WO2023189814A1 - 偏光フィルム、及び画像表示装置 - Google Patents

偏光フィルム、及び画像表示装置 Download PDF

Info

Publication number
WO2023189814A1
WO2023189814A1 PCT/JP2023/010858 JP2023010858W WO2023189814A1 WO 2023189814 A1 WO2023189814 A1 WO 2023189814A1 JP 2023010858 W JP2023010858 W JP 2023010858W WO 2023189814 A1 WO2023189814 A1 WO 2023189814A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizing film
film
polarizing
thickness
resin
Prior art date
Application number
PCT/JP2023/010858
Other languages
English (en)
French (fr)
Inventor
慎太朗 三木
勝則 高田
亮 菅野
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Publication of WO2023189814A1 publication Critical patent/WO2023189814A1/ja

Abstract

偏光膜と樹脂フィルムが、粘着剤層又は接着剤層を介さずに、直接、接合されており、前記偏光膜の厚さは、２０μｍ以下であり、かつ前記樹脂フィルムの厚さよりも薄い偏光フィルム。当該偏光フィルムは、カールを抑制できる。

Description

偏光フィルム、及び画像表示装置
　本発明は、偏光フィルム、及び画像表示装置に関する。
　従来、液晶表示装置や有機ＥＬ表示装置等の各種画像表示装置に用いる偏光膜としては、高透過率と高偏光度を兼ね備えていることから、染色処理された（ヨウ素や二色性染料等の二色性物質を含有する）ポリビニルアルコール系フィルムが用いられている。当該偏光膜は、ポリビニルアルコール系フィルムに、浴中にて、例えば、膨潤、染色、架橋、延伸等の各処理を施した後に、洗浄処理を施してから、乾燥することにより製造される。また前記偏光膜は、通常、その片面又は両面にトリアセチルセルロース等の透明保護フィルムが接着剤を用いて貼合された偏光フィルム（偏光板）として用いられている。
　また、上記の偏光フィルム（偏光板）としては、偏光膜と透明保護フィルムが、接着剤層又は粘着剤層を介さずに、直接、貼合されている偏光フィルムも知られている（特許文献１－４）。
国際公開第２００５／０８５９１８号 特開２００２－３０３７２５号公報 特開２００２－３０３７２６号公報 特開２００２－３０３７２７号公報
　偏光膜や偏光フィルムは、薄膜化の要望が強いが、上記のように、偏光膜と透明保護フィルムが接着剤層を介して貼り合わされている場合、接着剤層は接着剤の硬化時に応力が蓄積されやすく、偏光フィルムのカールの原因となる問題があった。また、特許文献１で具体的に開示されている製造方法で得られた偏光フィルムは、偏光膜と透明保護フィルムとの厚みの関係により、偏光フィルムのカールを招く恐れがあること、さらに、偏光膜と透明保護フィルムとの接着力が弱い問題があった。また、特許文献２－４で具体的に開示されている製造方法で得られた偏光フィルムは、１３５℃という高温での圧着工程を要するため、偏光フィルムのカールが生じる問題があった。
　以上のような事情に鑑み、本発明は、カールを抑制できる偏光フィルムを提供することを目的とする。
　また、本発明は、上記の偏光フィルムを有する画像表示装置を提供することを目的とする。
　すなわち、本発明は、偏光膜と樹脂フィルムが、接着剤層又は粘着剤層を介さずに、直接、接合されており、前記偏光膜の厚さは、２０μｍ以下であり、かつ前記樹脂フィルムの厚さよりも薄い偏光フィルムに関する。
　また、本発明は、前記偏光フィルムを有する画像表示装置に関する。
　本発明の偏光フィルムにおける効果の作用メカニズムの詳細は以下のように推定される。ただし、本発明は、この作用メカニズムに限定して解釈されない。
　本発明の偏光フィルムは、偏光膜と樹脂フィルムが、接着剤層又は粘着剤層を介さずに、直接、接合されており、前記偏光膜の厚さは、２０μｍ以下であり、かつ前記樹脂フィルムの厚さよりも薄いため、接着剤層の収縮による界面応力が抑制され、かつ偏光膜の収縮を樹脂フィルムで保持できる構成であることから、偏光フィルムのカールを抑制することができる。
　また、本発明の偏光フィルムは、偏光膜と透明保護フィルムとを、粘着剤層又は粘着剤層を介さずに、直接、接合できるため、粘着剤層又は接着剤層へのヨウ素等の二色性物質の拡散が抑えられることから、加湿信頼性にも優れる。
＜偏光フィルム＞
　本発明の偏光フィルムは、偏光膜と樹脂フィルムが、接着剤層又は粘着剤層を介さずに、直接、接合されており、前記偏光膜の厚さは、２０μｍ以下であり、かつ前記樹脂フィルムの厚さよりも薄い。
＜偏光膜＞
　前記偏光膜は、ポリビニルアルコール系フィルムにヨウ素や二色性染料等の二色性物質が吸着配向して形成される。前記偏光膜は、偏光膜の初期の偏光性能の観点から、前記二色性物質としてヨウ素を含む、ヨウ素系偏光膜が好ましい。
　前記ポリビニルアルコール（ＰＶＡ）系フィルムは、可視光領域において透光性を有し、ヨウ素や二色性染料等の二色性物質を分散吸着するものを特に制限なく使用できる。前記ポリビニルアルコール系フィルムの材料としては、ポリビニルアルコール又はその誘導体が挙げられる。前記ポリビニルアルコールの誘導体としては、例えば、ポリビニルホルマール、ポリビニルアセタール；エチレン、プロピレン等のオレフィン；アクリル酸、メタクリル酸、クロトン酸等の不飽和カルボン酸、及びそのアルキルエステル、アクリルアミド等で変性したもの等が挙げられる。前記ポリビニルアルコールは、平均重合度が１００～１０，０００程度であることが好ましく、１，０００～１０，０００程度であることがより好ましく、１，５００～４，５００程度であることがさらに好ましい。また、前記ポリビニルアルコールは、ケン化度が８０～１００モル％程度であることが好ましく、９５モル％～９９．９５モル程度であることがより好ましい。なお、前記平均重合度及び前記ケン化度は、ＪＩＳ　Ｋ　６７２６に準じて求めることができる。
　前記偏光膜は、従前の偏光膜の製造方法により得られ、例えば、前記ポリビニルアルコール系フィルムに、任意の膨潤工程及び洗浄工程と、少なくとも、染色工程、架橋工程、及び延伸工程を施して得られる。
　前記偏光膜は、偏光膜の初期の偏光度を向上させる観点から、厚みが１μｍ以上であることが好ましく、２μｍ以上であることがより好ましく、そして、パネルの反りを防止する観点から、１５μｍ以下であることが好ましく、１０μｍ以下であることがより好ましく、８μｍ以下であることがさらに好ましい。とくに、厚みが８μｍ程度以下の偏光膜を得るためには、前記ポリビニルアルコール系フィルムとして、熱可塑性樹脂基材上に製膜されたポリビニルアルコール系樹脂層を含む積層体を用いる、以下の薄型の偏光膜の製造方法が適用できる。
　偏光膜（薄型の偏光膜）は、従前の偏光膜の製造方法により得られ、例えば、長尺状の熱可塑性樹脂基材の片側に、ポリビニルアルコール系樹脂（ＰＶＡ系樹脂）を含むポリビニルアルコール系樹脂層（ＰＶＡ系樹脂層）を形成して積層体を準備する工程と、得られた積層体を長手方向に搬送しながら、前記積層体に、任意の不溶化処理工程、架橋処理工程、及び洗浄処理工程と、少なくとも、空中補助延伸処理工程、染色処理工程、及び水中延伸処理工程を施して得られる。
＜樹脂フィルム＞
　前記樹脂フィルムは、厚さが前記偏光膜の厚さよりも厚ければ、特に制限されず、例えば、偏光フィルムに用いられている透明保護フィルム、位相差フィルム等の有機基材等を用いることができる。
　前記偏光膜の厚さに対する前記樹脂フィルムの厚さの比（樹脂フィルムの厚さ／偏光膜の厚さ）は、カール抑制の観点から、１．２以上であることが好ましく、２．０以上であることがより好ましく、３．０以上であることがさらに好ましく、そして、厚み差が大きすぎることに起因する偏光板のカール・ひずみの観点から、２０．０以下であることが好ましく、１０．０以下であることがより好ましく、５．０以下であることがさらに好ましい。
　また、前記樹脂フィルムの厚さは、適宜に決定しうるが、一般には薄層性等の観点から、５００μｍ以下であることが好ましく、３００μｍ以下であることがより好ましく、１００μｍ以下であることがさらに好ましい。
　前記透明保護フィルムを構成する材料としては、例えば、セルロールエステル系樹脂、ポリカーボネート系樹脂、（メタ）アクリル系樹脂、環状ポリオレフィン系樹脂、ポリエステル系樹脂等が挙げられる。前記位相差フィルムとしては、例えば、高分子素材を一軸または二軸延伸処理してなる複屈折性フィルム、液晶ポリマーの配向フィルム、液晶ポリマーの配向層をフィルムにて支持したもの等が挙げられる。また、前記透明保護フィルムおよび前記位相差フィルムには、ハードコート層、反射防止層、スティッキング防止層、拡散層ないしアンチグレア層等の他の層；反射板や半透過板、位相差板（１／２や１／４等の波長板を含む）、視野角補償フィルム等の画像表示装置等の形成に用いられる光学層；が１層または２層以上設けられていてもよい。
　前記樹脂フィルムを、前記偏光膜の両面に貼り合わせる場合、その両面の樹脂フィルムは、同じものであってもよく、異なっていてもよい。
　前記樹脂フィルムには、紫外線吸収剤、酸化防止剤、滑剤、可塑剤、離型剤、着色防止剤、難燃剤、帯電防止剤、顔料、着色剤等の任意の適切な添加剤を含んでいてもよい。
＜偏光フィルムの製造方法＞
　前記偏光膜と前記樹脂フィルムを、接着剤層又は粘着剤層を介さずに、直接、接合する方法は、圧着する方法、紫外線、電子線等のエネルギー線を照射して貼合する方法等が挙げられ、とくに、偏光フィルムのカールを抑制し、接着性を高める観点から、前記樹脂フィルムと前記偏光膜のいずれか一方、又は両方の貼合面に紫外光を照射して表面処理をした後、揮発性媒体を介して貼合し、当該揮発性媒体を乾燥する方法が好ましい。前記揮発性媒体が存在することにより、貼合面に気泡等が入らずに密着でき、さらに、揮発性媒体を乾燥することにより、著しく接合面（界面）の接着力が高まる。紫外光としては、例えば、波長が２５０－１００ｎｍであることが好ましく、２００－１００ｎｍであることがより好ましく、なかでもキセノンエキシマランプ（エキシマＵＶ）を使用した１７２ｎｍの波長が、量産性の観点から特に好ましい。
　また、上記の紫外光は、照度が、処理能力の観点から、１ｍＷ／ｃｍ２以上であることが好ましく、５０ｍＷ／ｃｍ２以上であることがより好ましい。また、積算光量が、接着性の観点から、１ｍＪ／ｃｍ２以上であることが好ましく、５０ｍＪ／ｃｍ２以上であることがより好ましく、そして、フィルムへのダメージの観点から、５０００ｍＪ／ｃｍ２以下であることが好ましく、２０００ｍＪ／ｃｍ２以下であることがより好ましい。また、紫外光照射時における温度は、特に限定されず、表面改質の安定化の観点から、０～５０℃程度であることが好ましく、１０～４０度程度であることがより好ましく、偏光フィルムの生産上、室温であることが簡便である。また、紫外光照射時における雰囲気は、酸素濃度が２１％以下であればよく、処理効率の観点から、酸素濃度は７．０％以下が好ましい。
　前記揮発性媒体は、特に限定されず、乾燥効率の観点から、水、エタノール、トルエン、シクロヘキサン、アセトンなどの溶剤が好ましく、環境の観点から、水がより好ましい。
　前記加熱の温度は、前記揮発性媒体を適切に乾燥できればよく、例えば、前記揮発性媒体が水の場合、４０～８０℃程度であることが好ましく、５０～７０℃程度であることがより好ましい。また、前記乾燥の時間は、偏光膜の温度の影響を受けるため一概に決定できないが、１分～６０分間程度であることが好ましく、３～１５分間程度であることがより好ましい。前記乾燥工程は１回だけ実施されてもよく、必要に応じて複数回実施されてもよい。
　上記の貼合は、ロールラミネーターなどにより行うことができる。
　前記偏光膜と前記樹脂フィルムの接合界面は、貼合時の処理に由来する改質層や高弾性層があってもよい。
　前記偏光フィルムにおいて、前記樹脂フィルムと前記偏光膜との接着力（剥離強度）は、剥離角度９０°、剥離速度１０００ｍｍ／分の条件下の剥離強度測定で、０．５Ｎ／１５ｍｍ以上であることが好ましく、１．０Ｎ／１５ｍｍ以上であることがより好ましく、１．２Ｎ／１５ｍｍ以上であることがさらに好ましく、２．０Ｎ／１５ｍｍ以上であることがよりさらに好ましい。
　前記偏光フィルムは、画像表示装置に適用され得る。画像表示装置の代表例としては、液晶表示装置、有機エレクトロルミネセンス（ＥＬ）表示装置が挙げられる。画像表示装置は業界で周知の構成が採用されるので、詳細な説明は省略する。
　以下に実施例を挙げて本発明をさらに詳細に説明するが、本発明はこれらの実施例のみに限定されるものではない。
＜実施例１＞
＜偏光膜の作製＞
　非晶性ＰＥＴ基材に９μｍ厚のＰＶＡ層が製膜された積層体を延伸温度１３０℃の空中補助延伸によって延伸積層体を生成し、次に、延伸積層体を染色によって着色積層体を生成し、さらに着色積層体を延伸温度６５度のホウ酸水中延伸によって総延伸倍率が５．９４倍になるように非晶性ＰＥＴ基材と一体に延伸された５μｍ厚の偏光膜を含む光学フィルム積層体を生成した。このような２段延伸によって非晶性ＰＥＴ基材に製膜されたＰＶＡ層のＰＶＡ分子が高次に配向され、染色によって吸着されたヨウ素がポリヨウ素イオン錯体として一方向に高次に配向された厚さ５μｍの偏光膜を含む光学フィルム積層体を得た。
＜偏光フィルムの作製＞
　酸素濃度約２．５％の窒素置換雰囲気下において、上記で得られた偏光膜を含む光学フィルム積層体の偏光膜面、及び、樹脂フィルムとして、厚み１３μｍのシクロオレフィン系樹脂フィルム（日本ゼオン社製、ＺＦ１４）に、エキシマＵＶ処理装置（ウシオ電機株式会社製、ＳＶＣ３４２Ｓ－１Ｎ２－ＭＮ３－ＫＷＯ１、キセノンエキシマランプ）を用い、エキシマＵＶ光（波長１７２ｎｍ、ピーク照度７５ｍＷ／ｃｍ２、積算光量４５０ｍＪ／ｃｍ２）を照射し、表面改質を施した。続いて、各フィルムの表面改質面に水を塗布し、水が乾燥する前に、ラミネーターを用いて偏光膜と樹脂フィルムを貼り合わせた後、６０℃のオーブンで５分３０秒間乾燥させ、偏光膜と樹脂フィルムが直接接合した偏光フィルムを得た。
＜カールの評価＞
　上記の偏光膜と透明保護フィルムが直接接合した偏光フィルムのＰＥＴ基材を剥離した後、２３℃相対湿度５５％環境で７２時間調湿し、１００ｍｍ×１００ｍｍで切り出し、樹脂フィルムの面を上にしてフィルムの４隅それぞれの水平面からの高さを測定し、４点の平均値を、フィルムのカールとした。表では、カールが２ｍｍ未満のものを◎、２ｍｍ以上３ｍｍ未満のものを〇、３ｍｍ以上５ｍｍ未満のものを△、５ｍｍ以上のものを×で示している。
＜接着力（剥離強度）の評価＞
　上記の偏光膜と透明保護フィルムが直接接合した偏光フィルムのＰＥＴ基材を剥離し、剥離面に両面テープ（Ｎｏ．５００、日東電工社製）を貼り合わせた。さらに、偏光膜の延伸方向と平行に２００ｍｍ、直行方向に１５ｍｍの大きさに切り出し、偏光膜と透明保護フィルムとの間にカッターナイフで切り込みを入れた後、両面テープの剥離フィルムを剥がし、粘着剤面をガラス板に貼り合わせた。角度自在タイプ粘着・皮膜剥離解析装置（ＶＰＡ－２、協和界面化学社製）により、９０度方向に偏光膜と透明保護フィルムとを剥離速度１０００ｍｍ／ｍｉｎで剥離し、その剥離強度（Ｎ／１５ｍｍ）を測定した。
＜加湿信頼性の評価＞
　上記偏光フィルムのＰＥＴ基材を剥離した後、偏光膜側に粘着剤層（厚み２０μｍ）を介して、厚さ０．７ｍｍの無アルカリガラスの一方に貼り合わせた偏光フィルム（加湿耐久性試験評価用サンプル）を準備した。得られた偏光フィルムの透過率Ｔｓについて、紫外可視分光光度計（日本分光社製Ｖ－７１００）を用いて測定し、単体透過率Ｔｓ、平行透過率Ｔｐ、直交透過率Ｔｃをそれぞれ、偏光フィルムのＴｓ、ＴｐおよびＴｃとした。これらのＴｓ、ＴｐおよびＴｃは、ＪＩＳ　Ｚ８７０１の２度視野（Ｃ光源）により測定して視感度補正を行なったＹ値である。６０℃９５％ＲＨの環境下に１２０時間曝露し、投入後の偏光フィルムについても同様の方法で透過率Ｔｓを測定し、透過率変化ΔＴ（％）＝｜（投入前の透過率Ｔｓ（％））－（投入後の透過率Ｔｓ（％））｜を求めた。透過率変化ΔＴ（％）が小さいほど、湿熱環境下での耐久性に優れると判断した。ΔＴ（％）は、好ましくは、０．４以下であり、より好ましくは、０．３以下である。
＜実施例２＞
　樹脂フィルムとして、厚み２３μｍのシクロオレフィン系樹脂フィルム（日本ゼオン社製、ＺＦ１２）を用いたこと以外は、実施例１と同様の操作にて、偏光膜と樹脂フィルムが直接接合した偏光フィルムを得た。
＜実施例３＞
＜偏光膜の作製＞
　平均重合度２４００、ケン化度９９．９モル％の厚み４５μｍのポリビニルアルコールフィルムを、３０℃の温水中に６０秒間浸漬し膨潤させた。次いで、ヨウ素／ヨウ化カリウム（重量比＝１／７）の濃度０．３％の水溶液に浸漬し、２．６倍まで延伸させながらフィルムを染色した。その後、６５℃の４重量％ホウ酸水溶液中で、トータルの延伸倍率が６倍となるように延伸を行った。延伸後に、５５℃のオーブンにて１分間乾燥を行い、ＰＶＡ系偏光膜を得た。この偏光膜の厚さは１８μｍ、水分率は１５重量％であった。
＜偏光フィルムの作製＞
　上記で得られた偏光膜を用い、実施例２と同様の操作にて、偏光膜と樹脂フィルムが直接接合した偏光フィルムを得た。
＜比較例１＞
　樹脂フィルムとして、厚み１３μｍのシクロオレフィン系樹脂フィルム（日本ゼオン社製、ＺＦ１４）に、下記の活性エネルギー線硬化型接着剤をバーコーターで塗布し、ラミネーターを用いて、実施例１で得られた厚さ５μｍの偏光膜を含む光学フィルム積層体の偏光膜面と貼り合わせた。その状態で樹脂フィルム側から、活性エネルギー線照射を行い、接着剤を硬化させ、偏光膜に樹脂フィルムが活性エネルギー線接着剤を介して接合している偏光フィルムを得た。
［活性エネルギー線硬化型接着剤］
　２－ヒドロキシエチルアクリルアミド（ＫＪケミカルズ社製、商品名：ＨＥＡＡ）１６．５重量部、４－ビニルフェニルボロン酸（東京化成工業社製）１重量部、２－ヒドロキシ－３－フェノキシプロピルアクリレート（東亞合成社製、商品名：アロニックスＭ－５７００）３０．５重量部、１，９－ノナンジオールジアクリレート（共栄社化学社製、商品名：ライトアクリレート１，９ＮＤ－Ａ）２５重量部、ヒドロキシピバリン酸ジアクリレート（共栄社化学社製、商品名：ライトアクリレートＨＰＰ－Ａ）１３重量部、（メタ）アクリレートを重合してなるオリゴマー（東亞合成社製、商品名：ＡＲＦＯＮ　ＵＰ－１１９０）１５重量部、２－メチル－１－［４－（メチルチオ）フェニル］－２－モルフォニルプロパン－１－オン（ＩＧＭ　ｒｅｓｉｎｓ社製、商品名：Ｏｍｎｉｒａｄ　９０７）３重量部、２，４－ジエチルチオキサントン（日本化薬社製、商品名：ＫＡＹＡＣＵＲＥ－ＤＥＴＸ－Ｓ）３重量部
［活性エネルギー線］
　活性エネルギー線として、可視光線（ガリウム封入メタルハライドランプ）　照射装置：Ｈｅｒａｅｕｓ社製Ｌｉｇｈｔ　ＨＡＭＭＥＲ１０　バルブ：Ｖバルブ　ピーク照度：８００ｍＷ／ｃｍ２、積算照射量８００／ｍＪ／ｃｍ２（波長３８０～４４０ｎｍ）を使用した。なお、可視光線の照度は、Ｓｏｌａｔｅｌｌ社製Ｓｏｌａ－Ｃｈｅｃｋシステムを使用して測定した。
＜比較例２＞
　３０μｍの偏光膜（ポリビニルアルコール系フィルム）の片面に、厚み４０μｍのシクロオレフィン系樹脂フィルム（日本ゼオン社製、ＺＦ１４）、１４５℃の温度にてロールラミネーターを用いて圧着して積層し、偏光膜と樹脂フィルムが直接接合された偏光フィルムを得た。
　上記の各実施例及び比較例で得た偏光フィルムを用い、実施例１と同様の評価を行った。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000001

Claims (3)

  1. 　偏光膜と樹脂フィルムが、粘着剤層又は接着剤層を介さずに、直接、接合されており、
    　前記偏光膜の厚さは、２０μｍ以下であり、かつ前記樹脂フィルムの厚さよりも薄いことを特徴とする偏光フィルム。
  2. 　前記偏光膜の厚さに対する前記樹脂フィルムの厚さの比（樹脂フィルムの厚さ／偏光膜の厚さ）が１．２～１０．０であることを特徴とする請求項１に記載の偏光フィルム。
  3. 　請求項１又は２に記載の偏光フィルムを有することを特徴とする画像表示装置。
PCT/JP2023/010858 2022-03-30 2023-03-20 偏光フィルム、及び画像表示装置 WO2023189814A1 (ja)