据本申请的实施例，其中，所述无机颗粒包括以下各者中的至少一者：三 氧化二铝、勃姆石、氧化锆、氮化硼、氮化硅或氮化铝。
根据本申请的实施例，其中，所述多孔涂层还包括润湿剂，以所述多孔涂层的总重量计，所述无机颗粒的含量为m1重量％，所述粘结剂的含量为m2重量％，所述润湿剂的含量为m3重量％，其中90≤m1≤96，3≤m2≤9，0.5≤m3≤2，且m1+m2+m3＝100。
根据本申请的实施例，其中，所述润湿剂包括以下各者中的至少一种：聚氧乙烯烷基酚醚、聚氧乙烯脂肪醇醚、聚氧乙烯聚氧丙烯嵌段共聚物或硅氧烷。
根据本申请的实施例，其中，将所述隔膜在150℃下放置1小时，相较于所述隔膜的初始长和宽，所述隔膜在长度(MD)方向上的热收缩率为L1，在宽度(TD)方向上的热收缩率为L2，L1＜10％，L2＜10％，0.75≤L1/L2≤1.2。
根据本申请的实施例，其中所述多孔涂层的厚度为Tμm，0.5≤T≤3。
根据本申请的实施例，其中所述多孔涂层的粘结力为FN/m，5≤F≤100。
根据本申请的另一个方面，本申请还提供了一种电化学装置，其包括本申请上述实施例所述的隔膜。
根据本申请的另一个方面，本申请还提供了一种电子装置，其包括本申请上述实施例所述的电化学装置。
附图说明
在下文中将简要地说明为了描述本申请实施例或现有技术所必要的附图以便于描述本申请的实施例。显而易见地，下文描述中的附图仅只是本申请中的部分实施例。对本领域技术人员而言，在不需要创造性劳动的前提下，依然可以根据这些附图中所例示的结构来获得其他实施例的附图。
图1示出了经直径为R且加热到500℃的圆针热穿刺后本申请所述隔膜的电荷耦合器件(CCD)图像。
图2示出了经直径为R且加热到500℃的圆针热穿刺后现有技术中的隔膜的CCD图像。
具体实施方式
本申请的实施例将会被详细的描示在下文中。本申请的实施例不应该被解释为对本申请的限制。
如本申请所用，术语“包括”、“含有”和“包含”以其开放、非限制性含义使用。
另外，有时在本文中以范围格式呈现量、比率和其它数值。应理解，此类范围格式是用于便利及简洁起见，且应灵活地理解，不仅包含明确地指定为范围限制的数值，而且包含涵盖于范围内的所有个别数值或子范围，如同明确地指定每一数值及子范围一般。
在具体实施方式及权利要求书中，由术语“中的一者或多者”、“中的一个或多个”、“中的至少一种”或其他相似术语所连接的项目的列表可意味着所列项目的任何组合。例如，如果列出项目A及B，那么短语“A或B中的至少一种”意味着仅A；仅B；或A及B。在另一实例中，如果列出项目A、B及C，那么短语“A、B或C中的至少一种”意味着仅A；或仅B；仅C；A及B(排除C)；A及C(排除B)；B及C(排除A)；或A、B及C的全部。项目A可包含单个元件或多个元件。项目B可包含单个元件或多个元件。项目C可包含单个元件或多个元件。
隔膜
隔膜作为电化学装置的重要组成部分，位于电化学装置的正极和负极之间以在传输金属离子(例如，锂离子)的同时隔离正极和负极，实现防止短路的功能。然而，当被非正常使用时，电化学装置的电极组件内部的温度可能会急剧升高，导致隔膜产生较大程度的热收缩甚至熔融，从而造成正负极之间直接接触而发生短路。一旦发生短路，电化学装置内部会发生热失控，从而发生起火、爆炸等安全问题。
现有技术通常会在电化学装置中采用油性隔膜(例如，芳纶耐高温隔膜)来提高隔膜对高温的耐受性。然而，油性隔膜对生产工艺的要求很高，且会产生环境污染等问题。另外，相比于水性隔膜，油性隔膜的生产成本较高，因此会相应的增加电化学装置的生产成本。
至少基于对现有技术的上述洞察，本申请以水性隔膜作为研究对象，通过改善隔膜中多孔涂层的成分和其含量来提高隔膜的热稳定性和机械安全性能。具体的，本申请提出的隔膜包括多孔基材和多孔涂层，多孔涂层设置在多孔基材的至少一个表面上，多孔涂层包括无机颗粒和粘结剂。其中，本申请隔膜的一个主要特征在于：所述粘结剂包括第一粘结剂，所述第一粘结剂包括金属元素，其中以直径为R且加热到500℃的圆针对隔膜进行热穿刺得到在隔膜上产生的破裂孔， 对破裂孔边缘上的任意两点进行连线并计算两点之间的距离，取最大值为r，以及其中，400μm≤R≤1000μm且0.9≤r/R≤5。
根据本申请的其中一个实施例，图1示出了经直径为R(500μm)且加热到500℃的圆针热穿刺后隔膜的CCD相机拍摄的图像。如图1所示，经高温圆针热穿刺后会在隔膜上产生破裂孔，而在CCD相机的观察下，找到破裂孔边缘上距离最远的两点，并计算这两点之间的距离r，其中r为451μm。与之相比，采用现有技术常用的水性隔膜进行相同的热穿刺实验，由图2可以看出，现有技术的水性隔膜会产生破损孔面积较大，例如，该孔边缘上距离最远的两点之间的距离高达3088μm。破损孔面积的增大会造成正负极之间的接触风险增大，从而造成电池内部短路，导致电池热失控。
在一些实施例中，R可以，但不限于为400μm、500μm、600μm、700μm、800μm、900μm或1000μm，或者处于上述任意两个数值所组成的范围内。在一些实施例中，r/R可以，但不限于为0.9、1、1.2、1.4、1.6、1.8、2、2.2、2.4、2.6、2.8、3、3.2、3.4、3.6、3.8、4、4.2、4.4、4.6、4.8或5，或者处于上述任意两个数值所组成的范围内。在一些实施例中，1≤r/R≤1.5。在一些实施例中，1≤r/R≤2.5。在一些实施例中，1≤r/R≤3.5。在一些实施例中，1≤r/R≤4.5。
在一些实施例中，400μm≤r≤1500μm。例如，r可以，但不限于为400μm、500μm、600μm、700μm、800μm、900μm、1000μm、1100μm、1200μm、1300μm、1400μm、或1500μm，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，粘结剂的压缩强度为αMPa，其中0.5≤α≤10。当粘结剂的压缩强度处于上述范围内时，粘结剂不仅能够将分散的无机颗粒牢固地连接成网络骨架结构，还能够将无机颗粒与基材粘接在一起从而成为一体，最终提高隔膜整体的压缩强度，使得隔膜能够更好地抵抗应力冲击，进一步抑制冲击导致的破损，从而进一步改善电化学装置的热安全性能和机械安全性能。在一些实施例中，α可以，但不限于为0.5、1、2、3、4、5、6、7、8、9、或10，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，粘结剂的玻璃化转变温度为Tg，其中150℃≤Tg≤300℃。当粘结剂的玻璃化转变温度处于上述范围内时，粘结剂在高温下不易变软，也不易变脆，且能够处于适当的强度来抵抗应力冲击，减少冲击造成的破损，从而进一步改善电化学装置的热安全性能和机械安全性能。在一些实施例中，Tg可以， 但不限于为150℃、200℃、250℃、或300℃，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第一粘结剂中的金属元素包括化合价为+1、+2或+3的金属元素中的至少一种。在一些实施例中，第一粘结剂还包括羧基或磺酸基中的至少一种。第一粘结剂中的金属离子能够与其中的羧基或磺酸基络合形成金属键，进一步提高粘结剂的强度(例如，压缩强度)，使得隔膜能够更好地应对应力冲击，抑制冲击导致的破损，从而进一步改善电化学装置的热安全性能和机械安全性能。
在一些实施例中，第一粘结剂中的金属元素包括化合价为+1、+2或+3的金属元素中的至少两种。相较于仅含有一种金属元素，在第一粘结剂中使用至少两种不同的金属元素能够进一步增强粘结剂的强度，从而进一步改善隔膜应对应力冲击的能力以及其在高温下的稳定性。这可能是由于相较于单一金属元素，不同的金属元素更易与粘结剂中的羧基和/或磺酸基形成互穿金属键以构建互穿交联网络结构，从而改善材料力学性能。
在一些实施例中，化合价为+1的金属元素包括Li、Na或K中的至少一种。在一些实施例中，化合价为+2的金属元素包括Ca、Mg或Ba中的至少一种。在一些实施例中，化合价为+3的金属元素包括Al。在一些实施例中，第一粘结剂包括Li、Na、Ca、Mg或Al中的至少一者。
在一些实施例中，第一粘结剂同时包括化合价为+1和+2的金属元素，其中化合价为+1的金属元素与化合价为+2的金属元素的摩尔含量比为a，1≤a≤10。在一些实施例中，a可以，但不限于为1、2、3、4、5、6、7、8、9或10，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第一粘结剂同时包括化合价为+1和+3的金属元素，其中化合价为+1的金属元素与化合价为+3的金属元素的摩尔含量比为b，1≤b≤50。在一些实施例中，b可以，但不限于为1、10、20、30、40或50，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第一粘结剂同时包括化合价为+2和+3的金属元素，其中化合价为+2的金属元素与化合价为+3的金属元素的摩尔含量比为p，1≤p≤10。在一些实施例中，p可以，但不限于为1、2、3、4、5、6、7、8、9或10，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第一粘结剂满足以下条件中的至少一者：
(1)第一粘结剂同时包括Li和Na，其中Li和Na的摩尔含量比为c，1≤c≤8；
(2)第一粘结剂同时包括Li和Mg，其中Li和Mg的摩尔含量比为d，2≤d≤4；
(3)第一粘结剂同时包括Na和Mg，其中Na和Mg的摩尔含量比为e，2≤e≤4；
(4)第一粘结剂同时包括Li和Ca，其中Li和Ca的摩尔含量比为f，2≤f≤4；
(5)第一粘结剂同时包括Na和Ca，其中Na和Ca的摩尔含量比为g，2≤g≤4；
(6)第一粘结剂同时包括Li和Al，其中Li和Al的摩尔含量比为m，1≤m≤20；
(7)第一粘结剂同时包括Na和Al，其中Na和Al的摩尔含量比为n，1≤n≤20。
在一些实施例中，通过调整第一粘结剂中羧基或磺酸基以及金属元素的含量和比例能够调整第一粘结剂的pH值。在一些实施例中，第一粘结剂pH值为pH 1，7≤pH 1≤11。当第一粘结剂的pH值处于上述范围内时，第一粘结剂能够提供足够多的金属离子与其中的羧基或磺酸基形成金属离子络合键，从而进一步改善隔膜的热稳定性和机械性能。在一些实施例中，pH 1可以，但不限于为7、8、9、10或11，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第一粘结剂包括，但不限于，以下各者中的至少一种：聚甲基纤维素钠、聚甲基纤维素锂、聚羧甲基纤维素锂、聚羟丙基甲基纤维素锂、聚丙烯酸钙、聚丙烯酸锂、或聚甲基丙烯酸钙。
在一些实施例中，基于多孔涂层的总重量，第一粘结剂的重量含量为w 1％，其中0.5≤w 1≤4。在一些实施例中，w 1可以，但不限于为0.2、0.5、1、1.5、2、2.5、3、3.5或4，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第一粘结剂为溶液型粘接剂。溶液型粘接剂是指粘接剂高分子溶解在溶剂中形成溶液。在一些实施例中，溶剂是水。
在一些实施例中，粘结剂包括第二粘结剂。在一些实施例中，第二粘结剂是 与第一粘结剂类型不同的粘结剂。例如，第二粘结剂为乳液性粘结剂。乳液性粘结剂是指粘接剂高分子分散在分散介质中形成乳液。在一些实施例中，分散介质是水。
在一些实施例中，基于多孔涂层的总重量，第二粘结剂的重量含量为w 2％，其中2.5≤w 2≤5。在一些实施例中，w 2可以，但不限于为2.5、3、4或5，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第二粘结剂包括羧基或磺酸基中的至少一种。当粘结剂同时包括第一粘结剂和第二粘结剂时，第一粘结剂中的金属离子也能够与第二粘结剂中的羧基或磺酸基络合，形成金属键和互穿网络结构，从而进一步提高粘结剂的强度，加强隔膜抵制外力冲击的能力，从而进一步改善电化学装置的热安全性能和机械安全性能。
此外，当粘结剂同时包括第一粘结剂和第二粘结剂时，通过优化第一粘结剂与第二粘结剂的重量比能够进一步提高粘结剂的强度。在一些实施例中，基于多孔涂层的总重量，第一粘结剂与第二粘结剂的重量比(即，w 1/w 2)为β，0.2≤β≤4。在一些实施例中，β可以，但不限于为0.2、0.5、1、1.5、2、2.5、3、3.5或4，或者处于由上述任意两个数值组成的范围内。
在一些实施例中，通过调整第二粘结剂中羧基和/或磺酸基的含量和比例能够调整第二粘结剂的pH值。在一些实施例中，第二粘结剂pH值为pH 2，3≤pH 2≤7。当第二粘结剂的pH值处于上述范围内时，能够进一步改善隔膜的热稳定性和机械性能。这可能是由于第二粘结剂能够提供额外的活性基团(例如羧基或磺酸基)，提高其与金属离子络合的机率，形成更多金属离子络合键，改善材料力学性能。在一些实施例中，pH 2可以，但不限于为3、4、5、6或7，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，第二粘结剂包括，但不限于，以下各者中的至少一种：聚丙烯酸丁酯、聚丙烯酸乙酯、聚甲基丙烯酸丁酯、聚甲基丙烯酸甲酯或丁苯橡胶。
在一些实施例中，位于多孔涂层中的无机颗粒的比表面积为S BETm 2/g，2≤S BET≤10。在一些实施例中，S BET可以，但不限于为2、3、4、5、6、7、8、9或10，或者处于上述任意两个数值所组成的范围内。在一些实施例中，2≤S BET≤5。
在一些实施例中，无机颗粒的粒径Dv50满足0.3μm≤Dv50≤3μm。在一些实 施例中，无机颗粒的粒径Dv99满足Dv99≤4μm。其中，Dv50也可称为中值粒径，其为体积分布中百分数达到50％时所对应的粒径值；Dv99则为体积分布中百分数达到99％时所对应的粒径值。当无机颗粒的粒径处于上述范围内时，既有利于对多孔涂层的厚度进行减薄，提高电化学装置的能量密度，又能够确保粘接位点处于合适的范围内，降低粘结剂的用量，改善电化学装置的动力学性能。
在一些实施例中，可用于本申请隔膜的无机颗粒包括，但不限于，以下各者中的至少一种：三氧化二铝、勃姆石、氧化锆、氮化硼、氮化硅、氮化铝、二氧化硅、氧化镁、氧化钛、碳化硅、氢氧化铝或者氢氧化镁。
在一些实施例中，多孔涂层还包括润湿剂，其中润湿剂的作用在于改善多孔涂层浆料对基材的润湿性，避免涂布加工过程产生的漏涂。此外，通过优化无机颗粒、粘结剂和润湿剂在多孔涂层中的重量占比，能够进一步增强隔膜的热安全性能和机械稳定性。在一些实施例中，以多孔涂层的总重量计，无机颗粒的含量为m1重量％，粘结剂的含量为m2重量％，润湿剂的含量为m3重量％，其中90≤m1≤96，3≤m2≤9，0.5≤m3≤2，且m1+m2+m3＝100。
在一些实施例中，润湿剂包括，但不限于，以下各者中的至少一种：聚氧乙烯烷基酚醚、聚氧乙烯脂肪醇醚、聚氧乙烯聚氧丙烯嵌段共聚物或硅氧烷。
在一些实施例中，将本申请隔膜在150℃下放置1小时，相较于隔膜的初始长度，隔膜在长度(MD)方向上的热收缩率为L1，相较于隔膜的初始宽度，隔膜在宽度(TD)方向上的热收缩率为L2，其中L1＜10％，L2＜10％，0.75≤L1/L2≤1.2。在一些实施例中，L1和L2可以，但不限于，分别为1％，2％，3％，4％，5％，6％，7％，8％，或9％，或者处于上述任意两个数值所组成的范围内。在一些实施例中，L1/L2可以为，但不限于，0.8、0.9、1.0、1.1或1.2，或者处于上述任意两个数值所组成的范围内。
在一些实施例中，多孔涂层的厚度为Tμm，其中0.5≤T≤3。当多孔涂层的厚度处于上述范围内时，既能够提高电化学装置的能量密度，还能够改善电化学装置的动力学性能。在一些实施例中，T可以为，但不限于，0.5、1、1.5、2、2.5或3，或者处于由上述任意两个数值组成的范围内。其中，当多孔基材的两个表面上均涂覆有多孔涂层时，上述提到的“多孔涂层的厚度”指的是这两个表面上经涂覆的多孔涂层的厚度之和。
在一些实施例中，多孔涂层的粘结力为F N/m，5≤F≤100。当多孔涂层的 粘结力处于上述范围内时，不仅能够使无机颗粒牢固地粘结至多孔基材上而不易脱落，而且还不必使用过多的粘结剂从而恶化电化学装置的动力学性能。在一些实施例中，F可以为，但不限于，5、10、20、30、40、50、60、70、80、90或100，或者处于由上述任意两个数值组成的范围内。在一些实施例中，20≤F≤85。
在一些实施例中，多孔基材可以包括，但不限于，以下各者中的至少一种：聚乙烯(PE)、超高分子量聚乙烯(UHMWPE)、高密度聚乙烯(HDPE)、聚丙烯(PP)、聚对苯二甲酸乙二醇酯(PET)、聚苯硫醚(PPS)、纤维素、聚酰亚胺、聚苯乙烯(PS)、聚4-甲基-1-戊烯(TPX)、聚甲基丙烯酸甲酯(PMMA)、聚偏氟乙烯(PVDF)、聚偏氟乙烯-六氟丙烯(PVDF-HFP)、聚四氟乙烯(PTFE)和聚砜。
本申请另提供了一种电化学装置，其包含本申请上述实施例的隔膜。在一些实施例中，电化学装置还包括负极、正极和电解液，其中隔膜位于正极和负极之间。如下，本申请将详细描述正极、负极和电解质的组成。
正极
正极包括正极材料，正极材料包括能够吸收和释放锂(Li)的正极材料(下文中，有时称为“能够吸收/释放锂Li的正极材料”)。能够吸收/释放锂(Li)的正极材料的例子可以包括钴酸锂、镍钴锰酸锂、镍钴铝酸锂、锰酸锂、磷酸锰铁锂、磷酸钒锂、磷酸钒氧锂、磷酸铁锂、钛酸锂和富锂锰基材料。
具体的，钴酸锂的化学式可以如化学式1：
Li x1Co a1M1 b1O 2-c1      化学式1
其中M1表示选自镍(Ni)、锰(Mn)、镁(Mg)、铝(Al)、硼(B)、钛(Ti)、钒(V)、铬(Cr)、铁(Fe)、铜(Cu)、锌(Zn)、钼(Mo)、锡(Sn)、钙(Ca)、锶(Sr)、钨(W)、钇(Y)、镧(La)、锆(Zr)和硅(Si)中的至少一种，x1、a1、b1和c1值分别在以下范围内：0.8≤x1≤1.2、0.8≤a1≤1、0≤b1≤0.2、-0.1≤c1≤0.2；
镍钴锰酸锂或镍钴铝酸锂的化学式可以如化学式2：
Li y1Ni d1M2 e1O 2-f1      化学式2
其中M2表示选自钴(Co)、锰(Mn)、镁(Mg)、铝(Al)、硼(B)、钛(Ti)、钒(V)、铬(Cr)、铁(Fe)、铜(Cu)、锌(Zn)、钼(Mo)、锡(Sn)、钙(Ca)、锶(Sr)、钨(W)、锆(Zr)和硅(Si)中的至少一种，y1、d1、e1和f1值分 别在以下范围内：0.8≤y1≤1.2、0.3≤d1≤0.98、0.02≤e1≤0.7、-0.1≤f1≤0.2；
锰酸锂的化学式可以如化学式3：
Li z1Mn 2-g1M 3g1O 4-h1     化学式3
其中M3表示选自钴(Co)、镍(Ni)、镁(Mg)、铝(Al)、硼(B)、钛(Ti)、钒(V)、铬(Cr)、铁(Fe)、铜(Cu)、锌(Zn)、钼(Mo)、锡(Sn)、钙(Ca)、锶(Sr)和钨(W)中的至少一种，z1、g1和h1值分别在以下范围内：0.8≤z1≤1.2、0≤g1＜1.0和-0.2≤h1≤0.2。
负极
负极包括负极材料，负极材料包括能够吸收和释放锂(Li)的负极材料(下文中，有时称为“能够吸收/释放锂Li的负极材料”)。能够吸收/释放锂(Li)的负极材料的例子可以包括碳材料、金属化合物、氧化物、硫化物、锂的氮化物例如LiN 3、锂金属、与锂一起形成合金的金属和聚合物材料。
碳材料的例子可以包括低石墨化的碳、易石墨化的碳、人造石墨、天然石墨、中间相碳微球、软碳、硬碳、热解碳、焦炭、玻璃碳、有机聚合物化合物烧结体、碳纤维和活性碳。其中，焦炭可以包括沥青焦炭、针状焦炭和石油焦炭。有机聚合物化合物烧结体指的是通过在适当的温度下煅烧聚合物材料例如苯酚塑料或者呋喃树脂以使之碳化获得的材料，将这些材料中的一些分成低石墨化碳或者易石墨化的碳。聚合物材料的例子可以包括聚乙炔和聚吡咯。
在能够吸收/释放锂(Li)的这些负极材料中，更进一步地，选择充电和放电电压接近于锂金属的充电和放电电压的材料。这是因为负极材料的充电和放电电压越低，电化学装置(例如锂离子电池)越容易具有更高的能量密度。其中，负极材料可以选择碳材料，因为在充电和放电时它们的晶体结构只有小的变化，因此，可以获得良好的循环特性以及大的充电和放电容量。尤其可以选择石墨，因为它可以给出大的电化学当量和高的能量密度。
此外，能够吸收/释放锂(Li)的负极材料可以包括单质锂金属、能够和锂(Li)一起形成合金的金属元素和半金属元素，包括这样的元素的合金和化合物等等。特别地，将它们和碳材料一起使用，因为在这种情况中，可以获得良好的循环特性以及高能量密度。除了包括两种或者多种金属元素的合金之外，这里使用的合金还包括包含一种或者多种金属元素和一种或者多种半金属元素的合金。该合金可以处于以下状态固溶体、共晶晶体(共晶混合物)、金属间化合物及其混 合物。
金属元素和半金属元素的例子可以包括锡(Sn)、铅(Pb)、铝(Al)、铟(In)、硅(Si)、锌(Zn)、锑(Sb)、铋(Bi)、镉(Cd)、镁(Mg)、硼(B)、镓(Ga)、锗(Ge)、砷(As)、银(Ag)、锆(Zr)、钇(Y)和铪(Hf)。上述合金和化合物的例子可以包括具有化学式：Ma sMb tLi u的材料和具有化学式：Ma pMc qMd r的材料。在这些化学式中，Ma表示能够与锂一起形成合金的金属元素和半金属元素中的至少一种元素；Mb表示除锂和Ma之外的金属元素和半金属元素中的至少一种元素；Mc表示非金属元素中的至少一种元素；Md表示除Ma之外的金属元素和半金属元素中的至少一种元素；并且s、t、u、p、q和r满足s＞0、t≥0、u≥0、p＞0、q＞0和r≥0。
此外，可以在负极中使用不包括锂(Li)的无机化合物，例如MnO 2、V 2O 5、V 6O 13、NiS和MoS。
电解质
电解质可以是凝胶电解质、固态电解质和电解液中的一种或多种，电解液包括锂盐和非水溶剂。
锂盐选自LiPF 6、LiBF 4、LiAsF 6、LiClO 4、LiB(C 6H 5) 4、LiCH 3SO 3、LiCF 3SO 3、LiN(SO 2CF 3) 2、LiC(SO 2CF 3) 3、LiSiF 6、LiBOB和二氟硼酸锂中的一种或多种。例如，锂盐选用LiPF 6，因为它可以给出高的离子导电率并改善循环特性。
非水溶剂可为碳酸酯化合物、羧酸酯化合物、醚化合物、其它有机溶剂或它们的组合。
碳酸酯化合物可为链状碳酸酯化合物、环状碳酸酯化合物、氟代碳酸酯化合物或其组合。
链状碳酸酯化合物的实例为碳酸二乙酯(DEC)、碳酸二甲酯(DMC)、碳酸二丙酯(DPC)、碳酸甲丙酯(MPC)、碳酸乙丙酯(EPC)、碳酸甲乙酯(MEC)及其组合。环状碳酸酯化合物的实例为碳酸亚乙酯(EC)、碳酸亚丙酯(PC)、碳酸亚丁酯(BC)、碳酸乙烯基亚乙酯(VEC)及其组合。氟代碳酸酯化合物的实例为碳酸氟代亚乙酯(FEC)、碳酸1，2-二氟亚乙酯、碳酸1，1-二氟亚乙酯、碳酸1，1，2-三氟亚乙酯、碳酸1，1，2，2-四氟亚乙酯、碳酸1-氟-2-甲基亚乙酯、碳酸1-氟-1-甲基亚乙酯、碳酸1，2-二氟-1-甲基亚乙酯、碳酸1，1，2-三氟-2-甲基亚乙酯、碳酸三氟甲基亚乙酯及其组合。
羧酸酯化合物的实例为乙酸甲酯、乙酸乙酯、乙酸正丙酯、乙酸叔丁酯、丙酸甲酯、丙酸乙酯、丙酸丙酯、γ-丁内酯、癸内酯、戊内酯、甲瓦龙酸内酯、己内酯、甲酸甲酯及其组合。
醚化合物的实例为二丁醚、四甘醇二甲醚、二甘醇二甲醚、1，2-二甲氧基乙烷、1，2-二乙氧基乙烷、乙氧基甲氧基乙烷、2-甲基四氢呋喃、四氢呋喃及其组合。
其它有机溶剂的实例为二甲亚砜、1，2-二氧戊环、环丁砜、甲基环丁砜、1，3-二甲基-2-咪唑烷酮、N-甲基-2-吡咯烷酮、甲酰胺、二甲基甲酰胺、乙腈、磷酸三甲酯、磷酸三乙酯、磷酸三辛酯、和磷酸酯及其组合。
本申请的电化学装置包括发生电化学反应的任何装置，它的具体实例包括所有种类的一次电池、二次电池、燃料电池、太阳能电池或电容。特别地，该电化学装置是钠二次电池、锂二次电池、聚合物二次电池。
本申请另提供了一种电子装置，其包括根据本申请的电化学装置。
本申请的电化学装置的用途没有特别限定，其可用于现有技术中已知的任何电子装置。在一些实施例中，本申请的电化学装置可用于，但不限于，笔记本电脑、笔输入型计算机、移动电脑、电子书播放器、便携式电话、便携式传真机、便携式复印机、便携式打印机、头戴式立体声耳机、录像机、液晶电视、手提式清洁器、便携CD机、迷你光盘、收发机、电子记事本、计算器、存储卡、便携式录音机、收音机、备用电源、电机、汽车、摩托车、助力自行车、自行车、照明器具、玩具、游戏机、钟表、电动工具、闪光灯、照相机、家庭用大型蓄电池和电容器等。
下面以锂离子电池为例并且结合具体的实施例说明锂离子电池的制备，本领域的技术人员将理解，本申请中描述的制备方法仅是实例，其他任何合适的制备方法均在本申请的范围内。
实施例
以下说明根据本申请的锂离子电池的实施例和对比例进行的性能评估。
一、锂离子电池的制备
1、粘结剂的制备
丙烯酸类粘结剂的制备过程：1、将适量丙烯酸单体加入到反应釜中，并加入适量催化剂，慢速搅拌均匀；2、加入适量含磺酸基单体或者羧基单体(例如： 甲基丙磺酸或者甲基丙烯酸)到反应釜；3、反应釜通入惰性气体形成反应保护气氛；4、反应釜升温加热至反应温度，单体聚合，得到同时含有两种功能基团的粘结剂；5、反应完成后，可通过加入金属碱，调整粘结剂出料pH，即可得到所需粘结剂。
其中通过改变反应单体类型，可以得到含有不同功能基团的粘结剂。选择不同类型金属碱(例如：氢氧化钠，氢氧化镁)或者不同含量添加的金属碱，可以实现粘结剂中金属碱类型与含量比例的设计调控；
纤维素类粘结剂的制备过程：1、将适量原料纤维素置于反应釜，然后加入金属碱(氢氧化钠)，对纤维素碱化处理，得到碱化的纤维素；2、碱化纤维素中加入适量氯乙酸，进行醚化反应，最后得到纤维素钠粘结剂。
其中，在碱化处理过程中，通过更换金属碱类型或者金属碱比例等相关工艺参数，可以实现粘结剂中金属碱类型与含量比例的设计调控。
2、隔膜的制备方法
将水与无机颗粒充分混合后，再加入一定量的粘接剂，放入搅拌器中搅拌均匀。随后将一定量的润湿剂加入上述浆料中，继续搅拌直至混合均匀。最后，在基材PE单面均匀涂覆至合适的厚度，待涂覆完成后放入烘箱中干燥，得到本申请的隔膜。其中无机颗粒、粘结剂和润湿剂的成分和含量以及涂覆厚度等参数详见表1。
3、锂离子电池的制备方法
将正极活性物质钴酸锂、导电碳(Super P)和粘结剂聚偏二氟乙烯(PVDF)按重量比96∶2∶2溶解于N-甲基吡咯烷酮溶剂体系中，充分搅拌混合均匀，制得正极浆料。将正极浆料涂覆于铝箔上、烘干、冷压、分条，得到正极。
将负极活性物质人造石墨、导电剂(Super P)、粘结剂丁苯橡胶和增稠剂羧甲基纤维素钠按照重量比98∶0.5∶1∶0.5溶解于去离子水溶剂体系中，充分搅拌混合均匀，制得负极浆料。将负极浆料涂覆于铜箔上、烘干、冷压、分条，得到负极。
将锂盐LiPF 6与非水有机溶剂(碳酸乙烯酯(EC)∶碳酸二乙酯(DEC)∶碳酸亚丙酯(PC)∶丙酸丙酯(PP)∶碳酸亚乙烯酯(VC))＝20∶30∶20∶28∶2，质量比)按质量比8∶92配制而成的溶液作为锂离子电池的电解液。
将正极、隔离膜和负极按顺序叠好，使隔离膜处于正极和负极中间，卷绕得 到电极组件。将电极组件置于外包装中，注入电解液并封装，进行化成之后制成最终的锂离子电池产品。
二、测试方法
1、隔膜的穿刺测试
首先，将多孔涂层隔膜平整的固定在测试夹具上，并将夹具置于高铁拉力机移动支架垂直下方；其次，将测试热针垂直固定在高铁拉力机的移动支架，确保热针能够垂直刺穿隔膜；然后，高铁拉力机移动支架以一定速度(20cm/min)带动热针垂直刺穿隔膜，刺穿深度2-4cm，刺穿后热针停止1min后回归初始位置；最后，取出隔膜样品，在CCD相机下测量破裂孔边缘上任意两点进行连线并计算所述两点之间的距离，取最大值为r。
2、粘接剂的压缩强度测试
将粘接剂胶膜样品(尺寸为10mm×10mm×10mm)置于万能试验机的两个压板的中间位置，在沿样品两端面的竖直方向，以恒定速率(10mm/min)施加应力压缩样品，使样品沿轴向缩短，而径向方向增大，产生压缩变形，直到样品破裂为止。读取万能试验机施加最大负荷应力值Pmax，并通过以下公式计算粘接剂的压缩强度α：
α＝Pmax/S，
其中S为样品初始截面积。
3、粘接剂的玻璃化转变温度测试
取一定量(10-20mg)粘结剂胶膜样品，置于差示扫描量热仪的加热坩埚中，启动设备测试程序，通过测试软件得到Temp-DSC曲线图，一般读取曲线的第一个变化台阶对应的温度即为粘结剂的玻璃化转变温度；
4、粘接剂中金属元素及其含量比的测定
将电池放入手套箱中拆解，取出隔膜并去除涂布在多孔涂层上的PVDF/PMMA胶层之后，留下多孔涂层，再通过“水洗”方式将多孔涂层重新分散在水中，经离心分离无机颗粒后得到水洗清液，水洗清液中包括粘结剂。通过电感耦合等离子体(ICP)测试测定水洗清液，得到粘接剂中金属元素及其含量比。
5、无机颗粒的比表面积测试
启动测试软件，取一定量无机颗粒置于样品测试仓，采用BET比表面积测 定方法测试无机颗粒比表面。测试完成后，测试软件自动读取无机颗粒比表面积数值。
6、无机颗粒的粒径测试
启动测试软件，将满足测试质量要求的无机颗粒置于马尔文3000型激光粒度仪的测试仓中，然后启动超声5分钟以确保颗粒无团聚，之后进入测试粒径步骤，由软件输出粒径分布曲线。
7、隔膜在MD和TD方向上的热收缩测试
首先，将隔膜裁切为长度为MD1和宽度为TD1的尺寸(MD1＝10cm，TD1＝5cm)，得到测试隔膜样品。其次，将裁切好的隔膜样品放于两张A4纸之间，置于150℃烘箱中烘烤1小时。然后，用CCD相机测量于150℃烘烤1小时后的隔膜样品的长度和宽度，分别记为MD2和TD2。最后，通过以下公式计算隔膜在MD方向上的热收缩率L1和隔膜在TD方向上的热收缩率L2：
L1＝(MD1-MD2)/MD1；
L2＝(TD1-TD2)/TD1。
8、多孔涂层的厚度测试
利用台式隔膜测厚仪分别测定基材和隔膜的厚度，并分别记作T 1μm和Tμm。利用如下公式计算多孔涂层的厚度T 2μm：
T 2＝T-T 1。
9、多孔涂层的粘结力测试
首先，将涂布好的隔膜样品平铺在玻璃板上，保持多孔涂层朝上，四边用胶带固定，确保隔膜平整固定在玻璃板上；其次，用剥离力测试专用胶带平直地贴附在多孔涂层的表面；然后，用1KG压辊来回碾压剥离力测试专用胶带粘贴区域；之后，在剥离力测试专用胶带粘贴区域裁切出15mm×54.2mm隔膜测试样品；最后，将隔膜测试样品一侧固定在高铁拉力机一端，胶带侧固定在高铁拉力机移动支架一端，移动支架以一定的速度拉伸胶带，使得胶带从隔膜表面180°剥离，测试软件读取数值即为多孔涂层的粘结力。
10、热箱测试
取100个锂离子电池样品，在常温下以0.5C倍率恒定电流充电至4.5V，进一步在4.5V恒定电压下充电至电流低于0.05C，使其处于4.5V满充状态。将锂离子电池样品放入烘箱中，在137℃中放置1h，锂离子电池若没有发生冒烟、起 火、爆炸，则记为通过，反之则记为不通过。热箱通过率是指通过测试的锂离子电池数量与锂离子电池总数的比值。
11、穿钉测试
首先，在穿钉测试前后检查电池外观并拍照；其次，将感温线黏贴在电池表面的中心处；然后，在20±5℃测试环境中，将测试电池放置于测试台面，使用2.5mm直径的钢钉以150mm/s的速度从样品中心位置测试，样品完全刺穿；若电池不起火也不爆炸，则说明电池通过测试。
三、测试结果
表1展示了粘结剂的pH值和含量对粘结剂性质、隔膜性质和电化学性质的影响。从表1可以看出，相较于对比例，在实施例中同时采用第一粘结剂和第二粘结剂，并同时调整第一粘结剂和第二粘结剂的pH值和含量满足7≤pH 1≤11、3≤pH 2≤7、0.5≤w 1≤4和2.5≤w 2≤5，(1)能够得到具有较大压缩强度和较高Tg温度的粘结剂；(2)在经历150℃烘烤1小时后，实施例中的隔膜的MD和TD热收缩率更低且在经过热穿刺实验中产生更小的破裂孔；(3)实施例中的电化学装置全部通过热箱测试和穿钉测试。
表2是在实施例1-1的基础上进行的改进，其中所添加的第一粘结剂和第二粘结剂的总含量是相同的，其差别仅在于第一粘结剂和第二粘结剂的含量比不同。从表2的数据可以看出，通过进一步调整第一粘结剂和第二粘结剂的含量比w 1/w 2满足0.2≤w 1/w 2≤1.6能够进一步改善粘结剂的拉伸强度、隔膜的热稳定性以及电化学装置的安全性能。
表3是在实施例1-1的基础上进行的改进，其中第一粘结剂中所添加的金属元素的电荷总含量是相同的(即，第一粘结剂中一个酸性基团(羧基/磺酸基)反应一个1+价金属离子，以此类推)，其差别仅在于所添加的金属元素的种类和含量比不同。从表3的数据可以看出，相较于仅添加一种金属元素，在第一粘结剂中添加了两种金属元素后，粘结剂的压缩强度、隔膜的热稳定性以及电化学装置的安全性能均得到了进一步的改进。
此外，从实施例3-6至3-15可以看出，当化合价为+1的金属元素与化合价为+2的金属元素的含量比a处于1≤a≤10的范围内时，能够进一步改善粘结剂、隔膜和电化学装置的性能。从实施例3-16至3-20可以看出，当化合价为+1的金 属元素与化合价为+3的金属元素的含量比b处于1≤b≤50的范围内时，能够进一步改善粘结剂、隔膜和电化学装置的性能。
表4是在实施例3-7的基础上进行的改进，其差别仅在于无机颗粒的组分、中值粒径和含量不同。从实施例3-7至4-5可以看出，选用三氧化二铝、勃姆石、氧化锆、氮化硼、氮化硅或氮化铝作为多孔涂层中的无机颗粒均可以获得高温性能优异的隔膜和电化学装置。
从实施例4-6至4-12可以看出，当无机颗粒的中值粒径Dv50满足0.3μm≤Dv50≤2μm，能够得到高温性能更优异的隔膜和电化学装置。
从实施例4-13至4-16可以看出，以所述多孔涂层的总重量计，当无机颗粒的含量m 1重量％满足90≤m 1≤96，能够得到高温性能更优异的隔膜和电化学装置。
表5是在实施例3-7的基础上进行的改进，其差别仅在于润湿剂的组分和含量不同。从表5可以看出，选用聚氧乙烯烷基酚醚、聚氧乙烯脂肪醇醚、聚氧乙烯聚氧丙烯嵌段共聚物或硅氧烷作为多孔涂层中的润湿剂均可以获得高温性能优异的隔膜和电化学装置。
从实施例5-3至5-7可以看出，以所述多孔涂层的总重量计，当润湿剂的含量m 3重量％满足0.5≤m 3≤1.5，能够得到高温性能更优异的隔膜和电化学装置。
表6是在实施例4-6的基础上进行的改进，其差别仅在于多孔涂层的厚度不同。从表6可以看出，当多孔涂层的厚度T处于0.5≤T≤3的范围内时，能够得到高温性能更优异的隔膜和电化学装置。
整个说明书中对“实施例”、“部分实施例”、“一个实施例”、“另一举例”、“举例”、“具体举例”或“部分举例”的引用，其所代表的意思是在本申请中的至少一个实施例或举例包含了该实施例或举例中所描述的特定特征、结构、材料或特性。因此，在整个说明书中的各处所出现的描述，例如：“在一些实施例中”、“在实施例中”、“在一个实施例中”、“在另一个举例中”、“在一个举例中”、“在特定举例中”或“举例”，其不必然是引用本申请中的相同的实施例或示例。此外，本文中的特定特征、结构、材料或特性可以以任何合适的方式在一个或多个实施例或举例中结合。
尽管已经演示和描述了说明性实施例，本领域技术人员应该理解上述实施例不能被解释为对本申请的限制，并且可以在不脱离本申请的精神、原理及范围的情况下对实施例进行改变，替代和修改。
Figure PCTCN2022088840-appb-000001
Figure PCTCN2022088840-appb-000002
Figure PCTCN2022088840-appb-000003
Figure PCTCN2022088840-appb-000004
Figure PCTCN2022088840-appb-000005
Figure PCTCN2022088840-appb-000006
Figure PCTCN2022088840-appb-000007
Figure PCTCN2022088840-appb-000008
Figure PCTCN2022088840-appb-000009

Claims (23)

  1. 一种隔膜，其包括：
    多孔基材和多孔涂层，所述多孔涂层设置在所述多孔基材的至少一个表面上，所述多孔涂层包括无机颗粒和粘结剂，所述粘结剂包括第一粘结剂，所述第一粘结剂包括金属元素；
    其中，以直径为R且加热到500℃的圆针对所述隔膜进行热穿刺得到在所述隔膜上产生的破裂孔，对所述破裂孔边缘上的任意两点进行连线并计算所述两点之间的距离，取最大值为r，以及
    其中，400μm≤R≤1000μm且0.9≤r/R≤5。
  2. 根据权利要求1所述的隔膜，其中，400μm≤r≤1500μm。
  3. 根据权利要求1所述的隔膜，其中，所述粘结剂的压缩强度为αMPa，0.5≤α≤10。
  4. 根据权利要求1所述的隔膜，其中，所述粘结剂的玻璃化转变温度为Tg，150℃≤Tg≤300℃。
  5. 根据权利要求1所述的隔膜，其中，所述金属元素包括化合价为+1、+2或+3的金属元素中的至少一种。
  6. 根据权利要求1所述的隔膜，其中，所述金属元素包括化合价为+1、+2或+3的所述金属元素中的至少两种。
  7. 根据权利要求1所述的隔膜，其中，所述第一粘结剂满足以下条件(a)～(c)中的至少一者：
    (a)化合价为+1的所述金属元素包括Li或Na中的至少一种；
    (b)化合价为+2的所述金属元素包括Ca或Mg中的至少一种；
    (c)化合价为+3的所述金属元素包括Al。
  8. 根据权利要求1所述的隔膜，其中，所述粘结剂满足以下条件(d)～(e)中的至少一者：
    (d)化合价为+1的所述金属元素与化合价为+2的所述金属元素的摩尔含量比为a，1≤a≤10；
    (e)化合价为+1的所述金属元素与化合价为+3的所述金属元素的摩尔含量比为b，1≤b≤50。
  9. 根据权利要求1所述的隔膜，其中，所述第一粘结剂包括羧基或磺酸基中的至少一种，所述第一粘结剂的pH值为pH 1，7≤pH 1≤11。
  10. 根据权利要求1所述的隔膜，其中，所述第一粘结剂包括以下各者中的至少一种：聚甲基纤维素钠、聚甲基纤维素锂、聚羧甲基纤维素锂、聚羟丙基甲基纤维素锂、聚丙烯酸钙、聚丙烯酸锂或聚甲基丙烯酸钙。
  11. 根据权利要求1所述的隔膜，其中，所述粘结剂还包括第二粘结剂，基于所述多孔涂层的总重量，所述第一粘结剂与所述第二粘结剂的重量比为β，0.2≤β≤4。
  12. 根据权利要求11所述的隔膜，其中，所述第二粘结剂包括羧基或磺酸基中的至少一种，所述第二粘结剂pH值为pH 2，3≤pH 2≤7。
  13. 根据权利要求11所述的隔膜，其中，所述第二粘结剂包括以下各者中的至少一种：聚丙烯酸丁酯、聚丙烯酸乙酯、聚甲基丙烯酸丁酯、聚甲基丙烯酸甲酯或丁苯橡胶。
  14. 根据权利要求1所述的隔膜，其中，所述无机颗粒的比表面积为S BETm 2/g，2≤S BET≤10。
  15. 根据权利要求1所述的隔膜，其中，所述无机颗粒的粒径Dv50和Dv99分别满足0.3μm≤Dv50≤3μm和Dv99≤4μm。
  16. 根据权利要求1所述的隔膜，其中，所述无机颗粒包括以下各者中的至少一者：三氧化二铝、勃姆石、氧化锆、氮化硼、氮化硅或氮化铝。
  17. 根据权利要求1所述的隔膜，其中，所述多孔涂层还包括润湿剂，以所述多孔涂层的总重量计，所述无机颗粒的含量为m1重量％，所述粘结剂的含量为m2重量％，所述润湿剂的含量为m3重量％，其中90≤m1≤96，3≤m2≤9，0.5≤m3≤2，且m1+m2+m3＝100。
  18. 根据权利要求17所述的隔膜，其中，所述润湿剂包括以下各者中的至少一种：聚氧乙烯烷基酚醚、聚氧乙烯脂肪醇醚、聚氧乙烯聚氧丙烯嵌段共聚物或硅氧烷。
  19. 根据权利要求1所述的隔膜，其中，将所述隔膜在150℃下放置1小时，相较于所述隔膜的初始长和宽，所述隔膜在长度MD方向上的热收缩率为L1，在宽度TD方向上的热收缩率为L2，L1＜10％，L2＜10％，0.75≤L1/L2≤1.2。
  20. 根据权利要求1所述的隔膜，其中所述多孔涂层的厚度为Tμm，0.5≤T≤3。
  21. 根据权利要求1所述的隔膜，其中所述多孔涂层的粘结力为F N/m，5≤F≤100。
  22. 一种电化学装置，其包括权利要求1-21中任一者所述的隔膜。
  23. 一种电子装置，其包括权利要求22所述的电化学装置。
PCT/CN2022/088840 2022-04-24 2022-04-24 隔膜及包含其的装置 WO2023205967A1 (zh)